Search Results (4)

Natural bone is a complex material that has been carefully designed. To prepare a successful bone substitute, two challenging conditions need to be met: biocompatible and bioactive materials for cell proliferation and differentiation, and appropriate mechanical stability after implantation. Therefore, a hybrid Poly ε-caprolactone/Poly(lactic-co-glycolide)/β-tricalcium phosphate (PCL/PLGA/β-TCP) scaffold has been introduced as a suitable composition that satisfies the above two conditions. The blended PCL and PLGA can improve the scaffold’s mechanical properties and biocompatibility compared to single PCL or PLGA scaffolds. In addition, the incorporated β-TCP increases the mechanical strength and osteogenic potential of PCL/PLGA scaffolds, while the polymer improves the mechanical stability of ceramic scaffolds. The PCL/PLGA/β-TCP scaffold is designed using spiral structures to provide a much better transport system through the gaps between spiral walls than conventional cylindrical scaffolds. Human fetal osteoblasts (hFOBs) were cultured on spiral PCL/PLGA/β-TCP (PPBS), cylindrical PCL/PLGA/β-TCP (PPBC), and cylindrical PCL scaffolds for a total of 28 days. The cell proliferation, viability, and osteogenic differentiation capabilities were analyzed. Compared with PCL and PPBC scaffolds, the PPBS scaffold exhibits great biocompatibility and potential to stimulate cell proliferation and differentiation and, therefore, can serve as a bone substitute for bone tissue regeneration. Full article

Preventive and regenerative techniques have been suggested to minimize the aesthetic and functional effects caused by intraoral bone defects, enabling the installation of dental implants. Among them, porous three-dimensional structures (scaffolds) composed mainly of bioabsorbable ceramics, such as hydroxyapatite (HAp) and β-tricalcium phosphate (β-TCP) stand out for reducing the use of autogenous, homogeneous, and xenogenous bone grafts and their unwanted effects. In order to stimulate bone formation, biodegradable polymers such as cellulose, collagen, glycosaminoglycans, polylactic acid (PLA), polyvinyl alcohol (PVA), poly-ε-caprolactone (PCL), polyglycolic acid (PGA), polyhydroxylbutyrate (PHB), polypropylenofumarate (PPF), polylactic-co-glycolic acid (PLGA), and poly L-co-D, L lactic acid (PLDLA) have also been studied. More recently, hybrid scaffolds can combine the tunable macro/microporosity and osteoinductive properties of ceramic materials with the chemical/physical properties of biodegradable polymers. Various methods are suggested for the manufacture of scaffolds with adequate porosity, such as conventional and additive manufacturing techniques and, more recently, 3D and 4D printing. The purpose of this manuscript is to review features concerning biomaterials, scaffolds macro and microstructure, fabrication techniques, as well as the potential interaction of the scaffolds with the human body. Full article

The purpose of this study was to compare bone regeneration and space maintaining ability of three-dimensional (3D) printed bone grafts with conventional biphasic calcium phosphate (BCP). After mixing polycaprolactone (PCL), poly (lactic-co-glycolic acid) (PLGA), and β-tricalcium phosphate (β-TCP) in a 4:4:2 ratio, PCL/PLGA/β-TCP particulate bone grafts were fabricated using 3D printing technology. Fabricated particulate bone grafts were mixed with atelocollagen to produce collagen-based PCL/PLGA/β-TCP composite block bone grafts. After formation of calvarial defects 8 mm in diameter, PCL/PLGA/β-TCP composite block bone grafts and BCP were implanted into bone defects of 32 rats. Although PCL/PLGA/β-TCP composite block bone grafts were not superior in bone regeneration ability compared to BCP, the results showed relatively similar performance. Furthermore, PCL/PLGA/β-TCP composite block bone grafts showed better ability to maintain bone defects and to support barrier membranes than BCP. Therefore, within the limitations of this study, PCL/PLGA/β-TCP composite block bone grafts could be considered as an alternative to synthetic bone grafts available for clinical use. Full article

This study was conducted to evaluate the effects of a 3D-printed resorbable polycaprolactone/poly(lactic-co-glycolic acid)/β-tricalcium phosphate (PCL/PLGA/β-TCP) membrane on bone regeneration and osseointegration in areas surrounding implants and to compare results with those of a non-resorbable titanium mesh membrane. After preparation of PCL/PLGA/β-TCP membranes using extrusion-based 3D printing technology; mechanical tensile testing and in vitro cell proliferation testing were performed. Implant surgery and guided bone regeneration were performed randomly in three groups (a no membrane group, a titanium membrane group, and a PCL/PLGA/β-TCP membrane group (n = 8 per group)). Histological and histometric analyses were conducted to evaluate effects on bone regeneration and osseointegration. Using the results of mechanical testing; a PCL/PLGA/β-TCP ratio of 2:6:2 was selected. The new bone areas (%) in buccal defects around implants were highest in the PCL/PLGA/β-TCP group and significantly higher than in the control group (p < 0.05). Bone-to-implant contact ratios (%) were also significantly higher in the PCL/PLGA/β-TCP and titanium groups than in the control group (p < 0.05). When the guided bone regeneration procedure was performed using the PCL/PLGA/β-TCP membrane; new bone formation around the implant and osseointegration were not inferior to those of the non-resorbable pre-formed titanium mesh membrane. Full article