1.​ “Reheating” of a metal is the application of heat, b.

​ A dull finish due to the topcoat 'sinking in'

usually to remove to primer that is still too soft

a.​ Extreme hardness and brittleness c.​ Corrosion

b.​ Carbon content d.​ Reflection of ultraviolet from the fabric

c.​ Cracks, voids, and cold shuts 8.​ The replacement of a damaged vertical stabilizer
with a new identical stabilizer purchased from the
d.​ The effects of heat treatment aircraft manufacturer is considered a _____.

2.​ What is the usual cause of runs and sags in a.​ major alteration
aircraft finishes?
b.​ minor alteration
a.​ Low atmospheric humidity
c.​ major repair
b.​ Material is being applied too fast
d.​ minor repair
c.​ Material is being applied too slow
9.​ Impact resistance measures the material's _____.
d.​ Too much material applied in one coat
a.​ Toughness
3.​ The most important consideration when selecting
welding rod is ______. b.​ Hardness

a.​ ambient conditions c.​ Fusibility

b.​ amount of acetylene d.​ ductility

c.​ flame temperature 10.​ Which heat-treating operation would be performed

when the surface of the metal is changed
d.​ material compatibility chemically by introducing a high carbide or nitride
content?
4.​ An aircraft had an empty weight of 2886 lb with a
moment of 101,673.78 lb-in before several a.​ Tempering
alterations were made. The alterations include:
removing two passenger seat (45lb) at +69”; b.​ Case hardening
installing a cabinet (97lb) at +71”; installing a seat
and safety belt (30lb) +71”; installing a new radio c.​ Normalizing
equipment (45lb) at +94”. The alterations caused
the new empty weight to move ______ d.​ Welding

a.​ 36.6 in aft of the original empty CG 11.​ How should a welding torch flame be adjusted to
weld stainless steel?
b.​ 2.81 in aft of the original empty CG
a.​ Slightly carburizing
c.​ 1.88 in aft of the original empty CG
b.​ Slightly oxidizing
d.​ 1.40 in aft of the original empty CG
c.​ Neutral
5.​ It is the test for material hardness in which a
hardened steel ball one centimeter in diameter is d.​ Welding stainless steel is not acceptable
pressed under a known pressure into a flat surface for aircrafts.
of the test specimen.
12.​ Refer to weight of an item multiply by its arm
a.​ Moh
a.​ Moment
b.​ Tig
b.​ Vertical axis
c.​ Brinell
c.​ Reference datum
d.​ Hooke
d.​ arm
6.​ In cases of elongated boltholes in a wood spar or
cracks in the vicinity of boltholes, 13.​ A squib, as used in a fire-protection system, is a
_____.
a.​ a new section of spar should be spliced in
or the spar replaced entirely. a.​ device for causing the fire-extinguishing
agent to be released
b.​ the spar may be reinforced by using
hardwood reinforcing plates. b.​ probe used for installing frangible disks in
extinguisher bottles
c.​ it is permissible to ream the hole, plug with
hardwood, and redrill. c.​ temperature-sensing device

d.​ redrill the bolt hole and file to smoothen d.​ wizard-born muggle
the edges.
14.​ In Gas Tungsten Arc welding, a stream of inert gas
7.​ What is likely to occur if hydrated wash primer is is used to _____.
applied to unpainted aluminum and then about 30
a.​ attract oxygen to the puddle of molten
to 40 minutes later a finish topcoat, when the
metal
humidity is low?

a.​ A glossy, blush-free finish

 b.​ concentrate the heat of the arc and 21.​ The side clearances of piston rings are measured
prevent its dissipation with a

c.​ lower the temperature required to properly a.​ Dial gauge

fuse the metal
b.​ Micrometer caliper gauge
d.​ prevent the formation of oxides in the
puddle c.​ Thickness gauge

15.​ What is the color of an AN fitting? d.​ Protractor

a.​ Black 22.​ A category of plastic material that is capable of

softening or flowing when reheated is described as
b.​ Brown a

c.​ Red a.​ Thermocure

d.​ Yellow b.​ Thermoplastic

16.​ Why is steel tempered after being hardened? c.​ Thermoset

a.​ To increase its hardness and ductility d.​ Thermoflow

b.​ To increase its strength and decrease its 23.​ How are pressure hoses categorized
internal stresses.
a.​ According to the outer diameter
c.​ To relieve its internal stresses and
increase its brittleness. b.​ According to the inner diameter

d.​ To relieve its internal stresses and reduce c.​ According to the maximum applied
its brittleness. pressure

17.​ The part of the aircraft which receives or encloses d.​ According to the maximum allowable load
the landing gear as it retracts?
24.​ Why is Nickel Chromium used in many exhaust
a.​ Wheel fairing systems

b.​ Wheel well a.​ Lightweight and flexible

c.​ Wheel bay b.​ Corrosion-resistant and low-heat

conductivity
d.​ Engine pod
c.​ Corrosion-resistant and high-heat
18.​ The shear strength of an AN470DD-6-8: rivet, conductivity
immediately after driving is approximately 75
percent of its ultimate shear strength. The d.​ Corrosion-resistant and low expansion
remaining 25 percent is obtained by coefficient

a.​ Standing at ordinary room temperature for 25.​ If a material is forced to be the tertiary phase of
about 4 days (age harden) creep, it _______.

b.​ Chilling the riveted unit for an hour a.​ Should be stop drilled and be
condition-monitored
c.​ Shear loads imposed on the riveted
assembly in use b.​ Should undergo dye penetrant inspection
for evaluation
d.​ Heating the unit in which the rivet was
used to 960F, holding for 3 hours, and c.​ Should be replaced immediately
allowing the unit to cool slowly until room
temperature is recovered. d.​ Is still safe to be used

19.​ What is the allowable manufacturing tolerance for 26.​ At what temperature should steel be tempered
a bushing where the outside dimensions shown on
the blueprint are 1.0625 + 0.0025, - 0.0003? a.​ Above annealing temperature

a.​ 0.0025 b.​ At annealing temperature

b.​ 0.0028 c.​ Below annealing temperature

c.​ 1.0650 d.​ 1.5 times the “annealing temperature”

d.​ 1.0647

20.​ In what direction/s are composite fabric materials

considered to be strongest?
27.​ What does an “X” on a cable indicates
a.​ All
a.​ AC power
b.​ Bias
b.​ Auxiliary power
c.​ Weft
c.​ Control system
d.​ Warp
d.​ Close-tolerance structure
28.​ Normalizing is a process of heat treating 35.​ Joggles in removed rivet shanks would indicate
partial
a.​ Non-ferrous metals aside from aluminum
a.​ Bearing Failure
b.​ Aluminum alloys only
b.​ Shear Failure
c.​ Ferrous metals only
c.​ Tear Failure
d.​ Both ferrous and non-ferrous metals
d.​ Tension Failure
29.​ When an aircraft is being weighted, the brakes
should be: 36.​ The means by which FAA notifies aircraft owners
and other interested persons of unsafe conditions
a.​ Full on and prescribes conditions under which product
may still operate
b.​ Set to park
a.​ Airworthiness Directives
c.​ Set just enough to retard any tendency of
the aircraft to move b.​ Aviation Safety Data

d.​ Full off and wheel chocks should be used c.​ Airworthiness Alert
30.​ When preparing an aircraft for weighing, which of d.​ Airworthiness Alert and Aviation Safety
the following should be filled unless otherwise Data
noted in the aircraft specification or manufacturer’s
instruction 37.​ Alclad is a metal consisting of

a.​ Lavatory tanks a.​ aluminum alloy surface layers and a pure
aluminum core.
b.​ Potable water container
b.​ pure aluminum surface layers on an
c.​ Hydraulic reservoir aluminum layer core.

d.​ Fluid reservoir for injection in the engines c.​ a homogenous mixture of pure aluminum
and aluminum alloy.
31.​ Plasticized lacquer applied to fabric coated aircraft
d.​ a homogenous mixture of pure aluminium
a.​ Matrix and a pure aluminum core
b.​ Plastic Dope 38.​ In rotorcraft external-loading, the ideal location of
the cargo release is where the line of action
c.​ Epoxy Resins passes
d.​ All of the above a.​ aft of the center of gravity at all times.
32.​ Alloy 2117 rivet are heat treated b.​ forward of the center of gravity at all times.
a.​ Heated to 490 deg C to 500 deg C and c.​ through the center of gravity at all times
quenched in cold water
d.​ answer a and b are correct
b.​ By manufacturer but require heat
treatment before being driven 39.​ Alloy cool at room temperature
c.​ By manufacturer but do not require heat a.​ Idk
treatment before being driven
b.​ Idk
d.​ Heated to 500 deg C to 510 deg C and
quenched in cold water c.​ Idk
33.​ Aircraft was not approved for RTS after annual d.​ Idk
inspection and owner wanted to fly to another
maintenance base 40.​ Provide shim when needed at a mouth laid bearing
surfaces and ????? of castle nut
a.​ Owner must obtain special flight permit
a.​ Bolt
b.​ Aircraft becomes restricted category type
until approved for RTS b.​ Sealant

c.​ May be flown up to 10 hours to reach c.​ Rivet

another maintenance base
d.​ Washers
d.​ Owner should obtain special flight permit

34.​ When locating FS 150

a.​ 150 inches aft of buttock line

b.​ 150 inches aft of zero or fixed reference

line

c.​ 150 centimeters aft of nose

d.​ 150 inches forward of empennage