    Domex 700 MC is a cold forming steel that is thermo-mechanically rolled to carefully control its heating, rolling, and cooling processes. It has a precise chemical composition including low carbon and manganese with additions like niobium that give it a clean structure and make it competitive for cold forming and welding applications. It has a minimum yield strength of 700 MPa and can be used in applications like truck chassis and cranes to reduce weight and increase payload.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    421 - Domex 700 MC

    Uploaded by

    lalamed21
    255 views2 pages
    Domex 700 MC is a cold forming steel that is thermo-mechanically rolled to carefully control its heating, rolling, and cooling processes. It has a precise chemical composition including low carbon and manganese with additions like niobium that give it a clean structure and make it competitive for cold forming and welding applications. It has a minimum yield strength of 700 MPa and can be used in applications like truck chassis and cranes to reduce weight and increase payload.

    Original Title

    421_Domex 700 MC

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Domex 700 MC is a cold forming steel that is thermo-mechanically rolled to carefully control its heating, rolling, and cooling processes. It has a precise chemical composition including low carbon and manganese with additions like niobium that give it a clean structure and make it competitive for cold forming and welding applications. It has a minimum yield strength of 700 MPa and can be used in applications like truck chassis and cranes to reduce weight and increase payload.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    255 views2 pages

    421 - Domex 700 MC

    Uploaded by

    lalamed21
    Domex 700 MC is a cold forming steel that is thermo-mechanically rolled to carefully control its heating, rolling, and cooling processes. It has a precise chemical composition including low carbon and manganese with additions like niobium that give it a clean structure and make it competitive for cold forming and welding applications. It has a minimum yield strength of 700 MPa and can be used in applications like truck chassis and cranes to reduce weight and increase payload.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Domex 700 MC Hot rolled, extra high strength, cold forming steel

    Page 1/2

    DATA SHEET: 11-02-03 GB8421 DOMEX

    PRODUCT
    Domex cold forming steels are thermo-mechanically rolled in modern plants where the heating, rolling and cooling processes are carefully controlled. The chemical analysis, consisting of low levels of carbon and manganese has precise addition of grain refiners such as niobium, titanium or vanadium. This together with a clean structure, makes Domex Steels the most competitive alternative for cold formed and welded products. Domex 700 MC with designation D and E meet and exceed the demands for steel S700MC in EN-10149-2. APPLICATION The extra high strength steel grades are used in applications such as truck chassis, cranes and earthmoving machines. In these applications, the high strength of the steels is used to save weight and/or to increase the payload. As a result of this and the good formability of the steels, the total costs can be reduced.

    MECHANICAL PROPERTIES
    Yield strength ReH N/mm2 min 700*) Tensile strength Rm N/mm2 min - max 750 - 950 Elongation on failure < 3 mm A80% min 10 > 3 mm A5 % min 12

    *) For thicknesses > 8 mm, the minimum yield strength may be 20 N/mm2 lower.

    DIMENSION RANGE Domex 700 MC is available in the range of sizes tabulated below in as rolled or pickled condition with mill edge. For material with trimmed edges, the width is reduced by 35 mm. Some exceptions may occur.
    Thickness (mm) 2.00 - (3.00) 3.00 - (4,00) 4.00 - (5,00) 5.00 - (6,00) 6.00 - (7,00) 7.00 - 10,00 Width (mm) 1000 - 1035 885 - 1300 885 - 1400 885 - 1600 885 - 1550 885 - 1300 Length (mm) 1500 - 13000 1500 - 13000 1500 - 13000 1500 - 13000 1500 - 13000 1500 - 13000

    IMPACT STRENGTH

    The Charpy V-notch test is carried out according to EN 10045-1.


    Designation B D E Test temperature Energy level

    Not impact tested - 20 C - 40 C 40J 27J

    1) Other test temperatures and impact strengths are available subject to special agreement.

    BENDABILITY
    Nominal sheet thickness, t <3 mm Min. recommended bending radius (<90) 0.8 xt 3 mm <t <6 mm 1.2 xt >6 mm 1.6 xt

    www.ssab.com

    Domex 700 MC Hot rolled, extra high strength, cold forming steel
    Page 2/2

    DATA SHEET: 11-02-03 GB8421 DOMEX

    WELDING The low contents of carbon, phosphorus and sulphur enable all conventional welding methods to be readily used for Domex 700 MC. No preheating is necessary. A narrow heat affected zone with a somewhat lower hardness is formed immediately adjacent to the weld. However, if normal welding parameters and methods are used, the heat affected zone is of no practical significance. Tensile test pieces taken across the weld can meet the same minimum tesile strength requirements as the base metal. CHEMICAL COMPOSITION
    C% max 0.12 Si % max 0.101) Mn % max 2.10 P% max 0.025 S% max 0.010 Al % min 0.015 Nb % max 0.092) V% max

    There are a large number of matching or over matching filler metals that can be used for welding of Domex 700 MC, which gives a weld that can meet the same minimum tensile strength requirements as the base metal. Some examplesof different filler metals that can be used are tabulated below. HEAT TREATMENT Stress relief annealing should be carried out within the temperature range of 530 - 580 C. Heat treatment above this range, e.g. normalizing and hot forming, reduces the strength and should be avoided.

    Ti % max 0.152)

    0.202)

    1) If the material is to be hot-dip galvanized, thies must be specified in the order. 2) Sum of Nb, V and Ti = 0,22% max.

    EXAMPLES OF DIFFERENT MATCHING AND OVER MATCHING FILLER METALS


    MMA Cored electrode OK 75.75 Filarc 118 Maxeta 110 TENACITO 75 OK Tubrod 14.03 Elgacore M690 Fluxofil 42 GMAW Wire electrode OK AristoRod 13.29 OK AristoRod 69 Carbofil NiMoCr ESAB ESAB ESAB ELGA Oerlikon Manufacturer

    The particulars in this data sheet are correct at the time of going to print and are intended to give general guidance for the use of the product. Subject to changes arising from continual product development. The information and data must not be regarded as guaranteed values, unless specially confirmed in writing.

    TECHNICAL SERVICE AND INFORMATION Knowledge Service Center will be pleased to assist with additional information concerning this product and other products from SSAB.