Resin composition

Abstract
JP2000327847A
PROBLEM TO BE SOLVED: To obtain a resin composition having good moldability and being capable
Japan
of giving a product having a sufficiently practicable heat resistance, solvent resistance, low oxygen
permeability, low moisture permeability, transparency, suitable degradability, and high mechanical
strengths by mixing an aliphatic-ester-structure-containing polymer with a polyolefin. SOLUTION: Find Prior Art Similar
The aliphatic-ester-structure-containing polymer is particularly desirably an aliphatic polyester
carbonate. This is one obtained by reacting an aliphatic polyester oligomer obtained by reacting an Other languages: Japanese
aliphatic dibasic acid and/or its derivative with an aliphatic dihydroxy compound and/or a
Inventor: Atsushi Hirashima, Maki Ito, Mitsuru Nakamura, Kyohei
hydroxycarboxylic acid compound and having a number-average molecular weight of at most 10,000
Takakuwa, 充 中村, 真樹 伊藤, 敦 平島, 恭平 高桑
with a carbonate compound and having a carbonate unit content of at least 5 mol%, a weight-
average molecular weight of at least 100,000, and a melting point of 70-180 deg.C. It is desirable
that the composition comprises 5-95 wt.% aliphatic-ester-structure-containing polymer and 95-5 Worldwide applications
wt.% polyolefin.
1999 JP

Application JP11135682A events

1999-05-17 Application filed by Mitsubishi Gas Chem Co Inc,

三菱瓦斯化学株式会社

1999-05-17 Priority to JP11135682A

2000-11-28 Publication of JP2000327847A

Status Pending

Info: Cited by (9), Legal events, Similar documents, Priority and

Related Applications

External links: Espacenet, Global Dossier, Discuss

Claims (7) Hide Dependent

[Claims]

1. 1. A resin composition comprising a polymer having an aliphatic ester structure and a polyolefin.

2. 2. A polymer having an aliphatic ester structure of 5 to 9

The resin composition according to claim 1, wherein 5% by weight and the polyolefin are 95 to 5% by weight.

3. 3. The resin composition according to claim 1, wherein the polymer having an aliphatic ester structure is an aliphatic polyester carbonate and / or an aliphatic
polyester.

4. 4. An aliphatic polyester carbonate having a number average molecular weight of 10,000 or less obtained by reacting an aliphatic dibasic acid and / or a derivative
thereof with an aliphatic dihydroxy compound and / or a hydroxycarboxylic acid compound. An aliphatic polyester carbonate obtained by reacting an aliphatic
polyester oligomer with a carbonate compound, having a carbonate unit content of 5 mol% or more, a weight average molecular weight of 100,000 or more, a

temperature of 190 ° C, and a melt viscosity at a load of 60 kg. 2,000 to 50,000

The resin composition according to claim 3, wherein the resin composition has 0 poise and a melting point of 70 to 180 ° C.

5. 5. The polyolefin is selected from the group consisting of polyethylene, polypropylene, polyvinyl chloride, polyvinyl alcohol, polystyrene, PMMA and ABS resin.
The resin composition according to claim 1, wherein the resin composition is a single species, a mixture of two or more species, or a copolymer of two or more
species.

6. 6. A heat deformation temperature of 60 ° C. or more and a tensile elongation of 50 ° C.

% Or more, tensile strength is 20 MPa or more, and oxygen permeability is 20
0cc ・ mm / m 2・ day or less, moisture permeability coefficient is 20gmm / m 2・ day
The resin composition according to claim 1, wherein the resin composition has a haze of 50 or less.

7. 7. A molded article comprising the resin composition according to claim 1.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a resin composition comprising a polymer having an aliphatic ester structure and a polyolefin, and a molded article thereof.

[0002]

2. Description of the Related Art In recent years, there has been a demand for the development of a polymer material that can disintegrate in a natural environment in
response to environmental problems on a global scale. Plastics that have collapsed into the future have great expectations as environmentally compatible materials and
new types of functional materials.

https://patents.google.com/patent/JP2000327847A/en 1/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
It has been well known that polymers having an aliphatic ester structure have biodegradability, and poly-3-hydroxybutyrate (PHB) produced by microorganisms and poly
(polymer) which is a synthetic polymer have been known. Caprolactone (P
CL), polybutylene succinate (PBS) containing succinic acid and butanediol as main components, and polylactic acid (PLLA) using L-lactic acid produced by fermentation
as a raw material. Further, the present inventors have disclosed in
JP-A-5-3693 and JP-A-7-53695 have developed a biodegradable polyester carbonate having high thermal stability, excellent fluidity and moldability, and sufficient
mechanical strength, and a method for producing the same.

[0004] Except for polylactic acid, polymers having an aliphatic ester structure are generally polymers having properties similar to polyethylene and having good
moldability and biodegradability. However, in the field where high moisture permeability is required and low moisture permeability such as a film and a bottle is required,
there is no sufficient ability and the improvement has been desired. In addition, the rate of decomposition by microorganisms is high, and particularly in the case of a thin
film, the decomposition may be too fast. Furthermore, since it is a relatively expensive material, its cost reduction is desired.

On the other hand, polyolefins are general-purpose polymers having a long history, and are mainly derived from petroleum feedstocks.
Excellent physical properties and inexpensive. However, it is considered as a material that does not decompose in the natural environment and has a high environmental
load. It has also been pointed out that the incinerator may be damaged when the combustion heat is high. Therefore, there has been a demand for an improvement that
suppresses combustion heat by disintegrating in the environment. In addition, the oxygen permeability is high, and it is pointed out that it is necessary to improve the
oxygen permeability in packaging applications. Attempts to impart biodegradability to polyolefins to suppress heat of combustion have been studied for a long time by
blending with starch, etc., but with degradation of quality in the manufacturing process, microbial degradation is not uniform and does not degrade. Many remain, and
damage to aquatic animals has been reported. In addition, the deterioration of physical properties due to starch was unavoidable and was not satisfactory. Further, in
order to reduce the oxygen transmission rate, it is possible to cope with the deposition of aluminum or silicon, but the cost is high.

As described above, existing plastics have their respective features, but have many insufficient parts. Therefore, it is desired to develop a plastic having a good balance of
strength, disintegration, moisture permeability, oxygen permeability and cost. I was

[0007]

SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems in the prior art, have a practically sufficient heat resistance
temperature, moldability, solvent resistance, low oxygen permeability,
An object of the present invention is to provide a resin composition and a molded product thereof having low moisture permeability, transparency, moderate
disintegration, and high mechanical strength.

[0008]

Means for Solving the Problems As a result of intensive studies to solve the above problems, the present inventors have found that a polyolefin having high heat
resistance and mechanical strength, a low moisture permeability coefficient,
By mixing with a polymer having an aliphatic ester structure having high hydrolysis resistance and biodegradability and low oxygen permeability, it has sufficient
mechanical strength for practical use, moldability,
Shows heat resistance, solvent resistance, low moisture permeability coefficient and oxygen permeability,
It has been found that a resin composition that can be disintegrated by a microorganism without breaking its original form can be obtained. Among them, the aliphatic
polyester carbonate has high compatibility with the polyolefin, and exhibits sufficient biodegradability by lowering the crystallinity of the polyolefin in the obtained resin
composition,
The present inventors have found that a resin composition having excellent mechanical properties and a low moisture permeability coefficient and a low oxygen
permeability can be obtained, which has led to the present invention.

That is, the present invention relates to a resin composition comprising a polymer having an aliphatic ester structure and a polyolefin, and a molded article thereof. More
specifically, in the resin composition comprising a polymer having an aliphatic ester structure and a polyolefin, the polymer having an aliphatic ester structure is an
aliphatic polyester carbonate and / or an aliphatic polyester. The content of the polymer having an aliphatic ester structure in the resin composition is 5 to 95% by weight,
and the content of the polyolefin is 95 to 5% by weight. Further, the heat deformation temperature is 60 degrees or more, the tensile elongation is 50% or more, the tensile
strength is 20 MPa or more, the oxygen permeability is 200 cc · mm / m 2 · day or less, the moisture permeability is 20 gmm / m 2 · day or less and Haze is 50 or less.

[0010]

BEST MODE FOR CARRYING OUT THE INVENTION The polymer having an aliphatic ester structure in the present invention includes poly-3-hydroxybutyrate (PHB),
polycaprolactone (PCL), polybutylene succinate containing succinic acid and butanediol as main components. (Lactic acid) (PBS) or polybutylene succinate adipate,
polylactic acid (PL
Examples thereof include aliphatic polyesters such as LA) and aliphatic polyester carbonates. Among them, aliphatic polyester carbonate is particularly preferred.

In the present invention, the aliphatic polyester carbonate means an aliphatic dibasic acid and / or a derivative thereof,
A number average molecular weight of 10, obtained by reacting an aliphatic dihydroxy compound and / or a hydroxycarboxylic acid compound;
A carbonate unit content obtained by reacting an aliphatic polyester oligomer having a molecular weight of not more than 000 with a carbonate compound, at least 5
mol% or more, a weight average molecular weight of at least 100,000, a melt viscosity at a temperature of 190 ° C. and a load of 60 kg. Is 2,000-50,000
It is characterized by a poise and a melting point of 70 to 180 ° C.

The process for producing an aliphatic polyester carbonate according to the present invention comprises a first step of obtaining an aliphatic polyester oligomer from an
aliphatic dibasic acid and / or a derivative thereof and an aliphatic dihydroxy compound and / or a hydroxycarboxylic acid compound; It comprises a second step of
reacting an aliphatic polyester oligomer with a carbonate compound to obtain an aliphatic polyester carbonate.

The first step is carried out in the presence of a catalyst at a temperature of 100 to 100.
At 250 ° C., while removing water and excess dihydroxy compound produced as a by-product of the reaction, the number average molecular weight was 10,000.
This is a step of producing a polyester oligomer of 0 or less. It is preferable to reduce the pressure to 300 mmHg or less for the purpose of promoting the reaction.

The second step is a step in which the polyester oligomer obtained in the first step is reacted with a carbonate compound to obtain a high molecular weight product,
usually in the presence of a catalyst, usually at 150 to 150 wt.
The reaction is carried out at 250 ° C. to remove a hydroxy compound formed as a by-product of the reaction. Depending on the boiling point of the carbonate compound,
the pressure is increased at the beginning of the reaction. Preferably, the degree of pressure reduction is adjusted to finally reduce the pressure to 3 mmHg or less.

The content of the carbonate unit in the aliphatic polyester carbonate can be controlled to a desired ratio by controlling the amount of terminal hydroxyl groups of the
aliphatic polyester oligomer. If the carbonate unit content is too large,
The melting point of the aliphatic polyester carbonate obtained is low, and a polymer having practical heat resistance cannot be obtained. On the other hand, when the
carbonate unit content increases, the degradability by microorganisms increases. Therefore, the carbonate unit content, it is preferable to have an appropriate
biodegradability, and it is preferable to be an amount that can achieve practical heat resistance, in the present invention, the carbonate unit content in the aliphatic
polyester carbonate, It is preferably at least 5 mol% or more, usually 5 to 30 mol%.

https://patents.google.com/patent/JP2000327847A/en 2/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
As the aliphatic dibasic acid used in the production of the aliphatic polyester carbonate of the present invention, succinic acid is used as an essential component, and in
addition, for example, oxalic acid, malonic acid, glutaric acid, adipic acid, suberin acid,
Sebacic acid, dodecanoic acid, azelaic acid, etc. can be used in combination. The above aliphatic dibasic acids may be esters or acid anhydrides thereof.

The aliphatic dihydroxy compound used for producing the aliphatic polyester carbonate of the present invention is 1,1.
4-butanediol is used as an essential component. In addition, for example, ethylene glycol, trimethylene glycol, propylene glycol, 1,3-butanediol, pentanediol, hexanediol,
octanediol, neopentylglycol, cyclohexanediol, cyclohexane Dimethanol or the like can be used in combination as appropriate.

Examples of the hydroxycarboxylic acid compound used in the present invention include lactic acid, glycolic acid, β-hydroxybutyric acid, hydroxypivalic acid,
hydroxyvaleric acid and the like. These can also be used as derivatives such as esters and cyclic esters. .

These aliphatic dibasic acids, aliphatic dihydroxy compounds and hydroxycarboxylic acid compounds can be used alone or as a mixture, and can be combined in any
desired manner. And a melting point with a high degree of tightness that can realize practical heat resistance. Therefore, in the present invention,
It is necessary to contain 1,4-butanediol as an aliphatic dihydroxy compound and succinic acid as an aliphatic dibasic acid in an amount of 50 mol% or more.

Specific examples of the carbonate compound used for producing the aliphatic polyester carbonate of the present invention include diphenyl carbonate, ditolyl carbonate,
bis (chlorophenyl) carbonate, m
-Diaryl carbonates such as cresyl carbonate, and also aliphatic carbonate compounds such as dimethyl carbonate, diethyl carbonate, diisopropyl carbonate, dibutyl
carbonate, diamyl carbonate, and dioctyl carbonate, but are not limited thereto. . In addition to the above-mentioned carbonate compound composed of the same type of
hydroxy compound, an asymmetric carbonate compound or a cyclic carbonate compound composed of a different type of hydroxy compound can also be used.

In the present invention, polyolefins are generally commercially available polyethylene, polypropylene, polyvinyl chloride, polyvinyl alcohol, polystyrene, P
One type selected from MMA and ABS resin, a mixture of two or more types, or a copolymer of two or more types is used.

The resin composition of the present invention mainly comprises the above-mentioned polymer having an aliphatic ester structure and a polyolefin, and comprises a
modifier, a filler, a lubricant, an ultraviolet absorber, an antioxidant, a stabilizer, a pigment, a coloring agent. Agents, various fillers, antistatic agents, release agents,
plasticizers, fragrances, antibacterial agents, etc., as well as transesterification catalysts, various monomers, coupling agents, terminal treatment agents, other resins,
wood It can be denatured by adding powder, starch, etc.

At the time of production, it can be obtained by mechanically mixing at least the temperature at which one of the resins melts, or by mixing and pressing mechanically
pulverized both resins. Alternatively, it can be obtained by dissolving both resins in a solvent and then mixing with a poor solvent and precipitating, or by manufacturing a
solution obtained by dissolving both resins in a solvent and removing the solvent. It is not limited to them. The mixing device is not particularly limited, but is industrially
recommended because a method of mixing using an extruder can be continuously processed in a short time.

When the temperature at the time of mixing is 100 ° C. or less, the melt viscosity of the resin is high or the resin does not melt.
A range from 00 degrees to 300 degrees is preferred. If the temperature is 300 degrees or more, thermal decomposition of the resin occurs, which is not preferable. Even
at a temperature of 300 ° C. or less, it is preferable to mix them in a short time under a nitrogen atmosphere in order to prevent coloring, deterioration, thermal
decomposition, and the like at high temperatures. It is recommended that a specific mixing time be within 20 minutes. In addition, a vent may be provided for removing
oligomers, residual monomers, generated gas, and the like in the resin, and mixing may be performed under reduced pressure.

The resin composition of the present invention is not limited to a simple blend of a polymer having an aliphatic ester structure and a polyolefin, but may be formed by a
transesterification reaction or the like in a molten state in the presence of a catalyst. Polymers and the like are also included.

The content of the polymer having an aliphatic ester structure in the composition is preferably from 95 to 5% by weight, more preferably from 80 to 20% by weight. The
polyolefin content is preferably 5 to 95% by weight, more preferably 2 to 95% by weight.
0 to 80% by weight is preferred. If the content of the polymer having an aliphatic ester structure is 5% or less, sufficient disintegration by microorganisms cannot be
provided. Further, when the content of the polyolefin is 5% or less, the moisture permeability cannot be improved. The molecular weight of the polymer having an aliphatic
ester structure used here is desirably 100,000 or more as a weight average molecular weight by GPC in terms of styrene. If it is less than 100,000, the desired strength
cannot be achieved.

When the proportion of the polymer having an aliphatic ester structure is high, the disintegration and the flexibility by microorganisms are increased, and the oxygen
permeability can be lowered. When the proportion of the polyolefin is high, the transparency, The moisture permeability is improved. Resin design according to the
application and purpose is possible.

The molded article of the present invention is an article molded using the resin composition of the present invention. Specific molding forms and molding methods
include an injection molded article, an extrusion molded article, an inflation molding method, and a vacuum molding method. Compressed air products, blow molded
products, fibers, multifilaments, monofilaments, ropes,
Examples include, but are not limited to, nets, wovens, knits, nonwovens, films, sheets, laminates, containers, foams, various parts, and other molded articles. In
particular, the resin composition of the present invention has good film moldability, and the decomposition rate is moderated in agricultural multi-film applications, so
that a film can be designed with an appropriate disintegration rate according to the application, region, and climate.

From the viewpoint of the uniformity, strength, appearance and the like of the resin, it is preferable that the polymer having an aliphatic ester structure and the polyolefin
are mixed and pelletized before molding, but the polymer having the aliphatic ester structure and the polyolefin are preferably pelletized. In this state, in some cases,
various additives can be mixed at the same time, and directly added to a molding machine to obtain a molded product. Furthermore, it is also possible to obtain a film,
sheet or other molded product by dissolving both resins in a solvent, casting or applying the solution in a solution state, and removing the solvent.

The obtained resin composition and molded article have high mechanical strength and a sufficiently softening temperature for practical use, and are disintegrated by
microorganisms in soil, activated sludge, and compost until they cannot be retained by microorganisms.

The biodegradability of the resin composition and the molded article of the present invention can be adjusted by adjusting the molecular weight, the amount of the
polymer having an aliphatic ester structure and the polyolefin, and the thickness of the molded article.

As described above, according to the present invention, it is possible to obtain resin compositions and molded articles having practically sufficient heat resistance and
strength, disintegration by microorganisms, low moisture permeability, and low oxygen permeability.

Next, the present invention will be described in more detail with reference to examples.

In this example, the melting point was measured using DSC (SSC 5000 manufactured by Seiko Denshi Co., Ltd.). The molecular weight is determined by GPC using
chloroform as a solvent.
(Using GPC System-11 manufactured by Showa Denko KK)
As Mw and Mn in terms of styrene. The carbonate unit content is determined by NMR (JEOL Ltd.)
The ratio was determined as the ratio (mol%) of the carbonate unit to the total of the dicarboxylic acid ester unit and the carbonate unit by 13 C NMR using NMR EX-270).

The melt viscosity was measured using a flow tester (CFT-500C manufactured by Shimadzu Corporation) at a temperature of 190 ° C. and a load of 60 ° C.
It was measured in kg. The hydroxyl value and acid value of the oligomer of the aliphatic polyester carbonate were measured according to JIS K-1557. The heat

https://patents.google.com/patent/JP2000327847A/en 3/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
deformation temperature was measured according to ASTM-D648, and the tensile properties were measured according to JIS-K7113. Haze was measured on a 50
micron film. Oxygen permeability is M
Using the OCON method, the moisture permeability coefficient was measured according to JIS-Z208.

Production Example of Aliphatic Polyester Carbonate 18,740 g of succinic acid was placed in a 50-liter reaction vessel equipped with a stirrer, a fractionating condenser, a
thermometer and a gas inlet tube.
(158.7 mol), 1,4-butanediol 21,4
30 g (237.8 mol), 745 mg of zirconium acetylacetonate and 1.40 g of zinc acetate were charged and reacted under a nitrogen atmosphere at a temperature of 150 to 220
° C. for 2 hours to distill water. Then, the degree of decompression is 150-80 mm
Aging was performed for 3 hours at a reduced pressure of Hg to advance the dehydration reaction, and finally the pressure was gradually increased to a pressure of 2
mmHg or less to further distill water and 1,4-butanediol. The reaction was stopped when the amount reached 10,460 g. The number average molecular weight of the
obtained oligomer is 1,7.
80, the terminal hydroxyl value was 102 KOH mg / g, and the acid value was 0.51 KOH mg / g.

Next, 24,000 g of the obtained oligomer was charged into a 50-liter reaction vessel equipped with a stirrer, a fractionating condenser, a thermometer, and a gas
introduction tube, and 4,680 g of diphenyl carbonate was added. Temperature 210-220 ° C
Finally, the pressure was reduced to 1 mmHg, and the reaction was carried out for 5 hours.
The obtained high molecular weight product had a melting point of 104 ° C., a weight average molecular weight (Mw) measured by GPC of 188,000, and had 14.3% of
carbonate units as a polycarbonate component by 13 C NMR measurement. . The melt viscosity was 10,000 poise, it was completely dissolved in chloroform, and there
was no gel component.

Example 1 The aliphatic polyester carbonate pellets obtained in the production example were dried at a temperature of 90 ° C. for 10 hours by a vacuum dryer.
It was mixed with polyethylene in a V-type blender so that the weight ratio became 50/50, and the mixture was extruded into a twin-screw extruder (screw diameter 25 m
mφ, L / D = 30) to continuously make strands,
Pelletized to obtain a resin mixture. The pellets of the resin mixture were dried at a temperature of 90 ° C. for 5 hours or more, and then supplied to an injection molding
machine (mold clamping pressure: 1000 tons) to form a test piece for a physical property test. The evaluation results of the obtained test piece were as follows: heat
deformation temperature was 85 ° C., tensile elongation was 430%, and tensile strength was 40 M
Pa. Further, the pellets were subjected to the T-die method for 5 minutes.
A 0-micron film was prepared and physical properties were measured. Haze is 20 and oxygen permeability is 20 cc · mm / m 2 · day
・ Atm and moisture permeability coefficient is 12g ・ mm / m 2・ day
Met. In the disintegration test of the film in soil, 30% of the film was decomposed in 60 days. Table 1 shows the physical property evaluation results.

Examples 2 to 7 By exactly the same operation as in Example 1, the properties of the polymer (A) having an aliphatic ester structure and the polyolefin (B) were changed
and the mixing ratio was changed. Examples 2 to 7
And the results are shown in Table 1.

Comparative Examples 1 to 3 The same molding and measurement of the physical properties as in Example 1 were carried out with Comparative Example 1 using 100%
aliphatic polyester carbonate, Comparative Example 2 with 100% polyethylene, and 100% polypropylene. The results obtained are shown in Table 1 as Comparative
Example 3.

[0041]

The resin composition comprising a polymer having an aliphatic ester structure and a polyolefin according to the present invention has excellent moldability, and is
obtained by injection molding, extrusion molding, vacuum pressure molding, blow molding, fiber molding. Suitable for obtaining multi-filament, mono-filament, rope, net,
woven, knitted, non-woven, film, sheet, laminate, container, foam, various parts and other molded products, and the obtained molded products are sufficiently mechanical
It has strength and heat resistance and low oxygen permeability and moisture permeability, and is easily disintegrated by microorganisms in soil, activated sludge, and
compost until it does not retain its original shape. Therefore, it can be widely used for packaging materials, agriculture, fisheries, foods, and other applications where
recycling is difficult. For example, in the field of packaging materials, various types of packaging are possible as films, and heat sealing is also possible. In the agricultural
field, multi-films that cover the soil surface to keep the soil warm, pots and strings for planting,
Alternatively, it can be used as a coating material for fertilizers, or can be used as a fishing line or a fish net in the fishery field, or as a sanitary material such as a medical
material in the medical field or a sanitary article.

[0042]

[Table 1]

──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛
(Reference) C08L 33/00 C08L 33/00 55/02 55/02 67/00 ZAB 67/00 ZAB 69/00 69 / 00 // C08G 63/64 C08G 63/64 (72) Inventor Mitsuru Nakamura 22nd Wadai, Tsukuba-
shi, Ibaraki F-term in Mitsubishi Gas Chemical Company, Ltd. AA88 AF08Y AF09Y AF15Y AF30Y AF43Y AH12 AH17 AH19 BA01 BB05 BB06 BB09 BC01 BC04 BC07
4J002 BB032 BB122 BC032 BD042 BE022 BG062 BN152 CG04W 4J029 AA02 AA03 AA08 AB01 AC03 HC05 HC04 HC03 HC01 HC03 HC01 HC03

Cited By (9)

Publication number Priority date Publication date Assignee Title

JP2001240731A * 2000-02-25 2001-09-04 Mitsubishi Gas Chem Resin composition

Co Inc

JP2003088255A * 2001-09-14 2003-03-25 Mikado Kako Kk Agricultural mulching film

JP2005248160A * 2004-02-06 2005-09-15 Osaka Gas Co Ltd Biodegradable plastic material and molded article

JP2006070224A * 2004-09-06 2006-03-16 Tsutsunaka Plast Ind Polylactic-based resin composition for calendar molding
Co Ltd

JP2007106842A * 2005-10-12 2007-04-26 Mitsui Chemicals Inc Molded article comprising lactic acid-based resin composition excellent in
resistance to staining

JP2007211111A * 2006-02-08 2007-08-23 Mitsubishi Chemicals Thermoplastic resin composition and resin-molded article

https://patents.google.com/patent/JP2000327847A/en 4/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
Corp

JP2011117001A * 2011-03-17 2011-06-16 Toyota Tsusho Corp Polylactic acid thermoplastic resin composition and molding of the same

KR20120039001A * 2009-07-23 2012-04-24 가부시키가이샤 니토무 Pressure-sensitive adhesive sheet

즈

CN106633777A * 2016-12-29 2017-05-10 上海锦湖日丽塑料有限 PC/ABS material with high paint bonding force and preparation method of PC/ABS
公司 material

Family To Family Citations

* Cited by examiner, † Cited by third party, ‡ Family to family citation

Similar Documents

Publication Publication Date Title

CA2550002C 2009-07-14 Polymer blends with improved rheology and improved unnotched impact strength

CA2550402C 2009-07-07 Compatibilized blends of biodegradable polymers with improved rheology

JP4807544B2 2011-11-02 Polyester composition

EP0990678B1 2003-11-26 Biodegradable polyester/polyester carbonate resin composition

JP5200208B2 2013-06-05 Aliphatic aromatic polyester and resin composition

JP2001123055A 2001-05-08 Polylactic acid resin composition

JP2001335623A 2001-12-04 Impact resistance-imparting agent and polyester composition containing it

JP4200340B2 2008-12-24 Resin composition and molded body

JP2000327847A 2000-11-28 Resin composition

JP2004211008A 2004-07-29 Biodegradable copolymer and manufacturing method thereof

JP2004359730A 2004-12-24 Resin composition

JP5167502B2 2013-03-21 Aliphatic aromatic polyester and resin composition thereof

JPH11241009A 1999-09-07 Polylactate resin composition

JP4492767B2 2010-06-30 Resin composition

KR101690082B1 2017-01-09 Biodegradable resin composition and biodegradable film prepared therefrom

JP3756677B2 2006-03-15 Resin composition and molded body

JP2002371172A 2002-12-26 Lactic acid polymer composition and method of producing the same

JP2000129035A 2000-05-09 Resin composition and molding prepared therefrom

JP4171891B2 2008-10-29 Polyester carbonate copolymer and process for producing the same

JP4288456B2 2009-07-01 Resin composition and molded body

JP4089575B2 2008-05-28 Cellulose ester composition and molded product obtained therefrom

JP2000345012A 2000-12-12 Resin composition

US20010051692A1 2001-12-13 Resin composition and molded article

JP4048335B2 2008-02-20 Process for producing aliphatic polyester carbonate

JP5135740B2 2013-02-06 Polyester and production method thereof, and polyester block copolymer

Priority And Related Applications

Priority Applications (1)

Application Priority date Filing date Title

JP11135682A 1999-05-17 1999-05-17 Resin composition

Applications Claiming Priority (1)

Application Filing date Title

JP11135682A 1999-05-17 Resin composition

https://patents.google.com/patent/JP2000327847A/en 5/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
Legal Events

Date Code Title Description

2006-05-13 A621 Written request for application examination Free format text: JAPANESE INTERMEDIATE CODE: A621

Effective date: 20060512

2008-08-11 A977 Report on retrieval Free format text: JAPANESE INTERMEDIATE CODE: A971007

Effective date: 20080811

2008-08-28 A131 Notification of reasons for refusal Free format text: JAPANESE INTERMEDIATE CODE: A131

Effective date: 20080827

2009-02-26 A02 Decision of refusal Free format text: JAPANESE INTERMEDIATE CODE: A02

Effective date: 20090225

Concepts

machine-extracted Download Filter table

Name Image Sections Count Query match

resin composition title,claims,abstract,description 28 0.000

hydroxycarboxylic acid compound claims,abstract,description 31 0.000

polymer claims,abstract,description 31 0.000

aliphatic polyester claims,abstract,description 30 0.000

permeability claims,abstract,description 25 0.000

polyolefin claims,abstract,description 25 0.000

Carbonate dianion claims,abstract,description 22 0.000

O- O-

oxygen claims,abstract,description 16 0.000

oxygen claims,abstract,description 16 0.000

O O

oxygen claims,abstract,description 16 0.000

aliphatic group claims,abstract,description 15 0.000

carbonate group claims,abstract,description 12 0.000

acid claims,abstract,description 11 0.000

mixture claims,abstract,description 11 0.000

compounds claims,abstract,description 8 0.000

melting claims,abstract,description 7 0.000

Permeability coefficient claims,description 6 0.000

melt claims,description 6 0.000

Polyethylene (PE) claims,description 5 0.000

polyethylene claims,description 5 0.000

load claims,description 4 0.000

Polypropylene claims,description 3 0.000

polypropylene claims,description 3 0.000

Acrylonitrile butadiene styrene claims,description 2 0.000

Polystyrene claims,description 2 0.000

https://patents.google.com/patent/JP2000327847A/en 6/7
7/24/2021 JP2000327847A - Resin composition - Google Patents
Polyvinyl alcohol claims,description 2 0.000

copolymer claims,description 2 0.000

polystyrene claims,description 2 0.000

polyvinyl alcohol claims,description 2 0.000

polyvinyl chloride claims,description 2 0.000

polyvinyl chloride claims,description 2 0.000

species claims 3 0.000

poly(methyl methacrylate) claims 1 0.000

polymethyl methacrylate claims 1 0.000

mixing abstract,description 12 0.000

solvent abstract,description 10 0.000

Show all concepts from the description section

Data provided by IFI CLAIMS Patent Services

About Send Feedback Public Datasets Terms Privacy Policy

https://patents.google.com/patent/JP2000327847A/en 7/7