TECHNICAL DATA SHEET

2024-02-16
22

TEKNODUR COMBI 3430-05

High solids one layer polyurethane coating
TEKNODUR COMBI 3430-05 is a two pack anticorrosive pigmented
polyurethane paint with low solvent content where the hardener used is an
aliphatic isocyanate resin.

Used as a one layer paint. The paint can also be used as a top coat in Polyurethane coating cystems. It is suitable for use on
steel, zinc and aluminium surfaces.

The paint produces a film with good mechanical and weather resistance properties. The use of TEKNODUR 0250 Polyurethane
varnish is recommended on objects when the topcoat is required to have excellent gloss and colour retention.

TECHNICAL DATA
Recommended substrate Steel, Aluminium, Zinc
Binder Polyurethane
Solids 61 ±2 % by volume
Total mass of solids Approx. 1120 g/l
Volatile organic compound (VOC) Approx. 350 g/l (DIRECTIVE 2010/75/EU)
The VOC value provided is the average value for factory produced products, and
consequently it will be subject to variations between individual products
covered by this Technical Data Sheet.
Theoretical spreading rate Theoretical spreading rate
Dry film (µm) Wet film (µm)
(m²/l)
80 144 6.9
100 180 5.6
120 216 4.6

As many of the paint's properties will change if too thick coats are applied, it is
not recommended that the product is applied to a film thickness that is more
than double of the thickest recommended film.
Practical spreading rate The values depend on the application technique, surface conditions, overspray,
etc.
Tinting system Teknomix;Teknotint
Gloss (60°) Semi-gloss
Hardener Comp. B: TEKNODUR HARDENER 7230
Mixing ratio (A:B) 6:1 parts by volume
Pot life, +23°C 1 h 30 min
Thinner Standard thinner: TEKNOSOLV 9504, TEKNOSOLV 9524, TEKNOSOLV 9526,
TEKNOSOLV 9521 or TEKNOSOLV 6220

www.teknos.com 1/5
TECHNICAL DATA SHEET
2024-02-16
22
TEKNODUR COMBI 3430-05

Storage The storage stability is shown on the label. Store indoors in a cool and dry place
and in a tightly closed can.

The hardener reacts with air humidity and therefore the opened can is to be
kept carefully closed, and it is recommended to be used within 14 d of opening.

www.teknos.com 2/5
TECHNICAL DATA SHEET
2024-02-16
22
TEKNODUR COMBI 3430-05

DIRECTION FOR USE

Surface preparation Remove from the surfaces any contaminants that might be detrimental to
surface preparation and application. Remove also water-soluble salts by using
appropriate methods. The surfaces are prepared according to the different
materials as follows:

STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation
grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate
improves the adhesion of the paint to the substrate.

ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to

atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned
(SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and
natural sand. It is not recommended according to standard ISO 12944-5 to paint
hot-dip-galvanized objects that are subjected to immersion strain. Painting of
hot-dip-galvanized objects that are subjected to immersion strain must be
discussed separately with Teknos.
It is recommended that new zinc-coated thin-plate structures are treated with
sweep blast-cleaning (SaS). Surfaces that have been weathered to matt can be
treated also with RENSA STEEL washing agent.

ALUMINIUM SURFACES: Treat the surfaces with RENSA STEEL washing agent.
Surfaces that are exposed to weathering are also roughened up with sweep
blast-cleaning (AlSaS) or sanding.

OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that

might be detrimental to the application of paint (e.g. grease and salts) are
removed. The surfaces must be dry and clean. Old, painted surfaces that have
exceeded the maximum overcoating time are to be roughened as well. Damaged
parts are prepared in accordance with the requirements of the substrate and
the maintenance coating.

The place and time of the preparation are to be chosen so that the prepared
surface will not get dirty or damp before the subsequent treatment.

Additional instructive information for surface preparation can be found in

standards EN ISO 12944-4 and ISO 8501-2.
Application method Airless spraying, Conventional spraying

www.teknos.com 3/5
TECHNICAL DATA SHEET
2024-02-16
22
TEKNODUR COMBI 3430-05

Application Take into consideration the pot life of the mixture when estimating the amount
to be mixed at a time. Before application the base and hardener are mixed in
right proportion. Stir thoroughly down to the bottom of the vessel. Inadequate
stirring or incorrect mixing ratio results in imperfect curing and impaired film
properties.

Stir thoroughly before use. Before use clean the spray gun and paint vessels
with a thinner suitable for the paint.

Suitable airless nozzle size 0.013 - 0.017"

Application conditions The surface to be treated must be dry. During the application and drying period
the temperature of the ambient air, the surface and the product shall be above
+5°C and the relative air humidity below 80%. Additionally, the temperature of
the surface to be treated and the product must be at least +3°C above the dew
point of the ambient air.
Thinning When needed, thin the paint with TEKNOSOLV 9504 (standard thinner),
TEKNOSOLV 9524 (slow thinner), TEKNOSOLV 9526, TEKNOSOLV 6220 or
TEKNOSOLV 9521.

Do not use universal thinners, since they may contain alcohol which will react
with the hardener.
Drying time +23°C / 50% RH (dry film 80 μm)
- dust free 45 min (ISO 9117-3:2010)
- touch dry 5 h (ISO 9117-5:2012)
- fully cured 7d
Overcoatable by itself
surface temperature
min. max.*
+5°C 20 h 18 months or Extended**
+23°C 4h 18 months or Extended**
* A completely clean surface is mandatory to ensure the best intercoat
adhesion. If the maximum overcoating interval has been exceeded, the surface
must be roughened before overcoating. Increase in film thickness and rise in the
relative humidity of the air in the drying space slow down the drying process
and effect the overcoating properties.
** Maximum overcoating interval can be extended in certain circumstances. To
determine if extended overcoating interval is applicable please consult Teknos
representative in written form.

If some other top coats besides the ones mentioned above are used, please
contact Teknos representative for overcoating recommendations.
Cleaning TEKNOCLEAN 6496

www.teknos.com 4/5
 TECHNICAL DATA SHEET
2024-02-16
22
TEKNODUR COMBI 3430-05

HEALTH AND SAFETY

Safety and precaution measures See safety data sheet.

The hardener of the product and the ready mixture contain isocyanates. In
poorly ventilated areas and especially when using spray application we
recommend the use of a fresh air mask. In short or temporary work, a mask with
combined filter A2-P2 can be used. In this case eyes and face are to be
protected.

The hardener can must be opened with caution, as pressure may develop in the
can during storage.

Teknos Group Oy Takkatie 3, P.O.Box 107 FI-00371 Helsinki, Finland Tel. +358 9 506 091

The above information is normative and based on laboratory tests and practical experiences. The information is noncommittal, and we cannot accept liability for the results
obtained under working conditions beyond our control, and consequently the buyer or the user is not released from the obligation to test the suitability of our products for specific
means and application methods under the actual application conditions. Our liability covers only damage caused directly by defects in the products supplied by Teknos. This
product is intended for professional use only. This implies that the user possesses sufficient knowledge for using the product correctly with regard to technical and working safety
aspects. The latest versions of Teknos’ Technical Data Sheets and Safety Data Sheets are available from our homepage www.teknos.com. All trademarks displayed on this
document are the exclusive property of Teknos Group or its affiliated companies.

www.teknos.com 5/5