Carbohydrate Polymers 64 (2006) 134137 www.elsevier.

com/locate/carbpol

Short communication

Process for obtaining cellulose acetate from agricultural by-products*

Received 16 August 2005; accepted 31 October 2005 Available online 4 January 2006

Abstract Agricultural residues such as corn ber, rice hulls and wheat straw can be used as abundant low-cost feedstock for production of fuel ethanol. However, the cost of cellulase enzymes to saccharify cellulose to glucose is a major hindrance. As an alternative, a novel process to obtain industrially important cellulose acetate from these by-products after removing hemicellulosic sugars was developed. Rice-straw, wheat hull and corn ber were treated with dilute acid at a moderate temperature to hydrolyze the hemicellulose to monomeric sugars that can be fermented to ethanol. The cellulose was then treated with acetic anhydride and catalytic amount of sulfuric acid to make cellulose acetate. The production of cellulose acetate was conrmed by NMR analysis. The pretreatment used to hydrolyze the hemicellulose was also useful for cellulose acetate production. Without the pretreatment cellulose acetate conversions from wheat straw, corn ber, and rice hulls were 0.5, 1.8 and 13.5, respectively. After pretreatment the conversion rate increased to about 25 wt% for all three agricultural residues used. Published by Elsevier Ltd.
Keywords: Corn ber; Rice hulls; Wheat straw; Cellulose; Cellulose acetate; Agricultural by-products; Industrial products

1. Introduction In 2004, the production of fuel alcohol from corn starch reached about 3.41 billion gallons. Various lignocellulosic agricultural residues such as corn ber, corn stover, wheat straw, rice-straw, and rice hull contain about 4570% complex carbohydrates (cellulose and hemicellulose) and can serve as low-cost feedstocks for production of fuel ethanol (Saha, 2004). Four steps are generally involved in the conversion of lignocellulose to ethanol: (1) pretreatment, (2) enzymatic saccharication, (3) fermentation of mixed sugars to ethanol, and (4) product recovery. Native biomass is generally resistant to enzymatic attack (Saha & Bothast, 1999). Pretreatment of any lignocellulose is essential before enzymatic saccharication can ensue. Pretreatment with dilute acid at a moderate temperature has become a state of the art technology for any biomass substrate (Saha, 2003). This process generally hydrolyzes hemicellulose to fermentable sugars. Even though
* Names are necessary to report factually on available data: however, the USDA neither guarantees nor warrants the standard of the product, and the use of the name USDA implies no approval of the product to the exclusion of others that may also be suitable. * Corresponding author. Tel.: C1 309 681 6406. E-mail address: [email protected] (A. Biswas).

0144-8617/$ - see front matter Published by Elsevier Ltd. doi:10.1016/j.carbpol.2005.11.002

the acid helps to decrystallize cellulose depending on the substrate, it cannot degrade cellulose to glucose. Cellulase enzymes are generally used to hydrolyze cellulose to glucose. However, the rate is very slow and enzymatic saccharication by cellulases is not cost-effective (Saha & Bothast, 1999). It is estimated that the cost of cellulases needs to be lowered by at least 10-fold in order to be competitive. As an alternative, we have attempted to convert the cellulose to value-added cellulose acetate ($1.80/pound) once the hemicellulosic sugars are removed for use as substrate for ethanol fermentation. By converting the cellulose in these residues into cellulose acetate as opposed to saccharifying cellulose to glucose the overall cost of producing ethanol from lignocellulosic biomass may be reduced. There are numerous publications and patents on the preparation and utilization of cellulose acetate (Gedon & Fengl, 1993; Heinze & Liebert, 2004; Majewicz & Padlas, 1993; Serad, 1993). However, to the best of our knowledge there are no known reports addressing the utilization of agricultural by-products/waste to prepare cellulose acetate. Wood and cotton are the major resources for all cellulose products such as paper, textiles, construction materials, and cardboard, as well as cellulose derivatives, such as cellulose esters (Serad, 1993) and ethers (Majewicz & Padlas, 1993). It is estimated that annually 1.5 billion pounds of cellulose acetates are manufactured globally. Cellulose acetate, Fig. 1, is widely used in textiles because of its low-cost, toughness, gloss, high transparency, natural feel, and other

A. Biswas et al. / Carbohydrate Polymers 64 (2006) 134137

135

OCOCH3 H3COCO OH O CH3COOCH3 O

CH2COOCH3 O O OCOCH3

OCOCH3

CH2COOCH3 O OH

OCOCH3 O O

OCOCH3

OCOCH3

CH2COOCH3

OCOCH3

Fig. 1. Structure of cellulose triacetate, n is typically 4001000.

favorable aesthetic properties. Cellulose acetate bers in cigarette lters are designed to absorb vapors and accumulate particulate smoke components. Cellulose acetate is also used as a carrier for photographic negatives, motion picture lm (celluloid), microlm, microche and audio tape (Gedon & Fengl, 1993). 2. Experimental 2.1. Materials Corn ber, rice hulls and wheat straw were obtained from Pekin Energy Company, Pekin, IL (now Aventine Renewable Energy), Rice Hull Specialty Products Inc., Stuttgart, AR, and a local farmer, respectively. Methylene chloride and chloroform, acetic anhydride, and sulfuric acid were obtained from Aldrich. NMR spectra in CDCl3 were obtained by using Bruker Instruments DRX 400 spectrometer. 2.2. Pretreatment Corn ber, rice hulls and wheat straw were dried in a forced-air oven at 55 8C for 24 h and milled in a hammer mill to pass through a 1.27 mm screen. The milled samples were stored at room temperature. Corn ber was washed with hot hexane to remove the oil. Hexane washed corn ber (15% solids, w/v) was slurried in 0.5% H2SO4 and pretreated in an autoclave at 121 8C for 15 min (Saha & Bothast, 1999). The pretreated corn ber was neutralized to pH 5.0 with 10 M NaOH. Before using as a starting material, the solids were separated from the liquids, washed one time with three volumes of water and dried in an oven at 60 8C for 24 h. Milled rice hulls (15%, w/v) and wheat straw (8.6%, w/v) were slurried in 1% (v/v) H2SO4 separately and pretreated in an autoclave at 121 8C for 1 h (Saha, Iten, Cotta, & Wu, 2004, 2005). The pretreated substrates were neutralized to pH 5.0 with 10 M NaOH. The solids were separated from the liquids, washed one time with three volumes of water and dried in an oven at 60 8C for 24 h before using as a starting material. 2.3. Acetylation Acetylation was performed on pretreated and untreated samples from corn ber, rice hulls, and wheat straw. Two grams of sample along with 0.5 g of acetic acid, 5.0 g of acetic

anhydride, 30 ml of methylene chloride, and 0.04 g of sulfuric acid were added to 100 ml round bottom ask. The mixture was heated to 80 8C while stirring with a magnetic stirrer. The ask was xed with a reux condenser and Therm-o-watch (I2R) was used to ensure that the temperature was maintained at 80 8C. After 4 h, the reaction mixture was allowed to cool to room temperature and was sieved through a #60 Tyler screen, with the ltrate being collected in a large beaker. In order to extract the remaining cellulose acetate, the residue on the screen was collected and transferred to a beaker. Sixty milliliters of chloroform was added and the mixture was stirred for 30 min at room temperature and then sieved through a #60 Tyler screen. The ltrate was collected in a large beaker and combined with previous ltrates. The overs on the screen were discarded. The combined ltrates were further ltered into a round bottom ask using #54 Whatman lter paper. The ltrates were evaporated to dryness using a Rotavap (Buchi) to yield cellulose acetate as a lm coating inside the ask. Ethyl alcohol was used to remove the acetate lm from the ask. Filtration through a coarse lter paper yielded acetate as residue and ethyl alcohol as ltrate. The cellulose acetate collected on the lter paper was placed in evaporating dishes and dried at 80 8C in a vacuum oven overnight.

3. Results and discussion Corn ber, rice hulls, and wheat straw contain about 15, 36 and 45% cellulose, respectively (Saha & Bothast, 1999; Saha et al., 2004, 2005). Our objective was to convert cellulose into cellulose triacetate. Cellulose triacetate is soluble in methylene chloride or chloroform so it can be easily extracted from the unreacted substrate. Excess acetic anhydride was used and acetylation proceeded to the maximum extent to yield cellulose acetate having a degree of substitution of 2.8 from all the three sources. The acetylation of cellulose from corn ber, rice hulls, and wheat straw was conrmed by proton NMR of the product cellulose acetate (Fig. 2). The degree of substitution (DS) was determined by proton NMR, and by titration with aqueous sodium hydroxide solution. In the NMR method, we used the ratio of the seven cellulose proton absorbance in the range of 3.55.1 ppm to the absorbance of three methyl protons of acetyl groups in the range of 1.92.2 ppm. DS was calculated by 1/3 of the three methyl protons of acetyl group absorbance between 1.9 and

136

A. Biswas et al. / Carbohydrate Polymers 64 (2006) 134137

5.071

4.794

4.428

4.054

3.713

3.542

2.127 2.008 1.945

ppm (t1)

5.0

4.0

3.0

2.0

1.254 0.39 1.0

2.2 ppm divided by 1/7 of the total cellulose CH proton absorbance between 3.5 and 5.1 ppm. Table 1 shows the yields of cellulose acetate obtained from both untreated and pretreated corn ber, rice hulls, and wheat straw samples. When corn ber and wheat straw were acetylated without pretreatment, the recovered yields of cellulose acetate were extremely low. When untreated corn ber was used as the starting material only, 1.8% conversion was achieved. The amount of cellulose in corn ber is lower (15%) than the other starting materials which may account for its low yield (Saha & Bothast, 1999). However, based on the amount of the cellulose in corn ber, a conversion of about 12% was achieved. Untreated wheat straw gave the lowest conversion of only 0.5%. This is somewhat surprising since wheat straw contains about 30% cellulose (Saha et al., 2004). Wheat straw had the highest lignin content, however, of the substrates used. Untreated rice hulls used in the acetylation reaction gave yields of cellulose acetate, of about 13.5% conversion based on the starting weight. Rice hulls contain about 35% cellulose (Saha et al., 2005). Based on the amount of cellulose in rice hulls, the conversion of cellulose to cellulose acetate is about 35%. Since cellulose bers are embedded with lignin, this may interfere with the acetylation reaction. Pretreatment of the lignocellulose may be essential for making cellulose acetate and the process will benet from the pretreatment for ethanol production.

1.00

0.99

1.89

1.05

Fig. 2. Proton NMR of cellulose acetate (DS 2.8) in CDCl3.

1.19

0.99

The acetylation conversion of cellulose in rice hulls, wheat straw, and corn ber increased to about 25% for all substrates after the dilute acid pretreatment at a moderate temperature (Table 1). The increase in conversion is probably due to the pretreatment removing hemicellulose and other acid soluble materials. The result is an increase in the relative concentration of cellulose in the starting substrate. It is interesting to note that after pretreatment the acetylation conversion is about the same, regardless of the starting material. This may be due to remaining cellulose having the same reactivity. Native cellulose has an average degree of crystallinity of 70% (Daniel, 1985). It is assumed that the acetylation reaction would only work on the amorphous cellulose. This would put a theoretical conversion of cellulose to cellulose acetate at about 30%. This means that acetylation reaction of pretreated rice hulls, wheat straw, and corn ber may be near the theoretical limit of conversion without further treatments on the cellulose to reduce its crystallinity.
Table 1 Cellulose acetate by weight from corn ber, rice hull and wheat straw Starting material Corn ber, 2 g Rice hull, 2 g Wheat straw, 2 g Pretreated (% conversion) 0.48 g (23.9) 0.53 g (26.6) 0.51 g (25.8)

9.89

A. Biswas et al. / Carbohydrate Polymers 64 (2006) 134137

137

4. Conclusion The cellulose in corn ber, rice hulls, and wheat straw was converted into cellulose acetate. The conversion rate of untreated wheat straw and corn ber is extremely low. However, the conversion rate is 13.5 wt% for untreated rice hulls. It is unclear why the conversion rate for untreated rice hulls is greater than for the other untreated bers. When the substrates were preheated with dilute sulfuric acid to remove hemicellulosic sugars for alcohol production and other solubles, the yield of cellulose acetate greatly increased. We obtained cellulose acetate in about 25 wt% of the pretreated agricultural residues. We believe that the removal of the hydrolyzed water soluble materials increased the concentration of cellulose in the starting substrate available for acetylation. The acid treatment renders the cellulose more accessible to acetic anhydride and thus, more reactive towards acylation. More work is needed to improve the efciency of the conversion. This method may improve the cost efciency of the overall bioethanol production process by converting the cellulose in these residues into value-added cellulose acetate. Because, currently cellulase enzymes needed to saccharify cellulose to glucose for fermentation are not cost-competitive.

References
Daniel, J. R. (1985). In H. F. Mark, N. M. Bikales, C. G. Overberger, & G. Menges (Vol. Eds.), Encyclopedia of polymer science: Vol. 3 (2nd ed.) (pp. 90123). New York: Wiley. Gedon, S., & Fengl, T. (1993). In J. I. Kroschwitz, & M. Howe-Grant (Vol. Eds.), KirkOthmer encyclopedia of chemical technology: Vol. 5 (4th ed.) (pp. 496563). New York: Wiley. Heinze, T., & Liebert, T. (2004). In P. Rustemeyer (Ed.), Cellulose acetates: Properties and applications (pp. 167238). Weinham, Germany: Wiley. Majewicz, T. G., & Padlas, T. T. (1993). In J.I Kroschwitz, & M. Howe-Grant (Vol. Eds.), KirkOthmer encyclopedia of chemical technology: Vol. 5 (4th ed.) (pp. 541563). New York: Wiley. Saha, B. C. (2003). Journal of Industrial Microbiology and Biotechnology, 30, 279291. Saha, B. C. (2004). In B. C. Saha (Ed.), Lignocellulose biodegradation (pp. 1 34). Washington, DC: American Chemical Society. Saha, B. C., & Bothast, R. J. (1999). Applied Biochemistry and Biotechnology, 76, 6577. Saha, B. C., Iten, L. B., Cotta, M. A., Wu, Y. V. (2004). Proceedings of 2nd World Conference Biomass for Energy, Industry and Climate Protection, Rome, Italy (pp. 14811484). Saha, B. C., Iten;, L. B., Cotta, M. A., & Wu, Y. V. (2005). Biotechnology Progress, 21, 816822. Serad, G. H. (1993). In J. I. Kroschwitz, & M. Howe-Grant (Vol. Eds.), KirkOthmer encyclopedia of chemical technology: Vol. 10 (4th ed.) (pp. 598624). New York: Wiley.