PEX-AL-PEX PIPE

Pipe DN x Wall thikness

Indicator Name Measurment
16х2,0 20х2,0 26х3,0 32х3,0
Outer diameter with tolerance +/- in
mm 16.0+0.30 20.0+0.30 26.0+0.30 32.0+0.30
mm
Inner diameter with tolerance +/- in
mm 12.0+0.1-0.15 16.0+0.1-0.15 20.0+0.1-0.15 26.0+0.1-0.15
Mm
Maximum working pressure at
maximum Bar 10bar/95℃ 10bar/95℃ 10bar/95℃ 10bar/95℃
operating / working temperature, bar
Wall thickness мм 2.0+0.30 2.0+0.30 3.0+0.30 3.0+0.30

Aluminum Thickness, mm mm 0.25 0.3 0.35 0.5

Glue thikness mm mm 0.15 0.15 0.15 0.15

Operating working temperature at

pressure of 10 bar, ° C °С

Pass the test pressure test of 22Hour，95°С，2.5Mpa

according to DIN standard，
Working pressure 25bar is not allowed.

Operating working temperature at

pressure of 25 bar, ° C °С

Maximum permissible short

temperature ° C °С 110°С

Max operating working

Pressure at 95 ° C, bar Bar 10bar
95 ° C
Max (breaking) Pressure at 20 ° C, bar Bar 80 70 60 55

Pipes must have smooth outer and inner

surfaces. On the inner surface and side
The appearance of the surface
face surfaces of the pipes are not
allowed bubbles, cracks, roughness,
visual damages
The coefficient indicator of linear
0.025 mm/(m*k)
expansion no more than mm/m
Thermal conductivity Coefficient, W / m К 0.045
oxygen permeability % 0
0.8 μm
Coefficient equivalentt evenly-grained roughness no more mm
（μm is 1/1000 mm）
Pipe DN x Wall thikness
Indicator Name
16*2.0 20*2.0 26*3.0 32*3.0
pipe weight of 1 m in grams 110 147 268 355
The fluid volume in 1 meter in litres 0.11 0.2 0.31 0.53
tube length, accommodating a 1 Liter/meter 9 5 3.2 1.9
Operation Class Class 5 - High-temperature radiator heating
 Resistance of pipes to constant internal pressure at temperature, ° C Producer laboratory data
-20 - for 1 hour, MPa (not less) 4Mpa, 4Mpa, 4Mpa, 4Mpa,
This is test This is test This is test This is test
requirement. requirement. requirement. requirement.bur
burst burst burst st pressure is
pressure is pressure is pressure is listed above.
listed above. listed above. listed above.
-95 - for 1 hour, MPa (not less) 2.0 2.0 2.0 2.0
-95 - for 100 hours, MPa (not less) 1.6 1.6 1.6 1.6
-95 - for 1000 hours, MPa (not less) 1.5 1.5 1.5 1.5

Resistance of pressed pipe with fittings to constant internal pressure at temperature, ° C Producer laboratory
data
-20 - for 1 hour, MPa (not less) 4 4 4 4
-95 - for 1 hour, MPa (not less) 2.0 2.0 2.0 2.0

-95 - for 100 hours, MPa (not less) 1.6 1.6 1.6 1.6

-95 - for 1000 hours, MPa (not less) 1.5 1.5 1.5 1.5

Resistance of pressed pipe with fittings to constant internal pressure at temperature, ° C when the pipe is bent
= 5 outer DN Producer laboratory data
Durability strength of pipe ring samples with crossed 2400N 2600N 2990N 3320N
breaking, N
Length Change after heating at a temperature of ≤3% ≤3% ≤3% ≤3%
(120-3) ° C during (60 + 1) min,%
The minimum long-term strength of the material 0.5 Mpa 0.5 Mpa 0.5 Mpa 0.5Mpa
outer and inner layers, MRS, MPa
Mass fraction of volatile in <0.035% <0.035% <0.035% <0.035%
Raw materials in the outer and inner layers or or or or
0.035mg/ 0.035m 0.035m 0.035mg/
kg g/kg g/kg kg
Resistance to delamination of the adhesive compound of ≥25 ≥25 ≥25 ≥25
internal and metal layers, N / cm
Minimum bending radius manually mm 8*dn 8*dn 8*dn 8*dn
The bending radius using bending tool, mm 5*dn 5*dn 5*dn 5*dn
The strength of the aluminum welding line , N / mm2 >60,PASS >60,PAS >60,PAS >60,PASS
1.1 Times S 1.1 S 1.1 1.1 Times
expansion Times Times expansion
test expansio expansio test
n test n test
The service life of pipes according to passport operating 50 50 50 50
conditions, years
polyethylene crosslinking process organosilanes (B)
The degree of crosslinking of PEX layers,% ≥65% ≥65% ≥65% ≥65%
A method of aluminum welding Butt welded by TIG Method using Non-consumable
electrode in an inert gas
Press fittings Indicator Name Outer DN size
16*2.0 20*2.0 26*3.0 32*3.0
Outer diameter of pressed sleeve with manual press tool at place
of pressing with tolerance not more than mm 16.0+0.30 20.0+0.30 26.0+0.30 32.0+0.30

Outer diameter of pressed sleeve with electric press tool at

place of pressing with tolerance not more than mm
16.0+0.30 20.0+0.30 26.0+0.30 32.0+0.30

Maximum working pressure at maximum

10bar/95℃ 10bar/95℃ 10bar/95℃ 10bar/95℃
operating / working temperature, bar
Max operating working 10bar 10bar 10bar 10bar
Pressure at 95 ° C, bar
Max (breaking) Pressure at 20 ° C, bar 40 38 32 32
Critical pressure Bar during 1000 hours 95±2 °С 2.0MPa 2.0MPa 2.0MPa 2.0MPa
Operating working temperature °С Class1-2-4-5 Class1-2-4-5 Class1-2-4-5 Class1-2-4-5
Critical temperature °С 110℃ 110℃ 110℃ 110℃
Max Operating working temperature°С 95℃ 95℃ 95℃ 95℃
The compression force of the sleeve N SS304, SS304, SS304, SS304,
Hardness< Hardness Hardness< Hardness
hb200 <hb200 hb200 <hb200