Scribd Logo
Upload

Welcome to Scribd!

  • 4 views

    HC-BD Sgs Test Report PDF

    Uploaded by

    Pedro Chuquihuanga Chamba

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    HC-BD Sgs Test Report PDF

    Uploaded by

    Pedro Chuquihuanga Chamba
    4 views8 pages

    Original Title

    Hc-bd Sgs Test Report.pdf

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    4 views8 pages

    HC-BD Sgs Test Report PDF

    Uploaded by

    Pedro Chuquihuanga Chamba

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 8

    TEST REPORT

    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 1 of 8

    CUSTOMER NAME: GUANG ZHOU HUI CHI GLASS TECHNICAL CO., LTD.
    ADDRESS: 2ND LIKANG INDUSTRIAL SHITAN ROAD SHIJING BAIYUN DISTRICT
    510430 GUANGZHOU

    Sample Name : HC-BD EXTRA CLEAR EVA FILM ,


    EVA LAMINATED GLASS
    Model No. : HC-BD
    Other Information : EVA
    Above information and sample(s) was/were submitted and confirmed by the client. SGS, however,
    assumes no responsibility to verify the accuracy, adequacy and completeness of the sample
    information provided by client.
    ***********
    SGS Ref. No. : CP20-038802
    Date of Receipt : Jul 31, 2020
    Testing Start Date : Jul 31, 2020
    Testing End Date : Aug 11, 2020
    Test result(s) : For further details, please refer to the following page(s)
    (Unless otherwise stated the results shown in this test report refer only to
    the sample(s) tested)

    Signed for
    SGS-CSTC Standards Technical
    Services Co., Ltd. GZ Branch Testing
    Center

    Kelly Lee
    Authorized signatory
    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 2 of 8

    Summary of Results:
    No. Test Item Test Method Result Conclusion
    With reference to
    ASTM D3330/D3330M-
    1 180º Peel Strength 121N/10mm /
    04(2018) Method A and
    client's requirement
    ASTM D1003-13
    2 Haze 1.1% /
    Procedure A
    Tensile
    27.0MPa
    Strength
    3 Tensile Test ASTM D638-14 /
    Elongation
    610%
    at Break
    Total Luminous ASTM D1003-13
    4 91.2% /
    Transmittance Procedure A

    Note: Pass : Meet the requirements;


    Fail : Does not meet the requirements;
    / : Not Apply to the judgment.
    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 3 of 8

    1.Test Item: 180º Peel Strength


    Sample Description: Tape
    Test Method: With reference to ASTM D3330/D3330M-04(2018) Method A and client's requirement
    Test Condition:
    Specimen width: 25mm
    Testing speed: 300mm/min

    Lab Environmental Condition: 23±2℃, 50±5%RH

    Test Result:

    Sample Test Item Test Result

    A 180º Peel Strength 121N/10mm

    Note: The result was maximum peel force/specimen width.The result was for reference only as the
    adhesive transfer.

    Test Photo:

    Original Sample – Sample A


    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 4 of 8

    During test After test

    Equipment Information:
    Next Calibration
    Equipment Model Equipment No. Calibration date
    date
    Universal Testing
    Z010 GZMR-PL-E109 2020-07-17 2021-07-16
    Machine

    2.Test Item: Haze


    Sample Description: Sheet
    Test Method: ASTM D1003-13 Procedure A
    Test Condition:
    Specimen thickness: 8.15mm
    Light source: C
    Lab Environmental Condition: 23±2℃, 50±5%RH
    Test Result:

    Sample Test Item Test Result

    C Haze 1.1%

    .
    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 5 of 8

    Test Photo:

    Original Sample – Sample C During test

    Equipment Information:
    Next Calibration
    Equipment Model Equipment No. Calibration date
    date
    Hazemeter NDH5000 GZMR-PL-E083 2019-11-14 2020-11-13

    3.Test Item: Tensile Test


    Sample Description: Sheet
    Test Method: ASTM D638-14
    Test Condition:
    Specimen: Type Ⅳ
    Specimen thickness: 0.59mm
    Testing speed: 50mm/min
    Gauge length: 25mm
    Distance between grips: 65mm
    Lab Environmental Condition: (23±2)℃, (50±5)%RH
    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 6 of 8

    Test Result:

    Sample Test Item Test Result

    Tensile Strength 27.0MPa


    B
    Elongation at Break 610%

    Note:
    1. Test specimens were cut from the sample.
    2. The release paper of test specimens was ripped off before test.

    Test Photo:

    Original sample – Sample B During test

    Before test After test


    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 7 of 8

    Equipment Information:
    Next Calibration
    Equipment Model Equipment No. Calibration date
    date
    Universal Testing
    CMT6103 GZMR-PL-E022 2019-09-04 2020-09-03
    Machine

    4.Test Item: Total Luminous Transmittance


    Sample Description: Sheet
    Test Method: ASTM D1003-13 Procedure A
    Test Condition:
    Specimen thickness: 8.15mm
    Light source: C
    Lab Environmental Condition: 23±2℃, 50±5%RH
    Test Result:

    Sample Test Item Test Result

    C Total Luminous Transmittance 91.2%

    Test Photo:

    Original Sample – Sample C During test


    TEST REPORT
    No. : GZIN2007039756MR
    Date : Aug 11, 2020
    Page: 8 of 8

    Equipment Information:
    Next Calibration
    Equipment Model Equipment No. Calibration date
    date
    Hazemeter NDH5000 GZMR-PL-E083 2019-11-14 2020-11-13

    ******** End of report********