Panlite® L-1250Y

TEIJIN LIMITED - Polycarbonate Wednesday, June 5, 2024

General Information
General
Properties • Good Mold Release • Medium Viscosity
Uses • General Purpose
Appearance • Clear/Transparent
Forms • Pellets
Processing Method • Extrusion • Injection Molding

ASTM & ISO Properties 1

Physical Nominal Value Unit Test Method
Density 1.20 g/cm³ ISO 1183
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) 8.0 cm³/10min ISO 1133
Molding Shrinkage Internal Method
Across Flow : 4.00 mm 0.50 to 0.70 %
Flow : 4.00 mm 0.50 to 0.70 %
Water Absorption (24 hr, 23°C) 0.20 % ISO 62
Mechanical Nominal Value Unit Test Method
Tensile Modulus (23°C) 2400 MPa ISO 527-1/1
Tensile Stress (Yield, 23°C) 61.0 MPa ISO 527-2/50
Tensile Strain (Yield, 23°C) 6.0 % ISO 527-2/50
Nominal Tensile Strain at Break (23°C) > 50 % ISO 527-2/50
2 2300 MPa ISO 178
Flexural Modulus (23°C)
2 91.0 MPa ISO 178
Flexural Stress (23°C)
Impact Nominal Value Unit Test Method
Charpy Notched Impact Strength (23°C) 76 kJ/m² ISO 179
Charpy Unnotched Impact Strength (23°C) No Break ISO 179
Hardness Nominal Value Unit Test Method
Rockwell Hardness (M-Scale) 77 ASTM D785
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load ISO 75-2/B
0.45 MPa, Unannealed 142 °C
Deflection Temperature Under Load ISO 75-2/A
1.8 MPa, Unannealed 129 °C
Vicat Softening Temperature 149 °C ISO 306/B50
CLTE - Flow 7.0E-5 cm/cm/°C ISO 11359-2
CLTE - Transverse 7.0E-5 cm/cm/°C ISO 11359-2
RTI Elec (0.75 mm) 125 °C UL 746B
RTI Imp (0.75 mm) 115 °C UL 746B
RTI Str (0.75 mm) 125 °C UL 746B

Disclaimer:
■ The numerical values described in the data sheet are typical numerical values produced with a standard test method, and they do not guarantee the product’s performance in a particular application.
■ The flammability as described in the data sheet is an evaluation that resulted from a small-scale test, and it cannot be applied as it is to evaluate the actual risk of fire.
■ Please contact us if you wish to use the product in medical equipment, food containers and packaging, and toys.
■ If you wish to use various additives (antibacterial agents, stabilizers and flame retardants) or coloring agents with this resin, please consult with Teijin Ltd. beforehand. However, please note that Teijin
Ltd. does not offer any kind of guarantee or bear any responsibility with regards to using this resin in any of these applications.
■ The contents of the data sheet may change without notice.
■ For other details, please see the Material Safety Data Sheet (MSDS) before use.
■ Please contact the Resin & Plastic Processing Business Unit of Teijin Ltd. for detailed data.
■ The raw materials used in our products may be subject to regulations depending on the type of system that exists to manage chemical substances in places to which our products are delivered. In
addition, a separate application may need to be filed depending on the brand. There are also cases where imports of our products are not approved. If you are an importer or exporter and intend to
import or export our products to new destinations, please make sure you contact us for details of regulatory compliance in those destinations.
Panlite® L-1250Y
TEIJIN LIMITED - Polycarbonate
Electrical Nominal Value Unit Test Method
Surface Resistivity > 1.0E+15 ohms IEC 60093
Volume Resistivity > 1.0E+15 ohms·cm IEC 60093
3 30 kV/mm IEC 60243-1
Electric Strength
Relative Permittivity IEC 60250
100 Hz 3.10
1 MHz 3.00
Dissipation Factor IEC 60250
100 Hz 1.0E-3
1 MHz 9.0E-3
Arc Resistance 110 sec ASTM D495
Comparative Tracking Index 250 V IEC 60112
Flammability Nominal Value Unit Test Method
Flame Rating UL 94
1.5 mm HB
0.40 mm V-2
Glow Wire Flammability Index IEC 60695-2-12
1.5 mm 850 °C
3.0 mm 960 °C
Glow Wire Ignition Temperature IEC 60695-2-13
1.5 mm 875 °C
3.0 mm 875 °C
Optical Nominal Value Unit Test Method
Refractive Index 1.585 ASTM D542
Light Transmittance (3000 µm) 88.0 % ASTM D1003

Processing Information
Injection Nominal Value Unit
Drying Temperature 120 °C
Drying Time > 5.0 hr
Processing (Melt) Temp 270 to 320 °C
Mold Temperature 80 to 120 °C

Notes
1
Typical properties: these are not to be construed as specifications.
2
2.0 mm/min
3
short time test

Disclaimer:
■ The numerical values described in the data sheet are typical numerical values produced with a standard test method, and they do not guarantee the product’s performance in a particular application.
■ The flammability as described in the data sheet is an evaluation that resulted from a small-scale test, and it cannot be applied as it is to evaluate the actual risk of fire.
■ Please contact us if you wish to use the product in medical equipment, food containers and packaging, and toys.
■ If you wish to use various additives (antibacterial agents, stabilizers and flame retardants) or coloring agents with this resin, please consult with Teijin Ltd. beforehand. However, please note that Teijin
Ltd. does not offer any kind of guarantee or bear any responsibility with regards to using this resin in any of these applications.
■ The contents of the data sheet may change without notice.
■ For other details, please see the Material Safety Data Sheet (MSDS) before use.
■ Please contact the Resin & Plastic Processing Business Unit of Teijin Ltd. for detailed data.
■ The raw materials used in our products may be subject to regulations depending on the type of system that exists to manage chemical substances in places to which our products are delivered. In
addition, a separate application may need to be filed depending on the brand. There are also cases where imports of our products are not approved. If you are an importer or exporter and intend to
import or export our products to new destinations, please make sure you contact us for details of regulatory compliance in those destinations.