    WM-Z105 is a silane crosslinking halogen-free low smoke flame retardant polyolefin insulation material made from EVA and POE as main materials. It meets various Chinese and international standards for physical properties, mechanical properties, flame retardancy, and electrical properties. The document provides processing, packaging, storage, and transport instructions.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    2 - TDS of LSZH WM-Z105

    Uploaded by

    Muhammad Shabbir Awan
    39 views3 pages
    WM-Z105 is a silane crosslinking halogen-free low smoke flame retardant polyolefin insulation material made from EVA and POE as main materials. It meets various Chinese and international standards for physical properties, mechanical properties, flame retardancy, and electrical properties. The document provides processing, packaging, storage, and transport instructions.

    Original Description:

    THJKHJK JLKJ H HJLJHLJ WHSK JSLJA SLSJ LSHJLA

    Original Title

    2_TDS OF LSZH WM-Z105

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    WM-Z105 is a silane crosslinking halogen-free low smoke flame retardant polyolefin insulation material made from EVA and POE as main materials. It meets various Chinese and international standards for physical properties, mechanical properties, flame retardancy, and electrical properties. The document provides processing, packaging, storage, and transport instructions.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    39 views3 pages

    2 - TDS of LSZH WM-Z105

    Uploaded by

    Muhammad Shabbir Awan
    WM-Z105 is a silane crosslinking halogen-free low smoke flame retardant polyolefin insulation material made from EVA and POE as main materials. It meets various Chinese and international standards for physical properties, mechanical properties, flame retardancy, and electrical properties. The document provides processing, packaging, storage, and transport instructions.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 3

    105℃ Silane crosslinking halogen-free low smoke flame

    retardant polyolefin insulation material

    WM-Z105
    General Information
    Description:
    WM-Z105 is a kind of silane crosslinking halogen-free low smoke flame retardant polyolefin
    insulation material. This product is made from EVA, POE as the main base material, mixed with
    inorganic flame retardant, lubricant, antioxidant etc. It’s applied for production of insulation layer
    for construction wire. The physical and mechanical properties of the wire meet JB/T 10491. The
    flame retardant properties can pass single and A, B, C vertical combustion test specified in GB/T
    18380.
    Standard:
    GB/T 32129-2015

    Specification Sheet
    Product Properties:
    Unit Test method Standard Typical
    Nation International Value Value
    Physical
    HC1&HBr content % GB/T17650.1-1998 IEC 60754-1:1994 ≤0.5 0
    HF content % GB/T17650.1-1998 IEC 60754-1:1994 ≤0.1 0
    pH value — GB/T17650.2-1998 IEC 60754-2:1994 ≥4.3 4.9
    Mechanical
    Tensile strength MPa ISO 527-2:1993, ≥10.0 11.5
    GB/T 1040.2
    Elongation at break % IDT ≥150 200
    Brittleness temperature Piece GB/T 5470-2008 ISO 974:2000, ≤15 0
    (-25℃,30pieces) MOD
    Thermal
    Change of % ±25 +18
    Ageing
    tensile strength IEC60811-1:1985,
    (135±2℃, GB/T 2951.12
    Change of % IDT ±25 -10
    168h)
    elongation
    Immersion Change of % ±30 -4
    test tensile strength GB/T 2951.12 IEC60811-1
    (70±2℃, Change of % ±35 -9
    168h) elongation
    Smoke non-luminous — ≤350 224
    GB/T 8323.2-2008 ISO 5659-2:2006
    density flame
    Add: No.63 Nanhuan Road, Lin’an Economic Developing Zone, Hangzhou(311305), Zhejiang, China
    Tel: 0086 571 63755318 0086 571 63755568 Fax: 0086 571 63755318 0086 571 63755568
    Flame — ≤100 78
    combustion
    Hot set Elongation % ≤100 45
    elongation under load IEC
    (200±3℃, GB/T2951.21-200 60811-2-1:2001,
    Permanent % ≤25 0
    0.2Mpa, 8 IDT
    deformation
    15min)
    after cooling
    Oxygen index % GB/T 2406.2-2009 ISO 4589-2:1996 ≥28 32
    Electrical
    DC volume resistivity Ω·m GB/T 1410-2006 IEC60093:1980,
    ≥1.0x1012 2.0x1012
    (20℃) IDT
    DC volume resistivity Ω·m GB/T 1410-2006 IEC60093:1980,
    ≥2.0x108 4.0x108
    (105±2℃) IDT
    Electric strength MV/m GB/T 1408.1-2006 IEC60243-1:1998,
    ≥20 25
    IDT
    Conductivity μs/mm GB/T 17650-1998 IEC 60754:1994 ≤10 1.1

    Additional Information
    Processing Techniques:
    Extruding techniques：
    It is recommended to use low smoke halogen - free screw, L/D=20-25,compression ratio
    1.2-1.8；As the melt temperature is concerned to the length, compressor ratio of extruding machine

    Position Barrel Ⅰ Barrel Ⅱ Barrel Ⅲ Barrel Ⅳ Head Die


    Temperature（℃） 120 130 140 140 150 150
    Using：
    1. When using this product, mix the A and B components evenly and drop them into the

    hopper. If color is required, the cable factory can use polyethylene base color

    masterbatch and materials within 8 hours after unpacking.

    2. This product should not be shut down for a long time. If it is shut down for a long time,

    it is recommended to stop and clean the screw before starting up again.

    3. In order to ensure the material fully crosslinking, it is recommended that the cable in

    90 ℃ water bath or steam room place three to five hours, concrete placing time

    according to the product thickness and material of crosslinking degree, adjust, satisfies

    the requirement of performance of the cable.

    Add: No.63 Nanhuan Road, Lin’an Economic Developing Zone, Hangzhou(311305), Zhejiang, China
    Tel: 0086 571 63755318 0086 571 63755568 Fax: 0086 571 63755318 0086 571 63755568
    Package, Storage and Transport:
    the A and B groups are kept in different bags, net weight of
    Net weight
    A group is（23.5 ± 0.02）kg and B group（1.5±0.02）kg
    Package
    aluminum foil / polyethylene complex film bag for inner+
    Method
    PP woven bag / PE / Kraft paper bag for outer
    keep away from the sunshine, rain and soaking during
    Transport Requirement
    transport，as well as handle gently during carrying
    Environment clean, dry and ventilated warehouses
    Storage
    Warranty 6 months

    Add: No.63 Nanhuan Road, Lin’an Economic Developing Zone, Hangzhou(311305), Zhejiang, China
    Tel: 0086 571 63755318 0086 571 63755568 Fax: 0086 571 63755318 0086 571 63755568

    You might also like