Chemifix VS DYES

Chemifix 'VS' Dyes are based on β-sulfatoethylsufone reactive system. These dyes have low to medium substantivity/reactivity for
cotton and therefore better recommended for padding and printing applications. However, the substantivity of majority of the dyes
of this group is greatly enhanced after the addition of alkali, because of the generation of vinlsulphone from of dye from its
precursor and therefore can be used for exhaust dyeing also.

EXHAUST DYEING (Winch/jet dyeing):

a)All-in Process: In this method full amount of salt, soda and part of caustic soda are added to the bath in the beginning and the
fabric is run for 10 min at room temperature. Then the pre-dissolved dye is added in two portions and the temperature is raised to
the required level. Then the remaining amount of caustic soda is added and the dyening is contiuned for 60-90 min.
b)Normal Method: Start dyeing at room temperature with required amount of dye and run the machine for 10 min. Start raising the
temperature to the required level @1-20 c min and simultaneously add the salt in two portions over a period of 15 min. After the
“Colors For Right First Time Dyeing” required temperature is reached, alkali is added in two portions and dyeing is continued for 60-90 min. Salt and Alkali
requirements
Dyeing Temperature 600c 400c 300c
Glauber's salt/Common salf (g/l) 40-80 60-90 80-100
soda ash (g/l)
(or) 20 - -
caustic soda solution
(70 Tw cc/l) < 2% shade 1 2 5
> 4% shade 2 3 8
soda ash g/l 5 5 5

Notes:
Turq. Blue G gives maximum colour yeild at 800 C. For Turq, Blue 10-20 g/l soda ash is used as alkali. ...Combination shades with
Turq, Blue G can be dyed at 800 C by proper selection of other components..
it is preferable to use glauber's salt for Blue R, T. Blue G and T, Blue H2GP.

PAD-BATCH DYEING
Dissolve the required amount of dyestuff in hot water and cool the solution to room temperature and add urea (if required). Mix the
dye solution with the alkali just before padding. preferably the dye solution and alkali are fed to the padding trough through a dye
–alkali mixer. Pad the properly pre-treated fabric through the solution at 25-270 c and batch for 20-24 hrs. After fixation is
completed, fabric is given washing-off treatment.

concentration of dye in pad-liquor up to 20 g/l 20 to 40 g/l

urea (g/l) 80 150
sodium silicate (1100 Tw) 100 100
(Nao, sio2 ::1:2.1) (g/l)
Caustic soda (solid) (g/l) 3 3

Notes: 4. DISCHARGE PRINTING :

0range 3R is not recommended above 15 g/l concentration, Majority of the vinylsulfone dyes are suitable for white and
due to poor solubility/ stability of dye in the presence of colored discharge effects. Some of the dyes can be
alkali. discharged to white with netural or weakly alkaline
3. printing discharge paste. General method is as below:
a) print –Dry-steam ( saturated) Method: a)Treat the dyed fabric first with small quantity of Resist
Recipe: salt to protect the ground shade from reductive effect of
Dye................................... X parts printing paste.
Hot water......................... 100-300 parts b)Print the fabric with a paste prepared from the below
Resist salt......................... 10-20 parts mentioned recipe.
Sodium bicarbonate...........10-15 parts Rongalite C.......................... 10-20 parts
Thickening..........................Balance Titanium Dioxide (1:1)......... 10 parts
TOTAL................................. 1000parts Dischagre salt W.................. 6 parts
Thickening agent................. 40 parts
Chemistar offers full range of print-> Dry -> Saturated steam (7-10 min) -> wash off
B) print-> pad ( alkali) – Cold dwell Method: Caustic Soda 380 Be........... 10-20 parts
reactive dyes for dyeing & Printing of Water.................................... 4 parts
prepare print paste as per the above recipe without taking
cellulosic textiles. This shade card alkali. print and dry the fabric. Then pad the dried fabric Total..................................... 100 parts
gives technical information on our through a solution containing 995-950 ml/lit. of sodium After printing, fabric is dried at about 800c and the streamed
range of Reactive Dyestuffs and silicate (500 be/1040 Tw) and 5-50 ml/lit caustic soda for 10-15 min in a star ager. After steaming, fabric is rinsed
(380 be/170 Tw) and batch at room temperature for 20-24 in cold water and then with warm water. It is then soaped
their general application methods. hrs. After batching, the fabric is given usual washing-off with non-ionic or anionic detergent at boil for 15-20 min.
treatment.
VS DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES VS DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES

Exhaust Dying/Fixation Temp (c)

Exhaust Dying/Fixation Temp (c)

0
Light Washing Perspiration 0
Light Washing Perspiration

(Glauber’s Salt/Common Salt)

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application Solubility g/l at 30 C Application

Optimum % shade for

Optimum % shade for

Preferred electroyte

Preferred electroyte
with 50 gpl comm. Salt &

with 50 gpl comm. Salt &

light/pastel Shades

light/pastel Shades
Alkaline (Effect/ Stain)

Alkaline (Effect /Stain)

economical dyeing

economical dyeing
20 gpl soda ash at 300c

20 gpl soda ash at 300c

Dischargeabillity

Dischargeabillity
(AATCC, 16E, 20 AFU)

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

with 50gpl glauber’s

ISO-3 (Effect /Stain)

ISO-4 (Effect/ Stain)

ISO-3 (Effect/ Stain)

ISO-4 (Effect/ Stain)

with 50gpl common

with 50gpl common

Acid (Effect/ Stain)

Acid (Effect /Stain)

Rubbing (Dry/Wet)

Rubbing (Dry/Wet)
(1.0% 2.0% shade)
Suitability for

Suitability for
(1.0%, 2.0% shade)

(1.0%, 2.0% shade)

(1.0% 2.0% shade)
in water at 300C

in water at 300C
Pad Batch Dying

Pad Batch Dying

Chlorinated Water

Chlorinated Water
(ISO-105-B02)

(ISO-105-B02)
Exhaust Dying

Exhaust Dying
salt at 300c

salt at 300c
salt at 300c

salt at 300c
Product Product

(Effect Stain)

(Effect Stain)
1% Shade 4% Shade 1% Shade 4% Shade
Name Name
Reactive Reactive
# #
(C.I. No) (C.I. No)

T.Blue G 100 15 60 10 S S 80OC GS 6 S P 5-6 3-4 4 4 4-5 4 4 2

Yellow FG 100 30 50 20 LS S 600C GS 6 LS G 4 2-3 4 4 4 4 4 2
#Blue 21 6 4 4 3-4 4-5 4-5 3 4
# Yellow 42 5 3 4-5 3-4 4-5 4 3 4

T.Blue H2GP 100 15 60 10 S S 80OC GS 6 S P 5-6 3-4 4 4 4-5 4 4 2

Yellow GR 100 50 80 20 S S 60OC GS/CS 6 S G 4-5 2-3 4-5 4 5 5 4 2
#Blue 21 6 4 4 3-4 4-5 4-5 3 4
# Yellow 15 5 3 4 4 4-5 5 3 4

Golden 100 50 50 10 S S 60OC GS/CS 6 NS G 2-3 2 4 4 4 4 4 2 Blue R 200 20 100 10 S NS 60OC GS 6 LS P 6 4 4-5 4 5 5 4 3

Yellow R 3 2-3 4 3-4 4 3-4 3 4 # Blue 19 6-7 4 5 4 4 4 3 4

# Yellow 77

G.Yellow 100 100 100 30 S S 60OC CS/GS 6 S G 4-5 3 4 4 4 4-5 4 2 Blue BBID 100 40 80 10 S S 60OC GS 6 s G 6 3-4 4-5 4 5 5 4 3

RNL 5 3-4 4-5 4 4 4 3 4 # Blue 220 6-7 4 5 4 4 4 3 4

#Orange107

Orange 2R 60 30 50 10 S LS 60OC GS/CS 6 NS G 3 2-3 4 4 4 4 4 1-2 Black B H/C 100 100 100 30 S S 60OC CS/GS 10 NS G 5* 3-4* 4 4 4 4 4 1-2

# Orange 3-4 3 4 3-4 4 4 3 4 #Black 5 4 3-4 4 4 2-3* 3-4

Orange 3R 60 30 50 10 S LS 60OC GS 5 S G 4-5 3 4-5 4 4-5 4 4-5 2-3 Black B 100 100 100 30 S S 60OC CS/GS 10 NS G 5* 3-4* 4 4 4 4 4 1-2

#Black 5 4 3-4 4 4 2-3* 3-4

#Orange 16 5 3-4 4-5 4 4-5 4-5 3 4

Black RL 100 50 50 20 LS S 60OC CS/GS 5 LS G 5-6 3-4 4 4 4 4 4 2-3

Red 5B 60 40 40 10 NS S - GS/CS 4 S G 3-4 2-3 4 3-4 4-5 4-5 4 2
#Black-31 6 4 4 3-4 4 3-4 2-3* 4
# Red 35 4-5 3-4 4 4 5 5 3 4

Violet 5R 100 50 80 10 S S 60OC GS/CS 4 LS F 5-6 3 4-5 4 5 4 4 2-3

#Violet 5 6 4 4-5 4 5 5 3 4
Chemifix F DYES F DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES

Exhaust Dying/Fixation Temp (c)

0
Light Washing Perspiration

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application

chemifix 'F' Dyes are hetero bifunctional dyes. These dyes contain at least one vinylsulfone and one monochlorotriazine

Optimum % shade for

Preferred electroyte

Alkaline (Effect/ Stain)

econo-mical dyeing
with 50 gpl comm. Salt &

light/pastel Shades
20 gpl soda ash at 300c

Dischargeabillity

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

ISO-3 (Effect/ Stain)

ISO-4 (Effect/ Stain)

with 50gpl common

Acid (Effect /Stain)

(1.0%, 2.0% shade)

Rubbing (Dry/Wet)
(1.0% 2.0% shade)
Suitability for
reactive group and are mainly recommended for exhaust dyeing. These dyes can also be used in pad-batch (sillicate

in water at 300C

Pad Batch Dying

Chlorinated Water
(ISO-105-B02)
Exhaust Dying
salt at 300c

salt at 300c
Product

(Effect Stain)
method) and printing applications. 'F' dyes can be used in combination with vinylsulfone dyes for producing mixture 1% Shade 4% Shade
Name
shades. (all blacks (all blacks
4.0%) 8.0%) Reactive
#
EXHAUST DYEING METHOD (C.I. No)

Winch/jet Dyeing: start dyeing with required amount of dye at room temperature. Run the fabric for 10 min. Add the Yellow F-4G 100 20 80 10 S LS 60OC GS 6 LS G 5 2-3 4-5 4 4 4 4 2-3
required amount of salt in 2-3 portions of 20 min. Continue dyeing for 15 min at room temperature and then add 1/5th
150% 5-6 3 4-5 3-4 4 4 3 4
alkali and raise temperature to 600 C in 20-30 min and continue dyeing at 600 C for 30 min. Add remaining alkali in 2-3
#Yellow160A
portions and continue dyeing for 60-90 min.

Jigger Dyeing Method: Start dyeing at room temperature by adding the required amount of dye and salt over two ends. Yellow F3R 150 80 80 30 S S 60OC CS/GS 6 S F 6 4 4-5 4 5 5 4 2-3
Then give two ends and add half the amount of alkali over two ends and raise temperature to 600 C and add balance 150% 6-7 4 4 3-4 4 4 3 4
quantity of alkali over two ends and dye for further 4-6 ends, depending on the depth.
#Yellow145A

Salt and alkali Requirements:

Orange F2R 60 15 25 5 S LS 60OC GS 5 LS P 4-5 2-3 4-5 4 4 4 4 2-3
% Shade Common Salt Soda Ash
150% 5 3 4 3-4 4 3 3 4
(g/l) (g/l)
#Orange122A
up to 0.1 5-10 10
0.1 to 0.5 15-25 10-15
0.5 to 2.0 25-50 15-20 Red F3B 150 100 100 30 S S 60OC CS/GS 6 S P 4-5 2-3 4 4 4 4 4 3
above 2.0 60< 20
150% 5 3-4 4 3-4 4 4 3 4

#Red 195A
Pad Batch Dyeing and printing Methods generally used for vinylsulfone reactive dyes can be used for 'F' dyes also.

Red FRB, 100 80 80 30 S S 60OC CS/GS 6 S P 4-5 2-3 4-5 4 4 4 4 2

150% 5 3 4 3-4 4 4 3 3-4

#Red 198A

Red FBSID 100 80 80 30 S LS 60OC CS/GS 6 S P 4 2-3 4-5 4 4 4 4 2-3

#Red-111 5 3 4 3-4 4-5 4 3 3-4

N. Blue FBS 100 50 80 30 S S 60OC CS/GS 6 S F 5 3 4 4 4 4 4 2

#Blue 222A 5-6 3-4 4 3-4 4 4 3-4 4

Blue HFBR 100 50 80 30 S S 60OC CS/GS 6 S F 5 3 4 4 4 4 4 2

#Blue 221 5-6 3-4 4 3-4 4 4 3-4 4

Black FGR 100 100 30 10 S LS 60OC CS/GS 10 NS P 5* 3-4* 4 4 4 4 3 3

150% 3-4 3 3-4 3-4 2-3* 4

#Black
Chemifix ME DYES ME DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES

Exhaust Dying/Fixation Temp (c)

0
Light Washing Perspiration

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application

chemifix ‘ME’ Dyes are hetero bifunctional dyes. These dyes contain alteast one vinylusifone and one monochlorotriazine

Optimum % shade for

Preferred electroyte

Alkaline (Effect /Stain)

econo-mical dyeing
with 50 gpl comm. Salt &

light/pastel Shades
20 gpl soda ash at 300c

Dischargeabillity

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

ISO-3 (Effect /Stain)

ISO-4 (Effect/ Stain)

with 50gpl common

Acid (Effect /Stain)

(1.0%, 2.0% shade)

Rubbing (Dry/Wet)
(1.0% 2.0% shade)
Suitability for
reactive group and are mainly recommended for exhaust dyeing. These dyes can be used in pad-batch (silicate method)

in water at 300C

Pad Batch Dying

Chlorinated Water
(ISO-105-B02)
Exhaust Dying
salt at 300c

salt at 300c
Product

(Effect Stain)
and printing applications. ‘ME’ dyes can be used in combination with vinyl sulfone dyes for producing mixture shades. 1% Shade 4% Shade
Name
(all blacks (all blacks
4.0%) 8.0%) Reactive
EXHAUST DYEING METHOD #
Winch/jet Dyeing: Start dyeing with required amount of dye at room temperature. Run the fabric for 10 min. Add the (C.I. No)

required amount of salt in 2-3 portions over a period of 20 min. continue dyeing for 15 min at room temperature and then
add 1/5th alkali and raise temperature to 600C in 20-30 min and continue dyeing at 600C for 10 min. Add remaining alkali
Yellow 100 30 80 20 S LS 60OC GS 6 LS G 5 2-3 4 4 4 4 4 2-3
in 2-3 portions and continue dyeing for 60-90 min.
ME4GL 5-6 3 4-5 3-4 4 4 3 4

#Yellow160A
Jigger Dyeing Method: Start at room temperature by adding the required amount of dye and salt over two ends. Then give
two more ends and add half the amount of alkali over two ends and rise temperature to 600C and add balance quantity of
alkali over two ends and dye for further 4-6 ends, depending on the depth. G.Yellow 150 100 100 30 S S 60OC CS/GS 6 S F 6 4 4-5 4 4 4 4 2-3

MERL Conc 6-7 4 4 3-4 4 4 3 4

#Yellow145A
Salt and Alkali Requirements:
% Shade Common Salt Soda Ash
(g/l) (g/l) Orange 40 15 30 5 S LS 60OC GS 5 LS P 4 2-3 4-5 4 4 4 4 2

up to 0.1 5-10 10 ME2RL 4-5 3 4 3-4 4 4 3 4

0.1 to 0.5 10-25 10-15 #Orange122A
0.5 to 2.0 25-50 15-20
above 2.0 60< 20
Red ME4BL 150 100 100 30 S S 60OC CS/GS 6 S P 4-5 2-3 4 4 4 4 4 3

Conc. 5 3 4 3-4 4 4 3 4
Pad Batch Dyeing and printing Methods recommended for vinylsulfone reactive dyes can be used for ME dyes also. #Red 195A

Red RB conc. 100 80 80 30 S S 60OC CS/GS 6 S P 4-5 2-3 4-5 4 4 4 4 2-3

#Red 198A 5 3 4 3-4 4 4 3 3-4

Red BS 100 80 80 30 S LS 60OC CS/GS 6 S P 4-5 2-3 4-5 4 4 4 4 2-3

#Red 111 5 3 4 3-4 4-5 4 3 4

N.Blue BFID 100 50 80 30 S S 60OC CS/GS 6 S F 5 3 4 4 4 4 4 2

#Blue 222A 5-6 3-4 4 3-4 4-5 4 3 4

Black HFGR 100 100 100* 30 S S 60OC CS/GS 10 NS P 5* 3-4* 4 4 4 4 3* 3

#Black 3-4 3 3-4 3-4 2-3* 4

Chemifix M DYES M DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES

Exhaust Dying/Fixation Temp (c)

0
Light Washing Perspiration

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application

chemifix 'M' dyes are based on Dichlorotriazine reactive system. These dyes are highly reactive and can be applied to

Optimum % shade for

Preferred electroyte

Alkaline (Effect/ Stain)

econo-mical dyeing
with 50 gpl comm. Salt &

light/pastel Shades
20 gpl soda ash at 300c

Dischargeabillity

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

ISO-3 (Effect/ Stain)

ISO-4 (Effect /Stain)

with 50gpl common

Acid (Effect /Stain)

Rubbing (Dry/Wet)
cellulosic material at about 30-400 C.

Suitability for

(1.0%, 2.0% shade)

(1.0% 2.0% shade)

in water at 300C

Pad Batch Dying

Chlorinated Water
(ISO-105-B02)
Exhaust Dying
salt at 300c

salt at 300c
Product

(Effect Stain)
1% Shade 4% Shade
Name
EXHAUST DYEING:
Reactive
Set the dye bath at room temperature with predissolved dye and enter the goods. Run the machine..20-30 min. and then #
add common salt or Glauber's salt. Run the machine for 30-45 min. and add predissolved alkali and continue dyeing for (C.I. No)

60-90 min at room temperature. After dyeing goods are given thorough and efficient washing off treatment.
Yellow M4G 60 20 40 10 S NS 30OC GS/GS 6 S P 5 2-3 4-5 4 4 4-5 4 2

Salt and Alkali Requirement: #Yellow 22 5-6 3 5 4 4-5 5 3 3-4

% Shade Common Salt soda Ash (g/l) at M L R

(g/l) 1.5 1.10 1.20 1.30
Below 0.5 30 5 5 3 3 Yellow MGR 40 10 20 10 S NS 40OC GS 4 LS P 5-6 3 4-5 4 4-5 5 4 3-4

0.5-2.0 40 10 5 4 3 #Yellow 6 3-4 4-5 4 4 4 3 4-5

2.0-4.0 50 15 10 8 5
Above 4.0 60 20 15 10 5

Golden 80 50 50 20 S NS 30OC CS/GS 6 S P 5-6 3 4 4 5 5 4 2

Yellow MR 6 3-4 4-5 3-4 5 5 3 3-4

Notes: Yellow MGR and Blue MR should be dyed at 400C.
#Yellow 44
Use of Glauber's Salt is recommended for Yellow MGR & Blue MR

Orange M2R 100 50 80 30 S NS 30OC CS/GS 6 S P 4-5 2-3 4 4 4-5 4-5 4 2

#Orange 4 5 3 4 3-4 4 4-5 3 4

Red M5B 40 20 20 10 S NS 30OC CS/GS 6 S P 4-5 2-3 4-5 4 5 5 4 2

#Red2 5 3 4 4 4-5 5 3 4

Red M8B 50 10 20 10 S NS 30OC CS/GS 6 S P 4-5 2-3 4 4 4-5 4-5 4 2

#Red 11 5 3 4 3-4 4 4-5 3-4 4

Magenta MB 30 5 15 5 S NS 30OC CS/GS 6 LS P 4 2-3 4 4 4 4 4 2

#Violet13 4-5 3 4 3-4 4 4-5 3 3-4

Blue MR 60 20 40 10 S NS 40OC GS 4 LS P 6 3-4 4 4 5 5 4 3

#Blue 4 6-7 4 4-5 4 5 4-5 3 4

Chemifix RGB DYES RGB DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES
0
Light Washing Perspiration

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application

Optimum % shade for

Preferred electroyte

econo-mical dyeing
with 50 gpl comm. Salt &

light/pastel Shades

Alkaline (Effect/Stain)
Dying/Fixation Temp (c)
Chemifix 'RGB' Dyes are high performance dyes, produced from specialty dyestuff intermediates and reactive groups. These

20 gpl soda ash at 300c

Dischargeabillity

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

ISO-3 (Effect /Stain)

ISO-4 (Effect /Stain)

with 50gpl common

Rubbing (Dry/Wet)
Suitability for

(1.0%, 2.0% shade)

Acid (Effect/Stain)
(1.0% 2.0% shade)
in water at 300C

Pad Batch Dying

1% Shade 4% Shade

Chlorinated Water
dyes have been uniquely formulated by incorporating novel levelling agents and fixing agents to give excellent levelling and

(ISO-105-B02)
Exhaust Dying
salt at 300c

salt at 300c
Product

(Effect Stain)
reproducible result. These dyes can be used for exhaust, continuous and semi-continuous dyeing. Chemifix 'RGB' dyes can (all blacks (all blacks
Name
4.0%) 8.0%)
be used in combination with 'VS' and 'ME' dyes for producing whole gamut of shades.

Salient Features
 Suitable for Exhaust Dyeing at 600C
 Suitable for Continuous Dyeing Chemifix 150 50 100 10 S LS 600c GS 4 S G 4-5 3 4-5 4 4 4 5 3-4
 Excellent shade reproducibility Lemon 5 3-4 4-5 3-4 4 4 4 4
 Versatile Application
Yellow RGB
 Economical for Medium and Dark Shades
 Very Good Shade Build-up
 Very good solubility in water Chemifix 120 80 80 20 S S 600c GS/CS 6 S F 5 4 4-5 4 4-5 4-5 5 3
 Excellent levelling Characteristics
G.Yellow 5-6 4 4-5 3-4 4-5 4-5 4 4
 Eco Friendly Products
 Good alround fastnes properties RGB

EXHAUST DYEING METHOD Chemifix 120 80 80 20 S S 600c GS/CS 6 S P 4-5 3 4-5 4 4-5 4-5 5 4
Winch/soft flow Jet Dyeing : start dyeing with required amount of dye at room temperature. Run the fabric for 10 min. Add
Red 5 4 4-5 4 4 4 4 4
the required amount of salt in 2-3 portions over a priod of 20 min. and raise the temperature to 600 c in 20-30 min. Continue
dyeing at 600 C for 15-30 min. Add alkali in 2-3 portions over a period of 20 min and continue dyeing for 60-90 min. RGB

SALT AND ALKALI REQUIREMENTS Chemifix 100 50 80 15 S S 600c GS 4 N.S G 4 3 4-5 4 4-5 4-5 4-5 3-5

% Shade Common Salt Soda Ash Mixed Alkali (g/I) Deep Red 5 4 4 3-4 4-5 4 4 4

(g/I) (g/I) Soda Ash Caustic soda solid RGB

up to 0.1 5-10 8 8 -
0.1to 0.5 10-40 10-15 10 - Chemifix 150 100 100 20 S S 600c GS/CS 6 S P 4-5 3 4-5 4-5 5 5 4-5 4
0.5 to 1.0 40-50 15-20 5 0.2-0.4
Brill. Red 5 4 5 4-5 5 5 4-5 4
1.0 to 2.0 50-70 20 5 0.4-0.5
RGB
2.0 to 4.0 70-80 20 5 0.5-0.8
Above 4.0 80 20 5 1.0
Chemifix 100 50 80 20 S S 600c GS 4 L.S G 4-5 4 4-5 4 4-5 4-5 4-5 4

Blue 5 4 4-5 4 5 5 4 4

RGB

Chemifix 120 100 100 20 S S 600c GS/CS 6 N.S G – – 4-5 4-5 5 4 4-5 3

Navy Blue 4 3 5 4-5 5 4 4 4

RGB

Chemifix 100 100 100 20 S S 600c GS/CS 8 N.S G 5* 4* 4 4-5 4-5 4 4* 3

*
Black 4 5 4 4 3 4

RGB
SALIENT FEATURES OF RGB DYES Chemifix S/W DYES
Chemifix 'RGB' dyes are high performance dyes. These dyes are uniquely formulated to give on-tone shade build-up and
excellent shade reproducibillity These dyes give best performance in medium and dark shades. chemifix S/W Dyes are High Performance dyes, made from speciality dyestuff intermediates and reactive group. These
days are specially engineered to give high tinctorial value and therefore can be used for producing deep shades by exhaust
dyeing. Chemifix S/W dyes can also be used in combination with regular VS and ME dyes for producing mixture shades.

CHEMIFIX LEMON YELLOW RGB CHEMIFIX BLUE RGB SALIENT FEATURES

 high tinctorial yellow dyestuff  economical blue component for medium shades  Suitable for Exhaust Dyeing at 600 c
 appropriate component for bright green shades  excellent solubility and good levelling
 Possible to produce Deepest Shades
 excellent solubility in water  very good levelling in light and medium shades
 good levelling and wasting off characteristics  excellent shae build-up and medium shades  Very Much Economical for Medium and Dark shades
 gives best results with glauber's salt  good light fastness in medium shades  Excellent shade Build-up
 limited solubility in alkali-preferable to avoid color  suitable for trichromatic combination with G.Yellow  Excellent Solubility in water
addition in alkaline bath for shade correction RGB and Red RGB  Excellent Levelling Characleristics
 dischargeable upto2% shade  Least Sensitivity to Variation in Dyeing Conditions
CHEMIFIX NAVY BLUE RGB  Very Good Fastness to Washing, Rubbing and Light
CHEMIFIX GOLDEN YELLOW RGB  high tinctorial greenish navy shade
 very economical product for g. yellow shades  most economical navy for medium and dark shades
EXHAUST DYEING METHOD
 excellent solubility and good levelling  good trichromatic component for medium and dark
Winch/Soft flow jet Dyeing: Start dyeing with the required amount of dye at room temperature. Run the fabric for 10 min.
 excellent shade build-up and reproducibility shades
 very good light and wet rubbing fastness  not recommended for light shades and for toning
add the required amount of salt in 2-3 protions over a period of 20 min. and raise the temperature to 600 C in 20-30 min.
 suitable for trichromatic combination with Red RGB and  100% dischargeable product and continue dyeing for 60-90 min.
Navy Blue RGB
 dischargeable upto 1.0% shade CHEMIFIX BLACK RGB SALT AND ALKALI REQUIREMENTS
 high tinctorial bluish black
CHEMIFIX RED RGB  most economical for deep blacks % Shade Common Salt Soda Ash Mixed Alkali (g/I)
 economical red component for medium shades  very good shade build-up and reproducibility (g/I) (g/I) Soda Ash Caustic soda solid
 excellent solubility in water  acceptable light fastness
upto 0.1 5-10 8 8 -
 excellent levelling in pastel and light shades  100% dischargeable product
 excellent shade build-up and reproducibility 0.1 to 0.5 10-40 10-15 10 -
 acceptable light fastness in medium shades 0.5 to 1.0 40-50 15-20 5 0.2-0.4
 suitable for trichromatic combination with G.Yellow 1.0 to 2.0 50-70 20 5 0.4-0.5
RGB and Navy Blue RGB
2.0 to 4.0 70-80 20 5 0.5-0.8
 non-dischargeable product
Above 4.0 80 20 5 1.0
CHEMIFIX DEEP RED RGB
 very high tinctorial dyestuff
 most economical component for dull reds, browns and
maroons
 limited solubility in alkali-preferable to avoid color
addition in alkaline bath for shade correction
 gives best results with glauber's salt
 100% discahrgeable product

CHEMIFIX BRILL RED RGB

 very high tinctorial dyestuff
 most economical component for brilliant reds and
scarlets
 excellent solubility in water
 excellent levelling in pastel and light shades
 excellent washing off characteristics
 acceptable light fastness in medium shades
 non-dischargeable product
S/W DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES S/W DYES GENERAL PROPERTIES GENERAL PROPERTIES FASTNESS PROPERTIES
Washing Perspiration Washing Perspiration

Chlorinated Water (Effect /Stain)

Post Mercerization (Effect /Stain)

Chlorinated Water (Effect /Stain)

Post Mercerization (Effect /Stain)

0 0
Light Light

(Glauber’s Salt/Common Salt)

(Glauber’s Salt/Common Salt)

Solubility g/l at 30 C Application Solubility g/l at 30 C Application

Optimum % shade for

Optimum % shade for

Preferred electroyte

Preferred electroyte
Dying/Fixation Temp (0c)

Dying/Fixation Temp (0c)

Alkaline (Effect /Stain)

Alkaline (Effect /Stain)

econo-mical dyeing

econo-mical dyeing
with 50 gpl comm. Salt &

with 50 gpl comm. Salt &

(0.2%, 1.0% 2.0% shade)

(0.2%, 1.0% 2.0% shade)

light/pastel Shades

light/pastel Shades
20 gpl soda ash at 300c

20 gpl soda ash at 300c

Dischargeabillity

Dischargeabillity
(AATCC, 16E, 20 AFU)

(AATCC, 16E, 20 AFU)

with 50gpl glauber’s

with 50gpl glauber’s

ISO-3 (Effect/ Stain)

ISO-3 (Effect/ Stain)

with 50gpl common

with 50gpl common

Depth (% Shade)

Depth (% Shade)
Acid (Effect /Stain)

Acid (Effect /Stain)

ISO-4 (Effect/Stain)

ISO-4 (Effect/Stain)
Rubbing (Dry/Wet)

Rubbing (Dry/Wet)
Suitability for

Suitability for
in water at 300C

in water at 300C
Pad Batch Dying

Pad Batch Dying

1/1 Standard

1/1 Standard
Exhaust Dying

Exhaust Dying
salt at 300c

salt at 300c
salt at 300c

salt at 300c
% Shade % Shade Product % Shade % Shade Product
0.2% 2.0% Name 0.2% 2.0% Name
(All Blacks) (All Blacks) (All Blacks) (All Blacks)
4.0% 8.0% 4.0% 8.0%

Chemifix 2.4 150 50 80 10 S NS 60 GS 4 S G 2-3 4-5 4 4 4 5 4 4-5 Chemifix 2.3 150 100 100 50 S S 60 GS/CS 6 L.S. G - 4 4 4 4 4 3-4 3-4

Yellow S2G 3 4--5 3-4 4 4 3-4 4 4-5 Navy Blue - 4 3-4 4-5 4 3 3-4 3-4

200% 3 SGB, 200% 3

Chemifix 1.68 150 100 100 50 S S 60 GS/CS 4 S F 3 4-5 4 5 5 4-5 4-5 3-4 Chemifix 1.8 150 35 100 15 S S 80 GS 5 S P 4 4 4 4 4 4 2-3 4

Yellow S3R 4 4 4 4 4 3-4 4 4-5 T.Blue S2G 4 4 3-4 4 4 3 2-3 4

200% 4 200% 4

Chemifix 1.5 100 80 80 10 S S 60 GS 4 L.S. G 3 4-5 4 5 5 4-5 4 3-4 Chemifix 2.2 100 50 50 20 S LS 60 GS 4 S P 4 4-5 4 4 4 4 4 4

G.Yellow SR 3-4 4 4 4 4 3-4 4-5 4 Blue SNG 4 4 4 4 4 3-4 4-5 4

200% 4 150% 4

Deep Navy 7.2

Chemifix 1.33 100 80 80 10 S S 60 GS 4 L.S. G 3 4-5 4 5 5 4-5 4 3-4 Chemifix 150 100 100 50 S S 60 GS/CS 6 N.S. G - 4 4 4 4 4 3-4 3-4
* *
Orange W3R 3-4 4 4 4 4 3-4 4-5 4 Navy SRB - 4 4 4 4 3 3-4 3-4*

150% 4 200% 4*

Deep Navy 10
Chemifix 1.36 100 80 80 25 S LS 60 GS/CS 5 L.S. G 3 4-5 4 5 5 5 4 3-4 Chemifix 150 100 100 50 S S 60 GS/CS 8 N.S. G - 4-5 4 4 4 4-5 4 3

Deep Red WB 3-4 4 4 4 4 3-4 4-5 4 Navy WB - 4-5 4 4 4-5 4 4 2-3

150% 4 4*

Chemifix 1.4 100 50 50 25 S LS 60 GS/CS 4 L.S. P 2-3 4-5 4 4 4 4-5 4 3-4 Chemifix 150 100 100 50 S S 60 GS 8 L.S. G - 4 4 5 5 4 3-4 3-4

Deep Black 8
* *
Deep Red SB 3 4-5 4 4 4-5 4 4 3 Black WNN - 4 4 4 4 3 3-4 3-4*

200% 4 H/C 4-5*

Chemifix 1.90 150 100 100 50 S S 60 GS/CS 6 S P 2-3 4-5 4 5 5 4 3-4 3-4 Chemifix 150 80 80 50 S S 60 GS/CS 6 L.S. G - 4 4 5 5 4 3-4 3-4

Deep Black 6
* *
Brill. Red S3R 3 4-5 4 4 4 3-4 3-4 3-4 Black G - 4 4 4 4 3 3-4 3-4*

200% 4 4-5*

Chemifix 1.48 150 100 100 50 S LS 60 GS/CS 5 S P 2-3 4 4 4 4 4-5 3-4 3-4 Chemifix 150 80 80 50 S S 60 GS/CS 6 L.S. G - 4 4 5 5 4 3-4 3-4

Deep Black 6
* *
Red S2Y 2-3 4 3-4 4 4 3-4 4 4 Black - 4 4 4 4 3 3-4 3-4*

200% 3-4 R 4-5*

Chemifix 2.52 150 100 100 50 S LS 60 GS/CS 6 S P 2 4 3-4 4 4 4-5 3-4 3-4 Chemifix 150 100 100 50 S S 60 GS/CS 8 L.S. G - 4 4 4 4 4-5 3-4 3-4

Deep Black 8
Red Win 3 4-5 3-4 4 4 3-4 3-4 4 Black - 4 3-4 4 4 3-4 4 4

H/C 3 CDN 4-5

Chemifix 2.1 150 100 100 35 S LS 60 GS/CS 5 S G 2-3 4-5 4-5 4-5 4-5 4 4 3-4 Chemifix 10 100 80 80 30 S S 60 GS/CS 8 L.S. G - 4 4 4 4 4 3-4 3
*
Navy SG 3 4 4 4 4 3-4 4 4-5 Black - 4 3 4 4 3 4 2-3

200% 3-4 NX 4
SALIENT FEATURES OF S/W DYES
S/W dyes are high tinctorial dyes. Most of the dyes give 100-200% higher strength, when compared with conventional ME
or VS DYES. Therefore, these will give most economical dyeing result in medium and dark shades.

CHEMIFIX YELLOW S2G, 200% CHEMIFIX BRILL RED S3R, 200% CHEMIFIX NAVY SRB, 200%
 high tinctorial product  high tinctorial product  high tinctorial reddish navy shade
 lemon yellow shade, appropriate component for bright  brilliant red  100% dischargeable product
green shades  excellent solubility and good levelling characteristics  most economical navy for medium and dark shades
 excellent solubillity, acceptable light fastness  most economical product for brilliant reds and scarlets  good trichromatic component for medium and dark
 good leveling & washing off characteristics  good light fastness shades
 limited solubility in akali-preferable to avoid color  very good washing fastness  good wet rubbing fastness
addition in kaline bath for shade correction  least sensitive to residual alkali on fabric
CHEMIFIX NAVY WB
CHEMIFIX YELLOW S3R 200% CHEMIFIX RED S2Y,200%  economical Navy Blue
 high tinctorial product  high tinctorial value  100% dischargable product
 very economical product for G.Yellow shades.  brilliant red for scarlet and blood red shades  suitable only for medium and dark shades
 very good light fastness and wet rubbing fastness  excellent solubility, good levelling suitable for  good trichromatic component for dark shades
 excellent solubility, good levelling trichromatic combination with yellow S3R, 200% and
 suitable for trichromatic combination with Red S2Y, navy SG, 200% CHEMIFIX BLACK WNH H/C
200% and Navy SG,200%  least sensitive to residual alkali on fabric  high tinctorial dye
 100% dischargeable product
CHEMIFIX G.YELLOW SR,200% CHEMIFIX RED WIN H/C  suitable for post mercerisation ( under optimum
 Very high tinctorial dye  brilliant red shade conditions) excellent shade build up good light,
 100% dischargeable product  excellent levelling in pastel and light shades washing and wet rubbing fastness
 excellent shade build-up  suitable for trichromatic combination with yellow S3R,  most economical and reproducible jet black
 very economical product for orangish yellow shade 200% and navy SG, 200%
 very good light fastness and wet rubbing fastness CHEMIFIX BLACK G
 most economical toning component for black and CHEMIFIX NAVY SG, 200%  very high tinctorial greenish black dye
navys.  very high tinctorial value  jet black shades can be obtained at 6% shade
 most economical component for dull greens, browns,  excellent levelling in pastel and light shades  very good wet rubbing and washing fastness
etc.  good light fastness  suitable for post mercerisation (under optimum
 suitable for trichromatic combination with red S2Y, conditions)
CHEMIFIX ORANGE W3R 150% 200% and Yellow S3R, 200%  most ecenomical greenish black
 Very high tinctorial dye  gives best results with glauber's salt
 100% dischargeable product CHEMIFIX BLACK R
 excellent shade build-up CHEMIFIX NAVY BLUE SGB, 200%  very high tinctorial reddish black dye
 very good light fastness and wet rubbing fastness  high tinctorial greenish navy shade  jet black shades can be obtained at 6% shade
 most economical toning component for black and  100% dischargeable prdouct  very good wet rubbing and washing fastness
navys.  most economical navyfor medium & dark shades  suitable for post mercerisation (under optimum
 good wet rubbing fastness conditions)
CHEMIFIX DEEP RED WB,150%  most ecenomical jet black
 very high tinctorial product CHEMIFIX T.BLUE S2G, 200%
 100% dischargeable product  very high tinctorial value CHEMIFIX BLACK CDN
 excellent shade build-up  excellent levelling in pastel and light shades  high tinctorial dye
 most economical component for maroons, browns, dull  highest solubility in water and glauber's salt  100% dischargeable product excellent shade build-up
reds  excellent light fastness and wet rubbing fastness  most economical bluish black
 most economical toner for blacks and navys  give best result with glauber's salt
 good light fastness  limited solubility in common salt CHEMIFIX BLACK NX
 economical black dye
CHEMIFIX DEEP RED SB, 200%  good light and washing fastness
 very high tinctorial product CHEMIFIX BLUE SNG, 200%  suitable for post mercerisation (under optimum
 most economical component for dull reds, browns and  high tinctorial royal blue conditions)
maroons  excellent levelling in pastel and light shades
 excellent shade build-up  excellent light fastness
 very good light fastness and web rubbing fastness  gives best results with glauber's salt
 very economical/reliable component for royal blue
shades
 good solubility/stability in alkaline bath
 Chemifix CN DYES CN DYES GENERAL PROPERTIES FASTNESS PROPERTIES
Application Washing
Light Perspiration

(Glauber’s Salt/common Salt)

Solubility in water at 300C
Method

Water Fastness (CH / CO)

Dying/Fixation Temp (c)

Suitability for Light /

Preferred electrolyte
The CHEMIFIX CN dyes are hetero bifunctional reactive dyes for warm exhust dyeing.

Post Mercerization
ISO-105 C2S (CH/CO)
Dischargeabillity

(AATCC, 16E, 20 AFU)

Alkaline (CH/CO)
Pastel shade

(0.1%, 0.5%,1%)

(0.1%, 0.5%,1%)

Chlorinated Water
Exhaust Dyeing
Highly compatible range for Trichromatric shades and high all-round fastness performance.

(ISO-105-B02)

Acid (CH/CO)
0.25% 0.5% Product

(Effect Stain)
Excellent reproducibility and outstanding washing-off properties resulting in increased productivity. Shade Shade Name

Highlights of CHEMIFIX CN Dyer Benefits....

Outstanding speed of washing off Top Productivity
 high degree of fixation (over 80%)  saves water, energy and time Chemifix 100 S 600c GS S G 4 4 5 4-5 4-5 4 Very 5
 medium affinity of the dyes Yellow 5 4-5 5 5 5 Good 5
 very good diffusion Excellent wet and wash fastness
CN2R 6 4-5
 bond to cellulose, stable in both alkaline and  appropriate dye selection fulfills very high
acidic condition requirements (M&S, GAP... etc)
 excellent multiwash fastness (including C10A) Chemifix 100 S 600c GS S G 5 4 5 5 5 2-3 Very 5

Red 5-6 4-5 5 5 5 Good 5

Robust dyeing system outstanding reproducibility Fewer corrections, fewer re-dyeing
 excellent compatibility of the trichromy dyes  right first time CN2BL 6 4-5
 on-tone build up  excellent lab-to-bulk and bulk-to-bulk
 high degree of fixation reproducibility
Chemifix 100 S 600c GS S F 5 4 5 4-5 4-5 3-4 Very 5
 very good leveling properties  improved appearance of the fabric
Blue 6 4-5 4-5 5 5 Good 5
Excellent light fastness CNR 6-7 4-5
High Light fastness combinations  appropriate dye selection fulfills very high
requirements (M&S, GAP, IKEA...etc)

Very good ecological properties Cost Saving

 high degree of fixation (over 80%)  shorter washing off process:saves energy, water
 outstanding washing off, less washing baths and time
needed  less dye in waste water: reduced ecological costs
 AOX-free range

Exhaust Dyeing method for 100% cellulose Salt and alkali recommendations/liquor
600C method with soda ash ratio below 1 : 8
0 0
C F
CHEMIFIX CN % <0.5 0.5 1 2 3 4 >5
90 194
5 Salt* g/I 20 30 40 50 60 70 80
80 176 Soda ash g/I 10 12 14 16 18 20 20
70 158

60 140 Salt and alkali recommendations/liquor

50 122
ratio 1 : 8 and above
40 104 CHEMIFIX CN % <0.5 0.5 1 2 3 4 >5
30 86 Salt* g/I 20 30 40 50 60 70 80
Soda ash g/l 8 10 12 14 16 18 18
0 20 40 60 90 120 min

Aux. Dyes Salt Soda ash

Cold Pad Batch Dyeing on 100% Cellulose

Dyes Concentration in g/I

Alkali System Fixation Time
0
<10 20 30 40 50 60 >70 at 25 C

Sodium Silicate (58 - 60°Be) - g/I

90 90 90 90 90 90 90
(Na20 : Si02 1 : 2.1)
10 —12 hours
Caustic Soda (Solid) g/l - 2 3 3 4 4 5

Note:
 In order to increase the solubility of the dyes and reduction of substantivity as well as cooling of the pad liquor,
the use of 30-50 gpl Urea is recommended.
 Fixation (Dwelling) time is 10 —12 hours depending on the depth of the shade.
Chemifix Ultra 3D dyes
Chemifix Ultra 3D reactive dye series with an innovative chemistry, have been specially designed considering the increasing Salt & Alkali (Soda ash only) recommendations
market requirements for TOTAL COST-EFFECTIVENESS in dyeing. These innovative dyes are focused on cost reduction, better
dye yield and good overall fastness properties. Dye (% owf) 1 - 2% 2 - 3% 3 - 4% Above 4%

Chemifix Ultra 3D - Saves... Salt in g/I 30 - 40 40 50 60

• Dyes Consumption • Water consumption • Salt consumption • Energy consumption
• Effluent load reduction like TDS level, BOD & COD level etc • Production cost Soda ash in g/I 12 - 15 15 - 18 18 - 20 20

Problem & Challenges presently faced in Dark shade dyeing

• High Percentages of conventional dyestuffs required Salt & Mixed Alkali recommendations
• High amounts of water and energy required for washing off processes
• Reduction in overall fastness properties, especially wet fastness Dye (% owf) 1 - 2% 2 - 3% 3 - 4% Above 4%
• Cost of production is higher
Salt in g/I 30 - 40 40 - 50 50 - 60 60
Chemifix Ultra 3D dye range offers solutions to the above problems due to the following features
• Very high build-up properties Soda ash in g/I 5 5 5 5
• Good Washing-off properties
• Good Overall fastness properties Caustic soda (flakes) in g/l 1.0 1.0 1.5 1.5
• Most economical receipe cost
Note: Turquoise based shades are to be dyed with Isothermal dyeing method at 80°C using Glauber's salt for the best dyeing results.

Special Features Benefits

• Highest Build up Deepest shades are possible with lowest amount of dyes & hence dyes Consumption will be
reduced considerably offering cost effectiveness
• High degree of Fixation Shorter washing off cycles; saves energy, water and time.
• Excellent Washing off Drastically reduces water consumption, saves times & energy, reduced effluent load and
overall increased productivity with lowest processing cost
• Excellent compatibility Excellent lab to bulk & bulk to bulk Shade reproducibility Very good level dyeing
• Most Economical receipes Cheapest dye receipe cost & cheapest over all production cost

Exhaust Dyeing method for 100% cellulose unmercerized

60°C Mixed Alkali Method using Soda ash & Caustic soda

60°C 10' 30' 5' 30' 45'

1°C/min

10' 30' 10' D E

40°C Drain &
Washing off

A, B C

A - Auxiliaries B - Salt C - Dyes D - Soda Ash E - Caustic Soda

- Addition / Injection - Dosing

Ultra3D GENERAL PROPERTIES FASTNESS PROPERTIES Ultra3D GENERAL PROPERTIES FASTNESS PROPERTIES
Washing Chlorinated Perspiration Washing Chlorinated Perspiration
Solubility g/l at 300C Application Light Solubility g/l at 300C Application Light
Water/ISO Water/ISO

Post Mercerization CH/CO

Post Mercerization CH/CO

ISO 105 EO4 ISO 105 EO4

Dyeing/Fixation Temp (0c)

Dyeing/Fixation Temp (0c)

105 EO3 105 EO3

ISO-105 Co6, C2S, CH, CO

ISO-105 Co6, C2S, CH, CO

Damage/M & S C10A

Damage/M & S C10A

Rubbing (Dry/Wet)

Rubbing (Dry/Wet)
AATCC 6 1-2A, CH, CO

AATCC 6 1-2A, CH, CO

Dischargeabillity

Dischargeabillity
Oxidative Bleach

Oxidative Bleach
Depth (% Shade)

Depth (% Shade)
20 gpl soda at 300c

20 gpl soda at 300c

Pad Batch Dyeing

Pad Batch Dyeing

AATCC 16E, 20AFU

AATCC 16E, 20AFU

with 50 gpl Salt &

with 50 gpl Salt &

in water at 300C

in water at 300C
Exhaust Dyeing

Exhaust Dyeing
1/1 Standard

1/1 Standard
ISO 105 BO2

ISO 105 BO2

Alkaline CH/CO

Alkaline CH/CO
salt at 300c

salt at 300c
Product Product

with 50gpl

with 50gpl
4% Shade 4% Shade

Acid CH/CO

Acid CH/CO
Name Name
CH/CO CH/CO

Chemifix 2.2 150 50 20 S NS 60 G 5-6 3 4-5 4 2-3 4 4 4 2 4 Chemifix 1.4 100 80 50 S S 60 G 6 4 4-5 4 4 4 4 4 3-4 4

Ultra Lemon 4-5 4 4 4 4 3-4 3 Ultra 4-5 4-5 4-5 4 4 4-5 3

3D Caramine 3D

Chemifix 1.0 150 100 100 S S 60 F 6-7 4 4-5 4 4 5 4 4 3-4 4 Chemifix 0.85 200 150 100 S S 60 G 6 4 4-5 4-5 4 4 4 4 3-4 4

Ultra Yellow 4-5 4-5 4-5 4 4 4-5 3-4 Ultra Rust 4-5 4-5 4 4 4 4-5 3-4

3D Red 3D

Chemifix 1.1 150 10 100 S S 60 F 6-7 4 4-5 4 4 4-5 4-5 4 3-4 4-5 Chemifix 1.7 200 35 15 S S 80 P 6-7 4 4-5 4 2.3 4 4 4 3-4 4

Ultra Sun 4-5 4 4 4 4 4 4 Ultra 4 4 3 4 4 4-5 3

Yellow 3D Turquoise 3D

Chemifix 1.15 150 100 100 S S 60 F 6-7 4 4-5 4 3-4 4 4 4 4 4 Chemifix 2.3 200 100 80 S S 60 P 7 4-5 4-5 4-5 4 4-5 4-5 4 3-4 4

Ultra Golden 4-5 4 4 4 4 3-4 3 Ultra 4-5 4-5 4 4-5 4 4-5 3

Yellow 3D Ocean 3D

Chemifix 2.2 80 25 10 S NS 60 P 5 3 4 4 2 3-4 4 4 2 4 Chemifix 2.2 200 100 80 S S 60 P 7 4-5 4-5 4-5 4-5 4-5 4-5 4 3-4 4

Ultra 4-5 4-5 4 4 4 3-4 3 Ultra 4-5 4-5 4 4-5 4 4-5 3-4

Orange 3D Royal 3D

Chemifix 1.3 150 100 100 S S 60 P 6 4 4-5 4-5 3 4 4 4 3 4 Chemifix 1.55 200 50 25 S LS 60 P 7 4-5 4-5 4-5 4 4-5 4-5 4 3-4 4

Ultra 4-5 4 4 4 4 3-4 3 Ultra Brilliant 4-5 4-5 4 4-5 4 4-5 3

Scarlet 3D Blue 3D

Chemifix 1.25 150 100 100 S S 60 P 5-6 3-4 4-5 4 3 4 4 4 3 4 Chemifix 2.1 200 100 100 S S 60 G 6 3-4 4-5 4 4 4-5 4-5 4 3-4 4

Ultra 4-5 4 4 4 4 3-4 3 Ultra 4-5 4 4 4-5 4 4-5 4

Red 3D Blue 3D

Chemifix 1.15 150 100 100 S S 60 P 5-6 3-4 4-5 4 3-4 4-5 4 4 3 4 Chemifix 7.2 200 100 100 S S 60 G 5-6 3-4 4-5 4-5 4 4 4-5 3 3 4

Ultra 5 4-5 4 4-5 4-5 3-4 3 Ultra 4-5 4 4-5 4 4 4 4

Rubine 3D Navy 3D

Chemifix 1.0 150 80 50 S S 60 F 6 4 4-5 4-5 3 4 4 4 3 4 Chemifix 6.0 200 100 100 S S 60 G 5-6 3-4 4 4 3-4 4 4-5 4 3 4

Ultra 4-5 4-5 4 4 4-5 3-4 3 Ultra Jet 4 4 4 4 4 4 3

*
Bordeaux 3D Black 3D

* 8% Shade
Washing off: To achieve best possible fastness properties, it is essential to remove the unfixed /hydrolysed dye completely
from substrate. Following sequence can be used for this purpose.

Cold rinse -> Hot rinse -> Neutralise (with acertic acid) -> soap (1-3 times)-> Hot rinse -> Cold rinse.

Soaping can be done with 1-2 g/l non_ ionic or anionic detergent or polymeric washing off agent at boil for 15min
(M:L:1:15 to 1:20)

FASTNESS PROPERTIES
Fastness of dyed material to various agencies was assessed as per the standard test methods at 1/1 std. depth,
mentioned below:
Washing: ISO-3 and ISO-4 (Ratings by greyscale: 1-poor, 5-excellent)
Rubbing: ISO 105X12 (Rating by greyscale: 1-poor, 5- excellent)
Light: AATCC 16E 20hrs. (for blacks at 8.0% shade) (color change ratings by greyscale : 1-poor, 5-excellent)
Perspiration: ISO 105-E04 (Ratings by greyscale : 1-poor, 5-exceellent)
Chlorinated water: ISO 105-E03 (Rating by greyscale : 1-poor, 5-excellent)
Post Mercerisation: 300g/l caustic soda solution at 20 C for 5min. Followed by cold rinsing and neutralization with sulfuric
acid.(Ratings by greyscale: 1-poor, 5-excellent)
Note : 1 since post mercerization results are more sensitive to processing conditions/sequence, the data mentioned in this
shade card is only indicative, without any guarantee/assurance.
Note: 2. Standard depth was determined by using 40s mercerised poplin fabric, M:L::1:10, common salt: 60gpl, soda
ash:20gpl:Dyeing time: 90min.

KEY TO ABBREVIATIONS:
S=Suitable LS=less Suitable NS=Not Suitable
Dischargeabillity: G=Good F=Fair P=Poor
(The information contained herein is provided in good faith but without any warranty)

This information and our technical advice are given in good faith but without warranty. Our advice, does not release you from
the obligation to check its validity and to test our products as to their suitability for the intended processes and uses. The
application, use and processing of our products and the products manufactured by you on the basis of our technical advise are
beyond our control and therefore, entirely your own responsibility.
Chemistar Intermediates Pvt. Ltd.
Regd. Office & Works: Plot No. : 2709, Phase-lV,
G.I.D.C. Vatva, Ahmedabad-382 445. Gujarat, India
Phone: +91-79-4008 3311, 4008 3315
Fax: +91-79-4008 3318
Email: [email protected] l website: www.chemistar.net