CAP-HYDROSEAL

ACRYLIC MODIFIED FLEXIBLE CEMENTITIOUS

DESCRIPTION  To provide protection to foundations and basements.

 As a water proof coat to roofs.
CAP-HYDROSEAL is a cementitious, polymer modified,
 For tile adhesion in water retaining structure.
surface coating composed of two component.
A. Powder – A blend of special cement, silica sand and
auxiliary chemicals. ADVANTAGES
B. Liquid – Modified acrylic dispersion with wetting  Water proofing.
agents.  Creates a flexible membrane.
 Breathable.
It is applied by slurry brush, in two or more coats to the  Resistant to abrasion.
surface that will be in contact with water. During  Excellent adhesion.
membrane built up, a mesh glass fabric is embedded in  Resistant to frost and de-icing salts.
between the coats to provide extra strength to the  High resistance to carbon dioxide and chloride ion
coating and to enable gaps and angles to be bridged and diffusion.
coated effectively.  Ease of placement on horizontal, vertical and
overhead surfaces.
FEATURES  Efficient to arrest carbonation.
The cementitious dry mortar powder and the polymer
dispersion are balanced, so that mixing of two TYPICAL PROPERTIES
components results in a brushable compound. Plastic density (A+B):
After application, the bulk of the water evaporates and 1900 kg/m3.
the polymer forms a tough rubbery film which bridges Working time:
over fine cracks and water proofs the concrete without Approx. 30 minutes at 250C.
impeding water diffusion. Owing to the presence of
dispersed polymer, the fresh concrete treated with Tensile strength:
CAP-HYDROSEAL no longer carbonates and the chloride >380 kg/cm (3mm thick, reinforced membrane);
penetration is considerably suppressed. CAP-HYDROSEAL ASTM D-412.
is non-toxic and does not contain chlorides, or any other
Weight loss:
salts which could cause efflorescence.
Max. 20%; ASTM C-836.
COLOR Non-volatile content:
Min. 80%; ASTM C-836.
Grey.
Adhesion in peel:
USES >175 N/m; ASTM C-836.
 As a water proof lining for water retaining structures Service temperature:
like storage tank, swimming pool etc. -55 to +1000C.
 For coating sea water channels, ie. canals, culverts, Fire rating:
sewers etc. Non-combustiable.
 Protection of concrete against carbonation and
Toxicity:
chloride ion attack.
Non-toxic.
 Water proofing of new and existing buildings.

Rev.: 02 Mar 2015 Page 1 of 2 Ref No.: ACC/R&D/1503/CEM/0013

 CAP-HYDROSEAL
ACRYLIC MODIFIED FLEXIBLE CEMENTITIOUS

APPLICATION INSTRUCTIONS Drying time:

Prevent premature drying, protect from extreme heat, direct
Surface preparation:
sunlight, wind, rain and frost for at least 24 hours. Allow to
The surface must be level, free of dust, oil and grease.
cure for minimum 7 days.
Remove laitance, contamination and looseparticles. For
(Curing time varies with humidity, temperature and
substrate preparation, use of high pressure water jets and
substrate porosity).
sand blasting equipment are recommended. Any sharp edges
Once cured, surface should be flushed with several changes
and ridges should be rounded off to attain a flawless coat of
of water before water pond testing.
uniform thickness. The concrete must be adequately wetted
to avoid rapid water loss from fresh slurry or the conctere
surface must be primed with an acrylic primer to reduce
Finishing:
suction by the substrate to avoid plastic cracking and pin All CAP-HYDROSEAL treatment that may be subject to
holes. mechanical damage must be protected by a concrete,
cement, tile or other protective screed.
Mixing:
 CAP-HYDROSEAL is supplied in precisely proportioned Cleaning:
units ready for mixing (pre-conditioned material at The tools should be cleaned with water before
250C). CAP-HYDROSEAL hardens. Cured material can be removed
 Pour liquid component in a clean mixing container. mechanically.
 Add powder component gradually while stirring slowly
with a ¾” drill and mixing paddle. COVERAGE
 Mix to uniform consistency. Overmixing may entrap air.
A kit of CAP-HYDROSEAL will cover approximately 10 m2 at
 Mix for 3 to 5 minutes after addition of all components.
 The pot life of CAP-HYDROSEAL is approximately 20 to 1 mm thickness.
30 minutes depending on ambient conditions.
PACKAGING
Application: CAP-HYDROSEAL is supplied in 20kg kit that includes part A
 Throughly work the material either by brush or trowel and B.
into the substrate, make sure the rounded edges are fully
coated. Do not apply coats thicker than 1.5 mm.
 While the coat is still wet, embed fiberglass mesh into STORAGE
the coat. Use the trowel to work the material up and CAP-HYDROSEAL should be stored over pallets in a cool dry
through the mesh until it is completely embedded. place. Shelf life will be 12 months in unopened bags.
 Allow an overlapping of 50 to 100mm wide on each
side as well as over upstands. SAFETY PRECAUTIONS
 Apply the second or subsequent coat of 1.5mm thick
CAP-HYDROSEAL does not contain toxic materials. Care
after the previous coat has dried. The second coat
should be taken to avoid inhalation of dust and to prevent
should not cause the first coat to displace.
material entering into eyes
 Smooth over by flat edge, creating a smooth voidless
membrane.

TECHNICAL SERVICE:
Our Technical Service Department is available at any time to advise you in the correct use of this product or any other Ahlia products.
Note : The information presented herein is based on the best of our knowledge and expertise for which every effort is made to ensure its reliability. Although
all the products are subjected to rigid quality tests and are guaranteed against defective materials and manufacture, no specific guarantee can be extended
because results depend not only on quality but also on other factors beyond our control.
As all Ahlia Technical Data Sheets are updated on a regular basis, it is the user responsibility to collect most recent issue.

Rev.: 02 Mar 2015 Page 2 of 2 Ref No.: ACC/R&D/1503/CEM/0013