Data Sheet CuZn20Al2As

CuZn20Al2As is a brass alloy with excellent corrosion resistance due to its aluminum and arsenic content. It is primarily used for condenser tubes and finned tubes in river and domestic water applications. The alloy has excellent resistance to sea water and resistance to dezincification. It has good formability when hot and fair formability when cold. Joining can be done through resistance welding, inert gas shielded arc welding, and hard and soft soldering.

Uploaded by

Jean Carlos Reyna Pascual
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
55 views1 page

Data Sheet CuZn20Al2As

CuZn20Al2As is a brass alloy with excellent corrosion resistance due to its aluminum and arsenic content. It is primarily used for condenser tubes and finned tubes in river and domestic water applications. The alloy has excellent resistance to sea water and resistance to dezincification. It has good formability when hot and fair formability when cold. Joining can be done through resistance welding, inert gas shielded arc welding, and hard and soft soldering.

Uploaded by

Jean Carlos Reyna Pascual
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

EMH-Brass Tubes in CuZn20Al2As

CuZn20Al2As is a special brass with Chemical Composition * Material Description


excellent corrosion resistance due to the
Cu 78 % EN CuZn20Al2As, CW702R
addition of aluminium and arsenic. This
material is primarily used for condenser Zn Rest UNS C68700
tubes and finned tubes for river and Al 2% DIN * CuZn20Al, 2.0460
domestic water applications.
As 0.04 % BS * CZ110

* Standard values in % by weight NF * Cu-Zn22Al

* former national standards

Physical Properties * Processing Properties Heat Treatment

Electrical conductivity Melting point 930 – 970 °C


Forming
MS/m 12.5 Hot forming 750 – 820 °C
Machinability 30 %
% IACS 22 (CuZn39Pb3 = 100%) Soft annealing 700 – 750 °C, 1-3h

Cold forming Thermal


550 – 600 °C, 1-3h
fair stress-relieving
Thermal conductivity
W/(m*K) 100 Hot forming fair

Corrosion Resistance
Joining
Thermal expansion coefficient
Special brass alloys have in general an
(0 – 300 °C) 10-6/K 19.0 Resistance welding fair
excellent resistance to corrosion. This
Inert gas shielded arc welding good alloy has an excellent resistance as far
Density Hard soldering fair as sea water is concerned and is also
g/cm³ 8.3 Soft soldering poor not prone to dezincification.

Surface Treatment
Modulus of elasticity
GPa 103 Polishing
mechanical excellent
* Standard values at room temparature
1 GPa = 1 kN/mm²
1 MS/m =1 m/Ω • mm electrolytical excellent

Electroplating excellent

Mechanical Properties (attainable values, depending on the dimension and form)

Standard values from (soft) to (hard)


Rm [MPa] 340 430
Rp 0,2 [MPa] 120 200
A5 [%] 45 50
HB 65 95