FIBERGLAS

™ Fiberglas™ Thermal Insulating Wool (TIW) Types I-HP and II-HP

insulations are off-white, non-combustible wool with resilient, inorganic

THERMAL INSULATING
glass fibers bonded with a thermosetting resin. TIW Type I-HP insulation
is available in rolls; TIW Type II-HP insulation comes in batts.

WOOL (TIW) TYPES I-HP

& II-HP INSULATIONS
Features Physical Properties
• Excellent thermal performance helps contribute to lower energy costs PROPERTY TEST METHOD VALUE
due to reduced heat loss — savings1 may vary
• Easy to handle and install Density ASTM C167 Type I-HP: 1.0 pcf (16.1 kg/m3)
Type II-HP: 2.5 pcf (40.1 kg/m3)
• The insulation is easily impaled over welded studs or pins, or may be
held in place with wire ties, metal lath, or lagging
• There is no tendency for pin-hole elongation under vibration situations Operating Temperature ASTM C411 Rated to 1,000°F (538°C)
Range3
— a frequent source of heat leaks in heavy products
• Large batts or blankets cover greater areas quickly, eliminating tedious Water Vapor Sorption ASTM C1104 <5% by weight at 120°F (49°C),
95% R.H.
block-by-block hand layup and drilling for studs in hard insulations
• TIW is non-corrosive, and will not accelerate corrosion on copper, Fungi Resistance ASTM C1338 Meets requirements
aluminum, or steel per ASTM C1617/C665. CORROSION TEST METHOD VALUE
RESISTANCE
1 Savings vary. Find out why in the seller’s fact sheet on R-values. Higher R-values mean
greater insulating power. Corrosion to Copper ASTM C665 Pass - copper and aluminum
and Aluminum
Corrosion to Steel ASTM C1617 Pass
Standards, Codes Compliance Stress Corrosion ASTM C795 and Pass
Evaluation on External ASTM C692
• ASTM C553, Mineral Fiber Blanket Thermal Insulation, Types I, II, III, Stress Corrosion Cracking
IV, V, VI — Type I-HP and Type II-HP Tendency of Austenitic
• ASTM C612, Mineral Fiber Block & Board Thermal Insulation, Types Stainless Steel
IA, IB, II, III; Category 1 — TIW Type II-HP Chemical Analysis for Cl-, ASTM C795 and Results fall within
• ASTM C795, Thermal Insulation for Use Over Austenitic Stainless Steel2 Fl-, Na+, SiO3 ASTM C871 acceptability limits
• Nuclear Regulatory Commission Guide 1.36, Non-Metallic FIRE TEST METHOD VALUE
Thermal Insulation2
• Mil. Spec. MIL-DTL-32585, Insulation, Thermal and Acoustic, Fibrous Surface Burning UL 723, ASTM E84, UNFACED:
Characteristics4 CAN/ULC-S102 Flame Spread Index 0
Glass; Types I and II; Forms 1 and 2 Smoke Developed Index 0
• Mil. Spec. MIL-I-22023D (Ships), Insulation Felt, Thermal and Sound
Absorbing Felt, Fibrous Glass, Flexible, Types 1 & 2, Class 3 — TIW 3 Maximum allowable thickness at 1,000°F (538°C); Type I-HP — 8.5 inches
Type I-HP (216 mm); Type II-HP — 6 inches (152 mm).
• MIL-DTL-I-24244D (Ships) Insulation Material with Special Corrosion, 4 The surface burning characteristics of these products have been determined in
Chloride, and Fluoride Requirements2; Type XVI accordance with UL 723, ASTM E84, and CAN/ULC-S102. Values are reported to the
• U.S. Coast Guard Approval No. 164.109, Non-combustible Materials nearest 5 rating.
• Complies to ASTM E136, Behavior of Materials in a Vertical Tube
Furnace at 750°C (Non-combustible rating)
• CAN/CGSB-51.11 Class 4, Type 1 for TIW Type I-HP and Class 4, Thermal Conductivity5
Type 2 for TIW Type I-HP. MEAN k MEAN λ
TEMPERATURE °F (Btu•in/hr•ft2•°F) TEMPERATURE °C W/m•°C
2 Preproduction qualification testing complete and on file. Chemical analysis of each
TYPE TYPE
production lot testing required for total conformance. TYPE TYPE
I-HP II-HP
I-HP II-HP
75 0.24 0.22 25 0.034 0.031
100 0.25 0.23 50 0.039 0.034
200 0.33 0.28 100 0.049 0.041
300 0.42 0.34 150 0.060 0.049
400 0.53 0.41 200 0.075 0.059
500 0.69 0.51 250 0.095 0.071
600 0.88 0.63 300 0.119 0.086

5 Apparent thermal conductivity values determined in accordance with ASTM practice

C1045 with data obtained by ASTM test method C177. Values are nominal, subject to
normal testing and manufacturing tolerance.

Product Data Sheet | Fiberglas™ Thermal Insulating Wool (TIW) | March 2023
Applications Availability
• Fiberglas™ TIW Type I-HP Insulation is used in applications up to TIW TYPE I-HP (ROLLS ONLY)
1,000°F (538°C) at maximum recommended thickness requiring a
lightweight insulation, such as that used in panel systems, flexible THICKNESS WIDTH LENGTH NUMBER OF
(IN.) (IN.) (FT.) LAYERS
wrap, industrial ovens, or surfaces having irregularities. Its low
compressive strength makes it unsuitable for use as a base wool for 1" 87 2 layers
metal mesh blankets. 1.5" 58 2 layers
• Fiberglas™ TIW Type II-HP Insulation is especially suitable for use in
2" 24", 36" & 48" 87 1 layer
metal mesh blankets and for use on boilers, vessels, and many other
types of industrial equipment operating at temperatures up to 1,000°F 3" 58 1 layer
(538°C) at maximum recommended thickness. It may also be used in 4" 44 1 layer
panel systems for precipitators, ducts, and breechings
where more compressive resistance than Fiberglas™ TIW Type
I-HP Insulation is needed. TIW TYPE II-HP (BATTS ONLY)
THICKNESS WIDTH LENGTH NUMBER OF
(IN.) (IN.) (IN.) LAYERS
Technical Information 1" to 4"
24" & 36" 48" N/A
(1/2" increments)
TIW Type I-HP and Type II-HP are usually impaled over welded pins
on flat surfaces. For irregular surfaces, they are cut in segments and
impaled over welded pins to hold in place.
Certifications and Sustainable Features
See Installation Instruction Pub No. 10025339. • Certified by SCS Global Services to contain an average of
53% recycled glass content, 31% pre-consumer, and 22%
post-consumer
Thermal Performance, ASTM C6806
THICKNESS OPERATING TEMPERATURE, ˚F (˚C)
400 (204) 600 (316) 800 (427) 1,000 (538)
IN. (MM) HL ST HL ST HL ST HL ST
1 25 109 182 241 275 435 394 699 533
2 51 61 143 136 201 249 281 409 379
TIW Type I-HP

3 76 43 126 95 171 174 230 287 305

4 102 32 116 73 153 133 201 221 262
5 127 27 110 59 141 108 182 179 233
6 152 22 106 49 133 91 168 151 213
Environmental and Sustainability
7 178 19 102 43 126 79 157 130 198 Owens Corning is a worldwide leader in building material systems,
8 203 17 99 38 121 69 150 114 186 insulation, and composite solutions, delivering a broad range of
1 25 81 160 167 225 289 306 453 404 high-quality products and services. Owens Corning is committed
to driving sustainability by delivering solutions, transforming
TIW Type II-HP

2 51 45 128 92 167 159 219 251 282

3 76 31 115 63 145 109 183 173 229 markets, and enhancing lives. More information can be found at
4 102 23 107 48 131 84 162 132 198 www.owenscorning.com.
5 127 19 109 39 123 68 148 106 180
6 152 16 99 33 117 57 139 89 167
Disclaimer of Liability

6 The above table provides approximate heat loss values (HL), Btu/hr•ft2, and surface Technical information contained herein is furnished without charge or obligation
and is given and accepted at recipient’s sole risk. Because conditions of use may
temperatures (ST), ˚F, for flat surfaces. Values are based on horizontal heat flow,
vary and are beyond our control, Owens Corning makes no representation about,
vertical flat surface, 80˚F ambient temperature, still air, and weathered aluminum and is not responsible or liable for, the accuracy or reliability of data associated with
jacket. To convert heat loss values to W/m2, multiply values by 3.15. To convert particular uses of any product described herein.
surface temperatures, use the formula: °C = (°F-32)/1.8.
SCS Global Services provides independent verification of recycled content in
building materials and verifies recycled content claims made by manufacturers.
For more information, visit www.SCSglobalservices.com.
Sound Absorption Coefficients
ASTM C423; Type A Mounting7 — Material placed against solid backing
Notes
PRODUCT THICKNESS 1/3 OCTAVE BAND CENTER FREQUENCIES (Hz) For additional information, refer to the Safe Use Instruction Sheet (SUIS) found in the
TYPE SDS Database via http://sds.owenscorning.com.
INCHES (mm) 125 250 500 1000 2000 4000 NRC
Savings1 vary. Find out why in the seller's fact sheet on R-values. Higher R-values
TIW Type I 1 25 0.08 0.38 0.76 0.81 0.92 0.96 0.75 mean greater insulating power.
2 50 0.18 0.75 1.10 1.06 1.00 1.01 1.00
TIW Type II 1 25 0.12 0.46 0.95 1.07 1.04 1.06 0.90
2 50 0.32 1.19 1.25 1.17 1.11 1.13 1.20

7 Nominal samples were measured in accordance with ASTM C423. These measured
absorption coefficients were adjusted to values representative of the product with
mean specification properties. While these values are an accurate representation
of our product, they are for design approximations only. Production, testing, and
application variabilities will alter results. Specific designs should be evaluated in end-
use configuration. OWENS CORNING INSULATING SYSTEMS, LLC
ONE OWENS CORNING PARKWAY
TOLEDO, OH 43659 USA
1-800-GET-PINK®
www.owenscorning.com

Pub. No. 14729-U. Printed in U.S.A. March 2023.

The color PINK is a registered trademark of Owens Corning. © 2023 Owens Corning. All Rights Reserved.