MARITRANS TECHNICAL DATA SHEET

Date: 01.06.2018 – Version 18

Transparent, liquid-applied polyurethane waterproofing membrane


Product description Advantages

The MARITRANS is a transparent, hard-elastic, one • Simple application (roller or airless spray).
component, aliphatic polyurethane, high-solids coating, used • When applied forms seamless transparent membrane.
for long-lasting waterproofing. This high-technology coating is • UV stable
UV-stable, non-yellowing, weather stable, alkali and chemical • Resistant to water and frost.
resistant and even after aging it remains transparent and • Crack-bridging
elastic. • Provides water vapor permeability, so the surface can breathe.
The MARITRANS protects and waterproofs mineral surfaces • Provides excellent thermal resistance, it does not turn soft.
against water penetration, frost, smog and acid rain. Aged and • Provides excellent weather resistance.
oxidized plastic surfaces look more transparent after coating • Maintains its mechanical properties over a temperature span of
with MARITRANS. It waterproofs damaged glass surfaces -40oC to +90oC.
and protects of glass fragments in case of breaking. • Provides excellent adhesion to ceramic tiles and glazed surface
 • The waterproofed surface can be used for domestic (low)
The MARITRANS is used also as a transparent binder resin pedestrian traffic.
for sandcarpet floor coating applications, especially in exterior
• Resistant to detergents, oils, seawater and domestic chemicals.
applications where flexibility and UV stability is required.
• Even if the membrane gets mechanically damaged, it can be
easily repaired locally within minutes.
The MARITRANS is using a unique curing system (moisture
• Used as a binder resin for sandcarpet applications, provides
triggered), and unlike other similar systems it does not react
high elasticity and flexibility, making it ideal for applications on
with moisture (moisture-cured) and does not form bubbles.
balconies and terraces.
• Over 10 years of positive feedback worldwide.

Uses Consumption

• Transparent waterproofing of Balconies and Terraces 0,8 - 1,2 kg/m2 in two or three layers.
• Transparent waterproofing of Ceramic surfaces This coverage is based on application by roller onto a smooth
• Transparent waterproofing of Glass and Glass-Bricks surface in optimum conditions. Factors like surface porosity,
• Transparent waterproofing and protection of Natural Stones temperature and application method can alter consumption.
• Transparent waterproofing of Transparent Plastics
(e.g. Polyacrylate, Polycarbonate)
• Transparent waterproofing and protection of Wood Colors

Also used as a transparent binder resin for sandcarpet exterior The MARITRANS coating is supplied transparent.
floor coating applications.

Technical Data *
PROPERTY RESULTS TEST METHOD
Composition Polyurethane high-solids pre-polymer
Elongation at Break 322% DIN EN ISO 527
Tensile Strength 25.4 N/mm 2 DIN EN ISO 527
E-modulus 69.5 N/mm 2 DIN EN ISO 527
Tear resistance 56.9 Ν/mm DIN ISO 34, Method Β
Elongation at break after 2000h of accelerated aging 298% DIN EN ISO 527
(DIN EN ISO 4892-3, 400 MJ/m2)
Tensile strength after 2000h of accelerated aging 25.5 N/mm 2 DIN EN ISO 527
(DIN EN ISO 4892-3, 400 MJ/m2)
Gloss retention after 2000h of accelerated aging Good DIN 67530
(DIN EN ISO 4892-3, 400 MJ/m2)
Surface chalking after 2000h of accelerated aging No chalking observed. DIN EN ISO 4628-6
(DIN EN ISO 4892-3, 400 MJ/m2) Chalking grade 0
Hardness (SHORE D Scale) 25 ASTM D 2240
Water vapor permeability 8.05 gr/m2 .24hours EN ISO 12572
Resistance to Water Pressure No Leak (1m water column, 24h) DIN EN 1928
Adhesion to absorbent ceramic tile >2,0 N/mm 2 (ceramic tile failure) ASTM D 903 (ELCOMETER)
Hydrolysis (5% KOH, 7days cycle) No significant elastomeric change Inhouse Lab
Service Temperature -40oC to +90oC Inhouse Lab
Tack Free Time 6-8 hours
Light Pedestrian Traffic Time 24 hours Conditions: 20oC, 50% RH
Final Curing time 7 days
Chemical Properties Good resistance against detergents, seawater and oils.
Application as a Transparent Waterproofing Coating.
Surface Preparation
Careful surface preparation is essential for optimum finish and durability.
The surface needs to be clean, dry and sound, free of any contamination, which may harmfully affect the adhesion of the membrane.
Maximum moisture content should not exceed 5%. New concrete structures need to dry for at least 28 days. Old coatings, dirt, fats,
oils, organic substances and dust need to be removed. Activate (prime) and degrease glass and glazed surfaces with the
MARISEAL® TILE-PRIMER. Possible surface irregularities need to be smoothened. Any loose pieces and dust need to be thoroughly
removed. Do not wash surface with water!

ATTENTION: Surfaces with trapped moisture (e.g. trapped moisture under tiles) must be left to dry completely (max. 5% moisture),
before the application of the MARITRANS coating.
WARNING: Do not apply the MARITRANS on ceramic surfaces with ascending nitric salts in the joints, without suitable pre-
treatment. Do not apply the MARITRANS on surfaces treated in the past with active silane, siloxane, silicon or other water-
repellents, because of expected poor adhesion. We recommend an adhesion test, if circumstances and surface history are not clear.
On marble and granite please perform an adhesion test, to ensure that adhesion is proper.

Repair of cracks and joints:


The careful sealing of existing cracks and joints before the application is extremely important for long lasting waterproofing results.
Clean concrete cracks, hairline cracks, expansion joints and control joints of dust, residue or other contamination. Prime locally with
the MARISEAL 710 Primer and allow 2-3 hours to dry. Fill all prepared cracks and joints with MARIFLEX PU 30 sealant. Allow to
cure.

Priming (Activation of surface)


Prime (activate) non-absorbent glazed surfaces, like glazed ceramic tiles, glass and glass bricks with MARITRANS® TILE-PRIMER.
Apply the MARITRANS® TILE-PRIMER by soaking a clean and dry cloth, and wipe the entire surface off. By this application
procedure, you ensure that besides the chemical activation (priming) of the surface, the surface is getting also very effectively
degreased. Change cloths often. Make sure that enough quantity of MARITRANS ® TILE-PRIMER is applied on the entire surface to
primed and make sure that you do not leave any untreated spots.
ATTENTION: If applied on transparent plastics (polycarbonate, polyacrylate, etc) do not use the MARITRANS ® TILE-PRIMER.

Transparent waterproofing membrane


Pour the MARITRANS coating onto the primed surface and lay it out by roller or by suitable teeth trowel, until all surface is covered.
After 12 hours - but not later than 18 hours –apply a second layer of the MARITRANS coating, by using roller or brush.
For better waterproofing and wear resistance results, apply a third layer of the MARITRANS coating.
ATTENTION: Do not apply the MARITRANS over 1mm thickness (dry film) per layer. For best results, the temperature during
application and cure should be between 5oC and 35OC. Low temperatures retard cure while high temperature speed up curing. High
humidity may affect the final finish.

Finishing
If a satin matt surface is desired, apply one layer of the MARITRANS FINISH.

WARNING: The MARITRANS and/or the MARITRANS SYSTEM is slippery when wet. In order to avoid slipperiness during wet
days, sprinkle suitable aggregates onto the still wet coating to create an anti-slip surface. Please contact our R+D Dept. for more
details.

Application as a Binder Resin for Sandcarpet Coating.


Surface Preparation
Careful surface preparation is essential for optimum finish and durability.
If applied on MARISEAL 250 make sure that the surface is clean, dry and sound, free of any contamination, which may harmfully
affect the adhesion of the sandcarpet coating. Maximum moisture content should not exceed 5%. Possible surface irregularities need
to be smoothened. Any loose pieces and dust need to be thoroughly removed. Do not wash surface with water!

If applied onto concrete, make sure that the surface is clean, dry and sound, free of any contamination, which may harmfully affect
the adhesion of the membrane. Maximum moisture content should not exceed 5%. New concrete structures need to dry for at least
28 days. Old coatings, dirt, fats, oils, organic substances and dust need to be removed. Possible surface irregularities need to be
smoothened. Any loose pieces and dust need to be thoroughly removed. Do not wash surface with water!

Priming
Prime concrete surfaces with MARISEAL 750 primer and broadcast silica sand while still wet.

Sandcarpet Coating
Mix the MARITRANS with colored Silica Sand (corn size 0,7-1,2mm or 2,0-3,5mm) in a mixing ratio of 1:10 (resin: sand) by
weight, with a low speed mechanical mixer, until the mixture becomes fully homogenous.
Pour the mixture onto the prepared surface and apply by flat trowel.

For best results, the temperature during application and cure should be between 5oC and 35OC. Low temperatures retard cure while
high temperature speed up curing. High humidity may affect the final finish.
Packaging
MARITRANS is supplied in 20 kg, 10 kg, 5 kg and 1kg pails. Pails should be stored in dry and cool rooms for up to 9 months.
Protect the material against moisture and direct sunlight. Storage temperature: 5 0-300C. Products should remain in their original,
unopened containers, bearing the manufacturers name, product designation, batch number and application precaution labels.

Safety measures
MARITRANS contains isocyanates. See information supplied by the manufacturer. Please study the Safety Data sheet.
PROFESSIONAL USE ONLY.

Our technical advice for use, whether verbal, written or in tests, is given in good faith and reflect the current level of knowledge and experience with our products. When using our products, a detailed object-related
and qualified inspection is required in each individual case in order to determine whether the product and /or application technology in question meets the specific requirements and purposes. We are liable only for
our products being free from faults; correct application of our products therefore falls entirely within your scope of liability and responsibility. We will, of course, provide products of consistent quality within the scope
of our General Conditions of Sale and Delivery. Users are responsible for complying with local legislation and for obtaining any required approvals or authorizations. Values in this technical data sheet are given as
examples and may not be regarded as specifications. For product specifications contact our R+D department. The new edition of the technical data sheet supersedes the previous technical information and renders
it invalid. It is therefore necessary that you always have to hand the current code of practice.
* All values represent typical values and are not part of the product specification.