BRS016 - Silicon FKM

FKM Cord Adhesive BRS016
TYPICAL APPLICATIONS PRODUCT DESCRIPTION

BRS016 is specially formulated for the bonding of plastics, BRS016 is a medium viscosity modified Ethyl
rubbers, wood, paper, leather, metals and other common Cyanoacrylate adhesive. BRS016 is suitable
substrates. for bonding a very wide range of materials,
BRS016 relies less on surface moisture for cure speed than including some porous ones, where a fast
standard cyanoacrylates. Recommended for use on close- cure speed is required.
fitting parts and fairly smooth, even surfaces
PROPERTIES OF UNCURED MATERIAL

TYPICAL CURING PERFORMANCE
Chemical type Ethyl Typical Speed:
Appearance Clear Steel/steel <20 seconds
Specific Gravity 1.06 ABS/ABS <10 seconds
Viscosity cPs1 Rubber/Rubber <5 seconds
– range 80-120
– typical value 100 Wood (balsa) <3 seconds
Tensile Strength2 (N/mm2) 21

Fixture Time (secs) 3-20
Full Cure (hours) 24
16
Flash Point (C) > 85
Shelf Life @ 5C (months) 12 14
Max Gap Fill (mm) 0.15 20 %
12
Operating Temperature Range (C) -50 to +80
10 30 %
1 ISO 3104/3105
2
ISO 6922
8 40 %
6
50 %
4
Cure speed vs. environmental conditions
2 60 %
Cyanoacrylates require surface moisture on the substrates in 0
order to initiate the curing mechanism. The speed of cure is 1 2 3 4 5 6 7
reduced in low-humidity conditions. Low temperatures will Cure vs Humidity
also reduce cure speed. All figures relating to cure speed
are tested at 21oC .
Cure speed vs. substrate

The speed of cure of Cyanoacrylates varies according to the substrates to be bonded. Acidic surfaces such as
paper and leather will have longer cure times than most plastics and rubbers. Some plastics with very low
surface energies, such as polyethylene, polypropylene and Teflon ® require the use of Procure 77 Primer
(see PC 77 TDS for further info).
Cure speed vs. activator Cure speed vs. bond gap

Activators 780 and 750 may be used in conjunction with
cyanoacrylates where cure speed needs to be accelerated. PROCURE/REACT Cyanoacrylates give best
results on close fitting parts. The product
Cure speeds of less than 2 seconds can be obtained with should be applied in a very thin line in order
most cyanoacrylates. to ensure rapid polymerisation and a strong
bond. Excessive bond gaps will result in
The use of an activator can reduce the final bond strength by slower cure speeds. PROCURE / REACT
up to 30% Testing on the parts to measure the effect is Cyanoacrylate Activators may be used to
recommended. greatly increase cure speeds
(see PC780 and PC750 TDS for further info).
TYPICAL ENVIRONMENTAL RESISTANCE HOT STRENGTH
PROCURE/REACT cyanoacrylates are suitable for use at temperatures up to 80°C. At 80°C the bond will be
approximately 70% of the strength at 21°C. The bond strength at 100°C is approximately 50% of full strength at
21°C.
Polymax Ltd, Building 91D, Prince Philip Barracks, SEME, Budds Lane, Bordon, Hampshire, GU35 0FJ
Tel: 01420 474123 | Fax: 01420 487816 | Email: [email protected]
FKM Cord Adhesive BRS016
Chemical / Solvent Resistance
Cyanoacrylates exhibit excellent chemical resistance to most oils and solvents including motor oil, leaded
petrol, ethanol, propanol and freon.
Cyanoacrylates are not resistant to high levels of moisture or humidity over time.
STORAGE REMOVAL OF CURED CYANOACRYLATE
Store in a cool area out of direct Cured cyanoacrylate may be removed from most substrates,
sunlight. Refrigeration to 5° C gives and parts disassembled, with a Debonder.
optimum storage stability. It is not possible to fully remove cyanoacrylate from fabrics
PRESENTATION Cyanoacrylates is supplied in 20g bottle
DIRECTIONS FOR USE
Bond speed is very fast so ensure that parts are properly aligned before bonding.
Activators may be required if there are gaps or porous surfaces. Some plastics may require application of
Primer.
Ensure parts are clean, dry and free from oil and grease.
Product is normally hand applied from the bottle. Apply sparingly to one surface and press parts firmly
together until handling strength is achieved. As a general rule, as little cyanoacrylate as possible should be
used – over application will result in slow cure speed and lower bond strength.
Please contact your representative for further advice on dispensing solutions.
GENERAL INFORMATION
For safe handling of this product consult the Material Safety Data Sheet.
NOTES AND DISCLAIMER

The information contained herein is produced in good faith and is believed to be reliable but is for
guidance only. We cannot assume liability or responsibility for results obtained in the use of its product
by persons whose methods are outside or beyond our control. It is the user’s responsibility to determine
the suitability of any of the products and methods of use or preparation prior to use mentioned in our
literature and furthermore the user’s responsibility to observe and adapt such precautions as may be
advisable for the protection of personnel and property in the handling and use of any of our products.
Polymax Ltd, Building 91D, Prince Philip Barracks, SEME, Budds Lane, Bordon, Hampshire, GU35 0FJ
Tel: 01420 474123 | Fax: 01420 487816 | Email: [email protected]

BRS016 - Silicon FKM

Uploaded by

Copyright:

Available Formats

BRS016 - Silicon FKM

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

BRS016 - Silicon FKM

Uploaded by

Copyright:

Available Formats

FKM Cord Adhesive BRS016

TYPICAL APPLICATIONS PRODUCT DESCRIPTION

PROPERTIES OF UNCURED MATERIAL

Tensile Strength2 (N/mm2) 21

Cure speed vs. substrate

Cure speed vs. activator Cure speed vs. bond gap

TYPICAL ENVIRONMENTAL RESISTANCE HOT STRENGTH

STORAGE REMOVAL OF CURED CYANOACRYLATE

PRESENTATION Cyanoacrylates is supplied in 20g bottle

DIRECTIONS FOR USE

Please contact your representative for further advice on dispensing solutions.

NOTES AND DISCLAIMER