TECHNICAL DATA SHEET

2023-09-04
18

TEKNOMASTIC 80 PRIMER
Epoxy primer
TEKNOMASTIC 80 PRIMER is a two-pack solvent-borne epoxy primer with
low solvent content.

Use: As a priming coat or as a single coat in abrasion and chemical resistant epoxy coating systems on blast-cleaned steel. Can
also be used for priming zinc, aluminium, thin-plate and acid-proof steel surfaces and as an intermediate coat over zinc epoxy
and zinc silicate primers.

The paint is quickly overcoatable and is therefore suited to a fast painting tempo. The paint film withstands heavy abrasion, oils,
grease, solvents and chemical splashing.
The paint is suitable for maintenance painting of steel surfaces which are cleaned at least to preparation grade St 2, for other
surface preparation methods see Surface preparation.

The paint comes up to the requirements of standard NORSOK M-501:2012 (Edition 6) systems 1, 7A and 7B (Certificates 11-
17-14/1, 11-17-14/2 and 6-9-15/1).

For the product there is also available a WINTER hardener TEKNOMASTIC WINTER HARDENER 7275, which is used when the
painting is done in temperatures below +10°C. When using the WINTER hardener it will strengthen the yellowing and chalking
that is typical for epoxy paints. White and light shades are especially susceptible to yellowing.

TECHNICAL DATA
Certificates, approvals and NORSOK M-501
classification
Recommended substrate Steel, Aluminium, Zinc
Binder Epoxy
Solids 82 ±2% by volume (ISO 3233:1988)
Total mass of solids Approx. 1300 g/l
Volatile organic compound (VOC) TEKNOMASTIC HARDENER 7465 / TEKNOMASTIC WINTER HARDENER 7275
Approx. 200 g/l / Approx. 190 g/l
The VOC value provided is the average value for factory produced products, and
consequently it will be subject to variations between individual products
covered by this TDS.

www.teknos.com 1/6
TECHNICAL DATA SHEET
2023-09-04
18
TEKNOMASTIC 80 PRIMER

Theoretical spreading rate Theoretical spreading rate


Dry film (µm) Wet film (µm)
(m²/l)
80 97 10.2
100 121 8.2
150 182 5.5
200 243 4.1
230 280 3.6

As many of the paint's properties will change if too thick coats are applied, it is
not recommended that the product is applied to a film thickness that is more
than double of the thickest recommended film.
Practical spreading rate The values depend on the application technique, surface conditions, overspray,
etc.
Colours RAL colours mentioned in standard NORSOK M-501:2012 (Edition 6). Other
colours by agreement.
Also available as MIOX-pigmented.
Gloss (60°) Semi-gloss
Hardener Comp. B: TEKNOMASTIC HARDENER 7465 or TEKNOMASTIC WINTER
HARDENER 7275
Mixing ratio (A:B) 4:1 parts by volume
Pot life TEKNOMASTIC HARDENER 7465 2 h,
TEKNOMASTIC WINTER HARDENER 7275 1.5 h
Thinner TEKNOSOLV 9506
Storage The storage stability is shown on the label. Store in a cool place and in tightly
closed containers.

DIRECTION FOR USE


Surface preparation Remove from the surfaces any contaminants that might be detrimental to
surface preparation and application. Remove also water-soluble salts by using
appropriate methods. The surfaces are prepared according to the different
materials as follows:

STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation
grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate
improves the adhesion of the paint to the substrate.

ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to


atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned
(SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and
natural sand. It is not recommended according to standard ISO 12944-5 to paint
hot-dip-galvanized objects that are subjected to immersion strain. Painting of
hot-dip-galvanized objects that are subjected to immersion strain must be
discussed separately with Teknos.

www.teknos.com 2/6
TECHNICAL DATA SHEET
2023-09-04
18
TEKNOMASTIC 80 PRIMER

It is recommended that new zinc-coated thin-plate structures are treated with


sweep blast-cleaning (SaS). Thin-plate surfaces that have been weathered to
matt can be treated also with RENSA STEEL washing agent for galvanized
surfaces.

ALUMINIUM SURFACES: Treat the surfaces with RENSA STEEL washing agent
for galvanized surfaces. Surfaces that are exposed to weathering are also
roughened up with sweep blast-cleaning (AlSaS) or sanding.

OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that


might be detrimental to the application of paint (e.g. grease and salts) are
removed. The surfaces must be dry and clean. Old, painted surfaces that have
exceeded the maximum overcoating time are to be roughened as well. Damaged
parts are prepared in accordance with the requirements of the substrate and
the maintenance coating.
From the bare steel surfaces the rust is removed to preparation grade at least
St 2 (ISO 8501-1).

An alternative method to dry cleaning is high-pressure water jetting with a


pressure of over 70 MPa. This water-jetting can be used on intact, well adhering
paint coats and/or on steel. After the water jetting the intact paint coats must
have a rough surface structure. The cleanliness of the steel surface must be Wa
2 (ISO 8501-4:2006) or according to the specification. A flash-rust degree of
maximum M (ISO 8501-4:2006) is allowed before application.
In addition, high pressure water cleaning (HP WC) at 34 – 70 MPa according to
the NACE VIS 7/SSPCS-VIS 4 can also be used as long as the cleanliness level of
SSPC-SP WJ-3/NACE WJ-3 can be reached. A flash-rust degree of maximum M
(NACE VIS 7/SSPCS-VIS 4) is allowed before application.

The place and time of the preparation are to be chosen so that the prepared
surface will not get dirty or damp before the subsequent treatment.

Additional instructive information for surface preparation can be found in


standards EN ISO 12944-4 and ISO 8501-2.

Prefabrication primer: KORRO E Epoxy, KORRO SE Zinc Epoxy and KORRO SS


Zinc Silicate Prefabrication Primers can be used, when required.

www.teknos.com 3/6
TECHNICAL DATA SHEET
2023-09-04
18
TEKNOMASTIC 80 PRIMER

Application MIXING OF THE COMPONENTS: Take into consideration the pot life of the
mixture when estimating the amount to be mixed at a time. Before application
the base and hardener are mixed in right proportion. Stir thoroughly down to the
bottom of the vessel. Inadequate stirring or incorrect mixing ratio results in
imperfect curing and impaired film properties.

Stir thoroughly before use.

Apply preferably by airless spray as only this method provides the


recommended film thickness in a single operation. Suitable airless nozzle size
0.015 - 0.019". Brush or roller can be used for touching up and painting small
areas.

When twin-feed spray is used for application, the mixing ratio of the dosage
pump must be 4:1. The feed pump pressure and the consumption of
components is to be checked during application to ensure of the correct mixing
ratio. The components cannot be thinned if twin-feed spray with fixed ratio is
used.
Application conditions The surface to be treated must be dry. When using the standard hardener the
temperature of the ambient air, the surface and the product shall be above
+10°C during the application and drying period and the relative air humidity
below 80%.
When using TEKNOMASTIC WINTER HARDENER 7275, during the application
and drying period the temperature of the ambient air and the surface shall be
above -5°C and the temperature of the product during mixing and spraying
shall be above +15°C. The surface to be treated must be free from ice.
Additionally, the temperature of the surface to be treated and the product must
be at least +3°C above the dew point of the ambient air.
Thinning If needed, thin the paint with TEKNOSOLV 9506.

www.teknos.com 4/6
TECHNICAL DATA SHEET
2023-09-04
18
TEKNOMASTIC 80 PRIMER

Drying time +23°C / 50% RH (dry film 100 μm)


TEKNOMASTIC HARDENER 7465 / TEKNOMASTIC WINTER HARDENER 7275
- dust free 2 h / 3 h (ISO 9117-3:2010)
- touch dry 6 h / 4 h (ISO 9117-5:2012)
- fully cured 7d/7d
Overcoatable Standard hardener
+10°C +23°C
surface temperature
min. max. * min. max. *
by itself 8h 6 months 4h 6 months
by TEKNOPLAST 50
8h 6 months 4h 6 months
epoxy paints
by TEKNODUR 0050,
TEKNODUR COMBI
3560-05 and
1d 3 months 6h 3 months
TEKNODUR COMBI
340-811 polyurethane
paints
by TEKNODUR COMBI
3560-75 and
TEKNODUR COMBI 1d 1 month 1d 1 month
3430-39 polyurethane
paints
WINTER hardener
-5°C 0°C +10°C +23°C
surface temperature
min. max. * min. max. * min. max. * min. max. *
by itself 1d 2 months 1d 2 months 8h 2 months 4h 2 months
by TEKNODUR COMBI
3560-68
- - - - 10 h 2 months 4h 2 months
or TEKNOPLAST HS
150
by TEKNODUR 0050 - - - - 10 h 2 months 5h 2 months

* Maximum overcoating interval without roughening.

When overcoating the product at low temperatures the lowest usability


temperature of the top coat has to be checked from the appropriate Data sheet.

A completely clean surface is mandatory to ensure the best intercoat adhesion.


If the maximum overcoating interval has been exceeded, the surface must be
roughened before overcoating. Increase in film thickness and rise in the relative
humidity of the air in the drying space slow down the drying process and effect
the overcoating properties.
Cleaning TEKNOSOLV 9506 or TEKNOSOLV 9530.

HEALTH AND SAFETY


Safety and precaution measures See safety data sheet.

www.teknos.com 5/6
TECHNICAL DATA SHEET
2023-09-04
18
TEKNOMASTIC 80 PRIMER

Teknos Group Oy Takkatie 3, P.O.Box 107 FI-00371 Helsinki, Finland Tel. +358 9 506 091

The above information is normative and based on laboratory tests and practical experiences. The information is noncommittal, and we cannot accept liability for the results
obtained under working conditions beyond our control, and consequently the buyer or the user is not released from the obligation to test the suitability of our products for specific
means and application methods under the actual application conditions. Our liability covers only damage caused directly by defects in the products supplied by Teknos. This
product is intended for professional use only. This implies that the user possesses sufficient knowledge for using the product correctly with regard to technical and working safety
aspects. The latest versions of Teknos’ Technical Data Sheets and Safety Data Sheets are available from our homepage www.teknos.com. All trademarks displayed on this
document are the exclusive property of Teknos Group or its affiliated companies.

www.teknos.com 6/6