Technical Data of Powder Coating

The document provides technical data for three powder coating series: 1803, 13.07, and 1308. It lists properties such as gloss, adhesion, impact resistance, flexibility, hardness, resistance to weathering, humidity, and corrosion for each series. The coatings exhibited good adhesion, impact resistance over 23 inch-pounds, indentation over 5mm without cracking, and flexibility by passing a 5mm mandrel test. They also showed high mortar and corrosion resistance along with excellent weathering performance.

Uploaded by

Lahore 4C2
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
162 views1 page

Technical Data of Powder Coating

The document provides technical data for three powder coating series: 1803, 13.07, and 1308. It lists properties such as gloss, adhesion, impact resistance, flexibility, hardness, resistance to weathering, humidity, and corrosion for each series. The coatings exhibited good adhesion, impact resistance over 23 inch-pounds, indentation over 5mm without cracking, and flexibility by passing a 5mm mandrel test. They also showed high mortar and corrosion resistance along with excellent weathering performance.

Uploaded by

Lahore 4C2
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

TECHNICAL DATA OF POWDER COATING

The data given below are typical Allocate to 0.8mm chromatic aluminum panels (65 micron film
thickness). Typical value when tested. Need not necessarily be of current revision

STANDARD Series 1803 Series 13.07 Series 1308


DIN-EN ISO 2813
Gloss 30 + 5 77 + 7 90 + 10
(60o)
Adhesion DIN-EN ISO 2409-2 mm Cross hatch rating Gt0 (100% adhesion)
Impact Resistance ASTM D 2794 5/8’ ball More than 23 inch-pounds without film cracking.
When tested at lower film thickness (i.e. 50-60
micros) most Alcoat PE-F qualities exceed this
value.
Erichsen Cupping DIN-EN ISO 1520 Indentation dept in excess of 5mm without film
Test cracking.
Flexibility DIN-EN ISO 1519 Cylindrical mandrel bending test-passes 5mm
mandrel diameter.
Film hardness DIN-EN ISO 2815 Indentation resistance acc. To Buchholz:>80
Mortar Resistance STM C 207 After 24 hours at specified conditions, mortar is
easily removed from the coating resulting neither in
loss of adhesion nor in surface marring.
Drilling, milling and No flaking of coating.
sawing test
Salt spray resistentce ASTM B 117 No blistering and maximum 1 mm corrosion creep
from scratch 3000 hours.
Resistance to humid D’IN – EN ISO 3231 (021 No blistering and maximum 1 mm corrosion creep
atmosphere SO2) from scratch 30 cycles.
containing (SO2)
Resistance to humid DIN 50017 No blistering and maximum 1 mm corrosion creep
atmosphere from scratch 3000 hours.

Artifical weather ISO 2809 (Subtest DIN No chalking, excellent gloss retention and color
resistance 53231) stability after 1000 hours testing.

Natural weather Florida (Angle of ° 5 to No chalking, excellent gloss retention and color
resistance south stability after 12 month exposure.
UV resistant Xenon test Excellent color stability
Surface spread of BS 476 part 7-1987 Class 1
flame
Fire propagation test BS 476 Part 6-1989 Excellent index of performance