    Rilsan Fine Powders Physical Properties

    Uploaded by

    ธนาชัย เต็งจิรธนาภา

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Rilsan Fine Powders Physical Properties

    Uploaded by

    ธนาชัย เต็งจิรธนาภา
    33 views2 pages

    Original Title

    Rilsan-Fine-Powders-Physical-properties

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    33 views2 pages

    Rilsan Fine Powders Physical Properties

    Uploaded by

    ธนาชัย เต็งจิรธนาภา

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    PHYSICAL PROPERTIES /

    Rilsan® Fine Powders and coatings main properties


    Rilsan® Fine Powders are thermoplastic polyamide 11 powders used primarily for metal coating. These coatings are
    characterized by their excellent durability, with outstanding toughness, impact and abrasion resistance, as well as
    excellent weatherability and corrosion resistance.

    GENERAL PROPERTIES

    Melt. point Standard grades ISO 11357 186-190°C


    Invent grades 201°C

    Vicat point ISO 306 181°C

    natural powders 1.040 g/cm3


    Specific gravity at 20°C ISO 1183 dipping and ES powders, white 1.065 g/cm3
    to 1.25 g/cm3

    at 20°C and 65% RH 0.9 to 1.1% depending on grade


    Water absorption to saturation ISO 62/1 at 20°C and 100% RH 1.6 to 1.9% depending on grade
    at 100°C and 100% RH (boiling water) 2.4 to 3% depending on grade

    PHYSICAL PROPERTIES OF NATURAL RILSAN® MATERIALS

    Laser sintered part Stripped coating


    Tensile modulus 1500 MPa 1000-1200 MPa
    Tensile strength at yield 45-50 MPa 40-45 MPa
    Elongation at yield ISO 527 18-24% 18-24%
    Tensile strength at break 45 MPa 39-47 MPa
    Elongation at break 45% >200%
    Flexural modulus ISO 178 (23°C) 1200 MPa 1100-1200 MPa
    Shore D hardness ISO 868 (20°C) 77 70-85
    Impact strength (Charpy – unnotched) ISO 179 1eU (23°C) No break No break

    ELECTRICAL PROPERTIES OF RILSAN ® COATINGS

    Surface resistivity ASTM D 257 2.4 x 1014 Ω


    at 20°C and 65% RH at 500 V
    Dielectric constant 102 Hz 3.9
    106 Hz 3.1
    Transverse or volume resistivity ASTM D 257 1014 to 1016 Ω.cm
    at 20°C and 65% RH at 500 V
    Tangent of the angle of loww (power factor) 0.05
    at 1,000 V R.M.S., with a current
    of 1,000 Hz (at 20°C and 65% RH)
    Resistance to surface tracking DIN 53-480 Grade KA3c
    KA method
    Dielectric rigidity ASTM D 149
    ES powders thickness ± 100 μm 55 to 90 kV/mm
    Dipping powders, thickness 350 to 450 μm 30 to 36 kV/mm
    Dielectric strength 0.20 mm 52.8 kV/mm
    Influence of the thickness studied 0.43 mm 38.4 kV/mm
    on a natural coating 0.70 mm 34.7 kV/mm
    (measured at 20°C and 65% RH) 0.90 mm 33.1 kV/mm
    SPECIFIC PROPERTIES OF RILSAN ® COATINGS

    Hardness measured with a Persoz pendulum at 20°C ISO 1522 200-280

    Surface hardness at 20°C, 10s under load DIN 53-456 80N/mm²

    Scratch resistance ISO 1518 59 N


    Clemen apparatus; load necessary to induce a scratch
    which reaches the underlying metal for a coating
    of 0.4 mm thickness

    Pencil hardness ECCA T4 Note: B

    Shear strength ASTM D 732 35-42N/mm2

    Impact resistance ASTM G14 >2J


    Dip coating powder (thickness 350 μm) ISO 3678 > 2.5 J
    ES powders (thickness 100 μm)

    Arkema France - A French «Société Anonyme» registered with the Commercial and Companies Register of Nanterre (France) under number 319 632 790
    ISO 6272 > 19 J

    Abrasion resistance ISO 9352 15mg


    Taber abrasimeter (wheel type CS 17, load 1 kg)
    Loss of weight after 1,000 cycles

    Coefficient of friction NFT 54-112 (8)


    Black powders Static K 0.15-0.3
    Dynamic K 0.05-0.2

    Dircom - 4416E/05.2015/20 - PA Spe - Photos: Arkema, Thinkstock, Fotolia - Design C. Dessirier - Rythmic
    Flexibility ISO 6860 > 35%
    Conical mandrel folding

    Specific heat 2.09kJ/kg.K

    Thermal conductivity 0.29 W/mK between 50° and 170°C

    Latent heat of fusion 83.7kJ/kg

    Inflammability ASTM D 635 self-extinguishing


    measured at a thickness greater than 3 mm
    to eliminate the influence of the substrate

    Resistance to boiling water ISO 1521 Excellent adhesion


    after 2,000 hours; neither bubbing nor modification

    Resistance to outdoor exposure ASTM D 1235 3 years Florida exposure: Excellent adhesion

    Resistance to salt water No corrosion after 10 years exposure

    Salt spray resistance ISO 9227on scribed < 1mm corrosion after 2000 hours
    primed plates
    (testing according
    to WIS 4-52-01)

    Disclaimer - Please consult Arkema’s disclaimer regarding the use of Arkema’s products on
    http://www.arkema.com/en/products/productsafety/disclaimer/index.html

    Headquarters: Arkema France


    420, rue d’Estienne d’Orves
    92705 Colombes Cedex – France
    rilsanfinepowders.com Tel.: 33 (0)1 49 00 80 80
    Fax: 33 (0)1 49 00 83 96
    [email protected] arkema.com

    You might also like