High-strength and ultra-highstrength thermomechanically rolled fine-grain steels

Technical terms of delivery for heavy plates

voestalpine Grobblech GmbH www.voestalpine.com/grobblech

High-strength and ultra-highstrength thermomechanically rolled fine-grain steels

alform plate Steel grades

High-strength: alform plate 700 M Ultra-high-strength: alform plate 960 M x-treme

More information you will find in our technical terms of delivery for thermomechanically rolled steels.

Subject to change pursuant to further development. The current version is available at www.voestalpine.com/grobblech

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

alform plate 700 M and alform plate 960 M x-treme

The high-strength steel grade alform plate 700 M and the ultra-high-strength steel grade alform plate 960 M x-treme are thermomechanically rolled fine-grain structural steels with excellent weldability and good bending properties.

The alloying concept provides very low carbon contents and low carbon equivalents, which aims in very good weldability. The high strength provide special advantages in areas, where weight savings are of great importance, e.g. for mobile cranes, concrete pump cars and vehicles. The technical terms of delivery apply for plate thickness from 8 60 mm for alform plate 700 M and for plate thickness from 8 - 15 mm for alform plate 960 M x-treme.

Steel grades
Steel grades
Steel grades alform plate 700 M alform plate 960 M x-treme

Table 1: Steel grades

Production process
alform plate 700 M and alform plate 960 M x-treme are produced via the LD-route.

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Chemical composition
Heat analysis

Guaranteed values
mass in % C Steel grades alform plate 700 M alform plate 960 M x-treme max. 0.12 0.12 Si max. 0.60 0.60 Mn max. 2.10 1.70 P max. 0.020 0.020 S max. 0.008 0.008 Altot. min. 0.020 0.020 Cr max. 1.50 1.50 Mo Ni V1) max. 0.12 0.12 Nb1) Ti1) B max. 0.0050 0.0050

Table 2: Chemical composition

max. max. 0.50 0.70 2.00 2.00 max. max. 0.06 0.06 0.05 0.05

1)

The total of Nb, V und Ti must not exceed 0.22%.

The chemical composition of alform plate 700 M is according to EN 10149-2 for steel grade S700MC. The chemical composition of alform plate 960 M x-treme is according to EN 10025-6 for steel grade S960QL.

Carbon equivalent

Standard values for carbon content and carbon equivalent

Plate thickness Steel grades alform plate 700 M alform plate 960 M x-treme mm 15 40 8 - 15 C % 0.04 0.06 0.08 CEV1) % 0.43 0.47 0.56 CET2) % 0.26 0.26 0.31 PCM3) % 0.18 0.19 0.24

Table 3: Carbon content and equivalent

1) 2) 3)

CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15, according to IIW CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40, according to SEW 088 PCM = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5*B, according to API 5L

As-delivered condition
Plates of alform plate 700 M are delivered in a thermomechanical rolled condition with accelerated cooling. Exceptionally conventional quenching and tempering is permitted. Plates of alform plate 960 M x-treme are delivered in a thermomechanically rolled condition with accelerated cooling and tempering.

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Mechanical properties
Mechanical properties in as-delivered condition
Plate thickness range Steel grades mm 8 < 15 alform plate 700 M > 15 < 50 > 50 < 60 alform plate 960 M x-treme 8 < 15 Yield strength YS min. MPa 700 680 650 960 Tensile strength1) Rm MPa 770 - 1,050 770 - 1,050 770 - 1,050 980 - 1,150 Fracture elongation1) L0 = 5,65 S0 min., % 10 12 12 10 Notch impact energy2), min. J 40 40 40 30

Table 4: Mechanical properties

1) 2)

Tensile test in accordance with EN 10002 on transverse samples. Notch impact bending test in accordance with EN 10045 on Charpy-V longitudinal samples at 40 C. The mean value from 3 individual samples must reach the specified requirements. No individual value may be below 70% of the guaranteed mean value. For thicknesses < 10 mm, samples similar to Charpy-V with dimensions of 10 x 7.5 mm or 10 x 5 mm are tested. The guaranteed value is reduced in proportion to the sample cross-section.

The mechanical properties of alform plate 960 M x-treme are according to EN 10025-6 for steel grade S960QL.

Quality test
Test unit
Unless otherwise agreed upon ordering, 40 t of a heat or a smaller portion is used as test unit for the mechanical properties. The test unit must consist of plates with the same steel grade and the same thickness range for the yield strength according to table 4.

Scope of testing
Quality testing includes the tensile test. The notch impact bending test is carried out on longitudinal samples at 40 C. A different sample position or testing temperature must be agreed on request. The heat analysis is provided as proof of the chemical composition.

Tolerances and surface finish

Unless otherwise agreed, tolerances pursuant to EN 10029 (thickness tolerance according to class A, flatness tolerance according to class N), and surface finish according to EN 10163-A1 are valid. On request and surcharge we offer reduced flatness tolerances according to table 5 for alform plate 700 M.

Flatness tolerances
Measure in mm Normal, Class N alform plate 700 M Steel group H acc. to EN10029 Measuring length Plate thickness > 8 < 15 > 15 < 25 > 25 < 40 > 40 < 60 1000 10 10 9 8 2000 14 13 12 12 1000 10 10 9 8 2000 14 13 12 12 1000 7 7 7 6 Reduced, Class S alform plate 700 M Steel group H acc. to EN10029 Measuring length 2000 12 11 11 10 1000 7 7 7 6 2000 12 11 11 10

Table 5: Flatness tolerances

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Marking
In general, marking consists of: voestalpine symbol Steel grade designation Heat number Plate number

Material testing certificate

Type of certificate accordig to EN 10204 must be agreed upon ordering.

Processing guidelines
Cold forming
Plates of alform plate 700 M and alform plate 960 M x-treme provide good cold forming properties.On condition that cut edges have been ground very smooth and that the bending process is done skillfully 90-bending without cracks is guaranteed for die-radius of minimum 3x plate thickness for alform plate 700 M and for die-radius of minimum 4x plate thickness for alform plate 960 M x-treme.

Hot forming and heat treatment

Heavy plates of alform plate 700 M and alform plate 960 M x-treme are in thermomechanically rolled condition and are intended for cold forming. Hot forming and stress relief annealing are possible up to 580 C. For optimum toughness properties of the weld we recommend stress relief annealing up to max. 520 C. Tensile strength of alform plate 700 M will decrease within the guaranteed values in table 4 compared to delivery condition due to heat input. Normalizing and quenching and tempering deteriorate the microstructure of TMCP-steels and therefore are not to be processed.

Welding
General information Thermomechanically rolled high-strength and ultra-high-strength steels alform plate 700 M and alform plate 960 M x-treme have excellent weldability, which results of a low carbon equivalent (CEV), and in particular, a low carbon content (C). The low CEV and C values provide reduced hardening in the heat-affected zone (HAZ) of welds. This leads to greater resistance to cold cracking (picture 1). However, despite this advantage, in view of the high yield point of the steel grade, it is advisable to take extra care during welding. The generally valid and accepted rules for the welding of low-alloyed, higher-strength fine-grain structural steels according to EN 1011-2 and STAHL-EISEN Werkstoffblatt (SEW) 088 must be observed.

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Hardening in heat-affected zone (HAZ)

400

Picture 1: Hardening in HAZ

380

360 Max. hardness in HAZ [HV10]

340

320

300

280

260 0 .5 0.6 0.7 0.8 0.9 1.0 1.1 1.2 1.3 1.4

Arc energy [kJ/mm]

alform plate 960 M x-treme alform plate 700 M

heat-affected zone (HAZ)

Weld preparation, thermal cutting Weld preparation can take the form by machining or thermal cutting. In the case of the latter, preheating is not required for plate thickness up to 20 mm at a workpiece temperature above +5 C. Prior to welding the weld edges must be dry and clean. Welding process All standard automatic and manual welding processes can be employed. Inert gas shielded welding (GMAW, IGSW) with solid wire has the advantage of providing very low hydrogen content in the weld material and is also especially suitable with regard to cold cracking resistance. Filler materials and welding conditions (preheating, welding parameters) The selection of the filler materials should result in a weld that matches the chemical composition and the mechanical-technological properties of the base material. For welding alform plate 700 M ER 110 S-G wires according to AWS A 5.28 are proven for inert gas shielded welding. Type E11018-G basic-coated stick electrodes according to AWS A 5.5 are suitable for shielded metal arc welding, and the wirepowder combination ~ F 10 A4-EM2-M2 according to AWS A 5.23-97 is suitable for submerged arc welding. Recommended filler materials for alform plate 700 M and alform plate 960 M x-treme are given in table 5.

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Base material

Welding process consumable

SAW wire flux BB 24

Steel grades

SMAW FOX EV 85

GTAW

GMAW

Table 6: Recommended welding consumables

NiCrMo 2,5-IG NiCrMo 2,5-IG 3 NiCrMo 2,5-UP Union NiMoCr/ Union X85 X90-IG Union X96/X90

alform plate 700 M

Phoenix SHNi2K100 Phoenix SHNi2K130

Union S 3 NiMoCr UV 421 TT

alform plate 960 M x-treme

You will find more information at www.boehler-welding.com and www.t-put.com. Experienced welding engineers are at your disposal.

As a result of their high strength, such welded joints show a higher tendency to cold cracking, which can be minimised by the selection of suitable welding conditions. The tendency to crack formation in the HAZ, in general, is distinctly lower than in the weld metal due to the lower hardening characteristics of the base metal. For reasons of cold cracking prevention, the hydrogen content in the weld material should be very low (HD < 3 ml/100g WM). This is guaranteed by inert gas shielded welding with solid wire. Basic electrodes and welding powder for submerged arc welding must be subjected to secondary drying. The instructions of the manufacturer concerning drying and the method of use to obtain the required hydrogen criterion must be adhered to. The risk of cold cracking can be minimised by moderate preheating in accordance with picture 2, even in case of unfavourable combinations between heat input and plate thickness.

Recommended preheating temperature

alform plate 700 M and alform plate 960 M x-treme
200

Picture 2: Recommended preheating temperature

180

160

Minimum preheating temperature [C]

140

120

100

80

60

40 GMAW (3 ml/100 g WM) SAW (7 ml/100 g WM) 20

0 0 10 20 30 Plate thickness [mm] 40 50 60

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

To ensure the high strength and impact properties of the weld (base material, HAZ and filler metal) cooling times t8/5 of 3 - 15 seconds and interpass temperatures of < 150 C are desirable. Cooling times t8/5 above 15 seconds are permitted under special conditions (e.g. overmatching, ...) but are to be proven by the welder in every case. Standard values for the arc energies to maintain the given cooling times are contained in picture 3.

Standard value for cooling time t8/5 acc. to EN 1011-2 annex B

alform plate 700 M and alform plate 960 M x-treme
Arc energy E [kJ/mm]
0.4 0.6 80 20 3 60 3 0.8 1.0 1.2 80 6 1.4 20 6 1.6 1.8 80 9 2.0 2.2 2.4 2.6 2.8 3.0 3.2 20 15 60

Picture 3: Standard value cooling time

20 Preheating temperature [C] 80 9 Cooling time t8/5 [s] 15

26 - 56

56

56

26

26

24

24

22

22 21

Plate thickness [mm]

20

20

18

18
2-dimensional thermal conduction

16

16

14

14

12

12

Manual electric arc and GMAW (K=0.85)

10 10

Recommended working range

6 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 1.8 2.0 2.2 2.4 2.6 2.8 6

Heat input Q=K*E [kJ/mm]

Precondition for high notch impact energy in the welded joint is multi-layer welding, in which the number of weld layers is calculated on the basis of the following approximation:

Minimum number of weld layers

Plate thickness (mm) 3

Following appropriate checking (e.g. using process tests according to EN 15614-1), other welding conditions can be selected, if the properties of the welded joint correspond with the requirements made on the component.

3-dimensional thermal conduction

58

58

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

Dimensions
alform plate 700 M

Thickness (mm)

60 55 50 45 40 35 30 25 20 15 10 8

Width

1,500

1,600

1,700

1,800

1,900

2,000

2,100

2,200

2,300

2,400

2,500

2,600

2,700

2,800

2,900

3,000

3,100

3,200

3,300

3,400

Maximum length: 12,750 mm

Different dimensions on request.

3,500

(mm)

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

10

Dimensions
alform plate 960 M x-treme

Thickness (mm)

15 14 13 12 11 10 8

Width

1,500

1,600

1,700

1,800

1,900

2,000

2,100

2,200

2,300

2,400

Maximum length: 12,750 mm

Different dimensions on request.

2,500

(mm)

Technical terms of delivery for heavy plates

alform plate high-strength

May 2011.

11

Technically More Advanced. Successful Together.

voestalpine The Partner You Can Trust.

High-quality materials are the basis for our products. We strive to be the best partner for our customers and want to provide them with the best-possible solution. We focus our expertise on two aspects: personal contact with dedicated, competent employees and highquality technically sound methods, products and services. The companies in the voestalpine Steel Division pledge the following: Understanding for the business of our customers Dedication to professionalism Reliability Partnerships based on trust Responsibility for satisfactory project completion

voestalpine Grobblech GmbH voestalpine-Strae 3 4020 Linz, Austria T. +43/50304/15-9440 F. +43/50304/55-9440 [email protected] www.voestalpine.com/grobblech