Optimum Utilization of Coal Ash As Additive For Blended Cement Production

Download as pdf or txt
Download as pdf or txt
You are on page 1of 87

ADDIS ABABA UNIVERSITY

SCHOOL OF GRADUATE STUDIES


ADDIS ABABA INSTITUTE OF TECHNOLOGY
SCHOOL OF CHEMICAL AND BIO ENGINEERING

OPTIMUM UTILIZATION OF COAL ASH AS ADDITIVE


FOR BLENDED CEMENT PRODUCTION

By
Mulatu Tadesse

A Thesis Submitted to the School of Graduate Studies of Addis Ababa University,


Institute of Technology, in Partial Fulfillment of the Requirements for the Degree
of Masters of Science in Chemical Engineering (Process Engineering)

Advisor
Whasik Min (Prof.)

February, 2016
Addis Ababa
Ethiopia
Addis Ababa University
School of Graduate Studies
Addis Ababa Institute of Technology
School of Chemical and Bio Engineering

Optimum Utilization of Coal Ash as Additive


For Blended Cement Production
By
Mulatu Tadesse

A Thesis Submitted to the School of Graduate Studies of Addis Ababa University,


Institute of Technology, in Partial Fulfillment of the Requirements for the Degree
of Masters of Science in Chemical Engineering (Process Engineering)

Approved by Board of Examiners

Name Signature Date

------------------------------------- ---------------------------------- ----------------------


Chair man, Graduate committee

--------------------------------------- ---------------------------------- -----------------------


Advisor

--------------------------------------- ---------------------------------- -----------------------


Internal Examiner

--------------------------------------- ---------------------------------- ----------------------


External Examiner
ACKNOWLEDGMENT

I do have an indebted acknowledgement and gratitude for my advisor Prof. Whasik Min,
for his expert guidance, timely response, encouragement and valuable advice throughout
this research.
I wish also to thank Chemical Industry Corporation Mugher Cement Factory, my
organization, for giving me the opportunity to undertake my study in Addis Ababa
Institute of Technology.
Also express my special thanks to the following persons who helped me during the
research period: Ato Mekonen Zergaw, CIC director and his colleagues, for providing the
requested amount of coal samples generously, Ato Geremew Kebede, MCF quality
control and assurance head, and his staffs, specially to W/ro Aberash Semere, for their
valuable guidance and help during experimental works in the laboratory.
I would like to thank Engineer Feleke Bayu, for his continuous advice during the research
report preparation and I wish to thank my friends and individuals who helped me in one
way or the other during this research work period.
Finally, my greatest of gratitude is to my wife W/ro Kelemua Wodajo, for her
encouragement, assistance she provides me in every aspect.

i
TABLE OF CONTENTS
List of tables…………………………………………… iv
List of figures………………………………………….. vi
List of abbreviations…………………………………… vii
List of cement chemistry abbreviations……………….. viii
Abstract………………………………………………... ix
1. Introduction
1.1Back ground .................................................................................. 1
1.2 Statement of the problem ............................................................. 4
1.3 Objectives of the study................................................................. 4
2. Literature review
2.1 Components and properties of cement ......................................... 5
2.2 Blended cement ............................................................................ 7
2.2.1 Cement classes .................................................................... 8
2.2.2 Hydration reaction of cement.............................................. 10
2.3 Coal reserve and its ash properties............................................... 15
2.3.1 Coal reserve and production ............................................... 15
2.3.2 Classification of coal and environmental implication ........ 16
2.3.3 Source and characteristics of Ethiopian coal ...................... 17
2.3.4 Ash generation .................................................................... 17
2.3.5 Properties of fly ash ........................................................... 21
2.4 Supplementary cementing materials ............................................ 26
2.4.1 Pozzolanic properties .......................................................... 26
2.4.2 Physical effects .................................................................. 27
2.4.3 Possible impurities .............................................................. 28
2.5 Behavior of cement and concrete containing coal ash ................. 29
2.5.1 Workability ......................................................................... 29
2.5.2 Setting time ......................................................................... 31
2.5.3 Compressive strength .......................................................... 31

ii
3. Materials and methods
3.1 Materials and methods for cement raw materials analysis .......... 34
3.1.1 Materials, apparatus and reagents ....................................... 34
3.1.2 Methods and test procedures ............................................... 35
3.2 Material and methods for cement performance test ..................... 40
3.2.1 Materials, apparatus and reagents ...................................... 40
3.2.2 Methods and test procedures .............................................. 40
3.3 Experimental program ................................................................. 45
4. Results and discussion
4.1 Characterization of cement raw materials ................................... 47
4.1.1 Chemical analysis of clinker and gypsum ........................ 47
4.1.2 Characterization of coal ash .............................................. 48
4.2 Effect of coal ash cement properties ........................................... 49
4.2.1 Normal consistency.......................................................... 49
4.2.2 Setting time and expansion .............................................. 51
4.2.3 Compressive strength ....................................................... 54
4.3 Economic analysis of producing at Yayu ................................... 60
5. Conclusion and recommendation
5.1 Conclusions .................................................................................. 64
5.2 Recommendations ........................................................................ 66
References………………………………………………. 67

Appendix A: Pictures of equipments used for the experiment…. 71


Appendix B: Average XRF test results of lab cements…………… 74

iii
LIST OF TABLES

Table 2.1 Comparison of wet and dry cement manufacturing process


Table 2.2 Types and composition requirements (% by mass) for European Cements
Table 2.3 Mechanical and physical requirements given as characteristic value from Ethiopian
Standard (ES 1177-1:2005)
Table 2.4 Classification of coal by rank and their characteristics
Table 2.5 Proximate analysis and calorific values of coal deposits in different basins
Table 2.6 Ranges of bulk chemical compositions of fly ash produced in North America (wt.%)
Table 2.7 Crystalline phases in fly ashes from North America
Table 2.8 Concentration range of minerals commonly found in fly ash
Table 2.9 ASTM C618-94 chemical and physical requirements for fly ash used as a mineral
admixture in concrete
Table 3.1 The experimental programs used in this research
Table 3.2 Characterization of cement produced and amount of raw materials used
Table 4.1 Chemical and mineralogical properties of cement raw materials
Table 4.2 ASTM C618 and ES 1177-1 Chemical requirements for fly ash used as mineral
admixture in cement production, and chemical analysis of Ethiopian Yayu coal
ash
Table 4.3 The normal water consistency of cement as coal ash addition
Table 4.4 Loss of ignition of cement as coal ash addition
Table 4.5 Experimental results of setting time and Le Chatlier expansion of blended cement
Table 4.6 Average results of setting time of with coal addition
Table 4.7 Average test results of Le Chatlier’s expansion of cement paste
Table 4.8 Test results of compressive strength of blended cement
Table 4.9 Compressive strength of more fine cements
Table 4.10 Mechanical and physical requirements of 32.5 classes cement (ES1177.1:2005)
Table 4.11 Compressive strength test results as compared to ES requirements
Table 4.12 Average test results of compressive strength
Table 4.13 Mugher Cement Factory performances in clinker production and cement delivery
for last five consecutive budget years

iv
Table 4.14 Amount of raw materials required in metric tons for production of 256,000 Mt
blended cement
Table 4.15 Current production and transport cost of raw materials
Table 4.16 Unit production cost of cement at Tatek site
Table 4.17 Unit production cost of cement at Yayu site

v
LIST OF FIGURES
Figure 2.1 Cement manufacturing process
Figure 2.2 Schematic layout of a coal-fired electrical generating station
Figure 2.3 Influence of coarse-particulate content of fly ash on the water required for equal
workability in concrete
Figure 3.1 Raw materials used for lab cement preparation
Figure 3.2 Test specimen used for compressive strength test
Figure 4.1 Effect of Yayu coal ash addition on normal consistency of blended cement
Figure 4.2 Effect Yayu coal ash ignition losses on blended cement
Figure 4.3 Effect of Yayu coal ash additions on cement setting time
Figure 4.4 Effect of Yayu coal ash additions on cement paste expansion
Figure 4.5 Effect of cement fineness on compressive strength A is 20% coal ash addition,
B is 25% coal addition, C is 30% coal addition, D is 35 % coal addition, and E
is 40% coal addition
Figure 4.6 Effect coal ash additions on cement compressive strength

vi
LIST ABBREVIATIONS

ACAA American Coal Ash Association


ASTM American Society for Testing and Materials
CCP Coal Combustion Product
CIC Chemical Industry Corporation
COMPLANT China National Complete Plant Import and Export Corporation
EDTA Ethylene Diamine Tetra Acetic Acid
EN European Standard
ES Ethiopian Standard
FGD Flue Gas Desulfurization
GTP Growth and Transformation Plan
LOI Loss On Ignition
MCF Mugher Cement Factory
OPC Ordinary Portland Cement
SCM Supplementary Cementing Material
SEM Scanning Electron Microscope
TEA Tri- Ethanol Amine
XRD X-Ray Diffraction
XRF X- Ray Florescence

vii
CEMENT CHEMISTRY ABBREVIATIONS
A Aluminum Oxide, Al2O3
C Calcium Oxide, CaO
F Ferric Oxide, Fe2O3
H Water, H2O
S Silica, SiO2
Š Sulfur Trioxide, SO3
C3 A Tricalcium Aluminate, 3CaO·Al2O3
C4AF Tetracalcium Aluminoferrite, 4CaO·Al2O3·Fe2O3
C2 S Dicalcium Silicate, 2CaO·SiO2
C3 S Tricalcium Silicate, 3CaO·SiO2
CH Calcium Hydroxide, Ca (OH) 2
CŠH2 Gypsum, Ca2SO4·2H2O
CŠ Anhydrite, Ca2SO4
C-S-H Calcium Silicate Hydrate, nCaO· SiO2·mH2O
C6AŠH32 Ettringite, 3CaO·Al2O3·3CaSO4·32H2O
C4AŠH12 Monosulfoaluminate, 3CaO·Al2O3·CaSO4·12H2O

viii
ABSTRACT
The government of Ethiopia has given a great attention for establishment of chemical
industries since 2011. The establishments of this chemical industry begin with coal based
urea plant with an integration of a 90MW coal based thermal power plant for electric
source. This power plant produces 75,000 ton per annum of coal ash as a waste during the
production process. Using this ash, as raw material is an enormous opportunity both for
cement and thermal power industries to reduce their environmental impact.

The aim of the research is to stress the characterization and optimum utilization of coal
ash as additive for blended cement production. In this study coal sample was collected
from Yayu and burned at home to get ash. The characteristics of coal ash and cement raw
materials were investigated by classical and analytical testing methods. 15 types of
blended cements having a solid residue of ≤ 10, (10-16], and (16-20]% on 45μm sieve
were produced by inter-grinding of coal ash, clinker and gypsum in laboratory ball mill,
with the clinker replacement levels of 20, 25, 30, 35, and 40% by mass. The performance
of the cements was evaluated by conducting the following tests: setting time, soundness
and compressive strength. The results showed that Yayu coal ashes possess sufficient
pozzolanic characteristics to be used in production of blended cement, and the optimum
clinker replacement level by this ash can range between 20-25% by mass.

Key words: setting time, soundness, compressive strength, pozzolanic, coal ash, blended
cement,

ix
CHAPTER ONE
1. INTRODUCTION
1.1 BACKGROUND

In the process of generating power from coal, large quantities of Coal Combustion Products
(CCPs) are produced. CCPs are the solid residues that remain after the combustion of coal within
a furnace, and are collected in emission control processes. These are mainly boiler slag, bottom
and fly ash and desulfurization products like spry dry absorption products and flue gas
desulfurization (FGD) gypsum.
Coal combustion products have been used in the construction industry since the 1930‘s.
Although the utilization of these products was limited to small scale applications in the early
days, the use of coal combustion products has gained increasing acceptance in the construction
industry in the last few decades. The interest in coal combustion products significantly increased
during the 1970‘s because of the rapid increase in energy costs and the corresponding increase in
cement costs [1].
In the early days of the power generation industry, coal combustion products (CCPs) were
considered to be a waste material. The properties of these materials were not studied or evaluated
seriously and nearly all of the coal combustion products were land filled. In the course of time,
the cementitious and pozzolanic properties of bottom and fly ash were recognized and studied by
several individuals and institutions. The products were tested to understand their physical
properties, chemical properties and suitability as a construction material. During the last few
decades these "waste" materials have seen a transformation to the status of ―by-products‖ and
more recently ―products‖ that are sought for construction and other applications.
In the 1920's, more effective methods of firing power plant boilers were invented. These new
processes involved burning pulverized coal instead of lump coal. While the process was a more
efficient method of firing, the process generated an increased stream of fine combustion products
and lower quantities of cinders. This fine combustion product is called fly ash, and the cinders
that are relatively coarser are called bottom ash. As environmental awareness and land filling
costs have grown, CCP generators and government regulators have encouraged the beneficial use
of industrial by-products, including coal ash [2].

Page 1
According to World Coal Ash Association 2011 report the worldwide production of coal
combustion products was approximately 780 Million metric tons (Mt). The largest coal
combustion product producing countries and reigns were; China 395 Mt, North America 118Mt,
India 105Mt, European union (EU15) 52.6Mt, Africa 31.1Mt and Middle East as minor
contributor. In Africa 92% of production coal combustion products was produced in South
Africa. From 780Mt of the global CCPs produced, some 415Mt or 53% were reported as utilized.
Utilization rate varies widely from country to country depending on the quality of CCPs
produced, technological capability and degree of awareness on utilization possibilities. Japan had
the highest reported effective utilization rate of 96.4% and Africa with lowest at 10.5% [3].
The American Coal Ash Association (ACAA) survey reported that the usage included a number
of applications, with construction industries and civil engineering at 32.0%, followed by mining
applications with 9.9% and other applications with 1.1%. These percentages are expected to
increase, as a result of the development of new uses for CCPs, increased awareness of proven
technologies, and global focus on sustainable development. 57% of the total CCPs produced in
the USA are being stockpiled or disposed in landfills. Due to continued research and marketing
efforts, the world was able to utilize 53 % of coal combustion products in 2010 compared to only
18 % in 1980 [4].
The disposal cost of CCPs has escalated significantly during the last couple of decades due to
significant changes in landfill design regulations. Utilization of CCPs helps preserve existing
licensed landfill capacity and thus reduces the demand for additional landfill sites.
Increased commercial use of CCPs translates to additional revenues and reduced disposal costs,
which in turn translates to lower electric bills for electric customers. The use of CCPs in
construction reduces the need for quarried raw materials, manufactured aggregates and Portland
cement. Replacement of these virgin and manufactured materials with CCPs helps to conserve
energy and reduce emissions associated with manufacturing and processing. When fly ash and
bottom ash are used beneficially as engineered backfill material, these materials are replacing
sand or gravel that would otherwise have been quarried and transported from various locations.
The use of CCPs helps preserve mineral materials from sand and gravel pits and quarries as well
as provides construction cost savings associated with operation. It is also important to keep in
mind that every time Portland cement is replaced or displaced with fly ash, CO 2 and other

Page 2
emissions to the atmosphere from cement production are reduced by decreasing the need for
limestone calcinations as well as the fossil fuel that is consumed for production [2].
In Ethiopia, the Chemical Industry Corporation (CIC) was established with Council of Ministers
Regulation No. 280/2012, on 7th January 2013 with the initial capital of birr 21.7 billion with the
intention to develop the sector and enhance its contribution to the development of the country.
The corporation integrated a public enterprise and two governmental projects namely; Mugher
Cement Enterprise, Coal Phosphate Fertilizer Project and the National Rubber Nucleus Project.

A comprehensive investigation on the possibilities of establishing a fertilizer plant in Ethiopia


had been made by China National Complete plant Import & Export Corporation (COMPLANT)
in 1997. A Detailed Techno-economic Viability Study of Yayu Coal-mine completed under a
contract awarded to COMPLANT in 2007.

A coal based fertilizer project is being undertaken to establish urea fertilizer production plant of
annual capacity of 300,000 metric tons in the first phase. A coal fired co-generation thermal
power plant of 90 MW capacity was also under construction. According to the techno-economic
viability study of the project, the coal fired plant will produce 75,000 metric tons of ash per year
[5].

The aim of this study is to investigate the suitability of Ethiopian Yayu coal ash as a cement
additive in blended cement production. Currently coal ash (especially fly ash) widely used as
cement additive all over the world. The properties of coal ash mainly fly ash vary significantly
with coal composition and plant operating conditions. Each fly ash from different place has
different quality, where quality requirements for fly ash vary depending on the intended use. In
this study the properties of cement and coal ash is examined to establish optimum level of
replacement for blended cement production.

Therefore, using this coal ash as cement additive will add to the competitiveness of the chemical
industry corporation in environmental pollution control, as well as the reduction of both cement
production and ash damping cost.

Page 3
1.2 STATEMENT OF THE PROBLEM

The establishment of a coal based urea fertilizer integrated with the 90MW coal fired power
plant for electrical energy source is in the Oromia regional state in the Ilubabor Zone in Yayu
Wereda. It is expected that the power plant will produce 75,000tons of coal ash annually. Many
researches on the effective utilization of coal ashes have been done all over the world, such as
aggregate for road construction, brick and tile fabrication, land filling, filler in plastics and paint,
and raw materials for cement industry [6].
However, the effective crucial and economical application has been varies from place to place on
the quality of coal ash produced and its intended use. In these circumstances, the effective
utilization of coal ashes is strongly desired from environmental, ecological and economical
points of view.
The major aim of this research is to stress the characterization and optimum utilization of
Ethiopian Yayu coal ash as additive for blended cement production. If this coal ash is proven
compatible for the cement additives, more than 75% by mass of ash produced will be utilized.
This will have dual advantages for CIC in green technology and reduction of cement production
the damping cost.

1.3 OBJECTIVES OF THE STUDY


The general objective of this study is to investigate the suitability of Yayu coal ash as a cement
additive and optimum utilization in blended cement production.
Specific objectives:
The specific objectives are:

 Analysis of the chemical compositions and physical properties of the cement raw
materials including Yayu‘s coal ash
 Determination and characterization of the optimum percent replacement of clinker with
coal ash without affecting cement quality.

Page 4
CHAPTER TWO
2. LITERATURE REVIEW
2.1 COMPONENTS AND PROPERTIES OF CEMENT

Cement is a common construction material; a binder in mortars and concretes that hardens in the
presence of water. Cement is called hydraulic, when the hardened product is stable in an aqueous
environment. The most widespread hydraulic cement today is portland cement – a finely ground
gray-to-white powder composed primarily of calcium silicates, calcium aluminates, and calcium
ferrites, derived from mineral ingredients.

The European prestandard ENV 197-1 states that: Cement is a hydraulic binder, a finely ground
in organic material which, when mixed with water, forms a paste which sets and hardens by
means of hydration reactions and processes and which after hardening ,retains its strength and
stability even under water[7],[12]. The cement as we know today is a specialized building
material which is a result of various innovations over the past and is made in sophisticated
manufacturing facilities.
The oldest use of cement dates back to the thousands of years of old Egyptian civilization. The
Egyptians used natural cement made by combining limestone and gypsum for the construction of
their massive and highly impressive pyramids. The fact that the Egyptian Pyramids have proudly
stood the test of time over such a long period of human history is a testimony to the phenomenal
strength of cement. However, it must be stated that the ancient Egyptian cement was very
different from the cement in use today. Later in the Roman era, the concept of cement advanced
further. Romans used a combination of slaked lime with Pozzolana, a volcanic ash from Mount
Vesuvius. The Romans made many impressive structures using this cement. The Basilica of
Constantine is one popular example of Roman construction in which they used such cement
mortar. In eighteenth century England, John Smeaton, a British engineer, was assigned the task
of re-constructing the Eddystone Lighthouse, a structure that had witnessed repeated structural
failure. In 1756, Smeaton conducted a number of experiments that led to the discovery that
cement made from limestone containing a considerable proportion of clay would harden under
water. Based on this discovery, Smeaton rebuilt this lighthouse in 1759 and this time, it stood
strong for 126 years.

Page 5
Cement went through many more improvements and developments in the nineteenth and
twentieth century. The industrial revolution and the subsequent development of the rotary kiln
paved the way for huge and sophisticated cement manufacturing plants. These plants possess the
capability of a homogenous mixing and intense heating of the raw material thus vastly improving
the quality of the cement produced. The sophisticated quality-testing equipment employed by
modern cement plants further helps in ensuring the quality of the cement produced [8],[ 9].

Basically there are two types of cement manufacturing processes. Wet process is grinding and
mixing of cement raw materials in the existence of water; while dry process is done at their dry
state.
Table 2.1 Comparison of Wet and Dry Cement Manufacturing Process (adapted from Dr. Basil
Salah, ―Concrete Technology‖ chapter one) [10].
Criteria Wet process Dry process
Hardness of raw material Any type of raw material Quite hard
Moisture content of Slurry 35-50% Raw mix less than 12%
Fuel consumption High Low
Time of process higher Lesser
Quality of product Superior and more consistent Inferior and less consistent
Size of kiln needed Bigger lower
Overall cost higher lower

Three production steps are distinguished in the description of the production of cement as shown
figure 2.1
 Preparing raw materials: Mixing/homogenizing, grinding and drying produces the raw
meal.
 Burning of raw meal to form cement clinker in the kiln: The components of the raw
meal react at high temperatures (900-1500 °C) in the precalciner and in the rotary kiln, to
give cement clinker.
 Finish grinding of clinker and mixing with additives: After cooling the clinker is ground
together with additives to produce different types of cement

Raw materials Pyro-process Finish grinding


preparation (Clinker) (Cement)
(Raw meal)

Figure 2.1.: Cement manufacturing processes Additives

Page 6
2.2 BLENDED CEMENT
Cement mixtures containing ordinary Portland cement clinker and at least one supplementary
cementing material (SCM) are called blended cements. Blended cements blended or interground
at cement plants are generally more uniform and produce better results than blended concrete
mixtures combined at the concrete mixer
Climate change is an important issue all over the world. Carbon dioxide emission has been a
serious problem in the world due to the greenhouse effect. Today many countries agreed to
reduce the emission of CO2. Many phases of cement and concrete technology can affect
sustainability. Cement and concrete industry is responsible for the production of 7 % carbon
dioxide of the total world CO2 emission [11]. The use of supplementary cementing materials
(SCM), design of concrete mixtures with optimum content of cement, and enhancement of
concrete durability are the main issues toward sustainability in concrete industry.
During the past thirty years the use of by-product materials in concrete, either as components of
blended cements, or as admixtures, has been increased significantly. One advantage offered by
blended cement is the possibility of using less clinker to produce the equivalent amount of
cement, thereby reducing energy consumption and CO2 emissions. Manufacturing blended
cement can save as much as 40% of the fuel and increase cement production by 50-100%
without reducing the quality or performance of the product. Secondly, the incorporation of
pozzolans can significantly improve the basic properties of fresh and hardened concrete. These
include improve the workability; control of alkali silica reactivity; improved resistance to
sulfates and dilute acids, and reduced heat evaluation which is the particular concern in hot
weather and mass concrete. [12]. Possible disadvantages include slower rates of strength gain,
particularly at lower curing temperatures, and greater sensitivity to poor curing, which can be
mitigated by proper proportioning, increasing the fines of the cement to be milled, and
appropriate additions of chemical admixtures.
Blended cements contain Portland cement clinker and other inorganic materials, both natural and
industrial, that are used in quantities of 5% or more by mass of cement. The production of
blended cements incorporating pozzolanic materials began in Italy in 1929. Cements containing
granulated blast furnace slag have been produced in Germany, France, Luxemborg, Belgium, and
other countries for more than half a century. In Ethiopia up to know natural pozzolan is used as

Page 7
supplementary cementing materials for production of blended cement. Production history of
blended cement in Ethiopia goes more than 40 years [13].
2.2.1 CEMENT CLASSES
Two approaches are normally used to classify cements - the first is in respect of their
composition, and the second is in terms of their performance-related properties.
The two major international contributions to the classification of cement have been made in the
USA through the American Society for Testing and Materials (ASTM) and European committee
for standardization (ENV). ASTM has a number of prescriptive standards for the use of SCMs in
blended cements and concrete: C618, C989, &C1240.ASTM C150 &C595 are the prescriptive
standard for Portland & blended cement respectively. The European prestanderd ENV 197-1 on
the types and composition requirements has also been proposed by European Committee for
Standardization as in Table 2.2
Portland cements are made in many parts of the world but go by different names. Portland
cement is denoted per ASTM standard C-150 as:
 Type I: general use portland cement. In some countries, this type is known as ordinary
portland cement.
 Type II: general use portland cement exhibiting moderate sulfate resistance and
moderate heat of hydration.
 Type III: high early strength portland cement.
 Type IV: portland cement having a low heat of hydration.
 Type V: portland cement having high sulfate resistance.

Page 8
Table 2.2 Types and composition requirements (% by mass) for European Cements1 adapted from PCA R&D bulletin RD112T [14]
Granulated
Silica Nature Industrial Siliceous Calcareous Burnt Minor
Cement Cllinker blast furnace limestone
Notation fume pozzolan pozzolan fly ash Fly ash shale additional
types Designation slag
constituents2
K S D3 P Q4 V W T L
CEM I Portland cement CEMI 95-100 - - - - - - - - 0-5
Portland Slag Cement CEM II/A-S 80-94 6-20 - - - - - - - 0-5
CEM II/B-S 65-79 21-35 - - - - - - - 0-5
Portland- Silica fume
CEM II/A-D 90-94 - 6-10 - - - - - - 0-5
Cement
CEM II/A-P 80-94 - - 6-20 - - - - - 0-5
CEM II Portland- pozzolan CEM II/B-P 65-79 - - 21-35 - - - - - 0-5
Cement CEM II/A-Q 80-94 - - - 6-20 - - - - 0-5
CEM II/B-Q 65-79 - - - 21-35 - - - - 0-5
Portland fly ash cement CEM II/A-V 80-94 - - - - 6-20 - - - 0-5
CEM II/B-V 65-79 - - - - 21-35 - - - 0-5
CEM II/A-W 80-94 - - - - - 6-20 - - 0-5
CEM II/B-W 65-79 - - - - - 21-35 - - 0-5
Portland Burnt shale CEM II/A-T 80-94 - - - - - - 6-20 - 0-5
cement CEM II/B-T 65-79 - - - - - - 21-35 - 0-5
Portland Limestone CEM II/A-L 80-94 - - - - - - - 6-20 0-5
Cement CEM II/B-L 65-79 - - - - - - - 21-35 0-5
Portland Composite CEM II/A-M 80-94 6-205
Cement CEM II/B-M 65-79 21-355
CEM III Blast furnace Cement CEM III/A 35-64 36-65 - - - - - - - -
CEM III/B 20-34 66-80 - - - - - - - -
CEM III/C 5-19 81-95 - - - - - - - -
CEM IV Pozzolanic Cement CEM IV /A 65-89 - 11-35 - - - -
CEM IV/B 45-64 - 36-55 - - - -
CEM V Composite Cement CEM V/A 40-64 18-30 - 18-30 - - - -
CEM V/B 20-38 31-50 - 31-50 - - - -
1
The value in the table refers to the cement nucleus, excluding calcium sulfate and any additives. 2Minor additional constitutes may be filler or may be one or more of the main
3 4 5
constitute unless included as main constitutes. The proportion of silica fume is limited to 10%. The proportion of non ferrous slag is limited to 15%. The
proportion of filler is limited to 5%.

Page 9
Table 2.3 Mechanical and physical requirements given as characteristic value from Ethiopian
Standard (ES 1177-1:2005) [15]
Strength Compressive strength in MPa Initial setting time Soundness
class Early strength Standard strength in Min. (expansion) in
2days 7days 28 days mm.
32.5N - ≥16.0
≥32.5 ≤ 52.5 ≥75
32.5R ≥10.0 -
42.5N ≥10.0 -
≥42.5 62.5 ≥60 ≤10
42.5R ≥20.0 -
52.5N ≥20.0 -
≥52.5 - ≥45
52.5R ≥30 -

2.2.2 HYDRATION REACTION OF CEMENT


In strictly chemical terms hydration is a reaction of an anhydrous compound with water, yielding a
new compound, a hydrate. In cement chemistry hydration is understood to be the reaction of non-
hydrated cement or one of its constituents with water, associated with both chemical and physico
mechanical changes of the system, in particular with setting and hardening. A partial hydration of
cement may even take place in humid air, whereas for a complete hydration the cement must be
mixed with sufficient amounts of water.
As Portland cement is a multi-component system, its hydration is a rather complex process consisting
of a series of individual chemical reactions that take place both in parallel and successively. The
process gets under way spontaneously upon contact of the binder with water and is associated with
liberation of heat [9].
The progress of hydration and its kinetics are influenced by a variety of factors, especially
• by the phase composition of the cement and the presence of foreign ions within the crystalline
lattices of the individual clinker phases;
• by the fineness of the cement, in particular by its particle size distribution and specific
surface;
• by the water-cement ratio used;
• by the curing temperature;
• by the presence of chemical admixtures, i.e. chemical substances added in small amounts to
modify the hydration rate and properties of the cement paste;
• by the presence of additives, i.e. materials interground with cement in larger amounts, such as
granulated blast furnace slag or pulverized fly ash.

Page 10
The major components of cement that react with water to produce reaction products are tricalcium
silicate (C3S),dicalcium silicate (C2S),tricalicum aluminate(C3A), and tetracalcium alumionferite
(C4AF) [7].
The important strength-developing hydration reactions are those of C3S and C2S. Typical hydration
reactions would be:
For C3S: 2C3S + 6H (water) → C3S2H3 (“tobermorite” gel) + 3CH (hydrated lime)
For C2S: 2C2S + 4H → C3S2H3 + CH
The formula shown for tobermorite is only approximate, and some texts denote it as C3S2H4, in which
case both hydration equations above would need additional water (H) to start with. Actually, instead
of just tobermorite, a whole family of similar calcium silicate hydrates (C-S-H) may be formed, and
C-S-H is the preferred general term for these compounds. It is the C-S-H colloid or gel that is the
actual binder in hydrated portland cement. The ultimate strength of the hardened cement paste will
depend not only on the original total content of C2S and C3S but also on the completeness of their
hydration.

Although the net hydration reactions for both C3S and C2S are similar, the reaction for C3S is
relatively fast, and C-S-H from it is responsible for virtually all of the early (e.g., within 3 days of
curing) strength development of the cement. Typically, about 60% (by mass) of the C 3S has hydrated
to C-S-H within the first 5 days of curing and about 70% has hydrated within about 10 days. Because
of the formation of protective hydration shells, the remaining un reacted C3S particle cores hydrate
much more slowly, reaching about 75% hydration after 20 days of curing, about 80% hydration after
28 days (a standard measurement interval), and 85% after 60 days. Beyond 60 days, the rate of C3S
hydration slows dramatically and the incremental hydration and strength contribution is of little
practical importance.

In contrast, the hydration of C2S is relatively slow, with only about 20% hydration after 5 days of
curing, about 30% after 10 days, 35% after 20 days, about 40% after 28 days, and only about 55% at
60 days. Its rate of hydration slows further after 60 days. Accordingly, the C-S-H derived from the
hydration of C2S, while making little contribution to the early strength of the concrete, contributes a
significant proportion of the strength gain after the first week or so of curing.
As shown above, the C3S and C2S hydration reactions release free lime. Based on the typical clinker
mineral proportions and their hydration reactions, it can be shown that the net free lime release during

Page 11
clinker hydration, overall, is roughly 25%–33% of the original CaO content of the clinker. Free lime
in hardened concrete is not particularly desirable because it increases the chemical reactivity of the
surface (including along cracks) and can leach out in an unsightly fashion. On the other hand, by
maintaining a high pH in the aqueous phase, free lime can help protect steel reinforcing bars (rebar)
in the concrete from corrosion should water and oxygen reach the rebar via cracks. The lime is also
available to react with any pozzolans that may have been added to the cement or concrete mix.
Alkalis, particularly sodium (Na2O, or N in shorthand), can combine with C-S-H to form complex
hydrates (e.g., C-S-N-H) that are unstable and prone to swelling compared with regular C-S-H.
Alkalis can also react with forms (amorphous, opaline, or very fine grained crystalline) of silica in
some aggregates used in concrete, forming highly hygroscopic alkali-silicate hydrates (e.g., N-S-H),
and generally weakening the bond between the aggregates and the cement paste and forming higher-
volume phases. These and similar reactions, collectively called alkali-silicate reactions (ASR) or
alkali-aggregate reactions, can cause cracking of hardened concrete. The cracks not only weaken the
concrete but render its interior susceptible to additional alkali or other chemical attack, and to freeze-
thaw damage in cold weather regions. Approaches to controlling ASR reactions include selecting
portland cements having lower alkali contents (e.g., ASTM C-150 provides for a low-alkali cement
designation if the cement has a total alkali content [defined as Na2O + 0.658 K2O] content of 0.60%
or less), testing of aggregates for reactivity, and the incorporation of pozzolans into the cement paste.
Pozzolans contain active silica which ―sacrificially‖ combines with the alkalis in the paste (thus
leaving less alkalis available to react with the aggregates), and significantly reduce the hardened
concrete‘s porosity [16].
The other two clinker minerals, C3A and C4AF, have complex hydration reaction paths that are
similar to each other, but those of C3A are more important because they are much more rapid and
exothermic. Having C3A in the cement primarily enhances initial set and speeds, via release of heat,
the hydration of C3S (the presence of C3A also has benefits to the cement manufacturing process
because it speeds the overall formation of the clinker). In the absence of significant sulfate, C 3A very
rapidly— almost instantaneously—forms C3A-hydrates, many of which are unstable and may
subsequently convert to other forms. One of the many possible sequential hydration reactions is:

2C3A + 21H → C2AH8 + C4AH13 → 2 C3AH6 + 9H.

Page 12
A minor, but lime-consuming, reaction is:

C3A + 12 H + CH → C4AH13

The hydration of C3A in the absence of sulfate can be so rapid as to cause the undesirable condition
known as flash set. This is controlled through the addition of sulfate, usually as gypsum and/or
anhydrite. Plaster is only rarely used because it hydrates so quickly back to gypsum that its use is
rather counterproductive. The use of plaster also increases initial water consumption. A typical
hydration reaction of C3A in the presence of rate-controlling sulfate (here shown as gypsum) would
be:
C3A + 3 C𝑆H2 + 26 H → C6A 𝑆3H32 (―ettringite‖)
Flash set is controlled because ettringite forms a shell around the C3A particles, which slows water
diffusion to, and hence the hydration of, the residual C3A cores. Ettringite is stable only in the
presence of excess sulfate. If this condition is not met (i.e. not enough gypsum present, or in the
evolving conditions at the ettringite-residual C3A core interface), then ettringite reacts with C3A to
form a monosulfate phase:
C6A 𝑆3H32 + 2 C3A+ 4H → 3 C4A 𝑆H12 (“monosulfate”)
Alternatively, C3A hydration under low sulfate conditions can be expressed by:
C3A +10H + C𝑆H2 → C4A𝑆H12
An important property of the monosulfate phase is that, in the presence of sulfate ions, it can re-form
ettringite, such as by the reaction:
C4A 𝑆H12 +2 C𝑆H2 + 16H → C6A 𝑆3H32
Ettringite has a molar volume of about 735 cubic centimeters (cm3) per mole and monosolfate about
313 cm3 per mole. Because of this volume difference, re-formation of ettringite from monosulfate
can cause expansion of the concrete. This is not much of an issue while the cement paste has yet to
harden, but if ettringite re-forms in hardened concrete, the result can be cracking or spalling of the
concrete. This process is known as sulfate attack and is prevalent in regions (commonly desert areas)
having sulfate-rich ground water, or it can occur if too much gypsum is present in the cement. Thus
the proportion of gypsum in the cement is important. Where sulfate attack from groundwater is likely,
concretes are better made using a sulfate resistant portland cement, such as Type II, or better yet,
Type V; both have low concentrations of C3A. Type IV cement would also show resistance to sulfate
attack, but would be less desirable for most applications because its relatively low C 3S content would

Page 13
cause it to develop strength relatively slowly. Alternatively, sulfate resistance is improved by using a
blended cement, as addition of pozzolans lowers the overall C3A content of the cement paste and
reduces the porosity (hence sulfate entry potential) of the concrete
The ferrite mineral C4AF does not play a critical role in cement hydration. The chief value of ferrite is
in its effects on kiln reactions to form C3S (see process mineralogy discussion below). The hydration
of C4AF is broadly similar to that of C3A, although the reactions tend to be slower and much less
exothermic. The reaction stoichiometries will vary given the fact that, as noted earlier, C 4AF is
merely a mean composition for the ferrite solid solution having end members C6A2F and C6AF2. In
the absence of sulfate, the F partially substitutes for some of the A (partial substitution denoted as A,
F) in the analogous C3A hydration products, as shown in the reaction:
2C4AF + 32H → 2C2(A,F)H8 + C4(A,F)H13 + (A,F)H3 where total AF = total (A,F)
In the presence of hydrated lime (from C3S and C2S hydration), however, the formation of (A,F)H3 is
suppressed and a stable AF-hexahydrate (C4(A,F)H6) is formed that is analogous to C3AH6, with a
possible net reaction being:
C2(A,F)H8 + C4(A,F)H13 + (A,F)H3 + 6CH → 3C4(A,F)H6 + 12H

Page 14
2.3 COAL RESERVE AND ITS ASH PROPERTIES
Economic growth of countries is strongly associated with the use of energy. However, clean energy
with minimum environmental impacts is vital for a sustainable socioeconomic development,
particularly in the developing countries. Today in all corner of the globe, fossil fuels are the major
source of energy generation. The demand for the fossil fuels has been increasing rapidly for the last
two decades due to increased economic activities and changing lifestyles.
Contemporarily, Coal remains a major source for the global energy generation. Coal currently
supplies around 30% of primary energy and 41% of total electricity generation; the remainder is used
for the production of steel, cement, certain chemicals and domestic purpose. Coal use is forecast to
rise over 50% by 2030, with developing countries responsible for 97% of this increase, primary to
meet improved electrification rates [3]. Coal‘s dominant position in the global energy mix is largely
due to the fact it is abundant, widely distributed across the globe and affordable [17].
Cement industry is said to be energy intensive together with steel, paper and petro-chemical
industries. The primary fuel used in cement industries is fossil fuel, i.e oil, natural gas and coal. The
cement industries in early fifties of the last century were using coal as a fuel in a wet processing and
at that time environment pollution was not a key issue. In the following two decades, however, with
the advent of dry process technology which required a uniform quality of raw materials for
satisfactory operation and with increasing stress on environmental issues, a transformation took place
and gradually the cement industries switched over to furnace oil. Since 1973, oil embargo, the steep
rise in the cost of oil has caused many plants to convert back to the use of pulverized coal to serve as
primary fuel. Since the last three decades and to date, cement plants converted from oil to coal and as
of today almost 90 % of cement plants around the world are using coal for clinker burning [18].

2.3.1 COAL RESERVE AND PRODUCTION


Coal is a fossil fuel resource formed from peat and decayed vegetative matter from prehistoric
swamps. Coal formation occurs over several hundreds of millions of years as the swamp humus
degrades and is buried under layers of sediment. Increases in pressure and temperature compress the
humus, reduce the moisture content and other organics, and create coal seams. Ultimately, coal is
sedimentary rock comprised primarily of carbon, hydrogen, oxygen, sulfur, and nitrogen.

Page 15
Coal resources are broadly dispersed across geographical locations with appreciable reserves on
every continent except Antartica. In 2004, global recoverable coal reserves were estimated over 900
billion metric tons with major reserves in United States, China, India, Russia, and Australia [19].
Global coal production and consumption is expected to increase on average at 1% to 2% annually
until 2030. China, India and the United States consume most of the world‘s coal. These countries,
along with Australia and South Africa, are also the top coal producing countries.
2.3.2 CLASSIFICATION OF COAL AND ENVIRONMENTAL IMPLICATION
Coal seams are characterized by the coal type (rank), the presence of organic and inorganic matter,
thickness and layering (banding), and fractures (cleats). In the US, the American Society of Testing
and Materials (ASTM) standardizes methods to analyze coal for chemical and physical characteristics
pertinent to industry use and coal bed science. An ASTM procedure to classify coal by rank (low to
high) approximates the heating value, fixed carbon, moisture content and volatile matter in coal.
Given the various characteristics and origins of coal, knowing the coal rank provides insight into coal
behavior during extraction and conversion. Lignite and sub-bituminous are considered low rank
coals, characterized by light brown or dull black color, high moisture content, and a low heating
value. By comparison, bituminous coal and anthracite are high rank coals, black and reflective in
appearance with less moisture and a higher heating value from more fixed carbon. Sub-bituminous
and bituminous coals are the most plentiful types of reserves worldwide.
Table 2.4 Classification characteristics by coal rank[19]
Coal rank Volatile matter (wt %) Fixed carbon (wt %) Heating value(MJ/Kg)
Lignite 27-35 65-73 26-28
Sub- bituminous 22-27 73-78 28-32
Bituminous 8-22 78-92 32-36
Anthracite ˂8 ˃ 92 36-37

Although coal is economically affordable, coal mining and conversion pollutes the environment more
than other fossil fuels. When utilized, coal is removed from its existing environment and converted to
heat, gases and particulate emissions (ash). An array of pollutants such as dioxins, mercury,
particulates, and greenhouse gases are released with coal conversion impacting the environment and
atmosphere. Mining and preparation also immediately effects the local physical environment. Coal is
mined from the surface (open cut) or underground depending on the depth of a coal seam. While
surface mining is safer than underground mining, the scale of current surface mine operations alters
the landscape, affecting soil and nutrient dynamics, animal and plant habitats as well as watersheds.

Page 16
Surface mining accounts for about 40% of world production. Therefore mitigation of these pollutants
must be applied when surface coal mining to protect the environment..
2.3.4 SOURCE AND CHARACTERISTICS OF ETHIOPIAN COALS
Ethiopia has discovered a significant potential of higher grade lignite resource at different places in
the country the most promising resource areas are found at Yayu, Debre birhan, Delbi Moye followed
by Chilga, Mush Valley and Wuchale with low grades lignite potential respectively. These lignite
deposits are found in various parts of the central high lands of Ethiopia but at present Yayu deposit is
mined in small quantity for different small scale industries. Proximate analysis and calorific value
data show that the Ethiopian coals fall under the soft coal series (lignite to bituminous coal), A total of
about 297,000,000 metric tons of coal reserve and registered in the country [20], [21].
Table 2.5 Proximate analysis and calorific values of coal deposits in different basins [20]

Basin Moisture Volatile Fixed Ash in% Calorific Reserve


in % matter % carbon in% Value in cal/g (X 106 )tons
Delibi –Moye 0.3 - 8.5 17.9 - 29 28.5-58.1 11.2 - 49.1 2,520-6,495 60
Yayu 8.1- 20.7 28.3 - 46.5 11.3 – 28.1 24.6 – 42.2 3,795-5,930 200
Chilga 5.9 - 10.7 21.1 - 31.8 34.4 – 45.2 16.6 – 41.6 3,072 – 4,560 19
Lalo-Sapo 9.1 – 13.4 18.2 – 32.4 20.9 – 58.3 11.5 – 33.1 2,626 - 4,120 7.5
Chida 11.2 - 18.9 15 – 29.5 19.6 -51 22.8 – 37.3 2,492 – 4,333 9
Mush Valley 21.3 - 21.4 31.8 – 40.4 10.6 -27.9 23.1-27.9 2,824 – 3,568 1
Nejo 14.4 - 16 35.2 – 40.4 10.6 – 28.8 23.1 – 27.6 3,400 – 3,987 3
Wuchale 10.4 – 12.3 18 – 29.7 22.6 - 45.4 35.2 – 48.7 3,700 – 5,445 3.3

The Yayu basins have the highest coal reserve in Ethiopia. This is the place where coal based
fertilizer integrated with electric power generation plants are under establishment by the Ethiopian
government. This coal based power generation plant will produce much coal combustions products
(ash). And this by products should be utilized by other factories for both economical and
environmental reasons.
2.3.5 ASH GENERATION
In the process of generating power from coal, large quantities of coal combustion products (CCPs)
are produced. CCPs are the solid residues that remain after the combustion of coal within a furnace,
and are collected in emission control processes.
In the coal combustion process, CCPs are also generated in direct proportion to the variety, quantity
and ash content of coal consumed. The pulverized coal is burned in the furnace to generate heat, and
the hot gases then pass around the bank of tubes in the boiler and are eventually cleaned and

Page 17
discharged through the plant chimney. In large power plants that consume large quantities of coal,
substantial quantities of coal ash are produced. The ash that is collected in electrostatic precipitators
or bag houses is called fly ash.
In electrostatic precipitators the flue gas is passed between electrically charged plates where the fly
ash particles are then attracted to the plates. Bag houses can also be used to collect ash with bags that
filter the fly ash out of the flue gas stream. The fly ash particles are periodically knocked off the
plates or bags and fall into the hoppers located at the bottom of the electrostatic precipitators or bag
houses. The fly ash is then pneumatically transported to storage silos. The storage silos are equipped
with dry un loaders for loading dry bulk semi tankers or rail cars, and wet un loaders for conditioned
ash or disposal applications.
Bottom ash is formed when ash particles soften or melt and adhere to the furnace walls and boiler
tubes. These larger particles agglomerate and fall to hoppers located at the base of the furnace where
they are collected and normally ground to a predominantly sand size gradation. Some bottom ash is
transported to storage dry, but most is transported wet from the furnace bottom to dewatering bins
where water is removed prior to unloading and transports to construction sites or storage stockpiles.
Figure 2-2 shows the typical ash generation process in a coal-fueled power plant.
The ash collected from pulverized-coal-fired furnaces is fly ash and bottom ash. For such furnaces,
fly ash constitutes a major component (80 to 90%) and the bottom ash component is in the range of
10 to 20%. Boiler slag is formed when a wet-bottom furnace is used. The non-combustible minerals
are kept in a molten state and tapped off as a liquid. The ash hopper furnace contains quenching
water. When the molten slag contacts quenching water, it fractures, crystallizes, and forms pellets,
resulting in the coarse, black, angular, and glassy boiler slag. The boiler slag constitutes the major
component of cyclone boiler by-products (70 to 85%). The remaining combustion products exit along
with the flue gases.
Flue gas desulfurization (FGD) material is the solid material resulting from the removal of sulfur
dioxide gas from the utility boiler stack gases in the FGD process. The material is produced in the
flue gas scrubbers by reacting slurried limestone or lime with the gaseous sulfur dioxide to produce
calcium sulfite. Then the calcium sulfite is further oxidized to calcium sulfate (synthetic gypsum)
which has the same chemical composition as natural gypsum. The dewatering system removes water
from the calcium sulfate leaving the FGD absorber modules into hydro cyclone centrifuges and onto
belt filter presses. Vacuum pumps beneath the belt siphon the water out of the material, leaving it

Page 18
with about 10 percent moisture content. A belt conveyor system transports the dewatered materials
from the dewatering building to an adjacent storage shed [3]. Figure 2.2 shows the ash production
process flow diagram.
Currently, close to a billion tons coal is burned annually in the world to generate electricity and as a
result, nearly 130 million tons of CCPs are produced. One –third of these CCPs are utilized, while the
rest are disposed of mainly in landfills. Increasing costs and heightened environmental regulations are
making the disposal of CCPs an undesirable option [22]. Utilization of CCPs as raw materials results
in numerous benefits, including:
• A decrease in the demand for landfill space and handling costs
• Conservation of natural resources
• A cleaner safer environment
• Reduction CO2 emissions
• A boost in economic development
Utilization of CCPs in cement and concrete industry has significant environmental benefits such as:
 Increasing the life of concrete roads and structures by improving concrete durability when
fly ash use as concrete mix, bottom ash and sag as sub base for construction,
 Reduction in energy use and greenhouse gas and other adverse air emissions when fly ash
is used to replace or displace manufactured cement,
 Reduction in amount of coal combustion products that must be disposed in landfills, and
 Conservation of other natural resources and materials when FGD used as cement retarded.

Page 19
Fly ash

Collector FGD
trapper

Figure 2.2. Schematic layout of a coal-fired electrical generating station [2]

Page 20
Out of four CCPs mentioned above fly ash is widely and commonly used as supplementary
cementitious materials (SCM) in concrete either as part of blended cement or a separate component
added at stage of when the concrete mix is prepared around the world. A supplementary cementitious
material, when used in conjunction with portland cement, contributes to the properties of the
hardened concrete through hydraulic or pozzolanic activity, or both. As such, SCM's include both
pozzolans and hydraulic materials. A pozzolan is defined as a siliceous or siliceous and aluminous
material that in itself possesses little or no cementitious value, but that will, in finely divided form
and in the presence of moisture, chemically reacts with calcium hydroxide at ordinary temperatures to
form compounds having cementitious properties. Pozzolans that are commonly used in blended
cement production include fly ash, silica fume and a variety of natural pozzolans such as calcined
clay and shale, and volcanic ash. SCM's that are hydraulic in behavior include ground granulated
blast furnace slag and fly ashes with high calcium contents (such fly ashes display both pozzolanic
and hydraulic behavior) [23].
2.3.6 PROPERTIES OF FLY ASH
a. Physical properties
Fly ash particle size is finer than Ordinary Portland cement. Fly ash consists of silt sized particles
which are generally spherical in nature and their size typically ranges between 10 and 100 μm [24].
The surface area of fly ash particles vary from 2,000-10,000 cm2/g depending on the proportion of
fine particles in the fly ash [7]. These small glass spheres improve the fluidity and workability of
fresh concrete. Fineness is one of the important properties contributing to the pozzolanic reactivity of
fly ash.
Fly ash colour depends upon its chemical and mineral constituents. It can be tan to dark gray. Tan and
light colours are generally associated with higher lime content, and brownish colour with the iron
content. A dark gray to black color is attributed to elevated unburned carbon (LOI) content. Fly ash
color is usually very consistent for each power plant and coal source.
Fineness of fly ash is most closely related to the operating condition of the coal crushers and the
grindability of the coal itself. Fineness of fly ash is related to its pozzolanic activity. For fly ash use in
concrete applications, fineness is defined as the percent by weight of the material retained on the 45
μm (#325) sieve. ASTMC618 limits the maximum amount of fly ash retained on the 45 μm (#325)
mesh sieve on wet sieving as 34%. Generally, a large fraction of ash particle is smaller than 3 μm in

Page 21
size. In bituminous ashes, the particle sizes range from less than 1 to over 100 μm. A coarser
gradation can result in a less reactive ash and could contain higher carbon content.
The specific gravity of fly ash is related to shape, color and chemical composition of fly ash particle.
In general, specific gravity of fly ash may vary from 1.3 to 4.8.
Any amount of moisture in Class C fly ash will cause hardening from hydration of its cementitious
compounds. Even surface spraying may cause caking. To prevent caking and packing of the fly ash
during shipping and storage and to control uniformity of fly ash shipments, a 3.0% limit on moisture
content is specified in ASTM C618. Therefore, it is important that such ashes have to be kept dry
before being mixed with cement [25].
b. Chemical properties
Although several dozen minerals are present in coals, most occur in trace amounts. The majority of
coal minerals that influence fly ash composition may be classified in to five groups: aluminosilicates
(clays), carbonates, sulphides, chlorides, and silica (quartz). With the exception of quartz, all other
minerals are substantially decomposed during coal combustion. Chemical reactions at high
temperatures result in the formation of new glassy and crystalline phases. The bulk chemical
composition of fly ash glassy and crystline phases consists mainly (95-99% by mass) of oxides of
silica, alumina, iron, and calcium with smaller amounts (0.5-3.5%by mass) magnesium, sulfur,
sodium, and potassium [26].
ASTM Standard C-618 specifies two classes of fly ash based on chemical composition. Class F fly
ashes, which were at one time the only class, are required to have a minimum sum of three major
oxides (SiO2 +Al2O3 +Fe2O3) of 70% by mass. This requirement was designed to ensure adequate
pozzolanic reactivity. Class F fly ashes are typically derived from burning anthracitic and bituminous
coals.
Fly ashes derived from burning liginitic and subbituminous coals were found to enhance concrete
quality even though therir silica, alumina, and ferric oxide contents were relatively low. Therefore, an
additional fly ash class was added, Class C. Class C fly ashes are required to have a sum of three
major oxides (SiO2 +Al2O3 +Fe2O3) of 50-70% by mass.
Since Class C fly ashes have relatively low proportion of silica, alumina, and ferric oxides, they have
relatively high proportions of the fourth major oxide, calcium. Class C fly ashes are often referred to
as high –calcium ashes while Class F fly ashes are often referred to as low –calcium ashes.

Page 22
A compilation of reported chemical composition of Class F and Class C ashes is shown in Table 2.6.
In addition to high calcium contents relative to Class F fly ashes, Class C fly ashes typically have
higher magnesium oxide, sulfur trioxide and alkali contents. Differences in the bulk chemical
composition of fly ashes are reflections of the different glassy and crystalline compound
compositions. The composition of glass and the types and proportions o crystalline compounds
influence fly ash reactivity.
Table 2.6 Ranges of bulk chemical compositions of fly ash produced in North America (wt. %) [26]

Oxide Class F fly ash Class C fly ash


SiO2 38-65 33-61
Al2O3 11-33 8.0-26
Fe2O3 3.0-31 4.0-10
CaO 0.6-13 14-37
MgO 0.0-5.0 1.0-7.0
Na2O 0.0-3.1 0.4-6.4
K2O 0.7-5.6 0.3-2.0
SO3 0.0-4.0 0.5-7.3
LOI* 0.1-12 0.2-1.4

* Loss on ignition

c. Mineralogical Characteristics
X-ray diffraction study of the crystalline and glassy phases of a fly ash is known as mineralogical
analysis. Mineralogical characterization determines the crystalline phases that contain the major
constituents of fly ash. Generally, fly ashes have 15–45% crystalline matter. The high-calcium ashes
(Class C) contain larger amounts of crystalline matter ranging between 25 and 45%. Table 3.2
presents crystalline phases in fly ashes identified by XRD analysis [25].
Although high-calcium Class C ashes may have less glassy or amorphous material, they do contain
certain crystalline phases such as anhydride (CaSO4), tricalcium aluminate (3CaOAl2O3), calcium
sulpho-aluminate (CaSAl2O3) and very small amount of free lime (CaO) that participate in producing
cementitious compounds. Also, glassy phase in Class C ashes is usually more reactive. The glassy
particles in Class C fly ashes contain large amount of calcium which possibly makes the surface of
such particles highly strained, and probably, it is because of highly reactive nature of Class-C fly
ashes

Page 23
Table 2.7 Crystalline phases in fly ashes from North America [25].

Class of fly ash and code Name Nominal composition


Low-calcium/Class F
Hm Hematite Fe2O3
Mu Mullite Al6Si2O13
Qz Quartz SiO2
Sp Ferrite Spinel (Mg.Fe)(Fe,Al)2O4
High-calcium/Class C
Ah Anhydrite CaSO4
AS Alkali sulfate (Na,K)2SO4
C2S Dicalcium silicate Ca2SiO4
C3A Tricalcium aluminate Ca3Al2O6
Hm Hematite Fe2O3
Lm Lime CaO
Ml Melilite Ca2 (Mg.Al) (Al,Si)2O7
Mu Mullite Al6Si2O13
Mw Merwinite Ca3Mg(SiO4)2
Pc Periclase MgO
Qz Quartz SiO2
So Sodalite structure Ca2(Ca,Na)6(Al,Si)12O24(SO4)1-2

Anhydrite (CaSO4) is formed from the reaction of CaO, SO2 and O2 in the furnace or flue. Quantity
of anhydrite increases with the increase in SO3 and CaO contents. It plays a significant role in fly ash
hydration behavior because it participates along with tricalcium aluminate and other soluble
aluminates to produce ettringite and calcium sulphoaluminate hydrate.
Tricalcium aluminate (3CaOAl2O3) is one of the most important crystalline phases to identify and
quantify the fly ash because it contributes to ettringite formation, and also in self-hardening reactions
as well as disruptive sulfate reactions in hardened concrete.
Periclase is the crystalline form of magnesium oxide (MgO). Presence of this form of MgO in fly ash
affects the soundness of the resulting concrete through its expansive hydration to brucite, Mg (OH) 2.
Crystalline iron oxide, ferrite spinel and/ or hematite are generally found in all fly ashes. In most of
the fly ashes, about 0.33–0.50% of iron is present as crystalline oxide. The reactivity of fly ash is,
however, dependent on the glassy phases of Fe2O3.

Page 24
Table 2.8 Concentration Range of Minerals Commonly found in Fly Ash [12]
Minerals Present Concentration range (%)
Mullite 6.5 – 9.0
Quartz 2.2 – 8.5
Magnetite 0.8 -8.5
Hematite 1.1 – 2.7
Free CaO Up to 3.5

Table 2.9. ASTM C618-94 Chemical and Physical Requirements for Fly Ash Used as a Mineral
Admixture in concrete [12].
Class F Class C
A. Chemical Requirements
(SiO2 +Al2O3+Fe2O3),min.,.% 70.0 50.0
SO3, max., % 5.0 5.0
Loss on ignition, max., % 6.0* 6.0
Supplementary optional chemical requirements
Available alkalis, as Na2O,max.,% 1.5 1.5
B. Physical Requirements
Fineness:
34 34
Amount retained when wet-sieved on No.325 (45μm) sieve, max.,%
Strength Activity Index:
With Portland cement, at 7days,min.,% of control 75 75
With Portland cement, at 28days,min.,% of control 75 75
Water requirement, max.,% of control 105 105
Soundness:
Autoclave expansion or contraction, max.,% 0.8 0.8
Uniformity Requirements:
Density, max. variation from average,%**
5 5
Percent retained on No.325(45μm) sieve max. variation, % points from 5 5
average**
Supplementary optional physical requirements
Multiple factor, product of L.O.I.,% and fineness,% ,max. 255 -
Increase of drying shrinkage of mortar bars at 28 d, max.,% 0.03 0.03
Uniformity requirements:
In addition, when air-entraining concrete is specified, the quantity of air
entraining agent required to produce air content of 18.0 vol.% shall not vary 20 20
from the average of the previous 10 by more than,%
Effectiveness in Controlling Alkali-Silica Reaction:
Expansion of test mixture as parcentage of low – alkali cement control,at 14
100 100
days,max.,%
*Reduced from 12%in 1984, with the provision that Class F pozzolan containing up to 12% loss on
ignition may be approved by the user if either acceptable performance records or laboratory test
results are made available
**Average established by the ten preceding tests, or by all preceding tests if fewer than ten.

Page 25
2.4 SUPPLEMENTARY CEMENTING MATERIALS
2.4.1 POZZOLANIC PROPERTIES
Fly ashes, blast furnace slags, and natural pozzolans are the most commonly used supplementary
cementing materials in blended cement today. These materials may be blended or interground with
Portland cement or added as admixtures to concrete. Each of these products is available in a very
wide range of compositions and there is not necessarily a full correlation between physic-chemical
characteristics and performance. The predominant reactive constituent in these additives is
amorphous silica.
Most supplementary cementing materials have at least some pozzolanic properties. In the pozzolanic
reaction the silica (SiO2) in the pozzolan reacts with calcium hydroxide (Ca (OH) 2) and water to form
calcium silicate hydrate, the main strength producing component of hydrated cement and concrete.
There are three characteristics of pozzolan that make it reactive. These are:
1. High silica content: Since silica is what participates in the reaction with calcium hydroxide.
2. High degree of amorphousness: On cooling from a disordered state such as gas or liquid,
silica becomes ordered in crystals because that is its lowest energy state. However, when it is
cooled rapidly it does not have time to order itself before solidifying, so that instead it
solidifies in an amorphous structure (glass) or in a structure intermediate between crystalline
and amorphous. Since this state has a higher free energy than the crystalline state, the silica is
metastable and thus more reactive. Fly ash can be made to have a high degree of
amorphousness by careful control of the temperature during burning process of the coal.
3. High specific surface, which provides more surface from which the material can react. Some
fly ashes are naturally fine. Others can also be ground (probably interground with the clinker
rather than separately), beneficiated by removal of the coarsest particle fractions.
In addition, the clinker can be formulated to enhance the reactivity of the pozzolan. Since alkalis
activate pozzolans, the alkali content of the clinker can be adjusted for optimal reactivity. Heat can
also activate the pozzolanic reaction and, in the case of Class C fly ash, the cementitious reactions as
well. The hydration of C3A generates the most heat of any of the hydration reactions. The hydration
of C3S also generates heats well as calcium hydroxide, one of the reactants in the pozzolanic reaction.
In addition, the particle size distribution of the clinker portion of the cement can be adjusted for
enhanced reactivity by adjustments to the grinding circuit or simply by finer grinding.

Page 26
2.4.2 PHYSICAL EFFECTS
Supplementary cementing materials, whether pozzolanic or not, have physical characteristics that
affect the properties of cement and concrete. The introduction of an additional component into the
particle system will affect cement production and the properties of fresh and hardened concrete. Inter-
grinding of clinker with materials that are harder to grind (such as slag) or easier to grind (such as
lime stone) will affect the particle size distribution of both clinker fraction and the cement as whole.
The material that is easier to grind will concentrate in the finer fractions, while the material that is
harder to grind will concentrate in the coarser fractions. Depending on the choice of materials and
their relative proportions, the net effect will be beneficial if it increases the width the particle size
distribution. However, it is not possible to predict the exact effects. Trials would have to be
conducted with the selected materials in the grinding plant in order to determine the specific result
and optimize the particle size distribution for both workability and reactivity.
Materials that have a high specific surface –fly ash, silica fume, clay, rice husk ash, limestone, and
cement kiln dust- will affect a number of the properties of the fresh concrete. If surfactant admixtures
such as water reducers, super-plasticizers, or air entraining admixtures are used, the dosages will
generally have to be increased because there is more surface with which to interact. However, once
the additional surface forces have been counteracted by a water reducer or super-plasticizer, the water
requirement for a mortar or concrete is a function of the space that must be filled rather than the
surface that must be coated. Fine particles fit into the interstices between clinker particles, thus
improving particle packing and displacing water that then becomes available to increase the flow.
This advantage may be exploited ether by increasing the flow at the same water/cement ratio or by
reducing the water/cement ratio while maintaining constant workability.
An additional physical effect when finely divided particles such as limestone, silica fume, or fine fly
ash are present in the cement paste is that of nucleation sites for the products of the hydration
reactions. In some cases the hydration reactions are accelerated because the products are more readily
precipitated from solution. Also, the hydration products are more uniformly distributed throughout
the hydrated cement paste matrix, leaving finer, less continuous pores.

Page 27
2.4.3 POSSIBLE IMPURITIES
The various materials that could be used in the manufacture of blended cement are either natural or
the by- products of industrial processes. In either case they are not reagent –grade chemicals. Thus
they do not consist of 100% silica, but rather of combinations of materials. This section discusses
only those impurities that can have negative effects on the properties of cement and concrete.
Carbon is always present in rice husk ash and fly ash, and may also occur in silica fume, clay and
limestone. Carbon may have two effects. The more important of these is its interaction with air
entraining admixtures and other surfactants, which are adsorbed on the surface of active carbon. In
the case of fly ash, most of the carbon is concentrated in the larger particles because they are less
likely to have been completely burned. These can be removed by air separation if desired. It should
be noted that not all carbon has the same effect on the surfactants because it may be encapsulated and
thus not available for surface interaction. Also, carbon detected by loss of ignition of limestone could
be in the form of CaCO3, which does not have any particular interaction with surfactants. Generally
the effect of carbon on surfactants can be compensated by increasing the dosage of the surfactants.
However, the air void system in hardened concrete should be checked to determine the dosage of air
entraining admixture needed to produce acceptable spacing factors.
Another effect of carbon on cement and concrete is color. For normal structural use it is not of
particular concern, but occasionally the dark color imparted by carbon can be a problem, particularly
if the carbon content varies so that the color irregular. As mentioned earlier, fly ash can be
beneficiated to remove most of the carbon. Limestone deposits may contain clay, which absorbs
water. The effect on the fresh concrete is an increase in water demand, and the effect on hardened
concrete is deleterious to frost resistance. Since the European prestandared ENV 197-1 allows up to
35% limestone in blended cement, it also specifies limits on the clay content which could be used.
Alkali present in fly ash or cement kiln dust could react with aggregates susceptible to alkali-silika or
alkali-carbonate reactions. Supplementary cementing materials are more or less effective in
controlling alkali-silica reactivity, and alkalis in fly ash do not contribute to alkali-silica reactivity in
the same way that alkalis from clinker or cement kiln dust do [12].

Page 28
2.5 BEHAVIOR OF CEMENT AND CONCRETE CONTAINING
COAL ASH
The performance of fly ash in concrete is strongly influenced by its physical, mineralogical and
chemical properties. The mineralogical and chemical compositions are dependent to a large extent on
the composition of the coal and since a wide range of domestic and imported coals (anthracite,
bituminous, sub-bituminous and lignite) are burned in different generating stations all over the world;
the properties of the fly ash can be very different between sources and collection methods. The
burning conditions within a power plant can also affect the properties of the fly ash [23].

2.5.1 WORKABILITY
Rheology is the science of flow and deformation of matter. The rheological properties of a fresh
cement paste are of interest because of its role in determining the workability of concrete. In practice,
the consistency of mortar or concrete is measured in tests where the material is deformed under the
force of gravity (the slump test) or a combination of vibration and gravity.
The water requirement for flow, hydration behavior, and the properties of the hardened state largely
depends on the degree of dispersion of the cement in water. Parameters such as fineness, particle size
distribution, and mixing intensity are the important in determining the rheology of a cement paste.
Due to the charges that develop on the surface, cement particles tend to agglomerate in the paste and
form flocs that trap some of the mixing water. Factors such as water content, early hydration
reactions, water reducing admixtures, and mineral admixtures determine determines the degree of
flocculation in cement paste. The loss of workability due to false set is generally attributed to the
formation of fine interlocking gypsum crystals. These crystals also imbibe water that would otherwise
be available to maintain flow. The gypsum crystals can be broken up by mild agitation. Flash set, on
the other hand, occurs when the hydration reaction of C3A is not properly controlled. Flash set causes
rapid loss of workability and must be avoided for proper placement of concrete.
The use of good quality fly ash with a high fineness and low carbon content reduces the water
demand of concrete and, consequently, the use of fly ash should permit the concrete to be produced at
a lower water content when compared to a portland cement concrete of the same workability (Figures
6 and 7). Although the exact amount of water reduction varies widely with the nature of the fly ash
and other parameters of the mix, a gross approximation is that each 10% of fly ash should allow a
water reduction of at least 3% [12].

Page 29
A well-proportioned fly ash concrete mixture will have improved workability when compared with a
portland cement concrete of the same slump. This means that, at a given slump, fly ash concrete
flows and consolidates better than a conventional portland cement concrete when vibrated. The use of
fly ash also improves the cohesiveness and reduces segregation of concrete.
Several investigations have been conducted to study the role of Class F fly ash on the rheology of
fresh concrete . Brown (1982) conducted several studies with fly ash replacing cement and fine
aggregate at levels of 10–40% by volume. He concluded that for each 10% of ash substituted for
cement, the compacting factor or workability changed to the same order as it would by increasing the
water content of the mix by 3–4%. When fly ash was substituted for sand or total aggregate,
workability increased to reach a maximum value at about 8% ash by volume of aggregate. Further
substitution caused rapid decrease in workability. Owens (1979) reported that with the use of fly ash
containing large fraction of particles coarser than 45μm or a fly ash with high amount of unburned
carbon, exhibiting loss on ignition more than 1%, higher water demand was observed. Water demand
was noticeably increased to maintain the desired level of fluidity. Figure 3.4 shows the effects of
coarse fly ash particles on the water demand of concrete mixtures.

Figure 2.3 Influence of


coarse-particulate content of
fly ash on the water required
for equal workability in
concrete [11].

Page 30
2.5.2 SETTING TIME

With the addition of water to concrete, hydration reaction start and the cement paste begins to stiffen
accompanied by heat release. The rate of stiffening of cement paste is expressed in terms of setting
time.
Investigations have revealed that the addition of low calcium Class F fly ashes generally show some
degree of retarding effect on cement setting. Generally, the effect of fly ash on the time of setting
depends on the characteristics and amount of fly ash used. The interacting effects of fly ash with
other chemical and mineral admixtures used in concrete may also influence the setting of concrete. It
has been observed that all Class F fly ashes, especially low calcium fly ashes with high carbon
content or LOI, increase the setting time.
High calcium fly ashes, generally low in carbon and high in reactive and/or cementitious components
sometimes exhibit opposite behavior of reduced setting time. Not all Class C fly ashes cause rapid
setting.
The impact of fly ash on the setting behavior of concrete is dependent not only on the composition
and quantity of fly ash used, but also on the type and amount of cement, the water-to-cementitious
materials ratio (w/cm), the type and amount of chemical admixtures, and the concrete temperature. It
is fairly well-established that low-calcium fly ashes extend both the initial and final set of concrete.
The hydration or setting of Portland cement paste is accompanied by an evolution of heat that causes
a temperature rise in fresh concrete. Replacement of cement by fly ash results in a reduction in the
temperature rise in fresh concrete. This is of particular importance in mass concrete, where cooling
following a large temperature rise can lead to cracking.
2.5.3 COMPRESSIVE STRENGTH
The strength of a porous material is governed largely by its pores. Unlike permeability, this is
governed by the continuity of the pore system. Strength is governed by the size of the largest pores,
which act as local stress concentrations from which failure will begin. This concept first demonstrated
on glass specimens, but it also applied to other brittle materials such as cement pastes and concrete.
On the submicroscopic scale, hydrated cement paste is held together by Vander Waals forces.
However, in cement paste the pores that weaken the material are much larger, and in concrete the
areas of weakness, can be larger still. Thus the strength of the cement is not necessarily a good
predictor o the strength of concrete made from it.

Page 31
Concrete considered being a three- phase material comprising hydrated cement paste, aggregate, and
an interfacial region between them. The interfacial region the weak link, as it is the most porous of
the three. The porosity arises primarily from the accumulation of bleed water under aggregate
particles and reinforcing bars. As hydration proceeds, solid hydration products begin to fill in the
space, but generally they will be less dense than in the bulk cement paste. In low-strength concretes,
on the other hand, the cement paste matrix is so weak that the weakness of the interfacial region does
not make much difference.
Cracks form in concrete when the local tensile stress exceeds the local tensile strength of the material.
Although applied loads cause stress in the concrete, they are only one possible cause off cracking.
Volume changes resulting from temperature changes, thermal gradients, drying, creep, and various
chemical reactions will generate stresses if they are restrained. In cases where only the paste is
affected, such as in drying shrinkage, the aggregate acts to restrain the volume change.
The strength of hardened concrete is the fundamental importance to structural designers. It is also
extensively used as index of other properties and concrete quality.
The measured compressive strength of concrete depends on the intrinsic properties off the concrete.
Many variables influence the strength development of fly ash concrete, these being:
 fly ash characteristics such as its chemical and mineralogical composition, fineness,
pozzolanic reactivity
 type of cement;
 replacement level of cement with fly ash;
 mixture proportions;
 Ambient temperature and curing conditions
The pozzolanic reaction has several characteristics that affect the strength
1. The reaction is slow, so that the rates of both heat libration and strength development are
correspondingly slow.
2. The reaction consumes lime rather than producing it.
3. The reaction products are efficient in filling up space and subdivided pores
Lowering the rate of heat liberation reduces thermal gradients that lead to cracking; however, the
reduced rate of strength gain may not be acceptable in all application. The consumption of CH is
beneficial to strength because large deposits of CH tend to form in voids and along the interfaces of
aggregate particles and reinforcing bars. Generally large crystals form parallel to the interface.

Page 32
Since their cleavage planes are also parell to the interface, these large, oriented crystals serve as areas
of weakness in the concrete. The consumption of CH in the pozzolanic reaction thus replaces a weak
material with a stronger one, C-S-H, which has the additional advantage of filling more space with
solid material. All supplementary cementing materials, given good curing conditions for sufficient
time, will provide these benefits to the strength of concrete [12].
The main components of fly ash contributing to its pozzolanic reactivity are its reactive silicates and
aluminates (contained in the glass phase), whereas mullite and quartz are ineffective. It has been
suggested that the reactivity of fly ash depends on the temperature at which the coal is burned rather
on than the quality of coal [27].
The highly pozzolanic fly ashes start their contribution to strength development almost from the onset
of Portland cement hydration. But the low calcium fly ashes do not exhibit significant pozzolanic
activity to affect strength until about two weeks after hydration. However, some high calcium fly
ashes, with calcium oxide content more than 15%, may start contributing to strength development as
early as 3 days after mixing because of their self hardening and pozzolanic properties.
The sulphate content of a fly ash has been reported to contribute significantly to the early hardening
of fly-ash mortars Increased carbon content (indicated by high loss on ignition) is found to affect the
strength of fly-ash concrete adversely. This is attributed to an increased water requirement and an
increased amount of air-entraining agent (needed to maintain the same workability and air content as
in control concretes) as the carbon content of fly ash increases.
Because of its fineness as well pozzolanic reactivity, fly ash in cement concrete significantly
improves the quality of cement paste and the micro-structure of the transition zone between the
binder matrix and the aggregate. As a result of the continual process of pore refinement, due to the
inclusion of fly ash hydration products in concrete, a gain in strength development with curing age is
achieved. When high calcium Class C fly ash is used, the strength development with time is likely to
be different from the one using Class F fly ash. The self-hardening reactions in the Class C fly ashes
are likely to occur within the same time frame as the normal Portland cement hydration reactions,
giving equal or sometimes greater strengths at early ages. The pozzolanic activity of such
cementitious fly ashes further enhances strength at later ages [28].

Page 33
CHAPTER THREE
3. MATERIALS AND METHODS
The aim of this chapter is to discuss the materials, equipments and testing methods used in the
practical analysis of the physical and chemical properties of Yayu coal ash, clinker, gypsum and
laboratory produced cement by performing test for particle size, chemical, and x-ray analysis. In
addition cement performance like water consumption, setting time, soundness and compressive
strength testing procedures are described. All physical and chemical tests used for this research are
according to the Ethiopian Standard (ES 1176:2005) and European Standard (EN 196:1998) methods
of testing. All experimental work was performed in Mugher Cement Factory quality control and
assurance laboratory.

3.1 MATERIALS AND METHODS FOR CEMENT RAW MATERIALS


ANALYSIS
3.1.1 MATERIALS, APPARATUS AND REAGENTS
Clinker, gypsum and coal ash are the direct materials used as cement raw materials for chemical
compositions analysis.

The following basic apparatus and instruments used are watch glass, graduate cylinder, burette, glass
rod, pipette, wash bottle, drying oven, digital balance, muffle furnace, desiccators, crucible, funnel,
beaker, coarse filter paper (black band), red, blue-band filter paper, electric furnace, lid, Porcelain
dish, evaporating dish, sand or water bath, volumetric flask, platinum crucible, Florence flask, funnel,
cover.
The chemical reagents used in this analysis are: hydrochloric acid (HCl), Phenolphateline indicator,
Sodium hydroxide (NaOH),EDTA(ethylene diamine tetra acetic acid),TEA(tri-ethanol amine), Ethyl
glycol, Nitric acid (HNO3), Ethanol, Acetic acid, Bromocresol green indicator, Fusion mixture
(NaKCO3), Barium chloride (BaCl2) , Congo-red, and distilled water.

Page 34
3.1.2 METHODS AND TEST PROCEDURES
 Clinker and gypsum are collected form Mugher Cement Factory
 Since Yayu coal based thermal power plant is under establishment the coal ash is prepared at
home as follows:
 A coal sample was collected from Oromiya regional state Ilubabor zone, Yayu coal
mining area.
 Coal was crushed in Mugher lab by P100 x 100 jaw crusher.
 The crushed coal was burned by locally made burner.
 The ash was collected from the burner and screened by locally made screen to
separate the ash from unburned one. See below the coal ash prepared at home.

The cement made in laboratory was by intergrading of clinker, gypsum and coal ash in SM-500 ball
mill which derived by motor having 48 revolution per minute. The mill grinding capacity was 5Kg
per batch.
Figure 3.1 Raw Materials Used For Lab Cement Preparation.

Yayu coal Yayu coal ash Clinker Gypsum

The following test procedures are used for these experimental works; which were complying with
Ethiopian standard and Mugher cement factory methods of testing cement and cement raw materials.
In chemical analysis the characteristics (oxide and compound compositions) of cement raw materials
can be determined [29]. The contents determined include oxides of silica, ferric, alumina, calcium,
magnesium, sulphate, and loss on ignition. The chemical tests for basic cement raw materials were
performed using classical testing method.

Page 35
The classical chemical analysis techniques/procedures to find out basic parameters are described in
details as follows:
1. Determinations of major oxide contents
Ethiopian Standard (ES 1176-2:2005 and EN 196-2:1998) [30] stated the procedure as follow:
In order to get appropriate results mix the sample very well and take some part of the sample and let
it to dry in the oven at 1050C this helps to remove the moisture contents. After dried cool in
desiccators and weigh 2.5 g fusion mixture (NaKCO3) was put in to platinum crucible and 0.5 g of
sample over the fusion mixture again cover the surface of the mixture with 0.5 g NaKCO3. The
mixture was placed in the Muffle furnace at 10000C for 20 minutes, removed from the furnace and
gently swirls in order to spread the melt on the sides of the crucible. To make it cool placed and hold
on porcelain basin about 50ml cold distilled water of the basin. After cooled on the basin removed the
crucible and the lid from the basin and places it in a clean dry porcelain dish.
In this solution added 20 ml of Concentrated HCl to lose the fuse and rinse with distilled water. After
successful washing remove the crucible and lid. Put the dish on water bath and the contents of the
dish evaporated to dryness wash with another 20 ml Concentrated HCl while it was dried.
Removed from the water bath, bake for an hour in a drying oven at 105 0C. Removed from the oven,
cooled and 20 ml of 1+1 HCl was added to digest for 10 minutes. Prepare 500 ml volumetric flask to
filter the contents while hot with coarse filter paper (black band), wash repeatedly with hot water,
cool and fill up to the mark.
N.B.The The precipitate is used for SiO2 analysis, while the filtrate is used for CaO, MgO, Fe2O3 and
Al2O3
2. Determination of silica oxide (SiO2)
For this analysis the above major oxide determination procedures must be considered so dry and char
the precipitate obtained above in dried and weighted porcelain crucible. This dried precipitate was
ignited in a muffle furnace at 1000 0C for an hour and cooled in desiccators and weighed to nearest
mg. The concentration of SiO2 is determined from the formula:
𝑇−𝐶
%SiO2 = [ ] x 100
𝑆

Where: T = mass of crucible and precipitate, C = mass of empty crucible and S = mass of sample.

Page 36
3. Determination of calcium oxide (CaO)

Like silica content analysis, major oxide determination procedures should be considered, then take
filtrate obtained above. (Filtrate placed in the 500 ml volumetric flask).
From the filtrate pipette out 25 ml of the filtrate in to 300 ml Erlenmeyer flask and dilute to about 100
ml with distilled water. In this solution 13 ml of 30% Tri-ethanol amine (TEA) was added and adjust
the pH between 12 and 13 with 10% KOH (without formation of precipitate and check if by pH-
meter). Again add about 50 mg of the mixed fluorexone indicator. Finally titrate with 0.01M EDTA
from light green to pink and recorded the volume of EDTA consumed. The concentration of CaO is
determined from the formula:
%CaO = (2.2432) x (FEDTA) x (VEDTA)
Where: FEDTA = factor of EDTA and VEDTA = the volume of EDTA used to end point.
4. Determinations of magnesium oxide(MgO )
Similarly as CaO determination pipette out 25 ml of the filtrate and dilute to about 100ml. In this
solution 10 ml of 30% T.E.A added and adjust the pH between 10 and 11 with pH = 10 buffer. Add 5
drops of par and 5 drop of copper complexomate and titrate with 0.01M EDTA from red to orange
yellow. The concentration of MgO is determined from the formula:
%MgO = (1.6128) x (FEDTA) x (VEDTA)
5. Determinations of ferric oxide( Fe2O3)
For this analysis also pipette out 100 ml of the filtrate prepared at above major oxide determination
and add the Sulpho-Salicilic indicator about 50 mg. In this solution add drop wise 1+4 NH4OH
solution till the yellow color is observed (the change observed is from colorless to violet and the
yellow).
Return back the color to violet by adding 1+4 HCl solution and check the pH of the solution to
between 1 and 2.Heat the solution gently to body temperature (do not exceed 500C). Finally titrate
with 0.01M EDTA from violet to colorless and recorded the volume of EDTA consumed. The
concentration of Fe2O3 is determined from the formula:
% Fe2O3 = (0.7985) x (FEDTA) x (VEDTA)

Page 37
6. Determinations of aluminum oxide( Al2O3)
Similarly pipette out 100 ml of the filtrate prepared at above major oxide determination and add the
volume of EDTA consumed for Fe2O3. In this solution 40 ml of pH 3 buffer was added and heated
just to boiling. To control the effect of other oxides add exactly three drops of copper complexomate.
Add 10 drops of pan indicator, boil and finally titrate while hot form red-violet to yellow. Repeat
boiling and titrating until yellow color became stable. The concentration of Al 2O3 is calculated from
the formula:
% Al2O3 = (0.5098) x (FEDTA) x (VEDTA), FEDTA = 1.0029
7. Determination of free calcium oxide(CaO)
Free calcium oxide the oxide left uncombined during clinkerization process. The value is directly
related to the quality of clinker produced.
To determine the free lime transfer 1.0 g of sample in to 300ml flask and add 50 ml of ethyl glycol
and 1.0 g -2.0 g of laboratory sand and after shake well place it in a water bath at 70 oC for 20
minutes. Filter with suction and rinse with 10ml of ethyl glycol or absolute alcohol. The filtrate is
titrated with 0.1N HCl in the presence of 5 drops of bromocresol green indicator.
The end point is attained when dark blue color changed to light green. The concentration of free lime
in gram is determined from the formula:
%CaO = (Vtitration x 2.8x10-3) x100
Where: Vtitration = the volume of 0.1N HCl consumed for titration.
8. Determination of sulfur trioxide (SO3)
Exactly 0.50 g of sample was weighed. In this sample added 25 ml of distilled water and 13 ml of
Conc. HCl for digestion. Break the lamps with glass rod, heat to boil and 100 ml of boiled distilled
water was added. Immediately filtered with a medium (red band) filter paper and wash it several
times with hot water. This filter used for SO3 analysis while the residue (precipitate) used for
insoluble residue (IR) analysis. Heat the filtrate to boil, while placing a glass rod and piece filter
paper in it. After adding 10 ml of BaCl2 solution slowly removed from the hot plate and stirred very
well. In this solution added 50-60 ml of Congo-red carefully and leave it for 20-25 minutes for
settlement.
Clear upper layer shows enough amount of Congo-red is added, otherwise additional amount might
needed. After the settlement filtered with fine (blue band) filter paper, washed the residue several
times with hot water and placed the precipitate in previously weighed porcelain crucible. Placed this

Page 38
crucible on one of the hole of rapid incinerator or hot plate until the paper became blacken and then
ignited in the muffle furnace controlled at 1000 0C for an hour. Finally cool in desiccators and
weighed. The sulphate content expressed as %SO3 is calculated from the formula:
𝑇−𝐶
% SO3 = [ ] x34.3
𝑆

Where: T = mass of crucible and precipitate, C = mass of empty crucible and S = mass of the
sample.
9. Determinations of loss on ignition (LOI)
This is the loss of weight due to release of volatiles on ignition. A sample is ignited in a furnace under
controlled conditions and the weight loss measured. This applies to materials which have to be
calcined for use.
To determine the LOI weighed exactly 1.0 g of the sample; put this sample into a crucible and ignite
at 1000 0C for 5 minutes then removed the lid and left the crucible in furnace for further 20minutes.
Cooled the crucible to room temperature in desiccators, and ascertaining whether constant mass is
obtained by weighing the sample. The observed loss on ignition is determined from the formula:
𝐴−𝐵
%LOI = [ ] x100
𝐴

Where: A is the mass of the crucible and sample before ignition and B is the mass of the crucible and
sample after ignition.

Page 39
3.2 MATERIAL AND METHOD FOR CEMENT PERFORMANCE
TEST
3.2.1 MATERIALS, APPARATUS AND REAGENTS
The basic materials used for cement performance analysis are lab cement, and standard sand.
The following basic apparatus and instruments are used for cement performance analysis such as:
drying oven, digital balance, muffle furnace, desiccators, platinum crucible, XRF machine, sieve
machine, blain testing machine, stop watch, small brushes, LeChatelie ring, sample mixer, ruler,
Vicat apparatus, compressive strength testing machine, prism molds, jolting apparatus, humidity
cabinet and water bath. Lithium tetra borate (Li2B4O7) and distilled water are used as chemical
reagents for the test.
3.2.2 METHODS AND TEST PROCEDURES
The cement used for performance analysis was produced in Mugher cement laboratory by
intergrading of clinker, gypsum and coal ash in SM-500 ball mill which derived by motor having 48
revolution per minute, and grinding capacity was 5Kg per batch according to ES1176-7:2005 [31].
The laboratory cement produced as follows:
 Cement raw materials clinker and gypsum are crushed by lab jaw crusher for easy
blending.
 Moisture is removed from gypsum and coal ash.
 Using 20,25,30,35 &40 % clinker replacement level and each level at three % residue

on 45μm sieve 15 different cement types are produced by intergrounding with ball
mill.
 Lab cement without coal ash is produced for reference purpose
The lab cement was produced according to the ES 1176-7:2005 and EN 196-7:1998
The chemical and physical analysis procedures of cement produced are as follows:
1. Chemical analysis with X- ray fluorescence spectroscopy(XRF)
An XRF spectrometer was used to investigate the characteristic spectra of elements present in the
solid sample. For quantification analysis, the intensity of characteristic line of the element analyzed
was measured. The powdered cement sample was calcined at 850oC for 4 hours in order to remove all
organic compounds and water contained in the sample. The calcined sample was converted into a
solid solution by fusion with lithium tetra borate (Li2B4O7). The prepared solid solution and standard

Page 40
were placed in sample holders and placed in the sample compartment of the DY1507 Epsilon3 XRF
spectrometer. The intensity of a characteristic line of the element to be determined was measured.
The concentration of the element in the sample was calculated from the intensity measured.
2. Physical analysis
The effect of coal ash used as cement additives on the properties of cement produced was determined
by physical analysis of cement properties like fineness, compressive strength, soundness, and setting
time. All tests were complying with Ethiopian Standard of cement testing methods (ES 1176:2005)
and European norm of testing method (EN 196:1998).
a. Testing method of cement fineness: As given in ES 1176-6:2005 [32]:
Cement fineness one of the physical properties of cement that mainly affect the hydration reaction of
cement. Therefore controlling the cement fineness is mandatory for cement manufacturers. The
cement fineness can be measured by two ways. These are by blain (specific surface area) and sieve
(% residue) methods.
For Blain method: A mass 2.66 g of cement sample weighed and placed in to the blain sample holder
of PC- Controlled Automatic Blaine apparatus. Adjust the level of the oil at the correct position, set
the stop watch and take the time taken in seconds from initial level to the final level of the oil travels
repeated for three times and we taken the average. Specific surface area was calculated with the
following formula:
Specific surface area = k tav
Where: k = constant [cm2/g.s], and tav = average time in second.

For Sieve method: A mass of 25g of the cement sample weighed and placed on 45μm Hosokawa
Alpine Ag sieve. Run the sieve machine that develops a pressure of 4KPa for four minute. Determine
the mass percent of the residue by the following formula.
𝑏
% residue =( 𝑎 ) x100

Where a= mass of the sample, and b = mass of the residue


b. Consistency of Standard Cement Paste: As given in ES 1176-3:2005 [33]
A 500g of cement sample was weighed and 25% water content of the mass of dry cement was added
as a start. The mixture was mixed for 3.0 minutes by using a trowel to give a paste and was
immediately transferred into the mould lying on the steel plate. The top of the mould was smoothened
off as quickly as possible with the aid of the trowel. The mould and paste were placed under the

Page 41
plunger in the Vicat apparatus and the plunger lowered gently to contact the surface of the paste. This
material was released quickly and allowed to sink into the paste.
The scale reading of the vicat apparatus was noted after 1 minute and recorded. If the plunger
penetrates to a point 5 to 7 mm above the bottom of the mould, the water-cement ratio is taken as the
consistency, if not, a new water-cement ratio is taken and the procedure repeated.
c. Setting Time Determination on Cement: As stated in ES 1176-3:2005
A sample of cement paste of standard consistency was prepared and the time of first mixing the water
with cement was noted down. A slight excess of paste was immediately transferred into the mould in
one layer by using hand trowel. The top of the mould was smoothened and leveled. The mould was
placed under the initial set needle of cross-sectional area of 1mm and the needle was covered gently
onto the surface of the paste and was quickly released by allowing it to sink to the bottom. These
tasks were repeated several times at regular intervals of 10 minutes in different positions of mould
until the paste has stiffened sufficiently for the needle not to penetrate deeper than 5mm above the
bottom of the mould.
The time interval between the addition of water and the initial setting time was recorded. Finally, the
needle was replaced with a 1mm square needle fitted with a metal annular attachment and this probe
was allowed to come gently with contact with the surface of the invertied cement paste at an interval
of 15 minutes. The final set was reached when the needle makes an impression on the surface but
annular cutting edges fail to do so.
d. Soundness Test (Expansion Determination on Cement : As stated in ES 1176-3:2005
Soundness is a measurement of its tendency to crack, distort, pit or disintegrate.
The cement paste was prepared as of a standard consistency and filled in to the expansion mould, or
Le Chatelier mould, placed on a glass plate. The split end of the mould was gently closed by tying it
with a piece of cotton as the operation was being carried out. The surface of the paste was well
smoothened and leveled with the blade of a gauging trowel and was covered with another piece of
glass and was immediately immersed in clean water.
After 24 hours, the mould was removed from the water and the distance between the pointers
measured by using a meter rule. The mould was re-immersed in water again and was brought to
boiling point within 30 minutes and afterwards allowed to boil for one hour. This material was then
kept in the water and allowed to cool. The distance between the pointers was again measured.
The percentage expansion of the composite sample is calculated using the formula:

Page 42
Lo −L
% Expansion = [ ] x100
L

Where: Lo is initial length, and L is final length


e. Compressive Strength Test
As stated on Ethiopian standard of cement testing method (ES 1176-1:2005) [34], the
compressive strength was carried out as follows.
A 450g cement, and 1350g standard sand were weighed into the mixing bowl. Starting from
10% by mass of cement distilled water was added and mixing was carried out until a cement
mortar of homogenous consistency was obtained. The test specimens (molds) used is 40mm x
40mm x 160mm prisms as seen figure 3.2

Figure 3.2 Test specimen used for compressive strength test


Molds were set on the working bench and all bolts were tightened using the spanners. The base
of the mould was greased with a thin film of petroleum jelly and also the joints of the two
halves. As quick as possible, the concrete mixture was scooped into each mould (to half the
depth) in a single layer. The mortar mixture was tamped in each mould with 25 strokes of the
tamping bar spread uniformly over the cross-section of the mould and exerting the same force
in each case by raising the bar about 30mm above the surface of the concrete and guiding it as it
is then allowed to fall under its own weight.
More mixture was scooped into each cube being completely filled to the brim. This material
was tamped again 35 times for each mould. The assembled mould was placed on a vibrating
machine and well secured in place, a suitable hopper was used to facilitate filling. The mould
was vibrated on a jolting machine for 2 minutes. Afterwards, the prisms were covered with an
impervious sheet to avoid evaporation and were allowed to cure at room temperature of 22oC
and relative humidity of 55% for 24 hours. The prisms were removed from their mould after 24
hours and were marked for identification. This material was then immersed in clean water to be
removed for testing ages of 2 and 28 days.

Page 43
The prisms were brought out of the water in due time and their surface was carefully wiped
clean of water and adhering loose sand. The DY- 208MC compression machine was switched
on 15 minutes before use. Prisms are supported on the supports 100mm apart and loaded with a
point load at mid span. The prism was broken into approximately two equal pieces. The two
halves of each prism are tested in the press and the average of the six results obtained is taken
as the compressive strength. The compressive strength of each a prism is calculated as follows:
𝐹𝑐
Rc= 1600

Where: Rc = compressive strength (MPa), Fc= maximum load at fracture (N) 1600= 40mm x
40mm, area of the plates (mm2)

Page 44
3.3 EXPERIMENTAL PROGRAM
The following test programs were used for this project:
Table 3.1. The experimental programs used in this research
S.No. Tests Number of Test method used
samples
1 Coal ash preparation 1 -
2 Chemical analysis of coal ash, clinker and 4 each ES 1176-2:2005 and
gypsum EN 196-2:1998
Lab cement production with six clinker 16 ES 1176-7:2005 and
replacement level (0,20,25,30,35,40) and EN 196-7:1998
3 except 0 replacement level all are made at
three different particle size on 45μm sieve
residue. (≤ 5, 10-16 & 16-20%)
4 Fineness of cements 16 ES 1176-6:2005 and
EN 196-6:1998
5 Chemical analysis of cement 16 Analytical method
(XRF)
6 Setting time and soundeness of cement paste 16 ES 1176-3:2005 and
EN 196-3:1998
7 Compressive strength of cement mortar 32 ES 1176-1:2005 and
EN 196-1:1998

The most important factors that influence cement qualities are the chemical compositions of
cement raw materials especially clinker, and gypsum, the grinding effect (fineness) and the
amount of supplementary cementing materials added to the production [35]. The main aim the
experiment was to know the performance of blended cement produced using of coal ash
addition. Due to the material and the time resource limitation only two factors are chosen for
the experiment. These two factors are cement fineness characterized by (CR) and the coal ash
addition percent characterized by (CAP). To reduce the effect of clinker compositions on the
cement performance the same clinker was used for cement production. The optimum and
recommended amount of gypsum added for blended cement production is 4-5% by mass of
cement [36]. For this experiment 4.5% by mass cement of gypsum was used for all cement
produced.
Behavior of cement is strongly dependent on the properties of the individual particles, and the
size effects become more important as the particles become smaller [37]. Using supplementary
cementing material have many advantages on cement properties like increasing workability,
reducing of heat of hydration etc, but increasing the amount of cementing additives have a

Page 45
negative effect on the early strength of the cement [11]. Therefore, these two variables were
selected as candidates for influencing the optimization of properties of blended cement. Three
levels of cement fineness and five levels of clinker replacement percent were used. These levels
of cement fineness on 45μm sieve residue of ≤ 10, (10-16], and (16-20) % characterized as CR5,
CR13, CR18, and levels of clinker replacement percent (addition of coal ash) that are 20, 25, 30,
35, and 40% by mass of cement characterized as CAP10, CAP25, CAP30, CAP35, and CAP40
respectively. Accordingly 16 types of cement produced in laboratory including control OPC.
Sixteen cement pates were prepared according ES 1176-3:200 for consistency, setting time and
soundness test of the cement. In addition thirty two prisms of size 40mm x 40mm x 160mm
were also prepared according ES1176-1:2005 for 2 and 28 days compressive strength test.
Table 3.2 Characterization of cement produced and amount of raw materials used.
Cement Reside% Cement Raw Material [g] ®
% Coal Ash
Identification on 45μm Clinker Gypsum Coal ash
©
C0 ≤ 20 0 4,775 225 0
C1 ≤ 10 20 3,775 225 1,000
C2 (10-16] 20 3,775 225 1,000
C3 (16-20) 20 3,775 225 1,000
C4 ≤ 10 25 3,525 225 1,250
C5 (10-16] 25 3,525 225 1,250
C6 (16-20) 25 3,525 225 1,250
C7 ≤ 10 30 3,275 225 1,500
C8 (10-16] 30 3,275 225 1,500
C9 (16-20) 30 3,275 225 1,500
C10 ≤ 10 35 3,025 225 1,750
C11 (10-16] 35 3,025 225 1,750
C12 (16-20) 35 3,025 225 1,750
C13 ≤ 10 40 2,775 225 2,000
C14 (10-16] 40 2,775 225 2,000
C15 (16-20) 40 2,775 225 2,000
© ®
OPC for reference. The amount of cement raw materials was a dry base.

Page 46
CHAPTER FOUR
4. RESULTS AND DISCUSSION
4.1 CHARACTERIZATION OF CEMENT RAW MATERIALS
4.1.1 CHEMICAL ANALYSIS OF CLINKER AND GYPSUM
The chemical analysis of all three raw materials used for cement production was carried out in
Mugher Cement Factory quality control and assurance laboratory prior to cement production. The
chemical analysis results of raw materials were summarized on table 4.1.

Table 4.1 Chemical and Mineralogical Properties of cement raw materials


Compounds Clinker Gypsum
SiO2 21.67 4.74
Al2O3 5.24 1.08
Fe2O3 3.41 0.77
CaO 65.28 33.98
MgO 0.74 0.9
SO3 1.17 34.25
Free CaO 0.96 -
LOI 0.09 22.73
C3 S 60.94 -
C2 S 16.24 -
C3 A 8.12 -
C4AF 10.38 -
Mineralogical compositions of clinker were calculated according to Bogue equations.

According to ASTM classification there are five types of cement. These are Type I to IV. The
mineralogical value of clinker for modern Portland cement are C3S =50 -70, C2S =10 -30, C3A = 3 -
13 and C4AF = 5 -15. But the value of C3A ≤ 5% for cements Type IV and V [16]. Therefore, the
mineralogical analysis of clinker indicated on the table 4.1 shows that it is suitable only for the
production of Type I - III of Portland cement.

Page 47
4.1.2 CHARACTERIZATION OF COAL ASH
The performance of coal ash in cement production is strongly influenced by its physical,
mineralogical and chemical properties. The mineralogical and chemical compositions are dependent
to a large extent on the composition of the coal and burning conditions.
The most widely used specification for coal ash especially fly ash in world is ASTM C618. This
specification divides coal ash especially fly ash into two classes based on its source of origin and
composition.
These are class C and F with the sum of SiO2+Al2O3+Fe2O3 ≥ 50% and ≥70% respectively. Many fly
ashes produced from lignite or sub-bituminous coals meet the chemical requirement of Class F fly
ash.
Table 4.2 ASTM C618 and ES 1177-1 Chemical requirements for fly ash used as mineral admixture
in cement production, and chemical analysis of Ethiopian Yayu coal ash.
Compounds Coal ash Class F Class C
SiO2 59.83 - -
Al2O3 6.66 - -
Fe2O3 8.48 - -
SiO2+ Al2O3+ Fe2O3 74.97 ≥70 ≥50
CaO 3.26 ≤8 ≥8
MgO 2.26 - -
SO3 3.82 ≤5 ≤5
Loss on ingestion 10.04 ≤12® ≤6
® should be approved by the user

As described on table 4.2 the Yayu coal ash SiO2+ Al2O3+ Fe2O3 is 74.97% which is greater than
70%, CaO is 3.26% which is less than 8% and loss on ignition is 10.04% which is greater than 6%
and less than 12%. These values indicate that the Ethiopian Yayu coal ash is classified as class F fly
ash. They are predominantly non crystalline silica, which is the determinant factor for pozzolanic
activities. Therefore, the Ethiopian Yayu coal ash is suitable for utilizing it as cement additive for
production of blended cement. Even if the 10.04% loss of ingestion is the range of requirement the
higher the value has its negative effect on the cement properties by increasing the water requirement
for hydration reaction.

Page 48
4.2 EFFECT OF COAL ASH ON CEMENT PROPERTIES
In the previous sections, the pozzolanic properties of the Yayu coal ash were shown to be sufficient
for using them in blended cement production. However, in order to propose that ash can be used in
blended cements, the performance of the cements containing Yayu coal ash has to be investigated,
too. Moreover, these cements have to satisfy the requirements given in standard specifications. For
this purpose, the cements produced were tested to check their conformity with the three most widely
used cement specifications given in ES, and EN standards. The cements investigated can be classified
as ‗‗type Portland-fly ash‘‘ according to ASTM C 595, ‗‗type GU (General Use)‘‘ according to
ASTM C 1157, and ‗‗CEM II/A-V 32.5 R‘‘ or ‗‗CEM II/B-V 32.5 R‘‘ according to EN 196-1 and ES
1177-1

4.2.1 NORMAL CONSISTENCY

Consistency refers to the relative mobility (ability to flow) of a freshly mixed cement paste or mortar.
Five blended and one OPC cement pastes were tested for evaluation of normal consistency. The water
of consistency of the cement pastes containing different ratios of coal ash are shown in table 4.3
Table 4.3 The normal water consistency of cement as coal addition
Paste Id. P0 P1 P2 P3 P4 P5
% Coal ash 0 20 25 30 35 40
Consistency (%) 30 35 37 38 43 44

The results show that, the water of consistency of the blended cement pastes are higher than that of
the control OPC paste and increases with coal ash content; this is mainly due to the unburned carbon
content. LOI is a parameter that when done with coal ash mainly describes the carbon content in the
substance. Carbon has a low density and can absorb significant amounts of water. This means that the
maximum dry density and optimum moisture content of coal ash are influenced by the LOI. Higher
LOI ash is lower in density, but has higher optimum moisture contents. This will increase the water
demand for getting optimum workability of cement paste [38]. The ash analysis results show that the
loss of ignition was 10.04% which has a significant effect on water demand. The results show that the
water consistency of blended cement increase from control OPC by 16.7% for cement containing
20% ash and 46.7 % for cement containing 40% ash. The value of LOI of the ash was increased due

Page 49
to the burning method used for this experiment. The value should be decreased when the coal burning
done by thermal power plant boiler.
45
y = 0.355x + 28.95
R² = 0.934

40
Normal consistancy in %

35

30

25
0 5 10 15 20 25 30 35 40 45
Coal ash addition in %

Figure 4.1 Effect of Yayu coal ashes addition on normal consistency of blended cement
The results described on table 4.4 shows that the LOI of all blended cements were greater than the
control OPC cement and the results was increases with the coal ash addition. This indicates that the
coal ash is main source of LOI in this blended cement production. Therefore The Ethiopian standard
ES1177-1:2005 set the standard requirement for cement that limits its LOI. The value should be less
or equal to 5%. As result the addition amount of 35% and above Yayu coal ash for blended cement
production was causes the LOI of cement greater than 5% which is not allowed.
Table 4.4 Loss of ingestion of cement as coal addition
Cement Id. C0 C20 C25 C30 C35 C40
% Coal ash 0 20 25 30 35 40
LOI of cement (%) 1.65 3.87 4.20 4.38 5.44 6.51
C20 – C40 the average results of cements at three fineness level

Page 50
7

y = 0.113x + 1.507
6
R² = 0.959

4
LOI in %

0
0 5 10 15 20 25 30 35 40
Coal ash in %

Figure 4.2 Effect Yayu coal ashes ignition loss on blended cement

4.2.2 SETTING TIME AND EXPANSION


The standard specifications ASTM C 595 and C 1157 limit the initial setting time to minimum 45
minute and final setting time to maximum 420 minute. On the other hand, ES 1177-1 and EN 197-1
specifies a limit only for the initial setting time. It is 75 min for the cements like those produced in
this study. As seen from table 4.5, all cement types satisfied these requirements. Due to the lower
clinker content, the setting time values of the blended cements were longer than that of control OPC.
The results on table 4.5 show that as the fineness of the blended cement having the same
compositions increases the setting time was decreasing. This due to the cement hydration reaction
rate was increased with fineness. The setting time of the cement increases with the addition of coal
ash. see table 4.6. This implies that the pozzolanic nature of the ash decreases the rate of hydration by
decreasing heat of hydration.

Page 51
Table 4.5 Experimental results of setting time and Le chatlier expansion of blended cement.
Coal ash % residue on Setting time(min.) Le chatlier
Cement Id.
addition % 45μm Sieve Initial Final expansion ( mm)
C0 0 13.2 80 165 0.6
C1 17.92 112 191 0.3
C2 20 13.52 100 185 0.2
C3 2.24 94 180 0.4
C4 17.40 128 220 0.3
C5 25 12.36 120 198 0.3
C6 5.04 105 185 0.3
C7 17.6 158 258 0.2
C8 30 11.7 148 252 0.2
C9 7.72 120 220 0.4
C10 17.16 165 267 0.3
C11 35 12.76 152 245 0.4
C12 0.64 130 225 0.3
C13 16.2 188 269 0.3
C14 40 13.2 166 255 0.4
C15 0.44 142 230 0.3
.
Table 4.6 Average results of setting time of with coal addition
Cement Id. C0 C20 C25 C30 C35 C40
% Coal ash 0 20 25 30 35 40
Initial setting time 80 102 118 142 149 165
Final setting time 165 185 201 243 246 252

The average test results summarized in table 4.6 shows that the minimum initial setting time was 102
minute; that was found on the cement that contain 20% coal ash. This result was greater than the
minimum requirement 75minute by 36%. The highest final setting time 252minute was found for the
cement that has 40% coal ash. This value was less than the maximum requirement 420 minute by
40%. Therefore adding Yayu coal ash as additive for blended cement production was not having an
accelerating or retarding effect on setting of the cement. The workability of the produced cement was
very good.

Page 52
250

230

210

190
Setting time in min.

170

150
IST
130
FST
110

90

70

50
0 5 10 15 20 25 30 35 40

Coal ash in %

Figure 4.3 Effect of Yayu coal ash additions on cement setting time.

The standard specifications ES1177-1 and EN197-1 allow the Le chatlier expansion a maximum
value of 10 mm. Table 4.7 shows that the results for the blended cements were below this limit and
very small. It can be stated from this table that addition of Yayu coal ash reduces the expansions. The
results on table 4.5 shows that increasing the coal ash content in the production of blended cement do
not bring a significant change on cement paste expansion.

Table 4.7 Average test results of Le Chatiler‘s expansion of cement paste.

Cement Id. C0 C20 C25 C30 C35 C40


% Coal ash 0 20 25 30 35 40
Expansion in mm. 0.4 0.3 0.3 0.27 0.33 0.33

Page 53
0.45

0.4
Cement paste expansion[mm.]

0.35

0.3

0.25

0.2

0.15

0.1

0.05

0
0 5 10 15 20 25 30 35 40

Coal ash addition [ %]

Figure 4.4 Effect of Yayu coal ash additions on cement paste expansion

4.2.3 COMPRESSIVE STRENGTH


Of the various properties of concrete, it is generally the compressive strength, which attracts the
greatest interest since it is this property which is made use of in designing building units of structural
or of simple load bearing quality. In addition, it has a great practical and economic significance
because the sections and sizes of the concrete structures are determined by it. Since most concrete
structures are designed to resist compressive stress, it is this property which is usually prescribed by
standards. The main constitutes of concrete that affect compressive strength is the cement quality.
According to ES 1176-1:2005 test method, 450 gram cement and 1350gram EN standard sand and
0.5,0.51,0.52,0.53,0.54, and 0.55 water to cement ratio were used based on normal consistency of
mortal of OPC, blended cement of 20,25,30,35, and 40% respectively. The prepared mortal
specimens were tested for 2 and 28 days.

Page 54
Table 4.8 Test Results of Compressive Strength of Blended cement
Ash addition % residue Water to Compressive strength (MPa)
Mortar Id. cement ratio 2 days 28 days
[% ] on 45μm
M0 0 13.2 0.5 22.74 54.83
M1 17.92 13.83 46.66
M2 20 13.52 0.51 15.46 47.96
M3 2.24 21.26 49.94
M4 17.40 11.16 34.51
M5 25 12.36 0.52 12.16 36.45
M6 5.04 15.44 44.63
M7 17.6 7.94 29.09
M8 30 11.7 0.53 10.61 32.79
M9 7.72 20.3 40.36
M10 17.16 6.87 26.73
M11 35 12.76 0.54 7.89 30.71
M12 0.64 21.02 42.01
M13 16.2 7.06 24.93
M14 40 13.2 0.55 7.21 26.08
M15 0.44 20.48 37.27

The compressive strength of reference and blended cement are summarized on table 4.7.The results
shows that as normally expected compressive strength test results of all blended cement are less than
the reference OPC both at 2 and 28days. For all coal ash addition level the cement compressive
strength increases with fineness and age. And it decreases with the coal ash addition amount. This is
because of the hydration of cement increases with fineness and age. But the pozzolanic nature of coal
ash slows the reaction rate.
As we see from table 4.8 the slow compressive strength development of blended cement was
compensated by increasing cement fineness. These cements were produced in laboratory. But in bulk
cement production process making cement finer:
 It will incur more cost of production by increasing the electrical energy consumption, wear
and tear of grinding media and mill internals.
 More gypsum is required for proper retardation because increased fineness makes more
tricalcium aluminate available for early hydration.
 A higher early rate of hydration causes a higher early rate of heat liberation. If not properly
dissipated, this heat may cause cracking – especially in mass concrete construction.

Page 55
Therefore, optimization of cement fineness should be done for economical production of cement
without affecting quality. The fineness of C3, C6, C9, C12, and C15 used only to know its effect on
cement performance. But due to the above reasons it was not practically produced.
Table 4.9 Compressive Strength of More Fine Cements
Coal ash addition % residue on 45μm Compressive strength (MPa)
Mortar Id.
[% ] 2 days 28 days
M0 0 13.2 22.74 54.83
M3 20 2.24 21.26 49.94
M6 25 5.04 15.44 44.63
M9 30 7.72 20.3 40.36
M12 35 0.64 21.02 42.01
M15 40 0.44 20.48 37.27

50
Compressive strength [MPa]

45
40
35
30
25 2days
20 28days
15
10
0 5 10 15 20
Residue on 45μm sieve [%]
A

50 45
40
Compressive strength [Mpa]

Compressive strength [Mpa]

45
40 35
30
35
25
30
2days 20 2days
25
15
20 28days 28days
10
15 5
10 0
0 10 20 0 5 10 15 20
Residue on 45μm sieve [%] Residue on 45μm sieve [%]
B C

Page 56
45 40

Compressive strength [Mpa]


Compressive strength [Mpa]

40 35
35 30
30 25
25 20
20 15 2days
2days
15 10
28days 28days
10 5
5
0
0
0 10 20
0 10 20
Residue on 45μm sieve [%]
Residue on 45μm sieve [%]
E
D

Figure 4.5 Effect of cement fineness on compressive strength. A is 20% coal ash addition, B is 25%
coal addition, C is 30% coal addition, D is 35 % coal addition and E is 40% coal addition

For any cement application, one should know the compressive strength standard values and the
minimum required compressive strength. The Ethiopian Standard requirements of compressive
strength are given as in table 4.10.
After evaluate and compare the results based on standards it is possible to propose the optimum coal
addition level for blended cement for bulk production. All the specimens prepared were class 32.5R
cements and it is possible to compare the result data with standard class 32.5R.
Table 4.10 Mechanical and physical requirements of 32.5 classes cement (ES1177.1:2005)

Early strength Standard strength Initial Final Soundness


Strength
[MPa] [MPa] setting setting (expansion)
class
At 2 day At 7 day At 28 day time[min.] time[min.] [mm]
32.5N - ≥16
≥ 32.5 ≤ 52.5 ≥75 ≤ 420 ≤ 10
32.5R ≥10 -

As indicated on table 4.11 the results of all cement mortars having 20 and 25% coal addition was
satisfy the minimum requirement of both early and lateral compressive strength. Except M 8, M9, M12
and M15 all other cement mortars having 30 - 40% coal addition do not satisfy both early and lateral
strength. Cement mortalr (M8) very marginal to the minimum standard requirement. The results were
greater by 6.1% and 0.9% form early and lateral age minimum strength respectively. But M 9, M12 and
M15 including to M3 and M6 satisfy the requirement due to extreme fineness. Therefore, these samples
were not used for determination of optimum coal addition level.

Page 57
Table 4.11 Compressive strength test results as compared to ES requirements

Strength Class
32.5R
Mortar Id. Remark
2 day 28 day
≥10 ≥32.5
M0 22.74 54.83 OPC 42.5R
M1 13.83 46.66 Satisfy
M2 15.46 47.96 Satisfy
M3 21.26 49.94 Satisfy
M4 11.16 34.51 Satisfy
M5 12.16 36.45 Satisfy
M6 15.44 44.63 Satisfy
M7 7.94 29.09 Not satisfy
M8 10.61 32.79 Satisfy
M9 20.3 40.36 Satisfy
M10 6.87 26.73 Not satisfy
M11 7.89 30.71 Not satisfy
M12 21.02 42.01 Satisfy
M13 7.06 24.93 Not satisfy
M14 7.21 26.08 Not satisfy
M15 20.48 37.27 Satisfy

Table 4.12 Average test results of compressive strength

Coal ash addition [% ] Compressive strength (MPa)©


2 days 28 days
0 22.74 54.83
20 14.65 47.31
25 11.66 35.48
30 9.28 30.94
35 7.38 28.72
40 7.14 25.51
© Results of cement having extreme fineness that described on table 4.8 were excluded because if it
included it may lead to wrong conclusions.

Page 58
60

50
Compressive strength [Mpa]

40
OPC

30 20% CA
25% CA
30% CA
20
35% CA
40% CA
10

0
0 5 10 15 20 25 30

Curing time [days]

Figure 4.6 Effect coal ash additions on cement compressive strength

The average test results of compressive strength in table 4.12 and figure 4.5 shows that there is a
reduction of early strength by 51.3% and lateral strength by 46.1% as coal addition raised from 20 to
40%. The compressive strength of cement produced by addition of 30 to 40% coal ash does not
satisfy the minimum requirement set by Ethiopian standard. Therefore, the optimum Yayu coal ash
addition level of for blended cement production must between 20 - 25% by mass of cement. The
result indicates that, using Yayu coal ash one can able to produce blended cement that conforms to
ES1171-1- CEM II/B-V 32.5R (Portland fly ash cement containing a total quantity of siliceous fly ash
(V) between 21-35% by mass and strength class 32.5 with a high early strength.

Page 59
4.3 ECONOMICAL ANALYSIS OF PRODUCING CEMENT AT YAYU
Mugher Cement Factory (MCF), one of the organizations under Chemical Industry Corporation
which has a design capacity of 1.5million metric ton clinker or 2.1million metric tons cement per
annum. The organization is monopolizing the cement market for the last 20 years. But as the new
entrants in sector increases since last five years the cement market become stiffer.
Table 4.13 Mugher Cement Factory performances in clinker production and cement delivery for last
five consecutive budget years. (Source: MCF annual reports)
S.No. Fiscal Clinker production (ton) Cement delivery (ton)
year* Plan Actual Performance Plan Actual Performance
(%) (%)
1 2003 590,000 453,328 77 822,770 589,391 71
2 2004 1,114,800 544,870 49 1,446,860 864,958.16 60
3 2005 1,270,800 825,711 65 1,775,000 1,046,049.89 59
4 2006 1,335,000 789,403 59 1,895,000 1,002,847.53 53
5 2007 1,225,000 719,793 59 1,664,000 890,098.41 54
* Ethiopian calendar
The maximum capacity utilized in clinker production and cement delivery are 55 and 50 %
respectively in 2005 fiscal year. See table 4.
This mainly due to:
 Electrical energy shortage and interruptions.
 Technical and technological problem encountered
 Cement market become stiffer
The third problem become increasing for time to time, therefore CIC is using different market
strategy to increase the market share of Mugher Cement. Among these are reducing of sale price of
cement, increasing the capacity utilization of the plant, increasing the distribution channels, intensive
adverting the product qualities and service etc.
Yayu is found 600 kilo meters for capital city Addis Ababa at southern west of Ethiopia. There is no
cement factory at this part of the country. All cement delivered to southern west of Ethiopia is by car
transport mostly from central Ethiopia. But for CIC bringing coal ash from Yayu which is 600Km to
Tatek by truck is expensive as compared to currently transporting pumice from Adama which is
100Km for production of blended cement.

Page 60
Establish cement milling and packing plant at Yayu is one option for utilization of the coal ash from
thermal power plant. As seen from table 4.13 MCF has large unutilized capacity of clinker
production. Therefore, transporting clinker to Yayu for utilizing coal ash produced form thermal
power plant.
For cost analysis of cement producing at Yayu and Tatek the following assumptions are used bellow,
this assumptions are based on literature review and cement industrial benchmark.
 85% by mass coal ash is used as cement additive
 Average moisture of coal ash, gypsum and FGD used is 5%
 Average process loss of materials is 1%
 Average gypsum & FGD used in cement production is 5% by mass
 Average pumice used in cement production is 28% by mass and average moisture is 10%
 Except direct material and transportation cost all other cost at Tatek and Yayu considered to
be same.
 The synthetic gypsum is used in place of virgin gypsum at Yayu
 The cost of production of coal ash & FGD is 10 Birr/ton
 The working hours of mill 20hr/day and 360days/year
 The truck taking clinker to Yayu and in return will bring fertilizer to central market.
 Cement milling and packing plant established at Yayu will utilize the infrastructure
constructed for fertilizer and thermal power plant.
 Establishing of cement milling and packing plant at Yayu will integrate the chemical sectors
increase the awareness of utilizing coal ash in construction sector.
Annual coal ash production =75,000 Mt,
Using average of 80% by mass to be used for blended cement,
Total usable coal ash for cement additive is 60,000Mt
Considering average moisture 5% and process loss 1%
The dry coal ash used for cement additive is 56,400Mt.
Assuming 22% coal addition for blended cement production
56,400t
The annual cement production using dry coal ash = = 256,364 ≈256,000
0.22

Working hours of mill to be 20hr/day, 360 days/year


Total working hours per year = 7,200

Page 61
256,000t
The nominal mill capacity = = 35.6t/hr ≈ 36t/hr
7,200 hr

Table 4.14 Amount of raw materials required in metric tons for production of 256,000 Mt blended
cement
Site of cement production Source Distance from
Raw materials
Tatek Yayu source to site (Km)
Clinker 171,520 186,880 Mugher 70/690
Pumice 79,565 - Adama 100
Coal ash - 59,700 Yayu 0
Gypsum 13,440 - Mugher 70
FGD(synthetic
- 13,440 Yayu 0
gypsum)

Table 4.15 Current production and transport cost of raw materials


(Source: MCF 2008 E.C fiscal half year report)
Raw materials Production cost (Birr/t) Transportation cost (Birr/ton. Km)
Clinker 1620 0.86
Pumice 23 0.86
Gypsum 52 0.86
Coal ash 10® 0
FGD 10® 0
® assumed values

Table 4.16 Unit production cost of cement at Tatek site (considering direct material and transport)
Raw materials Amount (t) Direct material cost(Birr) Transportation cost (Birr)
Clinker 0.65 0.65*1620 = 1053 0.65*0.86*70 = 39.13
Pumice 0.31 0.31*23 = 7.13 0.31*0.86*100 = 26.66
Gypsum 0.053 0.053*52 =2.76 0.053*0.86*70 = 3.19
Sum 1,062.89 68.98
Cost of cement at Tatek 1,131.87
Cost to delivery at Yayu 1131.87+(1*0.86*600 ) = 1,647.87

Page 62
Table 4.17 Unit production cost of cement at Yayu site (considering direct material and transport)

Raw materials Amount (t) Direct material cost(Birr) Transportation cost (Birr)
Clinker 0.73 0.73*1620 = 1182.6 0.73*0.86*690 = 433.18
Coal ash 0.23 0.23*10 = 2.3 0
FGD 0.053 0.053*10 =0.53 0
Sum 1185.43 433.18
Cost of cement at Yayu 1618.61

Unit cost saving = Cost of cement at Yayu – cost of producing at Tatek and delivering at southern
west Ethiopia.
Unit cost saving= 1,647.87 – 1,618.61(Birr/ton of cement)
= 29.26 Birr/ton
Annual saving =29.26 Birr/ton*256,000ton
= 7,490,560 Birr
The results from above table and calculation shows that transporting clinker to Yayu and producing
cement have annual saving of 7,490,560 Birr cost advantages than producing at Tatek and
distributing at south west part of Ethiopia.

Establishing cement plant of nominal capacity of 35ton per hour should utilize the whole coal ash
produced by thermal power plant at Yayu. Beside the cost saving of cement producing at Yayu CIC
will take the geographical advantages to the delivery the southern west of Ethiopia. This will increase
the market share of Mugher Cement.

Page 63
CHAPTER FIVE
5. CONCLUSIONS AND RECOMMENDATIONS
5.1 CONCLUSIONS
In this study, the suitability and optimum utilization of Yayu coal ash for blended cement production
was investigated. The coal sample collected from Yayu was burned and sieved at home to get ash.
The chemical analysis of coal ash was done according to ES1176-3:2005 and EN 196.3:1998 testing
methods. Using coal ash blended cements were produced in laboratory ball mill with the clinker
replacement level of 20, 25, 30, 35, and 40% by mass of cement. Each level of replacement cements

were produced for three different fineness of 16-20, 10-16 and ≤10 % residue on 45μm sieve. 4.5%
by mass of cement gypsum were used for all cement mixture to reduce the effect of gypsum on
cement performance. The chemical and physical properties of cement were evaluated like SO 3, loss

on ignition, % residue on 45μm sieve, normal consistency, setting time, expansion and compressive
strength. Based on observations and trends determined from the results of this evaluation, the
following conclusions were made:

 The chemical and physical properties of the Yayu coal ash was suitable to use as cement
extender and based on ASTM C 618, the ash is grouped in F class. But the loss of ignition
10.42% was high, which leads to increase the water requirement above the reference OPC
cement. The water requirements were increased with replacement level. But this does not
reduce the cement quality.
 The initial and final setting times of all blended cements were greater than the reference OPC.
As the replacement level increases both initial and final setting times too. All blended cement
meets the minimum requirement set by ES 1177.1:2005 minimum 75 minute and maximum
requirement set by ASTM C1157 420 minute.
 The expansions of blended cements were greater than the reference OPC. The replacement
level does not have any significant effects. All cements have very small expansion as
compared to the maximum requirement level set by ES1177.1:2005 10mm.
 The compressive strength of the blended cements was increased with the cement fineness at
all replacement level. The ignition loss of coal ash forces to increase the water to cement ratio
during mortar preparation above the standard value of 0.5. As the cement % residue on 45
Page 64
μm sieve were below 5% all cement produced was satisfy the 2days and 28 days minimum
requirements set for 32.5R strength class 10 and 32.5 MPa. But producing cement to this
fineness was not economical. The optimum sieve residue used by many cement manufacturers
was greater than 10%. For cement % residue greater than 10% only cement mortars of 20 and
25 % replacement level fulfill the minimum requirements set for 32.5R strength class.
Therefore the optimum clinker replacement range was between 20- 25% by mass.
 Establishing cement milling and packing at Yayu site by transporting clinker from Mugher
have a cost saving advantages of producing cement at Tatek and distribute at southern west of
Ethiopia.
 The use of Yayu coal ash as presented is not only beneficial to the cement industry, but also is
friendly to the environment. This will increase the culture of green building and technology by
a sector that is a major contributor of emissions and reduction of landfills and landfill cost to
Chemical industry corporation
 The alternative use of coal ash are for road construction, soil stabilization, as aggregate in
concrete production etc,

Page 65
5.2 RECOMMENDATIONS
 Since the Yayu coal based thermal power plant under establishment, the ash used for this
experiment was prepared by burning of the coal at home. But the chemical and physical
properties of coal ash mainly depend on the burning conditions. Therefore, coal ash has to be
collected and investigated for further clarification when the power plant starts the operation to
arrive at the better coal ash blending ratio and other characterization.
 According to the test result stated in chapter four up to 25% by mass coal ash was used for
blended cement production without affecting the cement quality, and in the south west of
Ethiopia currently there is no cement industry. Therefore, CIC strongly recommend to
establish cement mill near power plant for efficient utilization of the opportunity of
infrastructure built for fertilizer and power plant, coal ash produced by power plant, clinker
from Mugher and the cement market found at south west Ethiopia.
 Due to the time and financial resources limitation this experiment was not cover some aspects.
But this does not change the above test results. Therefore, the following test should be
recommended in order to have farther constractive information of Yayu coal ash.
1. The XRD analysis in order to know the mineralogical compositions the ash.
2. SEM analysis in order to know the particle shapes of the ash
3. Effect of the Yayu coal ash addition in concrete

Page 66
REFERENCE

[1] Jozef Junák, & Nadežda Števulová., ―Effective utilization of coal fly ash in building material
production‖ Civil Engineering Faculty, Institute of Building and Environmental Engineering,
Technical University of Košice, Vysokoškolská 4, 042 00 Košice, Slovakia, August 10,
2011. 1-2.

[2]Ramme-Tharaniyil,‖Coal combustion products utilization handbook‖ 3rd edition, A we


energies publication, United state, 2013, 1-3, 6-7, 54-56.

[3]Craig Heidrich, Hans-Jochim Feuerborn, & Anne Weir, ―Coal combustion products: a Global
Perspective‖, World of Coal Ash (WOCA) conference-April 22-25, 2013 in Lexington, KY;
2013. 3-4, 7-8.

[4] Tarun R., & Shiw S. Singh., ―Fly ash generation and utilization - an overview‖ Department of
Civil Engineering and Mechanics, College of Engineering and Applied Science, The
University of Wisconsin-Milwaukee, June 1993, 6-7

[5] Messele Gebre Hiwot‖ Transformation ―National Journal No. 9, June-July 2014, 84-91

[6]J.Alam and M.N Akhtar,‖ Fly ash utilization in different sectors in Indian scenario‖
International journal of emerging trends in Engineering and Development Issue1, Vol. 1
August 2011, 3-4

[7] H Du Plessis,‖the use of gasification ash in cement concrete‖, University of Pretoria ETD
2006, p26 -27,p 31-32

[8] Bhatty, Javed I.; Miller, F.MacGregor; and Kosmatka, Steven H.; editors, ―Innovations in
Portland Cement Manufacturing‖, CD400, Portland Cement Association, Skokie, Illinois,
U.S.A., 2004, p1- 40

[9] Peter C.Hewlett,‖Lea‘s chemistry of cement and concrete‖ 4th edition, Elsevier Science &
Technology Books, January 2004, 1-19, 41-43, 241-245

Page 67
[10] Dr.B. Salah,‖Portland cement‖ concrete technology, seen on November 20/2015
uotechnology.edu.iq/dep.../Chapter%20One-portland%20cement.pdf

[11]Ali Akbar Ramezanianpour;‖cement replacement material, Properties, Durability,


Sustainability, Springer-Verlag Berlin Heidelberg, 2004, p17 – 20, p65

[12] Rachel J. Detwiler, Javed I. Bhatty,and Sankar Bhattacharja; ―supplementary cementing


materials for use in blended cements‖ PCA Research and Development Bulletin RD112T,
PCA R&D serial No. 2038,1996, p1-2, p40-45

[13] Mengistu Aregaw;‖ investigation of calcite and volcanic ash for their utilizations as cement
filling and additive materials‖ AAU faculty of Science, 2010,p 1-2

[14] Rachel J.Detwiler, Javed I. Bhatty, & Sankar Bhattacharja, ‖Supplementary cementing
materials for use in blended cements‖ ,Portland cement association research and
development bulletin RD112T, Serial.No.2038, 1996, 1-2.

[15] Ethiopian Standard (ES 1177-1:2005),‖Cement Part 1: composition, specifications and


conformity criteria for common cements‖, 2005

[16] Hendric G. van Oss;‖Background facts and issues concerning cement and cement data‖, U.S
geological servey,Open-File Report 2005-1152, p17-20,

[17] World energy resource: Coal world energy council 2013

[18] Mugher Cement Enterprise,‖ Feasibility study coal firing for clinker production‖, July, 2013,
Addis Ababa.

[19] Technical assessment report; ―a technical assessment of coal utilization and research trends‖,
Global climate and energy project, Stanford university, 2006

[20] Wolela Ahmed,‖ Fossil fuel energy resource of Ethiopia‖ Bulletin Chemical society of
Ethiopia, ISSN1011-3924, 2008, p67-84

[21] Yoseph Dejene;‖ the utilization of indigenous coal as energy substitute in cement industry‖,
Addis Ababa university department of chemical engineering, August, 2004, p34-47

Page 68
[22] Madawala Liyanage Duminda Jayaranjan, Eric D. van Hullebusch,& Ajit P. Annachhatre,‖
Reuse options for coal fired power plant bottom ash and fly ash‖, Springer Science +
Business Media Dordrecht, April 2014, 1-2

[23] Michael Thomas;‖Optimizing the use of fly ash in concrete‖ concrete thinking for
sustainable work, Portland Cement Association, p1-24

[24] Rakesh Kumar Behera,‖ Characterization of fly ash for their effective management and
utilization‖, National institute of technology Rourkela, Orissa – 769008,Department of
mining engineering, 2009-2010, 2

[25] R. Siddique and M. Iqbal Khan;‖ Supplementary Cementing Materials‖, Engineering


Materials, DOI: 10.1007/978-3-642-17866-5_1,© Springer-Verlag Berlin Heidelberg
2011, p2-5

[26] R.B. Freeman;‖Optimization of physical and compositional characteristics of fly ash


cement for the production of sulfate resistant concrete‖, University of Texas at Austin,
August, 1992, p81-82

[27] K. Wesche.,‖Fly ash in concrete properties and performance‖,Technical committee reports


67-FAB Use of Fly Ash in Building, ISBN 0-203-63026-2 (Adobe eReader Format),
RILEM, 1991, p57-60

[28] Rafat Siddique,‖ Waste materials and by-products in concrete‖, Engineering materials, e-
ISBN: 978-3-540-74294-4, Springer-Verlag Berlin Heidelberg, 2008, p190-196

[29] Mugher cement enterprise, ‖Product development and quality assurance service laboratory
working manual with basic notes in cement technology‖ June,2008

[30] Ethiopian Standard (ES 1176-2:2005),‖Method of testing cement Part 2: Methods of


chemical analysis of cement‖, 2005

[31] Ethiopian Standard (ES 1176-7:2005),‖Method of testing cement Part 7: Methods of


taking and preparing samples of cement‖, 2005

Page 69
[32] Ethiopian Standard (ES 1176-6:2005),‖Method of testing cement Part 6: Designation of
fineness‖, 2005

[33] Ethiopian Standard (ES 1176-3:2005),‖Method of testing cement Part 3: Designation of


setting time and soundness‖, 2005

[34] Ethiopian Standard (ES 1176-1:2005),‖Method of testing cement Part 1: Determination


of strength‖, 2005

[35] J. Talaber,‖Factor influencing the quality of cement‖, Department of Building


Materials,Technical University, Budapest, February 1981, p27-39

[36] Amin A. and Mohamad H.Aboud,‖Determination of optimum quantity of raw gypsum


addition for Atbara cement clinker‖ ,Department of mining, faculity of engineering,
Khartoum University, www.jeaconf.org/ on October 13/2015, p 1-6

[37] Gleb Gennadievich M.,‖ Improved cement quality and grinding efficiency by means of
closed mill circuit modeling‖,Texas A & M University, December 2007, p11-15

[38] Da-zuo CAO, Eva SELIC, Jan-Dirk HERBELL,‖ Utilization of fly ash from coal-fired
power plants in China‖, Journal of Zhejiang University SCIENCE A,ISSN 1673-
565X (Print); ISSN 1862-1775 (Online),March 27,2008, p681-686

Page 70
Appendix A:
PICTURES OF EQUIPMENTS USED FOR THE EXPERIMENT

Fig.1. Digital balance Fig.2.Laboratory ball mill

Fig.3.Compressive strength test machine Fig.4. Blain apparatus

Page 71
Fig.5. Molding plate Fig.6. Jolting apparatus

Fig.7. Graduated cylinder Fig.8. Le-chatelier apparatus

Fig.9. Sieve machines Fig.10. Muffle Farnese

Fig.11. Stop watch Fig.12. X ray fluoroscope /XRF/

Page 72
Fig.13. Mortar mixer Fig.14. Vicat apparatus

Fig.15. Humidity cabinet Fig.16. Water bath

Fig.17. Drying oven Fig.18 Powder mixer

Page 73
Appendix B:
AVERAGE XRF TEST RESULTS OF LAB CEMENTS

Coal ash addition amount [%]


Oxides
0 20 25 30 35 40
CaO 61.52 51.25 48.50 47.60 45.44 43.81
SiO2 21.85 29.72 31.43 31.56 31.97 32.05
Al2O3 6.57 6.84 7.25 7.62 7.85 7.93
Fe2O3 3.76 3.45 3.53 3.61 3.75 3.85
MgO 1.03 0.85 0.87 0.90 0.94 0.98
SO3 2.65 2.67 2.73 2.79 2.85 3.02
LOI 1.65 3.87 4.20 4.38 5.44 6.51

Page 74
DECLARATION
I, the undersigned, declare that this thesis entitled "Optimum utilization of coal ash as
additive for blended cement production" has not been submitted in any form for another
degree, diploma or an award at any university or other institution of the tertiary education.
Whenever contributions of others are involved, every effort is made to indicate this clearly, with
due references to the literature review and discussions.
Information taken from the published and unpublished work of the others has been
acknowledged in the text and a list of references was give.
The work was under the guidance of Prof. Whasik Min (Dean, School of Chemical and Bio
Engineering) ,and instructor in Addis Ababa University, Addis Ababa Institute of Technology,
School of Chemical and Bio Engineering.

---------------------------------------------------
Name

---------------------------------------------------
Signature

---------------------------------------------------
Place of Submission

---------------------------------------------------
Date of Submission
CERTIFICATION
This thesis has been read and approved as meeting the requirement of the School of Chemical
and Bio Engineering in the Addis Ababa Institute of Technology for the award of degree of
masters of Science in chemical engineering.

---------------------------------------------------
Advisor

---------------------------------------------------
Signature

---------------------------------------------------
Date