KIMA CHEMICAL CO.

LTD
Add:Zhangdian,Zibo, Shandong, P.R.China
Tel: +86-533-6281218
Email:[email protected]
www.kimachemical.com

Global cellulose ether grade

Supplier APPLICATION FIELD PRODUCT GRADE VISCOSITY PROPORTITY
modified hPMcgrade for long open time and very
Cement-Based Tile Adhesives (CBTA) WaloCel VP-M-49125 8,000
high slip resistance
modified hPMcgrade for long open time and very
Cement-Based Tile Adhesives (CBTA) WaloCel MKS 10000 PF 60 10,000
high slip resistance
medium viscosity heMcgrade recommended for
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 15000 PF 01 15,000 standard quality polymer
and non-polymer modified thin-sets
medium viscosity heMcgrade with delayed
Cement-Based Tile Adhesives (CBTA) WaloCel MW 15000 PFV 15,000 hydration; suitable for
dry-mix and ready-to-use
Cement-Based Tile Adhesives (CBTA) MeThoCel 327 20,000 multipurpose; good open time and slip resistance
modified heMcgrade; good open time and
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 20000 PP 10 20,000
workability
modified heMcgrade; long open time, good slip
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 25000 PF 25 l 25,000
resistance and workability
high viscosity heMcgrade; recommended for
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 40000 PF 01 40,000 standard quality polymer
and non-polymer modified thin-sets
high viscosity heMcgrade with delayed hydration;
Cement-Based Tile Adhesives (CBTA) WaloCel MW 40000 PFV 40,000 suitable for dry-mix
and ready-to-use
high viscosity heMcgrade offering good open
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 45000 PP 10 45,000 time, workability and
moderate slip resistance
 modified heMcgrade provides long open time,
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 45000 PF 20 l 45,000 excellent workability and
good slip resistance
very high viscosity heMc; high water
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 60000 PF 01 60,000
retention/open time at low dosage rates
very high viscosity heMcwith delayed hydration;
Cement-Based Tile Adhesives (CBTA) WaloCel MW 60000 PFV 60,000 high water retention/
open time at low dosage rates
ultra high viscosity heMc; high water
Cement-Based Tile Adhesives (CBTA) WaloCel M-20678 80,000
DOW retention/open time at low dosage rates
Tile Grouts WaloCel MK 3000 PF 3,000 excellent workability
Tile Grouts WaloCel MKW 4000 PF 01 4,000 easy workability
Tile Grouts WaloCel MKX 6000 PF 01 6,000 good workability and application properties
Self-Leveling Underlayments MeThoCel CP 7331 100 less segregation, good flow
Self-Leveling Underlayments MeThoCel CP 1119 300 less segregation, good flow
Self-Leveling Underlayments WaloCel MK 400 PF 400 less segregation, good flow
Self-Leveling Underlayments WaloCel MKW 2000 PF 01 2,000 easy workability
Mortars for EIFS/Skim Coat WaloCel MKW 4000 PF 01 4,000 easy workability
Mortars for EIFS/Skim Coat WaloCel MKX6000 PF 01 6,000 good workability and application properties
Mortars for EIFS/Skim Coat WaloCel MKS10000 PF 60 10,000 excellent open time,slip resistance
Mortars for EIFS/Skim Coat WaloCel MKW 10000 PP 01 10,000 good air void stabilization
Mortars for EIFS/Skim Coat WaloCel MKX 15000 PF 01 15,000 multipurpose
Mortars for EIFS/Skim Coat WaloCel MKW 15000 PP 30 15,000 good air void stabilization,sag resistance
Mortars for EIFS/Skim Coat WaloCel MKW 20000 PP 20 20,000 good air void stabilization
Mortars for EIFS/Skim Coat WaloCel MKX 20000 PP 10 20,000 easy workability
Mortars for EIFS/Skim Coat MeThoCel 327 20,000 multipurpose
Mortars for EIFS/Skim Coat WaloCel MKX 25000 PF 25 l 25,000 high yield, good workability
Mortars for EIFS/Skim Coat WaloCel MKX 45000 PP 10 45,000 high water retention
Mortars for EIFS/Skim Coat WaloCel MKX 45000 PF 20 l 45,000 good workability
Cement-Based Plasters WaloCel MKW 15000 PP 30 15,000 air void stabilization, good standing strength
Cement-Based Plasters WaloCel MKW 20000 PP 01 20,000 air void stabilization, good standing strength
Cement-Based Plasters WaloCel MKW 20000 PP 20 20,000 air void stabilization, easy workability
Cement-Based Plasters WaloCel MKW 20000 PP 30 20,000 air void stabilization, sag resistance
Cement-Based Plasters WaloCel MKW 20000 PP 40 20,000 air void stabilization, high yield
Cement-Based Plasters WaloCel MKW 30000 PP 01 30,000 air void stabilization
Cement-Based Plasters WaloCel MKW 30000 PP 10 30,000 air void stabilization, easy workability
Cement-Based Plasters WaloCel MKW 30000 PP 30 30,000 air void stabilization, sag resistance
Gypsum-Based Building Materials WaloCel MKX 20000 PF 40 20,000 reduced lump formation
Gypsum-Based Building Materials WaloCel MKX 30000 PF 60 e 30,000 easy workability, high yield
Gypsum-Based Building Materials WaloCel MKX 35000 PP 35 35,000 multipurpose
Gypsum-Based Building Materials WaloCel MKX 40000 PF 20 40,000 reduced lump formation
Gypsum-Based Building Materials WaloCel MKX 70000 PP 01 70,000 high water retention
Gypsum-Based Building Materials WaloCel MKX 70000 PP 40 70,000 easy workability, high water retention
Consistency development:moderate
Final consistency:very high
10000 Sag resistance:very high
Cement tile adhesive premium Tylose® MB 10008 P4 mPa•s Water demand:very high
Höppler Water retention:moderate
Influence on cement hydration:moderate
Heat stability:low
Consistency development:moderate
Final consistency:moderate
Sag resistance:moderate
Cement tile adhesive standard Tylose® MB 15009 P2 15000 Water demand:high
mPa•s Water retention:high
Höppler Influence on cement hydration:high
Heat stability:low
Consistency development:moderate
Final consistency:very high
3000 Sag resistance:very high
Cement tile adhesive premium Tylose® MB 3003 P4 mPa•s Water demand:high
Höppler Water retention:low
Influence on cement hydration:high
Heat stability:low
 Biostability:no
Gloss:moderate
60000 Pigment Compatibility:moderate
Paint-stripping pastes Tylose® MB 60000 P2 mPa•s Anti-spattering:moderate
Höppler Pseudoplasticity:moderate
Thickening effect:high
Wet scrub resistance:high
Water retention:very high
Consistency development:fast
Final consistency:high
Sag resistance:high
Gypsum spray plaster 100000
Tylose® MHS 100005 P3 Water demand:high
Gypsum trowelling compound mPa•s
Water retention:very high
Influence on cement hydration:low
Heat stability:high

Consistency development:very fast

Final consistency:high
10000 Sag resistance:moderate
Cement one coat Tylose® MHS 10012 P6
mPa•s Water demand:high
Water retention:moderate
Influence on cement hydration:moderate
Heat stability:high
Consistency development: very fast
Final consistency: high
Sag resistance: moderate
10000
Cement one coat Tylose® MHS 10012 P6 Water demand: high
mPa•s
Water retention: moderate
Influence on cement hydration: moderate
Heat stability: high
 Consistency development: very fast
Final consistency: moderate
Sag resistance: moderate
Block laying adhesive 150000
Tylose® MHS 150003 P4 Water demand: high
Gypsum mounting binder mPa•s
Water retention: very high
Gypsum spray plaster
Influence on cement hydration: moderate
Heat stability: high
Consistency development: very fast
Final consistency: low
Sag resistance: moderate
30000
Cement decorative render Tylose® MHS 30007 P6 Water demand: moderate
mPa•s
Cement skim coat Water retention: high
Influence on cement hydration: low
Heat stability: high
Tylose® MHS 30024 P4 30000 Consistency development: fast
mPa•s Final consistency: moderate

Consistency development: very fast

Final consistency: moderate
Cement render Höppler Sag resistance: moderate
EIFS Tylose® MHS 30027 P6 30000 Water demand: moderate
mPa•s Water retention: high
Influence on cement hydration: low
Heat stability: high

Consistency development: fast

Final consistency: low
Sag resistance: low
60000
Emulsion tile adhesive Tylose® MHS 60000 YP4 Water demand: low
mPa•s
Water retention:very high
Influence on cement hydration: low
Heat stability: high
 Consistency development: fast
Final consistency: high
Sag resistance: high
30000
Gypsum hand plaster Tylose® MO 30023 P4 Water demand: high
mPa•s
Water retention: high
Influence on cement hydration: moderate
Heat stability: high
Consistency development: fast
Final consistency: low
Sag resistance: low
60000 Water demand: low
Emulsion joint filler Tylose® MOT 60000 YP4
mPa•s Water retention:very high
Emulsion tile adhesive
Influence on cement hydration: low
Heat stability: high

Rubber gloves
Seed coating
Protective colloidal effect: good Tylose® MOBS 50 G4 50 mPa•s
Polymerisation
Particle size controll: good
Suspension polymerisation (PVC)

Consistency development: very fast

Final consistency: low
Sag resistance: moderate
60000
Cement one coat Tylose® MO 60016 P4 Water demand: moderate
mPa•s
Water retention: very high
Influence on cement hydration: low
Heat stability: high
4000
Pencils Tylose® MO 4000 P4
mPa•s
 Ceramic applications Thickening effect: moderate
Engobes & glazes Plasticity: good
Tylose® CER 406001 300 mPa•s
Extrusion Temperature stability: good
Binding effect: moderate
Thickening effect: high
Ceramic applications
20000 Plasticity: very good
Extrusion Tylose® E 407003
mPa•s Temperature stability: good
Binding effect: good
Thickening effect: very high
Ceramic applications
10000 Plasticity: good
Powder metallurgy Tylose® E 510024
mPa•s Temperature stability: very good
Binding effect: very good
Thickening effect: high
Ceramic applications Plasticity: good
15000
Extrusion Tylose® E 514016 Temperature stability: good
mPa•s
Binding effect: good
Shinetsu
Thickening effect: moderate
Further applications Higher purity: yes
Rubber gloves Clarity of the solution: high
4000
Personal and home care Tylose® E 707002 Stabilization of foam: high
mPa•s
Shaving products Pseudoplasticity: low
Compatibility with salts: moderate
Compatibility with surfactants:
150000 Biostability: yes
Paint-stripping pastes Tylose® PSO 810001
mPa•s Thickening effect: very high
Consistency development: fast
Final consistency: moderate
Sag resistance: moderate
6000
Cement decorative render Tylose® MH 6002 P4 Water demand: moderate
mPa•s
Water retention: moderate
Influence on cement hydration: low
Heat stability: standard
Cement render Consistency development: very fast
Cement tile adhesive standard Final consistency: high
Gypsum hand plaster Sag resistance: moderate
Gypsum joint compound 60000
Water demand: high
Gypsum mounting binder mPa•s
Tylose® MH 60010 P4 Water retention: very high
Gypsum spray plaster Influence on cement hydration:moderate
Gypsum trowelling compound Heat stability: standard
Consistency development: very fast
Final consistency: moderate
Sag resistance: moderate
Cement tile adhesive ordinary Tylose® MH 60004 P6 according Water demand: moderate
to Höppler Water retention: very high
60000 Influence on cement hydration: low
mPa•s Heat stability: standard
Consistency development: very fast
Final consistency: low
Sag resistance: moderate
60000 Water demand: moderate
Cement skim coat Tylose® MH 60001 P6
mPa•s Water retention: very high
Influence on cement hydration: low
Heat stability:standard

Consistency development: very fast

Final consistency: low
Cement one coat Sag resistance: moderate
60000 Water demand: moderate
Cement tile adhesive ordinary Tylose® MH 60001 P4
mPa•s Water retention: very high
Gypsum mounting binder
Gypsum trowelling compound Influence on cement hydration: low
Heat stability: standard

60000
Pet litter Tylose® MH 60000 P6
mPa•s
 Consistency development: fast
Final consistency: low
Sag resistance: low
Grouts Coating materials Limewash 6000
Tylose® MH 6000 YP4 Water demand:very low
paints Powder paints mPa•s
Water retention: moderate
Influence on cement hydration: low
Heat stability: standard
Consistency development: moderate
Final consistency: very high
Sag resistance: very high
30000
Gypsum joint compound Tylose® MH 30026 P4 Water demand: very high
mPa•s
Water retention: high
Influence on cement hydration: moderate
Heat stability: standard
Biostability: yes
Gloss: low
Pigment Compatibility: low
Cement paints 30000 Anti-spattering: good
Tylose® MH 30000 YP4
Exterior paints mPa•s Pseudoplasticity: low
Silicone resin paints Thickening effect: high
Wet scrub resistance: moderate
Water retention: high
Consistency development: slow
Final consistency: very low
Sag resistance: low
Self levelling floor compounds Tylose® MH 300 P2 300 mPa•s Water demand: very low
Water retention: low
Influence on cement hydration: low
Heat stability: standard
 Consistency development: fast
Final consistency: moderate
Sag resistance: moderate
Block laying adhesive 15000
Tylose® MH 15002 P6 Water demand:high
mPa•s
Water retention: high
Cement render
Influence on cement hydration: low
Heat stability: standard
Consistency development: fast
Final consistency: very high
Sag resistance: very high
10000
Cement tile adhesive premium Tylose® MH 10016 P4 Water demand: very high
mPa•s
Water retention: moderate
Influence on cement hydration: moderate
Heat stability: high
Consistency development: fast
Final consistency: very high
Sag resistance: very high
10000
Cement tile adhesive premium Tylose® MH 10015 P4 Water demand: very high
mPa•s
Water retention: moderate
Influence on cement hydration: moderate
Heat stability: high
Consistency development: fast
Final consistency: moderate
Sag resistance: moderate
Cement decorative render 10000
Tylose® MH 10007 P4 Water demand: moderate
mPa•s
Water retention: moderate
EIFS
Influence on cement hydration: moderate
Heat stability: moderate
 Consistency development: very fast
Final consistency: low
Sag resistance: moderate
100000
Cement skim coat Tylose® MH 100001 P6 Water demand: moderate
mPa•s
Cement tile adhesive ordinary Water retention: very high
Influence on cement hydration: low
Heat stability: standard
Thickening effect: moderate
Higher purity: no
Clarity of the solution: moderate
10000 Stabilization of foam: high
Toilet cleaners / WC-gels Tylose® MH 10000 KG4
mPa•s Pseudoplasticity: moderate
Compatibility with salts: moderate
Compatibility with surfactants: moderate

Consistency development: fast

Final consistency: very high
Sag resistance: very high
10000 Water demand: very high
Gypsum joint compound Tylose® MH 10013 P4
mPa•s Water retention: moderate
Influence on cement hydration: moderate
Heat stability: high

(Brookfield
BERMOCOLL CCA 612 prolongs the working time
LV)
admixture in gypsum and cement BERMOCOLL® CCA 612 and effectively counteracts the sagging tendency
5500 – 7
of the plaster.
500 mPa.s
BERMOCOLL CCA 470 ensures good water
2 500 – 3
admixture in gypsum-based mortars BERMOCOLL® CCA 470 retention and gives a mortar with suitable
500 mPa·s
working time.
5 000 – 7 BERMOCOLL CCA 328 effectively counteracts the
gypsum based mortars BERMOCOLL® CCA 328
000 mPa.s sagging tendency of glue.
 BERMOCOLL CCA 312 prolongs the open time and
2 300 – 3
admixture in gypsum and cement BERMOCOLL® CCA 312 effectively counteracts the sagging tendency of
000 mPa.s
the plaster
260 - 360 BERMOCOLL E 230 FQ is easily dispersed in cold
latex paints BERMOCOLL® E 230 FQ
mPa.s water of pH 7 or less
The simultaneous viscosity increase is moderate.
thickening and stabilizing effects in 260 - 360
BERMOCOLL® E 230X Normal dosage is 0.4 - 0.8 % calculated on the dry
mortars and other building glues mPa.s
mortar weight.
1 850 – 2 It improves the consistency, the stability, and the
latex paints BERMOCOLL® E 320 FQ
650 mPa.s water retention of water based products.
1 850 – 2 It improves the consistency, the stability, and the
stabilize aqueous dispersions BERMOCOLL® E 320 G
650 mPa.s water retention of water based products.
4 250 – 6 It improves the consistency, the stability, and the
cement-based tile fix and joint mortars BERMOCOLL® E 351 X
000 mPa.s water retention of water based products.
1 700 – 2 improve workability, consistency, water retention
cement-based tile fix and joint mortars BERMOCOLL® E 431 X
400 mPa.s and adhesion
4 250–6 It improves the consistency, the stability, and the
cement-based tile fix and joint mortars BERMOCOLL® E 481 FQ
000 mPa.s water retention of water based products.
6 500-8000 It improves the consistency, the stability, and the
cement-based tile fix and joint mortars BERMOCOLL® E 511 X
mPa.s water retention of water based products.
It improves the consistency, the
latex paints for 5 000 – 6
BERMOCOLL® EBM 5500 stability, and the water retention of water based
thickening and stabilizing effects 500 mPa.s
products.
latex paints for 7 000 – 9 It improves the consistency, the stability,
BERMOCOLL® EBM 8000
thickening and stabilizing effects, 000 mPa.s and the water retention of water based products.
latex paints for thickening and 7 500- 9 It improves the consistency, the stability, and the
BERMOCOLL® EBM 7590
stabilizing effects 000 mPa.s water retention of water based products.
latex paints 10000 –
It improves the consistency, the stability,
for efficient thickening and stabilizing BERMOCOLL® EBM 10 000 15000
and the water retention of water based products.
effects mPa.s
latex paints for thickening and 5 000 – 6 It improves the consistency, the stability, and the
BERMOCOLL® EBS 351 FQ
stabilizing effects 000 mPa.s water retention of water based products.
 latex paints for thickening and 3 000 – 4 It improves the consistency, the stability, and the
BERMOCOLL® EBS 451FQ
stabilizing effects 000 mPa.s water retention of water based products
latex paints for thickening and 4 000 – 6 It improves the consistency, the stability, and the
BERMOCOLL® EBS 481FQ
stabilizing effects 000 mPa.s water retention of water based products.
min 350 improves high shear viscosity, roller spatter, flow
a thickener in all types of latex paints BERMOCOLL® EHM 200
mPa.s and levelling
1 700 – 3 improves high shear viscosity, roller spatter, flow
thickener in all types of latex paints BERMOCOLL® EHM 300
000 mPa.s and levelling.
7000 -
improves high shear viscosity, roller spatter, flow
thickener in all types of latex paints BERMOCOLL® EHM 500 10000
and levelling
mPa.s
250 - 450 improves high shear viscosity, roller spatter, flow
thickener in all types of latex paints BERMOCOLL® EHM Extra
Akzo mPa.s and leveling.
nobel 6 000 – 8
latex paints for thickening and It improves the consistency, the stability, and the
BERMOCOLL® EM 7000 FQ §000
stabilizing effects water retention of water based products.
mPa.s
750 – 1 intended as a water retaining and consistency
cement-based tile fix and joint mortars BERMOCOLL® M10
200 mPa.s improving additive to cement based mortars.
2 500 – 3 giving a unique balance between workability and
cement-based tile fix and joint mortars BERMOCOLL® M30
500 mPa.s strength.
2 500 – 3 giving a unique balance between workability and
cement-based tile fix and joint mortars BERMOCOLL® M30 Q
500 mPa.s strength.
1 100 - 1 giving a unique balance between workability and
cement-based tile fix and joint mortars BERMOCOLL® ML 11
600 mPa.s strength.
cement-based tile fix and joint mortars
for improvement of workability, 2 900 – 3 giving a unique balance between workability and
BERMOCOLL® ML 31
consistency, water retention and 900 mPa.s strength
adhesion.
cement-based tile fix, adhesives and 6 000 – 9 retaining and consistency improving additive to
BERMOCOLL® M 70
plasters 000 mPa.s cement based mortars.
6 200 – 9 giving a unique balance between workability and
cement-based tile fix and joint mortars BERMOCOLL® ML 71
200 mPa.s strength.
 3 500 – 6 giving unique balance between workability and
cement based tile-fix BERMOCOLL® BCM 050
000 mPa.s strength.
3 500 – 6 giving a unique balance between workability and
cement based tile adhesive BERMOCOLL® BCM 051
000 mPa.s strength
3 400 – 4 giving a unique balance between workability and
tile fix and joint mortars BERMOCOLL® BCM 107
600 mPa.s strength
1 200 – 1 giving a unique balance between workability and
tile fix and joint mortars BERMOCOLL® BCM 108
600 mPa.s strength
11 000 –
It improves the consistency, the stability, and the
cement-based tile fix and joint mortars BERMOCOLL® M800 X 15 000
water retention of water based products.
mPa.s
12 000 It improves the consistency and the water
admixture in gypsum based plaster BERMOCOLL® CCM 812
mPa.s retention of gypsum based plaster
10 000 –
improving additive to cement and gypsum based
cement and gypsum based mortars BERMOCOLL® CCM 825 14 000
mortars
mPa.s
12 000
gypsum based mortars BERMOCOLL® CCM 879 improving additive to gypsum based mortars.
mPa.s
10 000 – improvement of workability, consistency and
gypsum based mortars BERMOCOLL® CCM 894 14 000 water retention, leading to a prolongation of the
mPa.s open time
11 000 –
It improves the water retention, the consistency
cement-based tile fix and joint mortars BERMOCOLL® ME 1000 X 15 000
and the stability of water based products.
mPa.s
10 000 –
gypsum based mortars BERMOCOLL® CCM 1079 15 000
mPa.s
rheology modifier in all types of latex 500 - 900 It improves the consistency, the stability, and the
BERMOCOLL® Prime 1000
paints mPa.s water retention of water based paints.
It improves the consistency, the stability, and the
rheology modifier in all types of latex 2 200 – 3
BERMOCOLL® Prime 2500 water
paints 200 mPa.s
retention of water based paints.
 3,000 – It improves the consistency, the stability, and the
rheology modifier in all types of latex
BERMOCOLL® Prime 3500 4,000 water
paints
mPa.s retention of water based paints.
High water retardation
34,000 –
FMC-24006 Excellent open time
44,000
Good heat resistance
High adhesion strength
33,000 –
FMC-24007 Excellent open time
43,000
High water retention
Excellent open time
Normal Tile Cement 45,000 –
FMC-25002 Good water retention
55,000
Good heat resistance
High adhesion strength
53,000 –
FMC-26002 Excellent open time
63,000
High water retention
33,000 –
FMC-23701
43,000
Overall good performance
14,000 –
FMC-2070 Long open time
22,000
Less retardation of cement hydration
Good open time
18,000 –
FMC-22501 Good slip resistance
26,000
Good heat resistance
Less retardation of cement hydration
27,000 –
FMC-23007 Long open time
35,000
standard tile cement Good workabilit
(c1) Excellent open time
32,000 –
FMC-23502 Good workability
40,000
Good heat resistance
High water retention
40,000 –
FMC-24502 Good Heat Resistance
50,000
Good slip resistance
High water retention
42,000 –
FMC-24503 Long open time
52,000
Good heat resistance
 Excellent slip resistance
High Performance 12,000 –
FMC-21010 Less retardation of cement hydration
Tile Cement 18,000
Very good open time
7,000 – Excellent workability
FMC-2071
13,000 Less retardation of cement hydration
Excellent crack resistance
7,000 – Fast setting time
FMC-21027
13,000 Excellent water retention
Good workability
Cement plaster Fast thickening effect
11,000 – Good water retention
FMC-21510
17,000 Good workability
Good air stability
Excellent workability
15,000 –
FMC-22013 Good water retention
23,000
Less stickiness
Excellent workability
28,000 –
FMC-23505 Long pot life
40,000
Good water retention
Skim coat Excellent workability
45,000 – Long pot life
FMC-25002
55,000 Less water absorption

Good workability
3,500 –
PMB-40HS Less retardation of cement hydration
5,600
Good heat resistance
Excellent Pressure
3,500 –
PMB-40H Very good Green-body hardness
5,600
Joint Compound Good Surface state
Long retarded grade
30,000 –
FMC-53001 Excellent workability
40,000
Good water retention
30,000 – Excellent workability
PMH-9860
40,000 Good water retention
Long retarded grade
45,000 –
FMC-8821 Excellent water retention
55,000
Good open time
Ready-to-use Tile Adhesive
 Ready-to-use Tile Adhesive
Long retarded grade
30,000 –
FMC-53001 Excellent workability
40,000
Good water retention
Very low air contents
13,000 –
FMC-51502 Good sag resistance
22,000
Easy handling
Putty Very high water retention
35,000 – High thickening efficiency
PMC-40US
45,000 Good open time
Easy handling
Lotte H 100K 100000
Joint Compound H 30K 30000
H 50K 50000
FMC-2051
Monocapa
FMC-22013
Excellent workability
12,000 –
FMC-21010 Less Retardation of Cement Hydration
18,000
High water demand
Excellent workability
27,000 –
Tile grout FMC-23007 High water demand
35,000
Long working time
Good workability
3,500 –
PMB-40HS Less retardation of cement hydration
5,600
Good heat resistance
FMC-20101
self leveling compound FMC-60150
H300
Excellent workability
12,000 –
FMC-21010 High water demand
18,000
Good compressive strength
Excellent water retention
27,000 –
FMC-23007 Good workability
35,000
Less stickiness
Masonry mortar
Excellent workability
34,000 –
FMC-24006 Less stickiness
44,000
Good sag resistance
Masonry mortar

Excellent workability
33,000 –
FMC-24007 Excellent water retention
43,000
Less stickiness
Excellent wetting capability
14,000 –
FMC-2070 Good workability
22,000
Good adhesion strength
Less stickiness
12,000 –
FMC-21010 Excellent adhesion strength
18,000
Good workability
Excellent workability
27,000 –
FMC-23007 Less stickiness
35,000
EIFS Excellent wetting capability
High water retardation
34,000 –
FMC-24006 Excellent open time
44,000
Good heat resistance
27,000 –
FMC-23504
39,000
Excellent workability
42,000 –
FMC-24503 Less stickiness
52,000
Excellent open time
High water demand
30,000 –
FMC-7150 Good sag resistance
40,000
Good workability & water retention
Excellent Workability
28,000 –
Gypsum Machine Plaster FMC-73516 Excellent sag resistance
38,000
Good water retention
Excellent water retention
48,000 –
FMC-75502 High water demand
62,000
Good workability & sag resistance
Excellent Workability
28,000 –
FMC-7117 Excellent sag resistance
38,000
Good water retention
Excellent water demand
35,000 –
Gypsum hand plaster FMC-74004 Excellent sag resistance
43,000
Good water retention
Gypsum hand plaster

Excellent water demand

47,000 –
FMC-75503 Excellent sag resistance
61,000
Good water retention
Good workability
27,000 –
FMC-7115 Good sag resistance
37,000
High water demand
Gypsum Finishing Plaster
Good water retention
25,000 –
FMC-72507 Less lump formation
35,000
High water demand
Good workability
27,000 –
FMC-7115 Good sag resistance
37,000
High water demand
Excellent workability
9,000 –
Joint filler FMC-51002 Less lumping
15,000
Good wet adhesion
High water retention
34,000 –
FMC-24006 Excellent workability
44,000
Good sag resistance
self leveling compound MHPC400
Excellent workability
18500-
C8352 High wetability
23000
High sag resistance
Economical Gypsum plaster Excellent workability
35000- High wetability
C8381
47000 High water retention
Good sag resistance
27000- Reduced lump formation
C8706
36000 For plasters with lower water demand
Excellent workability
Superior Gypsum plaster
34000- High wetability
C8381
46000 High water retention
Good sag resistance
35000- Long open time
C8381
47000 Good sag resistance
35000-
M4025
Skim coat 45000
腻子
Skim coat
腻子 34000-
LH40M
46000
63000-
LH70M
72000
Culminal C9166 25000 Outstanding open time
PREMIUM C2TE
Culminal C9167 9000 Superior water resistance
Brookfield RVT 2%
Culminal C9168 8000 Very high strength values
High sag resistance
Increased open time
10000- Excellent water retention
Culminal C8564
15000 High sag resistance
Good workability
High water retention
20000- Outstanding open time
SUPERIOR C2T/C1 TE Culminal C9164
30000 High sag resistance
Good heat resistance
Outstanding open time
Superior water resistance
Culminal C9166 25000
Very high strength values
High sag resistance
Outstanding correction
32000- High sag resistance
Culminal C8367
43000 Good water retention
Higher strength
Outstanding correction time
Economic C1NPD/C1/C1T
62000- Excellent heat resistance
Culminal C9115
75000 Good water retention
Sufficient sag resistance
35000- long open time
Culminal C8381
47000 good sag resistance
22000-
C8114
30000
17000-
C8555
23000
17000-
C9104
25000
Other related products
 Other related products
62000-
C9115
75000
C9133 4000-6000
18000-
MHEC15000PFF
24000
MHEC 6000PFS 6000
Excellent sag resistance
Economical EIFS C8352 21000
Excellent workability
Long embedding time
Superior EIFS Culminal C9164 2000-30000
Creamy workability
Very long embedding time
Ashland Premium EIFS Culminal C9166 25000
Creamy workability
17000-
C8355
23000
17000-
C9104
25000
62000-
C9115
75000
25000-
C9155
35000
Other related products
18000-
MHEC15000PFF
24000
MHEC 6000PFS 6000
18000-
Combizel LH20M
24000
38000-
Combizel LH40M
55000
Combizel LH70M >60000
C8475 35000 Improved wetability
17000- Excellent water demand
C8495
22500 High sag resistance
Special
High dissolution property
efficiency
High water demand
C8713 65000
Gypsum joint filler High water retention
Very strong thickening effect
Gypsum joint filler

High efficiency
High water demand
C8715 65000
High water retention
Strong thickening effect
35000- High water retention
Economical Renders(抹灰） C8381
47000 High sag resistance
10000- Increased open time
Superior Renders C8564
15000 Universal application properties
12000- Very good workability
C8301
17000 Used for one-coat render application
Premium Renders C8352 21000 Excellent workability
17000- Excellent sag-resistance
C8355
23000 Reduced stickiness

65000-
C4051
85000
38000-
C4053
51500
22000-
C8070
30000
18000-
C8315
24000
C8344 2000-26500
15000-
C8350
20500
25000-
C8351
30000
Other grades
24000-
C8353
32000
55000-
C8384
75000
35000-
C8704
45000
33000-
C8360
45000
28000-
C8376
38000
 57000-
C8711
67000
C9111 7500-10500