Copprint LF-360 is a screen-printable copper paste that provides high electrical conductivity. It has excellent adhesion and printability. The paste has high copper filler loading, flexibility, and can be sintered at low temperatures. It is suitable for applications in printed electronics and can be printed on substrates such as PET and PC.

Uploaded by

Ofer Shochet
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
89 views2 pages

TDS LF-360

Copprint LF-360 is a screen-printable copper paste that provides high electrical conductivity. It has excellent adhesion and printability. The paste has high copper filler loading, flexibility, and can be sintered at low temperatures. It is suitable for applications in printed electronics and can be printed on substrates such as PET and PC.

Uploaded by

Ofer Shochet
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Copprint LF-360

Sep 2022
Technical Data Sheet
PRODUCT DESCRIPTION
Copprint LF-360 provides the following product characteristics: Conditions (time and temperature) may vary based on customers'
Technology Screen printing experience and their application requirements, as well as customer
Appearance Copperish paste drying equipment, oven loading and actual oven temperatures.
Filler Type Copper
Product Benefits ● High conductivity
● Excellent adhesion TYPICAL PROPERTIES OF CURED MATERIAL
● Excellent printability with screen Physical Properties
printing Adhesion, (tape test 3M Scotch 234) pass
● High metal loading
● High flexibility Cross cut test ISO 2409-2007 3-4 b
● Low temperature sintering
Drying Hot air
Electrical Properties - Sheet resistivity
Sintering Hot roller or Hot press
Hot roller @ 190ºC, 20sec ohm/sq/25 µm <0.005
Application Conductive Ink
Key Substrates PET, PC Hot press @ 160ºC, 120sec ohm/sq/25 µm <0.006
Typical Assembly Printed electronics
Applications

Copprint LF-360 screen printable paste is formulated to provide high


electrical conductivity.

TYPICAL PROPERTIES OF UNCURED MATERIAL

Average particle Size, µm D50 < 1.0, D90 < 7.0


Solids Content, after 10 minutes @ 150ºC, % 91.5±1.5
Density, g/ml 4±0.2
Viscosity @ 250C , DVEHA Brookfield spindle 14,
100rpm, mPa∙s (cps) 13,000-17,000

Theoretical coverage @ 15 µm dry film thickness 11.4 m²/kg


Shelf Life @ -10°C, days 180
Pot life @ 25°C, Hours 72
Flash Point - See SDS

RECOMMENDED CURING

Drying cycle
120sec @800C (Hot air, Reflow oven)

Sintering cycle
20 sec @ 180°C-210°C (Hot roller)

120 sec @ 160°C-200°C (Hot press)

Relaxation cycle
PET: 120 sec @ 140C (Hot air, Reflow oven)

PC: 120 sec @ 110C (Hot air, Reflow oven)

Copprint LF-360 can be dried using hot air, (near) infrared or ceramic
lamps
GENERAL INFORMATION
For safe handling information on this product, consult the Safety Data Sheet, (SDS).

DIRECTIONS FOR USE


Preparation guidelines
1. Copprint LF-360 is supplied as “Sinter ready” formulation ready for use.
2. Mix formulation prior print.
*Detailed procedure can be found in Application Notes
www.copprint.com
Application (screen properties)
Emulsion, Solvent and Water-resistant emulsion, µm 10 to 40
Squeegee Shore Hardness 70 to 90
Screen Type, Polyester and SS screen, mesh 100 to 300

CLEAN-UP
The equipment can be cleaned with Dowanol DB followed by water and repeated if necessary.

STORAGE:
Store product in the tightly closed container in a dry location at a temperature below -100C. Open the container carefully.

Optimal Storage: below -10°C. Storage above -10°C damage product properties.

Material removed from containers may be contaminated during use. Do not return product to the original container. Copprint cannot assume
responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Not for product specifications


The technical data contained herein are intended as reference only.