ARCAP AP1D

Identification
VMI No. AP1D
UNS No. C76350
Relevant Specifications n/a
Strip Wire Bar Sheet
Forms
∗ ∗
Description Free Cutting bar and wire.

Chemical Composition (%)

Copper (+Silver) 61 Nominal
Nickel (+Cobalt) 25 Nominal
AP1D

Zinc 11.5 Nominal

Mechanical Properties (all values are for Full-Hard temper not intended for specification)
Tensile 87 ksi
600 MPa
Yield ----- ksi
----- MPa
Elongation >2 % in 2"
>2 % in 50mm
Hardness ----- HRB
----- Hv
Physical Properties
Density 0.3179 lb/in³
8.8 g/cm³
Resistivity (Nominal) 240 Ohm•circ mil/ft
40 microOhm•cm
Coefficient of Thermal Expansion 212°F 572°F 932°F 1112°F 1832°F
from 68°F (20°C) to 100°C 300°C 500°C 600°C 1000°C
(micro-in/in-°F) ----- 8.9 ----- 9.4 -----
(micro-m/m-K) ----- 16 ----- 17 -----

www.vismet.com
65 Ballou Blvd Bristol, RI 02809
401-253-1772 1-800-431-4113 fax: 401-253-1806
A N T I C O R R O S I O N
ANTICORROSION

Piece
(230mm x 250mm)
made from
ARCAP AP4
hot forged rod

THE STRUCTURE
OF TIME...

IN ORDER TO MAKE THE BODY OF THE PARIS

ATOMIC OBSERVATORY CLOCK,

-14 -10
(PRECISION 5.10 SECOND A 10 TORR),

IT WAS VITAL TO OBTAIN IT FROM A MATERIAL SUITABLE,

FOR VACUUM APPLICATION, AND COMPLEX TURNINGS.

THIS IS WHY, THE AP4 CORROSION RESISTANCE GRADE

HAS BEEN SELECTED.

SALES OFFICE - FACTORY AND STOCK :

CLAL-MSX
11, Rue du Menillet - BORNEL
60541 MERU CEDEX - FRANCE
Tel. : 03 44 08 25 25
Tel international : (0033) 3 44 08 25 25
Fax : 03 44 08 49 11
Fax international : (0033) 3 44 08 49 11
http://www.clal-msx.com
e-mail : [email protected]
ANTICORROSION

Alloys
with
high performance
HIGH CORROSION ARCAP alloys are very corrosion resistant to In particular ARCAP alloys have a very
RESISTANCE the majority of chemical and physical high resistance to scaling and clogging
environments. of pipes by hard water and the blocking of
CLAL can provide data for the corrosion pipes used for transport powder products
resistance of ARCAP alloys. such as sodium aluminate, cement, etc.

HIGH MECHANICAL In annealed temper ARCAP, alloys have In spr ing temper the ultimate tensile
PROPERTIES an elongation up to 45 %, which allows strength is above 800 MPa.
deep drawing.

NON-MAGNETIC A detector sensitive to 1/10 of nanotesla, This non magnetism is kept even at very low
placed at less than 1 mm from ARCAP alloys temperatures (measured at 4.2° k).
will not show any magnetic interference.

STABLE RESISTIVITY Temperature variations have almost no effect The temperature cœfficient of the grade AP4
on the resistivity of ARCAP alloys. is 4 x 10-5/°C and 25 x 10-5/°C for the other
grades.

EXCELLENT At low temperatures the mechanical A cryogenic application shows that the
BEHAVIOUR properties of ARCAP alloys are improved. ultimate tensile strength and the yield
AT LOW TEMPERATURE strength increase without any diminution of
the elongation or the impact strength.
VERY EASY ARCAP alloys are easily processed whether by They are also easily plated.
TO PROCESS forging, stamping, deep drawing, machining,
welding or brazing.

For free cutting,

milling, drilling, deep,
GRADES
drawing
AP1D The AP1D grade has been developed The very good machineability of the AP1D
Turned parts especially for being machined by lathe. grade may be summerised by :
Its machineability is one of the best of - cutting speed up to 150 m/minute
all of the corrosion resistant alloys. (according to the type of part, cutting tool
and lathe),
- very good quality of surface that can be
lapped or polished with a diamond tool,
burr free after drilling,
- reduction in frequency of tool sharpening.

AP1C - AP1 The AP1C grade (used in rods for parts that machineable under the same conditions
Good formability are to be deformed by torsion, bending, as carbon steel, in other words without
riveting, swaging... and for welding) and difficulty.
the AP1 grade (sheet, strip, wire, tubes) is

AP1M This grade has the same machineability as

Cast parts the AP1D grade.
AP4 - AP4M The AP4 grade is less easy to turn than the machined without more difficulty than the
Very good corrosion other grades of ARCAP. It can however be nickel chromium molybdenum steels.
resistance
 Mechanical properties
ANTICORROSION

Rolled products
Measurement made in the rolling direction (thicknesses from 0.25 to 1 mm)

GRADES Standards AFNOR Vickers Ultimate tensile 0.2% yield Elongation E %

tempers symbols hardness strength strength (Lo=50 mm)
NFA 02-008 HV MPa MPa

AP1 annealed 0 ≤ 120 ≤ 400 ≤ 300 ≥ 30

1/4 hard H11 120-150 370-470 > 300 ≥ 20
1/2 hard H12 150-170 450-550 > 370 ≥ 10
3/4 hard H13 165-185 520-600 > 470 ≥ 3
4/4 hard H14 180-210 ≥ 580 ≥ 530 ≈ 1
AP1C annealed 0 ≤ 130 ≤ 450 ≤ 300 ≥ 30
1/4 hard H11 130-165 450-550 > 300 ≥ 15
1/2 hard H12 160-190 520-620 > 400 ≥ 5
4/4 hard H14 190-220 620-730 > 550 ≥ 1
spring H15 ≥ 220 ≥ 730 ≥ 700
AP4 annealed 0 ≤ 140 ≤ 520 ≤ 300 ≥ 30
1/4 hard H11 140-180 500-600 > 300 ≥ 15
1/2 hard H12 175-205 550-650 > 450 ≥ 8
spring H15 ≥ 225 ≥ 720 ≤ 670
Typical values for references only.

Drawn products
GRADES Standard tempers Diameters Ultimate tensile strength MPa Elongation E %
(Lo = 100 mm)
Fils Barres Wire Rod
min 0,2 mini 1,5
maxi : maxi :
AP1 annealed 0 10 12* ≤ 420 ≤ 400 ≥ 30
1/4 hard H11 10 “ 420-480 400-450 ≥ 10
1/2 hard H12 10 “ 480-550 450-500 ≥ 5
3/4 hard H13 10 “ 550-610 500-550 ≥ 2
4/4 hard H14 9 “ 590-650 550-600 ≥ 1
spring H15 6 “ ≥ 650 ≥ 600
AP1C annealed 0 10 “ ≤ 550 ≤ 450 ≥ 30
1/4 hard H11 10 “ 550-650 450-500 ≥ 5
1/2 hard H12 10 “ 650-750 500-550 ≥ 2
3/4 hard H13 10 “ 700-800 550-600 ≥ 1
4/4 hard H14 9 “ 800-820 550-700
spring H15 “ ≥ 820 ≥ 700

AP4 annealed 0 10 “ ≤ 550 ≤ 500 ≥ 30

1/4 hard H11 10 “ 550-650 500-550 ≥ 10
1/2 hard H12 10 “ 650-750 550-600 ≥ 5
3/4 hard H13 10 “ 600-650 ≥ 2
4/4 hard H14 9 “ 750-850 650-800 ≥ 1
spring H15 6 “ ≥ 800 ≥ 800

AP1D Ø < 2,5 550-650 ≥ 2

Wire and rod 4/4 hard H14 2,5 ≤ Ø < 5 600-750 ≥ 2
5 ≤ Ø ≤ 11* 550-650 ≥ 2
Typical values for references only.

* Rod Ø > 12 mm, characterisation by hardness only.

12 < Ø ≤ 35 mm, minimum hardness for H14 temper : HV 160.
Ø > 35 mm : please ask our technical department.

Rm Mpa

800
AP1C - H14
Increase
in UTS 750
at low
700
temperatures
650

+ °C
-100 0 100 200
ANTICORROSION

CLAL-MSX offers
6 grades of ARCAP ® material
with specific characteristics
for all industrial applications

NOMINAL GRADES
CHEMICAL Pressing
COMPOSITION Deep/drawing
(% per weight) Free cutting

Stamping
Cast parts
Cast bars
Corrosion resistance

Color graphs Nickel Remainder Zinc Copper

* Please indicate if required for electronic application.

PHYSICAL Color Density

(g/cm3)
Melting
point
Modulus Coefficient of
of Elasticity linear
Optical Thermal
reflection conductivity
Resistivity
µΩ - cm
Temperature Electrical Non Magnetism
Coefficient conductivity (OERSTED **)
PROPERTIES (° C) Gpa expansion index W/(m°C) K-1 % IACS
X 10-6/°C (Ag = 100%)
0-300° C 0-600° C to 20°C to 200°C

AP1-AP1C-AP1D-AP1M white bluish 8.80 1150-1170 163 to 170 16 17 70 % 22 25 35 to 40 0.00025 4.3 to 4.9 10-6

AP4-AP4M white 8.91 1225-1285 145 16 17 70 % 22.5 23 49 0.00004 3.5 10-6

Typical values for reference only.

** The non magnetism measurements of ARCAP have been carried out by the Paris Physical Institute of the Globe.

PRODUCT
FORM

Rod, wire, coil, tube, profiles... ... available from stock.

s
Screw bolt

• HYDROCHLORYDE ACID
• SULFURIC ACID
EXTREMELY PERFORMANT
RESISTANCE
• OXYGEN
TO CORROSION.
• WASHING POWDERS
• PHOSPHORUS TRICHLORYDE
LOW ELECTROCHEMICAL
• ALCALIS
POTENTIAL NITRATUS
• SODIUM
WITH OTHER CHLORIDE
• FORMALIN
ALLOYS.
• GAZ OF LACQ

Cast parts
and cast bars
Corrosion tables on request
available on request
ANTICORROSION
Machining conditions for rods
The table below gives the main machining can be modified by the users according to
parameters for grades AP1D, AP1C and AP1. the parts they produce.
They should be considered as bases and

TURNING Cutting speed m/minute Feed mm/rev

HSS tool carbide tool HSS tool carbide tool
AP1D 125 150/170 0,04 0,06
AP1C - AP1 65 80 0,04 0,06
DRILLING carbide drill carbide drill
HSS drill with drill HSS drill with drill
bush Ø 1,5 to 12 bush Ø 6 to 12
AP1D 120 150 0,012 to 0,080 0,025 to 0,120
AP1C - AP1 60 80 0,012 to 0,080 0,025 to 0,120
Recommended tip angle : 160 to 164°.

CUTTING ANGLE AP1D and AP1C 7 to 8°.

TOOL SHARPENING Compared with stainless steel the frequency for the AP1C and AP1 grade and by 45 for
of tool sharpening can be divided by12 the AP1D grade.

CUTTING OIL AP1D : all good quality soluble oils. AP1C : preferably cutting oil for special alloys.

Processing
SHEET METAL WORK, AP1, AP1C, AP4, in annealed temper have AP4 can be hot worked.
SPINNING, similar formability as brasses and mild steel AP1D is suitable for some cold-working
SWAGING AP1 and AP1C can only be cold worked. operations.

ANNEALING In neutral or reducing atmosphere, tem-

perature about 750° C, duration 15 minutes
to 1 hour according to the quantity.
STRESS RELIEVED Cold rolled, drawn or stamped parts may
HEAT TREATMENT be stress relieved at 250°C, preferably in
neutral or reducing atmosphere.
PICKLING After annealing in air, remove the scale in a water, 9% sulphuric acid and 11% sodium,
bath of 10% of sulphuric acid and 2 to 3% of bichromate, preferably at 50 to 60°C.
nitric acid, then pickle in a bath with 80%

WELDING AND BRAZING Brazing, soldering, resistance welding, TIG

Grade AP1 - AP1C welding can be carried out without difficulty.
AP4 - AP4M

Grade The less conventional welding methods such welding, ca pacitor discharge, high
AP4 - AP4M as plasma, micro plasma, electron beam frequency, laser... give very good results.

Grade These grades are sensitive to high tempe-

AP1D - AP1M rature. Therefore soldering is the only process
that we recommend.
GB - 10/01 - 3 - Idegrif

Coaxial plug for Parts for armament Parts for clocks

telephone industry in AP1C in AP1D