ABS XR404 (AUTO)

Injection Molding

Description Application
Heat Resistance Automotives Interior & Exterior Housing (Garnish etc)

Properties Test Condition Test Method Unit Typical Value

Physical
Specific Gravity ASTM D792 - 1.05
Molding Shrinkage (Flow), 3.2mm ASTM D955 % 0.4~0.7
Melt Flow Rate 220℃/10kg ASTM D1238 g/10min 7

Mechanical
Tensile Strength, 3.2mm ASTM D638
@ Yield 50mm/min kg/cm 2 530
Tensile Elongation, 3.2mm ASTM D638
@ Break 50mm/min % 20
Flexural Strength, 3.2mm 15mm/min ASTM D790 kg/cm 2 860
Flexural Modulus, 3.2mm 15mm/min ASTM D790 kg/cm 2 27,000
IZOD Impact Strength, 6.4mm ASTM D256
(Notched) 23℃ kg·cm/cm 14
-30℃ kg·cm/cm 5
IZOD Impact Strength, 3.2mm ASTM D256
(Notched) 23℃ kg·cm/cm 16
-30℃ kg·cm/cm 6
Rockwell Hardness R-Scale ASTM D785 - 112

Thermal
Heat Deflection Temperature, 6.4mm ASTM D648
(Unannealed) 18.6kg ℃ 102
4.6kg ℃ 111
Vicat Softening Temperature ASTM D1525
5kg, 50℃/h ℃ 112
Flammability UL94 HB
Relative Temperature Index UL 746B
Electrical ℃ 60
Mechanical with Impact ℃ 60
Mechanical without Impact ℃ 60
Note) Ty pical v alues are only f or material selection purpose, and v ariation within normal tolerances are f or v arious colors.
Values giv en should not be interpreted as specif ication and not be used f or part or tool design.
All properties, except melt f low rate are measured on injection molulded specimens and af ter 48 hours storage at 23℃, 50% relativ e humidty .

Updated : 27-Apr-17

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that
the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or
advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as
binding minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own
particular use. Each user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use
under end - use conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.
 ABS XR404 (AUTO)
Injection Molding

Description Application
Heat Resistance Automotives Interior & Exterior Housing (Garnish etc)

Electrical
Comparative Tracking Index(CTI) Solution A IEC 60112 Volts 0
Surface Resistivity IEC 60093 Ohm -
Volume Resistivity 23℃ ASTM D257 Ohm·m 1.5E+01
Arc Resistance 23℃ ASTM D495 Ohm·cm 6
Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm 33
Dielectric Constant (10 6 Hz) 23℃ ASTM D150 sec -
Note) Ty pical v alues are only f or material selection purpose, and v ariation within normal tolerances are f or v arious colors.
Values giv en should not be interpreted as specif ication and not be used f or part or tool design.
All properties, except melt f low rate are measured on injection molulded specimens and af ter 48 hours storage at 23℃, 50% relativ e humidty .

Processing Guide (Injection Molding)

Processing Parameters Unit Value

Drying Temperature ℃ 80 ~ 90
Drying Time hrs 3~4
Recommendable Moisture Content % 0.05 below
Melt Temperature ℃ 220 ~ 250
Rear ℃ 180 ~ 200
Cylinder Temperature Middle ℃ 200 ~ 220
Front ℃ 220 ~ 230
Nozzle Temperature ℃ 220 ~ 230
Mold Temperature ℃ 40~60
2
Back Pressure kg/cm 10 ~ 30
Measuring Speed rpm Low speed
Note) Back Pressure & Measuring Speed are only mentioned as general guidelines.
These may not apply or need adjustment in specif ic situations such as low shot sizes, thin wall molding and gas-assist molding.

Updated : 27-Apr-17

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that
the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or
advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as
binding minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own
particular use. Each user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use
under end - use conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.