CONCRETE MIX DESIGN Date 1-Jun-22

Revision no. 1.0

Quality Control & Materials Testing Department
Grade C40 SRC Reference no.
CONTRACT DETAILS MIX DESIGN CRITERIAS
Mix Code : B 40GS Min. Cementitious Content, kg : 335
Project : Road & infrastructure in al Ebb & Leabaib Package 1 Required Cylinder Strength @ 28 days, Mpa : n/a Max. Water / Cement Ratio : 0.5
Required Cube Strength @ 28 days (F'c), Mpa : 40 Max. Aggregate Size, mm : 20
Contractor : QATAR TRADING & CONTRACTING GROUP Standard Deviation for the Mix (1) : 3.2 Target Temperature, oC : 32
Client/Consultant : Target Mean Strength @ 28 days (F'cr), Mpa : 44 Slump @ 45 - 90 mins, mm : 150 -50/+60
Usage : Structural
CONCRETE MIX PROPORTIONS

Batch Weight Sp. Gravity, Absorption, Batch Weight

Aggregates Source Cl- Content, SO3 Content, Volume, ltrs
(SSD), kg SSD % (DRY), kg(3)
kg(2) kg
(2)
Mixing Water (SSD/DRY Aggregates), kg(3) 134 / 150
20-mm GABBRO QPMC 750 2.92 0.08 0.90 0.5 256.85 746 Cl- / SO3 Content of Water, kg (2) 0.06 / 0.01
10-mm GABBRO QPMC 400 2.90 0.04 0.44 0.80 137.93 397 Actual water/cement Ratio 0.344
Washed Sand QNCC 853 2.64 0.09 3.41 1.10 323.11 844 Air Content, litrs 20
Total Volume of Concrete, ltrs 1000.76
Target Fresh Density of Concrete, kg/m3 2532

Batch Total Binder ,

Cementitious Material/s Source % by Weight Cl- Content, SO3 Content, Sp. Gravity Volume, ltrs.
Weight, kg kg
kg(2) kg(2) Theoretical Dry Density of Concrete, kg/m3 2378
Cement -SRC QNCC 100.0% 390 0.03 10.30 3.14 124.20 Bleeding of Concrete, % max. 0.5
Theoretical SO3 Content, kg (% by wt. of cement) 15.05 ( 3.86% )
390 Theoretical Cl- Content, kg (% by wt. of cement) 0.29 ( 0.07% )
Target Setting Time of Concrete, mins (Initial/Final) 360 / 840
Durability Properties of Concrete (QCS 2014)

Batch Cl- Content, SO3 Content, Max. Dosage

Chemical Admixture/s Made Sp. Gravity Volume, ltrs Range, kg
Weight, kg (2) (2) % of Cement
kg kg Concrete Exposure Condition (Class) : X1
Low Range PC Chryso or equivalent 1.07 5.0 0.00 0.00 4.7 ± 2.5 2.5

COMBINED AGGREGATES GRADING : BS EN 12620

BS EN Sieves Percent Passing by Weight
Size Distribution of Blended Aggregates : BS EN 12620 (All in)
Size Distribution of Blended Aggregates : BS EN 12620 (All in)
Size 42.6% 37.4% 20.0% Combined
(%)

20
Passing(%)

120.0
(mm) Sand 20 mm 10 mm Grading
PercentagePassing

100.0 40 100 100 100 100.0

80.0 31.5 100 100 100 100.0
60.0 20 100 96 100 98.5
Percentage

40.0 10 100 5 96 63.6

5 98 1 5 43.1
20.0
0
2 83 0 2 35.7
0.0 1 68 0 1 29.2
1
0.125 1 2 5 10 20 31.5
0.125 5 0 0 2.1
Sieve Size 0.063 1 0 0 0.4
Sieve Size

Prepared by: Received by:

QA/QC Manager Client/Contractor's Representative

Remarks: (1) Standard Deviation based on 30 number of samples, summary report of compressive strength tests ready upon request. (2) Based on attached test reports / certificates. Ctrl.no. BTN03/F18/CMD/rev.01
(3)Batch weights are subject to adjustments based on actual moisture content of aggregates.
 Road & infrastructure in al Ebb & Leabaib Package 1

QATAR TRADING & CONTRACTING GROUP

CONCRETE MIX DESIGN COMPLIANCE STATEMENT

Grade C40 SRC

Compliance
Description QCS 2014 Specification Beton WLL
(Y/N)
Mix Grade C40 B40 GS Y

Required Cube Compressive Strength @ 28d, MPa 40 40 Y

Water - Cement Ratio (w/c) 0.5 0.344 Y

Maximum Aggregate Size, mm - 20 Y

Cement Type SRC SRC Y

Minimum Cementitious Content, kg/cu.m 335 390 Y

Maximum Cementitious Content, kg/cu.m - 390 Y
Slump Limit, mm Tolerance of -50 / 60 150-50/+60 Y
Exposure Level / Durability X1 X1 Y

Prepared by:

QA/QC Manager