WELDING PROCEDURE SPECIFICATION

Facebook
Linkedin
WeldNote HQ - Rua da Prata 80
Twitter
WPS ASME IX – Powered By WeldNote, Welding Software Email
BASIC INFORMATION
PQR no: Sample PQR 1 STANDARD: ASME IX PRODUCT TYPE: Pipe

WELD TYPE: BW - Butt Joint WELDING PROCESSES: Root: GTAW Fill: GTAW Cap: GTAW

BASE MATERIAL DETAILS

BASE MATERIALS: SA 182 F348H & SA 182 F348H WELD THICKNESS 0 - 12.04 ≥0
DIAMETER (mm):
(mm)
GROUP: P8 Gr1 - P8 Gr1 WELDING POSITIONS: Root: 1G, 3G, 4G Fill: 1G, 3G, 4G :

FILLER MATERIAL DETAILS

Root Fill Cap Root Fill Cap
SPECIFICATION SHIELDING Gas Gas
SFA 5.18 SFA 5.18
I1 - ISO 14175 I1 - ISO 14175
CLASSIFICATION FLOW RATE (l/min)
ER70S-6 ER70S-6 11 11

COMMERCIAL NAME COMMERCIAL NAME

Lincoln ER70S-6 Lincoln ER70S-6

GROUP
F6 A1 F6 A1 BACKING & FLOW
Root Fill Cap
RATE (l/min)
DIAMETER (mm)
2 2
JOINT DETAILS
PREPARATION METHODS: Machining, Grinding THROAT (mm) 0 - 12.04 WELD DETAILS: Multi layer + Single side, no backing

GROOVE DESIGN WELD LAYER CONFIGURATION

ROOT GAP ® (mm): 3 - 4 GROOVE ANGLE (A) (º): 37.0 - 42.0

WELDING PARAMETER
TRAVEL SPEED
PASS # PROCESS FILLER METAL CURRENT (A) VOLTAGE (V) POLARITY WIRE FEED (m/min) (mm/min)
TRANSF. MODE HEAT INPUT (kJ/mm)
Ø (mm)

1 GTAW ER70S-6 2.0 80 - 100 14 - 18 DC- / 60 - 120 / 0.56 - 1.8

2 GTAW ER70S-6 2.0 100 - 130 11 - 14 DC- / 60 - 120 / 0.55 - 1.82
3 GTAW ER70S-6 2.0 100 - 130 11 - 14 DC- / 60 - 120 / 0.55 - 1.82
4 GTAW ER70S-6 2.0 100 - 130 11 - 14 DC- / 60 - 120 / 0.55 - 1.82
/ / / / / / / / / / /
/ / / / / / / / / / /
/ / / / / / / / / / /
ADDITIONAL DETAILS
ELECTR. TYPE AND # Root Fill Cap OSCILLATION
- - -
STICK OUT (mm) Root Fill Cap WEAVING Root Fill Cap

DETAILS OF BACK GOUGING: TORCH ANGLE (º):

THERMAL PARAMETERS
PREHEAT TEMPERATURE (ºC): INTERPASS TEMPERATURE (ºC): POSTHEAT TEMPERATURE (ºC):
145 - 255 145 - 355
POST WELD HEAT TREATMENT TIME (h): TEMPERATURE (ºC): METHOD: HEAT/COOL RATE
(ºC/h):
ADDITIONAL INFORMATION

NOTES: Visit WeldNote, Welding Software if you want to generate these WPSs dynamically with a full fledged welding software

REVISION WRITTEN BY VERIFIED BY APPROVED BY CLIENT APPROVAL STATUS

0 DATE:
WeldNote
26/02/2019 DAT
WeldNote
26/02/2019 DAT
WeldNote
26/02/2019 DAT