    The document provides information about an electrode for joining difficult to weld high-carbon steels and dissimilar metal combinations. It details the product description, welding features, applications and materials to be welded, weld metal analysis and properties, as well as welding amperage specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    3.28 & 3.29 Kawat Las Nikko Steel 312 2,6 X 350 MM & 3,2 X 350 MM

    Uploaded by

    umar
    125 views1 page
    The document provides information about an electrode for joining difficult to weld high-carbon steels and dissimilar metal combinations. It details the product description, welding features, applications and materials to be welded, weld metal analysis and properties, as well as welding amperage specifications.

    Original Title

    3.28 & 3.29 Kawat las Nikko Steel 312 2,6 x 350 mm & 3,2 x 350 mm

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document provides information about an electrode for joining difficult to weld high-carbon steels and dissimilar metal combinations. It details the product description, welding features, applications and materials to be welded, weld metal analysis and properties, as well as welding amperage specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    125 views1 page

    3.28 & 3.29 Kawat Las Nikko Steel 312 2,6 X 350 MM & 3,2 X 350 MM

    Uploaded by

    umar
    The document provides information about an electrode for joining difficult to weld high-carbon steels and dissimilar metal combinations. It details the product description, welding features, applications and materials to be welded, weld metal analysis and properties, as well as welding amperage specifications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    MANUFACTURERS OF A DIVERSE RANGE OF SECTION

    ADVANCED WELDING CONSUMABLES 10


    WI-0304 DS148 NSN-312 Rev. 2, Date 04.09.2019

    FOR JOINING DIFFICULT TO WELD DATA SHEET


    HIGH-CARBON STEELS AND NO.
    NSN-312 DISSIMILAR METAL COMBINATION
    WHEN NO EXACT SPECIFICATION OF
    148
    THE BASE METAL EXISTS

    SPECIFICATION AWS A5.4 EN ISO 3581-A JIS Z 3221


    CLASSIFICATION E312-16 E 29 9 R D312-16
    A metallurgically based rutile flux with balanced additions of chemically basic
    and amphoteric minerals that deposits duplex weld metal containing some 40%
    delta ferrite and 60% austenite.
    PRODUCT
    DESCRIPTION The flux is extruded onto a fully alloyed 29Cr 9Ni core wire using a blend of
    silicates that ensures both coating strength and resistance to subsequent
    moisture absorption.
    This unique flux formulation ensures excellent arc stability, ease of initial arc
    WELDING strike and re-strike, minimal spatter on AC and virtually none on DC+.
    FEATURES The resultant weld seams are smooth, evenly rippled and free from undercut
    OF THE while slag detachability is excellent. Metal recovery is some 103% with respect
    ELECTRODE to core wire weight.
    UNCONTROLLED
    Primarily designed for high carbon steels, cast or wrought, which are well known
    as difficult to weld or problem steels. The duplex microstructure of the weld
    APPLICATIONS metal will tolerate high dilution with such steels while still maintaining its strength
    AND ductility and thus resistance to cracking.
    MATERIALS It can also be used very successfully for joining carbon steels to stainless steels,
    TO BE WELDED the only exception to its extensive use on such applications is that at service
    temperatures above 300ºC a drop in weld metal ductility occurs.

    C Mn Si S P Cr Ni Mo Cu Fe
    WELD METAL
    Min. - 0.5 - - - 28 8.0 - -
    ANALYSIS
    COMPOSITION Max. 0.15 2.5 1.0 0.03 0.04 32 10.5 0.75 0.75
    % BY Wt. Typical 0.10 0.9 0.8 0.01 0.02 29 9.5 0.05 0.03 Bal.

    PROPERTY UNITS MINIMUM TYPICAL OTHERS


    2
    Tensile strength N/mm 660 820
    WELD METAL
    0.2% Proof stress N/mm2 - 640
    PROPERTIES
    (ALL WELD METAL) Elongation on 4d % 22 23 HV 260

    Reduction of Area (RA) % - 30

    ∅ x Length
    2.0 x 300 2.6 x 300 3.2 x 350 4.0 x 350
    WELDING (mm)
    AMPERAGE Min. 40 60 75 120
    AC or DC+
    Max. 60 90 125 170

    OTHER DATA Electrodes that have become damp should be re-dried at 120oC for 30 minutes