    Chang Chun Plastics CO., LTD

    Uploaded by

    ChunYenHuang
    This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Chang Chun Plastics CO., LTD

    Uploaded by

    ChunYenHuang
    49 views2 pages
    This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

    Original Description:

    TDS_PBT 5515F-200

    Original Title

    TDS_PBT 5515F-200

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    49 views2 pages

    Chang Chun Plastics CO., LTD

    Uploaded by

    ChunYenHuang
    This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    CHANG CHUN PLASTICS CO., LTD.

    NO. 301, SONGKIANG ROAD, 7TH FL.,TAIPEI, 10477 TAIWAN


    TEL : 886-2-2503-8131 (REF) FAX : 886-2- 2501-8018

    CCP PBT 5515F-200


    THERMOPLASTIC POLYESTER RESIN

    Product Description
    PBT 5515F-200 is a 15% glass fiber reinforced and flame retardant injection molding grade.
    (Halogen and Antimony Free)
    Characteristics
    Processing ‧Injection Moulding
    Deliver form ‧Pellets
    Additives ‧Glass fiber, Flame retardant, Modifier
    Physical properties Value Unit Test Method
    Density 1.4 g/cm3 ISO 1183
    Moulding shrinkage, parallel 0.3-0.6 % ISO 294-4, 2577
    Moulding shrinkage, normal 0.9-1.2 % ISO 294-4, 2577
    Moisture 0.2 % ISO 62
    Mechanical properties Value Unit Test Method
    Stress at break 80 MPa ISO 527-1/-2
    Strain at break 3.0 % ISO 527-1/-2
    Flexural Strength 125 MPa ISO 178
    Flexural Modulus 5300 MPa ISO 178
    Charpy impact strength – notched
    ISO 179/1eA
    23℃ 7.5 kJ/m2
    Thermal properties Value Unit Test Method
    Melting temperature, 10℃/min 225 ℃ ISO 11357-1/-3
    Heat deflection temperature under load ISO 75-1/-2
    1.80 Mpa 195 ℃
    0.45 MPa 215 ℃
    Flammability Value Unit Test Method
    Flammability acc. to UL94, 0.8mm V0 - UL 94
    Electrical properties Value Unit Test Method
    Dielectric strength, 2mm 24 kV/mm ATSM D149

    Revised: 2020-09-22
    CHANG CHUN PLASTICS CO., LTD.
    NO. 301, SONGKIANG ROAD, 7TH FL.,TAIPEI, 10477 TAIWAN
    TEL : 886-2-2503-8131 (REF) FAX : 886-2- 2501-8018

    CCP PBT 5515F-200


    THERMOPLASTIC POLYESTER RESIN

    Volume resistivity >1013 Ω*m IEC 60093


    Surface resistivity 1013 Ω IEC 60093
    Comparative tracking index 450 V IEC 60112
    Injection molding
    Pre-drying : 120℃, 5hours or longer
    140℃, 3hours or longer
    Processing moisture content : =< 0.04%
    Resin temperature : 240~270℃
    Mold temperature : 40~80℃
    These property values are typical values obtained under varying conditions prescribed by certain standards and
    test methods and therefore are not the minimum values of the material specifications.

    Revised: 2020-09-22