T O T A L C O N C R E T E P R O T E C T I O N

PENESEAL™ FH (1:1Concentrate)
FLOOR HARDENER, DUSTPROOFER AND CURING AID

DESCRIPTION
TECHNICAL DATA
PENESEAL™ FH is a clear, reactive penetrating sealer for
concrete and masonry building materials designed to Applicable standards:
permanently protect, preserve and strengthen them. Abrasion: ASTM C779 - 80.9% increase in abrasion resistance.
PENESEAL™ FH penetrates deep into concrete and reacts Bonding: ASTM D3359 - 60% increase in epoxy adhesion. 50% increase in polyure-
with the elemental concrete ingredients to solidify them thane adhesion.
into a harder, denser, stronger concrete mass. Alkali salts Curing: 61% greater moisture retention during the initial critical 24 hour curing
and minerals are flushed out in the process, eliminating period, as compared to untreated samples.
efflorescence and leaching and increasing bonding of Hardening: ASTM C39 - 40% increase in compressive strength 7 days; 38% increase
surface coatings. at 28 days over untreated samples. ASTM C805 (Schmidt hammer) - 16.1% increase
in impact resistance.
APPLICATIONS
Permeability:
Any cementitious based substrate such as, but not limited
Approximately 98% reduction in permeability at 100 psi
to: concrete, terrazzo, heavyweight concrete block,
plaster, stucco or mortar. Weathering:
Warehouses ASTM G23 – ultra-violet light and water spray exposure had no adverse effect on
Hangars PENESEAL™ FH treated samples.
Distribution and storage facilities Coverage:
Food processing plants Approximately 200 sq ft per gallon (5 m²/L) of diluted concentrate. Coverage can
Manufacturing facilities vary depending on the temperature and porosity of the concrete.
Any type of facility with exposed concrete flooring NOTE: Test results obtained under controlled laboratory conditions at 73°F (23°C) and
50% relative humidity unless otherwise specified. Reasonable variations can be expect-
ADVANTAGES ed due to atmospheric and job site conditions. General soundness of the concrete
Curing: PENESEAL™ FH allows concrete to cure uniformly substrate (porosity, strength, absorption …etc) as well ambient conditions, as already
through its chemical and moisture retention reaction. This noted, may yield varying results.
aids in a more complete hydration process and reduces
hairline and temperature cracking.
Sealing: PENESEAL™ FH penetrates deep into the SHELF LIFE / STORAGE
concrete, which allows its chemical reaction to lock the 24 months from the date of manufacture, when unopened, undamaged original container is
pores from within, providing an integral and permanent seal. properly stored in a cool and dry place, unexposed to moisture and sunlight. Always tightly
Hardening: PENESEAL™ FH binds the elemental parts of reseal container after use. DO NOT ALLOW TO FREEZE!
the concrete, solidifying them into a denser, tougher, harder
mass. This results in a more durable concrete with higher PACKAGING
surface abrasion resistance and compressive strength. 5-gallon (19-l) pails, 55-gallon (208-l) drums and 275-gallon (1041-l) containers.
Dustproofing: PENESEAL™ FH densifies the surface of
the concrete through its chemical bonding and flushing of DIRECTIONS FOR USE
the weaker concrete salts and minerals. This permanently Surface preparation:
seals the surface and eliminates surface dusting.
Surfaces to be treated should have an open pored surface so that PENESEAL™ FH can be
Protection from efflorescence and leaching: PENESEAL™ absorbed. Remove all coatings, form oils, curing or sealing agents through chemical or
FH penetrates deeply into concrete, neutralizing the alkali mechanical means. Remove dust, dirt, laitance or any other contaminants by sweeping
salts and minerals that cause efflorescence and salt all areas to be treated with a fine bristle broom or scrub brush. Hose off with water and
leaching. These weakening salts and minerals are forced to let dry. Remove any standing or puddled water to avoid dilution of PENESEAL™ FH before
the surface and flushed away during the application process. it is able to penetrate the surface.
Improved Bonding: PENESEAL™ FH eliminates the alkali
Mixing:
salts and minerals that weaken and delaminate surface
coatings. PENESEAL™ FH leaves the concrete surface PRIOR TO USE, agitate bucket or drum and thoroughly mix PENESEAL™ FH with clean
free of these salts and minerals, which improves bonding water in equal parts by volume.
of any type of covering. Application methods:
Non-Toxic: PENESEAL™ FH is non-toxic and is not Spray or pour followed by brooming or squeegeeing to saturate the surface.
harmful to lungs or hands. Complies with all VOC and Tools:
USDA regulations.
Low-pressure sprayer, soft bristle broom, squeegee, and water hose.
For new concrete:
Step 1. Apply PENESEAL™ FH immediately following the concrete finishing, as soon as
TOTA L CO N C R E T E P R OT E CT I O N ® Page 1
 PENESEAL™ FH (1:1Concentrate)

the concrete surface is firm enough to walk on and before hairline or temperature crack- SPECIAL CONSIDERATIONS
ing begins. Keep the entire surface wet with PENESEAL™ FH for 30 minutes, working it w Do not use PENESEAL™ FH on extremely porous
into the surface with a soft-bristled broom. masonry, such as lightweight block.
Step 2. As PENESEAL™ FH becomes slippery underfoot, lightly mist the surface with w Do not apply PENESEAL™ FH to frozen or freezing
water. This will keep the material in solution providing maximum penetration. Do not surfaces or when temperature falls below 40ºF
allow PENESEAL™ FH to dry on the surface. (4ºC) or if temperatures will drop below freezing
Step 3. As PENESEAL™ FH again becomes slippery underfoot, thoroughly flush the entire during the curing period (approximately 24 hours).
surface with water and squeegee the surface completely dry to remove all surface alkali w Prevent PENESEAL™ FH from getting on glazed
or PENESEAL™ FH residue. On exterior broom finished surfaces, no flushing is required, and finished surfaces such as glass, aluminum, etc.
but any remaining PENESEAL™ FH must be squeegeed or broomed from the surface In case of contact, flush immediately with water.
after 30-40 minutes. Do not allow PENESEAL™ FH to dry on the surface. w Protect surfaces from equipment leaks or other
For old concrete (All cured surfaces): leaks, such as oil, hydraulic fluid, etc.
Step 1. Saturate the surface with PENESEAL™ FH so the entire surface is wet for 30 w PENESEAL™ FH treated surfaces can become
minutes. Mist with water if necessary to keep from drying on the surface. slippery during application. Exercise caution and
Step 2 (Option 1). If after 30-40 minutes the majority of PENESEAL™ FH has been wear appropriate footwear and protective clothing.
absorbed into the surface, broom or squeegee any excess material from all low spots and w PENESEAL™ FH is not a vapor barrier.
puddles so all remaining PENESEAL™ FH is totally removed from the surface. Porous w Apply to colored concrete only after the slab is
surfaces may require an additional application of PENESEAL™ FH to achieve maximum fully cured.
protection.
Step 2 (Option 2). If after 30-40 minutes the majority of PENESEAL™ FH is still on the SAFE HANDLING INFORMATION
surface, wait until it becomes slippery underfoot, then thoroughly flush the entire surface Before using this product, review the PENESEAL™ FH
with clean water and squeegee completely dry to remove all PENESEAL™ FH residue. Safety Data Sheet (SDS) that can be found on our website:
General application notes: www.penetronsp.com. Avoid contact with eyes and wear
suitable protective eye wear. Avoid prolonged or repeated
Application temperature limits: 40ºF to 100ºF (4°C to 38°C). The reaction of PENESEAL™ FH contact with skin. Wear gloves and suitable protective
will be slowed at low temperatures. In these cases, the concrete should be protected from clothing. Do not breathe dusts or mists. In case of
freezing for six days. insufficient ventilation, wear respiratory equipment. For
Drying time: 1-3 hours. The surface can be used as soon as the application is complete additional information regarding first aid and emergency
and the surface is dry to the touch. procedures, refer to the product Safety Data Sheet (SDS).
Number of applications required: Typically only one application is required. An additional Waste disposal:
application may be required on porous substrates to achieve maximum performance. This material must be discarded or disposed of in
Time requirement for curing, sealing and hardening: 60-90 days. PENESEAL™ FH seals accordance with all local, state, provincial, and federal
concrete from within by permanently locking the pores, thus making the concrete itself regulations. The generation of waste should be avoided or
the penetration barrier. This process is essentially complete within 90 days, but may minimized wherever possible.
continue at a much slower rate up to one year. KEEP OUT OF REACH OF CHILDREN
Color: Clear. PENESEAL™ FH will not change the natural appearance of the masonry or
concrete. During application, all treated surfaces must be flushed clean with clean water 006bCPR2013-07-10
to prevent impurities from drying on the surface. EN 1504-2
Sheen: On smooth steel-troweled concrete surfaces, a natural wax-like sheen will appear Penetron International, Ltd.
between 6 and 12 months after treatment. This sheen is caused by the hardening and 601 South Tenth Street, Unit 300, Allentown, PA 18103
sealing effects of the PENESEAL™ FH, as well as the natural “buffing” action of foot 09
traffic, cleaning and everyday use of the floor. The sheen is a permanent part of the PENESEAL FH
concrete surface and will last the lifetime of the surface with proper maintenance. Impregnation for protection and repair of concrete structures
Painting or covering preparation: On old concrete – allow 3-7 days before applying paint [Protection against penetration Class 1.2 (I) and
or coverings to PENESEAL™ FH treated surfaces. On new concrete – allow 30 days for Increasing of physical resistance Class 5.2 (I)]
Abrasion resistance: ≥ 30 % improvement
proper curing of the concrete.
Capillary water absorption: Class II
Duration of effectiveness: PENESEAL™ FH is permanent. The concrete durability and Impact strength: Class III (≥ 20 Nm)
appearance improves with age. Bond strength by pull-off: ≥ 0,8 N/mm²
Clean up: Clean all equipment with water only. Do not use thinners. Penetration depth: ≥ 5 mm

WARRANTY: PENETRON INTERNATIONAL, LTD. warrants that the products manufac-

MAINTENANCE tured by it shall be free from material defects and will conform to formulation standards
Floors: and contain all components in their proper proportion. Should any of the products be
proven defective, the liability to PENETRON INTERNATIONAL, LTD. shall be limited to
Wash or wet mop with neutral or high pH detergent. Detergents must not contain caustic replacement of the material proven to be defective, and PENETRON INTERNATIONAL,
LTD. shall in no case be liable otherwise or for incidental or consequential damages.
soda, sulfates or hydroxides. Acids and acidic cleaners will dull the surface sheen and/or PENETRON INTERNATIONAL, LTD. MAKES NO WARRANTY AS TO MERCHANTABILITY OR FITNESS FOR
etch the surface. A PARTICULAR PURPOSE AND THIS WARRANTY IS IN LIEU OF ALL OTHER WARRANTIES EXPRESSED
OR IMPLIED. User shall determine the suitability of the product for its intended use and
Walls: assume all risks and liability in connection therewith.

Flush with clean water. PENETRON INTERNATIONAL, LTD.

45 Research Way, Suite 203, East Setauket, NY 11733
(631) 941-9700 • [email protected] • penetron.com