Falcon Zinc Metal Industries L.L.C

Download as pdf or txt
Download as pdf or txt
You are on page 1of 7

Format. No.

: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 012 Date: 05-08-2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Grating Panel (50 ×5m) – 86 No’s 125


2) 50×50 Angle with flat bar- 02 No’s 140
3) Support Frame (100×10m) – 02 No’ s 116
4) T-Support – 02 No’s 128 131 935.71
135
144

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 09 Date: 05.07.2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Fabricated Frame – 2 Nos 166


95
2) Fabricated Angles – 32 Nos 125
133 137 979
3) Fabricated Beams – 9 Nos 145
158
4) Fabricated Beam Support – 2 Nos
(D/N)- 05830

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 10 Date: 14.07.2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Fabricated Beam Support – 28 Nos 166


95
2) Fabricated Beam T-Support – 06 Nos 125
133 137 979
3) Fabricated Channel Frame – 04Nos 145
158
4) Fabricated Angle Support – 44 Nos
(D/N)- 05836

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 11 Date: 16.07.2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Fabricated Beam Connection– 19 Nos 147


133
2) Fabricated Beam T-Support – 02 Nos 125
97 121 863
3) Fabricated Channel Frame – 02 Nos 108
115
4) Fabricated Angle – 41 Nos
(D/N)- 05838

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 12 Date: 19.07.2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Fabricated Beam Support– 14 Nos 147


133
2) Fabricated T-Support – 03 Nos 125
97 121 863
3) Fabricated Channel Frame – 02 Nos 108
115
4) Fabricated Angle Frame – 22 Nos
(D/N)- 05839

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev :1.0

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No: - 13 Date: 29.07.2021

Customer: - Nael Steel


ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns

1) Fabricated Beam Support– 56 Nos 164


124
2) Fabricated T-Support – 12 Nos 133
187 142 1014
3) Fabricated Channel Frame – 08 Nos 114
130
4) Fabricated Angle Frame – 88 Nos
(D/N)- 05842

Status of the Galvanization: Temperature of Zinc Bath : 445˚ Celsius

Dipping time in Zinc : 5min

Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 610 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

Adhesion Test: Coating does not lift off in large flakes when tested with Stout
Knife as per BS EN ISO: 1461: 2009/ASTM A 123-17.

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.
QC Engineer Division Manager
Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com
Format. No.: FZM-IMS-FO-11E
Falcon Zinc Metal Industries Date : 20.07.2020

L.L.C. Rev : 00

ZINC COATING CERTIFICATE


Inspection and Testing in compliance with BS EN ISO 1461:2009 / ASTM A 123-17

Certificate No : - 007 Date : 22-06-2021


Company :-NBHH
Customer :- NAEL STEEL, AL
AIN Client :ALDAR :- Abu Dhabi,
Project: Saadiyath Reserve :- Abu Dhabi
ZINC COATING APPEARANCE

The acceptability of coating finish as judged by the inspection criteria laid down in BS EN ISO 1461:
2009 /ASTM A 123-17 was found to be within the acceptable limits for smoothness, and continuity.
Zinc coating is free of gross surface imperfections.
COATING THICKNESS AND MASS OF ZINC COATING
Reading
Corresponding Mass of Zinc
Item Description in
Average Coating – g/m2
Microns
151
1. I Beam Supports - 21Nos 127
2. Gratings -90Nos 133
3. T plates -34Nos 116 138 985.71
4. Channel Frames -02Nos 154
5. Angle -42Nos 126
165
134

Status of the Galvanization: Temperature of Zinc Bath : 448˚ Celsius

Dipping time in Zinc : 5min


Corresponding coating as per BS EN ISO 1461:2009 / ASTM A 123-17 with respect of material
thickness, 600 G/m2 i.e. = 85 Microns. (1 G/m2 = 0.14 Micron)

We certify that the above material has been Hot Dip Galvanized to BS EN ISO 1461:2009 / ASTM
A123-17.

QC Engineer Division Manager


Test By Approved By

Tel : 00 (971) 2 5510018


Fax :
Address : ICAD II Musaffah Tower, Floor 24, Office 2352
E-mail : [email protected]
Website : www.falconzinc.com