Aws D10.18 2018
Aws D10.18 2018
Aws D10.18 2018
1 8:201 8
An American National Standard
Approved by the
American National Standards Institute
November 1 4, 201 7
2nd Edition
Supersedes D10.18M/D10.18:2008
Prepared by the
American Welding Society (AWS) D10 Committee on Piping and Tubing
Approved by the
AWS Board of Directors
Abstract
This standard presents a detailed discussion of the metallurgical and welding characteristics and weldability of duplex
stainless steel used in piping and tubing. A number of tables and graphs are presented in order to illustrate the text.
AWS D1 0.1 8M/D1 0.1 8:201 8
Photocopy Rights. No portion of this standard may be reproduced, stored in a retrieval system, or transmitted in any
form, including mechanical, photocopying, recording, or otherwise, without the prior written permission of the copyright
owner.
Authorization to photocopy items for internal, personal, or educational classroom use only or the internal, personal, or
educational classroom use only of specific clients is granted by the American Welding Society provided that the appropriate
fee is paid to the Copyright Clearance Center, 222 Rosewood Drive, Danvers, MA 01 923, tel: (978) 750-8400; Internet:
<www.copyright.com».
ii
AWS D1 0.1 8M/D1 0.1 8:201 8
iii
AWS D1 0.1 8M/D1 0.1 8:201 8
iv
AWS D1 0.1 8M/D1 0.1 8:201 8
Personnel
v
AWS D1 0.1 8M/D1 0.1 8:201 8
vi
AWS D1 0.1 8M/D1 0.1 8:201 8
Foreword
This foreword is not part of this standard but is included for informational purposes only.
This guide is intended to provide information which may be used to avoid, or at least minimize, difficulties in welding
duplex stainless steel piping and tubing. The term used in the text also includes tube.
p ip e
This second edition of D1 0.18M/D10.18 continues as a guide for welding ferritic/austenitic duplex stainless steel piping
and tubing. The duplex stainless steels are finding increased use in industry and the information contained in this guide
will be most useful.
Tables listing specific chemical composition ranges for base metal and weld metal that fall under the jurisdiction of
other codes or documents have been omitted. Where helpful, however, comparison data is presented.
NOTE: The us e r’s a tte n tio n is c a lle d to th e p o s s ib ility tha t co mp lia n ce w ith this s ta n da rd ma y re q u ire use o f an
By publication of this standard, no position is taken with respect to the validity of any such claim(s) or of any patent
rights in connection therewith. If a patent holder has filed a statement of willingness to grant a license under these rights
on reasonable and nondiscriminatory terms and conditions to applicants desiring to obtain such a license, then details
may be obtained from the standards developer.
A vertical line in the margin or underlined text in clauses, tables, or figures indicates an editorial or technical change
from the 2008 edition.
Comments and suggestions for the improvement of this standard are welcome. They should be sent to the Secretary,
AWS D10 Committee on Piping and Tubing, American Welding Society, 8669 NW 36 St, # 1 30, Miami, FL 33166.
vii
AWS D1 0.1 8M/D1 0.1 8:201 8
viii
AWS D1 0.1 8M/D1 0.1 8:201 8
Pag e N o.
Personnel ...................................................................................................................................................................... v
Foreword .....................................................................................................................................................................vii
List of Tables ................................................................................................................................................................ xi
List of Figures .............................................................................................................................................................. xi
1. General Requirements ........................................................................................................................................ 1
1 .1 Scope .......................................................................................................................................................... 1
1.2 Units of Measure ........................................................................................................................................ 1
1.3 Safety .......................................................................................................................................................... 1
2. Normative References ......................................................................................................................................... 2
3. Terms and Definitions ......................................................................................................................................... 2
4. Material Compositions and Specifications ........................................................................................................ 2
4.1 Material Compositions ............................................................................................................................... 2
4.2 Specifications ............................................................................................................................................. 2
5. Basic Metallurgy .................................................................................................................................................. 4
5.1 Solidification and Ferrite/Austenite Phases................................................................................................ 4
5.2 Precipitating Phases.................................................................................................................................... 6
6. Corrosion .............................................................................................................................................................. 7
7. Joint Design and Fit-Up ...................................................................................................................................... 7
7.1 General ....................................................................................................................................................... 7
7.2 Open Root Joints ........................................................................................................................................ 8
7.3 Consumable Inserts .................................................................................................................................... 9
7.4 Autogenous Orbital GTAW ........................................................................................................................ 9
7.5 Orbital GTAW with Filler Metal Addition ................................................................................................. 9
8. Filler Metals ....................................................................................................................................................... 10
9. Welding Processes .............................................................................................................................................. 11
9.1 General ..................................................................................................................................................... 11
9.2 Single Pass Welding Small Diameter Tubing........................................................................................... 11
9.3 Root Pass Welding Heavier Walls ............................................................................................................ 11
9.4 Fill Welding .............................................................................................................................................. 12
10. Welding Procedures ........................................................................................................................................... 12
1 0.1 General ..................................................................................................................................................... 12
1 0.2 Cleaning Before Welding ......................................................................................................................... 12
1 0.3 Preheat ...................................................................................................................................................... 1 2
1 0.4 Interpass Temperature .............................................................................................................................. 12
1 0.5 Heat Input ................................................................................................................................................. 13
1 0.6 Purging (Backing) Gas ............................................................................................................................. 13
1 0.7 Postweld Heat Treatment.......................................................................................................................... 13
11. Weldment Quality Verification ......................................................................................................................... 1 4
1 1.1 Inspection Method .................................................................................................................................... 14
1 1.2 Visual Inspection ...................................................................................................................................... 14
ix
AWS D1 0.1 8M/D1 0.1 8:201 8
Pag e N o.
11 .3 Hydrostatic Testing................................................................................................................................... 1 4
11.4 Liquid Penetrant Methods ........................................................................................................................ 14
11 .5 Radiography ............................................................................................................................................. 14
11 .6 Ultrasonic Methods .................................................................................................................................. 1 4
11.7 Acoustic Emission Testing (AET) Methods ............................................................................................. 1 4
11.8 Mass Spectrometer Testing Method ......................................................................................................... 15
11.9 Ferrite Measurement................................................................................................................................. 1 5
11.1 0 Charpy Impact Test................................................................................................................................... 1 5
11.11 Corrosion Tests ......................................................................................................................................... 1 5
Annex A (Informative)—Guidelines for Weld Corrosion Testing and Welding Procedure Controls
for Corrosion Considerations ............................................................................................ 1 7
Annex B (Informative)—Informative References ...................................................................................................... 1 9
Annex C (Informative)—Requesting an Official Interpretation on an AWS Standard .............................................. 21
List of AWS Documents on Piping and Tubing ......................................................................................................... 23
x
AWS D1 0.1 8M/D1 0.1 8:201 8
Li st of Tabl es
Tabl e Pag e N o.
1 Chemical Composition by Weight Percent of Wrought Lean Duplex Stainless Steels .................................. 2
2 Chemical Composition by Weight Percent of Standard Duplex Stainless Steels........................................... 3
3 Chemical Composition by Weight Percent of Super Duplex Stainless Steels................................................ 3
4 Chemical Composition by Weight Percent of Cast Duplex Stainless Steels .................................................. 4
5 Welding Filler Metals for Duplex Stainless Steels ....................................................................................... 1 0
Li st of Fi g u res
Fi g u re Pag e N o.
xi
AWS D1 0.1 8M/D1 0.1 8:201 8
xii
AWS D1 0.1 8M/D1 0.1 8:201 8
1.2 Units of Measure. This standard makes use of both the International System of Units (SI) and U.S. Customary
Units. The latter are shown within brackets ([ ]) or in appropriate columns in tables and figures. The measurements may
not be the exact equivalents; therefore, each system must be used independently.
To identify nominal pipe sizes in both SI and U.S. Customary Units, the following designations are used:
1.3 Safety. Safety and health issues and concerns are beyond the scope of this standard and therefore are not addressed
herein.
Work performed in accordance with this standard may involve the use of materials that have been deemed hazardous,
and may involve operations or equipment that may cause injury or death. This standard does not purport to address all
safety and health risks that may be encountered. The user of this standard should establish an appropriate safety program
to address such risks as well as to meet applicable regulatory requirements. ANSI Z49.1 should be considered when
developing the safety program.
1
AWS D1 0.1 8M/D1 0.1 8:201 8
2. Normative References
The following standards contain provisions that, through reference in this text, constitute mandatory provisions of this
AWS guide. For undated references, the latest edition of the referenced standard shall apply. For dated references, subse-
quent amendments to, or revisions of, any of these publications do not apply.
AWS A3.0M/A3.0, Standard Welding Terms and Definitions, Including Terms for Adhesive Bonding, Brazing, Solder-
ing, Thermal Cutting, and Thermal Spraying .
orbital welding. Automatic or mechanized welding of tube or pipe in which a welding arc rotates (orbits) around a sta-
tionary weld j oint.
B eneficial features of DSSs include a yield strength about double that of the austenitic grades, while maintaining ductil-
ity and toughness approaching that of the austenitics. DSSs are especially resistant to chloride stress corrosion cracking,
pitting, crevice corrosion, and erosion corrosion. The useful service temperature range is more restricted than the austen-
itics and varies with the particular duplex alloy. In general, the duplex range is –40°C [–40°F] to 280°C [5 3 6°F] .
4.2 Specifications. The wrought DSS s are often classified into three families (lean, standard, and super) based on com-
position. The compositions of the wrought alloy families are shown in Tables 1 , 2, and 3 . Cast alloys are shown in Table
4. Type 2205 is the most widely used of the DSS s and is estimated to represent 80% of DSSs used. Most literature refer-
ences to welding DSSs refer to 2205, however details of welding procedures for the three groups are discussed in later
subclauses.
Table 1
Chemical Composition by Weight Percenta of Wrought Lean Duplex Stainless Steels
Common UNS
Name Number C N Cr Ni Mo P S Si Mn Other
Cu
LDX 21 01 S3 21 01 0. 04 0. 20–0. 25 21 . 0–22. 0 1 . 3 5–1 . 7 0. 1 0–0. 80 0. 040 0. 03 0 1 . 00 4. 0–6. 0
0. 1 0–0. 80
Cu
ATI 21 02 S8201 1 0. 03 0. 1 5–0. 27 20. 5–23 . 5 1 . 0–2. 0 0. 1 0–1 . 00 0. 040 0. 020 1 . 00 2. 00–3 . 00
0. 50
Cu
23 04 S3 23 04 0. 03 0. 05–0. 20 21 . 5–24. 5 3 . 0–5. 5 0. 05–0. 60 0. 040 0. 040 1 . 00 2. 50
0. 05–0. 60
a
Single values are maximums.
2
AWS D1 0.1 8M/D1 0.1 8:201 8
Table 2
Chemical Composition by Weight Percenta of Standard Duplex Stainless Steels
Common UNS
Name Number C N Cr Ni Mo P S Si Mn Other
2205 b S32205 0.03 0.14–0.20 22.0–23.0 4.5–6.5 3.00–3.50 0.030 0.020 1.00 2.00 —
AL 2003 S32003 0.03 0.14–0.20 19.5–22.5 3.0–4.0 1.50–2.00 0.030 0.020 1.00 2.00 —
Cu
255 S32550 0.04 0.10–0.25 24.0–26.0 4.5–6.5 2.9–3.9 0.040 0.030 1.00 1.6
1.50–2.50
S31200 0.03 0.14–0.20 24.0–26.0 5.5–6.5 1.2–2.0 0.045 0.030 1.00 2.00 —
Cu
0.20–0.80
S31260 0.03 0.10–0.30 24.0–26.0 5.5–7.5 2.5–3.5 0.030 0.030 0.75 1.00
W
0.10–0.50
W
S32506 0.03 0.08–0.20 24.0–26.0 5.5–7.2 3.0–3.5 0.040 0.015 0.90 1.00
0.05–0.30
Cr-Ni-Mo-N S32950 0.03 0.15–0.35 26.0–29.0 3.50–5.20 1.00–2.50 0.035 0.010 0.60 2.00 —
a Single values are maximums.
b There is an older UNS version of alloy 2205, UNS S31803. This older version has been replaced by S32205, but some references may still be made to
S31803. S32205 has a higher alloy content and is the preferred alloy to use.
Table 3
Chemical Composition by Weight Percenta of Super Duplex Stainless Steels
UNS
Common Name Number C N Cr Ni Mo P S Si Mn Other
2507 S32750 0.03 0.24–0.32 24.0–26.0 6.0–8.0 3.0–5.0 0.035 0.020 0.8 1.20 —
Cu
0.5–1.0c
ZERON® 100b S32760 0.03 0.2–0.3 24.0–26.0 6.0–8.0 3.0–4.0 0.03 0.01 1.0 1.0
W
0.5–1.0c
Cu
URANUS ® 52N+d S32520 0.03 0.20–0.35 24.0–26.0 5.5–8.0 3.0–4.0 0.035 0.020 0.8 1.5
0.50–2.00
Cu
0.20–0.80
DP3W S39274 0.03 0.24–0.32 24.0–26.0 6.0–8.0 2.5–3.5 0.030 0.020 0.80 1.0
W
1.50–2.50
a Single values are maximums.
b ZERON ® 100 is a registered trademark of Rolled Alloys, Incorporated.
c Other: %Cr + 3.3 × %Mo + 16 × %N ≥ 40
d URANUS ® 52N+ is a registered trademark of ArcelorMittal Industeel.
3
AWS D1 0.1 8M/D1 0.1 8:201 8
Table 4
Chemical Composition by Weight Percenta of Cast Duplex Stainless Steels
ACI Wrought UNS
Designation Equivalent Number C N Cr Ni Mo P S Si Mn Other
Cu
CD4MCu — J93 370 0. 04 — 24. 5–26. 5 4. 75–6. 00 1 . 75–2. 25 0. 04 0. 04 1 .0 1 .0
2. 75–3 . 25
Cu
CD4MCuN S3 2550 J93 372 0. 04 0. 1 0–0. 25 24.5 –26. 5 4. 7–6. 0 1 . 7–2. 3 0. 04 0. 04 1 .0 1 .0
2. 7–3 . 3
Cu
CD3 MN 2205 J92205 0. 03 0. 1 0–0. 3 0 21 . 0–23 . 5 4. 5–6. 5 2. 5–3 . 5 0. 04 0. 020 1 .0 1 .5
1 .0
CE3MN 2507 J93 404 0. 03 0. 1 0–0. 3 0 24. 0–26. 0 6. 0–8. 0 4. 0–5. 0 — — 1 .0 1 .5 Note b
ZERON® W
CD3 MWCuN J93 380 0. 03 0. 20–0. 3 0 24. 0–26. 0 6. 5–8. 5 3 . 0–4. 0 0. 03 0 0. 025 1 .0 1 .0
1 00 0. 5–1 . 0 b
a
Single values are maximums.
b
Other: %Cr + 3 . 3 × %Mo + 1 6 × %N ≥ 40
Common duplex stainless steel specifications for pipe and tubing, fittings, and castings are as follows:
(1 ) ASTM A3 80/A3 80M, Standard Practice for Cleaning, Descaling, and Passivation of Stainless Steel Parts,
Equipment, and Systems ;
(2) ASTM A789/A789M, Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing
for General Service ;
(3 ) ASTM A790/A790M, Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Pipe ;
(4) ASTM A81 5/A81 5 M, Standard Specification for Wrought Ferritic, Ferritic/Austenitic, and Martensitic Stainless
Steel Piping Fittings ;
Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic
(6) ASTM A923 ,
Stainless Steels ;
(7) ASTM A928/A928M, Standard Specification for Ferritic/Austenitic (Duplex) Stainless Steel Pipe Electric
Fusion Welded with Addition of Filler Metal ;
(8) ASTM A995/A995M, Standard Specification for Castings, Austenitic-Ferritic (Duplex) Stainless Steel, for Pressure-
Containing Parts
Standard Test Method for Detecting Detrimental Phases in Lean Duplex Austenitic/Ferritic Stainless
(9) ASTM A1 084,
Steels ; and
Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count
(1 0) ASTM E5 62, .
5. Basic Metallurgy
5.1 Solidification and Ferrite/Austenite Phases. All DSS s solidify as ferrite whether solidification is in an ingot, cast-
ing, or a weld. Islands of austenite form in the ferrite matrix down to a temperature of about 1 000°C [1 83 2°F] . When
wrought products are hot worked, the austenite phase typically assumes an elongated morphology. Figure 1 shows a
cross section of an alloy 2205 plate with elongated morphology. The austenite phase is the lighter constituent in the
darker ferrite matrix.
4
AWS D1 0.1 8M/D1 0.1 8:201 8
Source: Adapted, with permission, from International Molybdenum Association (IMOA), Practical Guidelines for the Fabrication of
Duplex Stainless Steels, Revised Edition, 2001, Figure 2.
The preferred amount of ferrite is 40% to 60%, although the range may be expanded somewhat depending upon the
application. Per industry practices, a range of 25% to 70% may be acceptable provided that mechanical and corrosion
properties have been achieved. When there is a high level of ferrite, toughness and ductility are reduced while at high
levels of austenite, resistance to stress corrosion cracking is reduced and mechanical properties may be somewhat
reduced. It is generally accepted that as long as there is at least 25% of the lesser phase, the expected properties of the
duplex alloy will be realized.
In mill or wrought product forms, the amount of ferrite and austenite depends upon the composition and the thermal his-
tory. Elements that mainly influence phase balance are chromium, molybdenum, nickel, and nitrogen. Thermal process-
ing employed by the mills include factors such as hot working temperature and cooling rates, both of which can vary
depending on the particular product being produced.
Weld ferrite measurements can be made using either destructive or nondestructive examinations. The most common
destructive technique is a ferrite point count, as described in ASTM E562, Standard Test Method for Determining Vol-
ume Fraction by Systematic Manual Point Count, which requires removing a section and metallographic preparation and
photography. Nondestructive measurements can be made using an electronic hand-held measuring device described in
11.9.
The duplex stainless steels have been known since the 1930s, and these early alloys are often referred to as first-generation
DSSs. However, these early grades characteristically had poor weldability and significantly reduced corrosion resistance
in the as-welded condition. The addition of nitrogen as an alloying element in the second-generation DSSs is primarily
responsible for the improvements in weldability and corrosion resistance.
One beneficial role of nitrogen is that of causing austenite to form more quickly and at a higher temperature during the
solid-state transformation. However, there are incidences such as in rapidly cooled welds where excessively high levels
of ferrite may be retained. This will be discussed in more detail later.
5
AWS D1 0.1 8M/D1 0.1 8:201 8
5.2 Precipitating Phases. As noted above, after the molten metal solidifies as ferrite, some ferrite transforms to austen-
ite down to a temperature of about 1 000°C [1 83 2°F] . As the DS S cools below this temperature, other phases such as car-
bides, nitrides, sigma, and other intermetallic phases can form. Chi phase and other intermetallic phases are often
lumped together with sigma phase, and the term “sigma phase” will be taken hereafter to include these other intermetal-
lic phases. S igma, in significant amounts, can be particularly detrimental in that toughness and corrosion resistance may
be reduced. Sigma forms in the temperature range of 700°C to 980°C [1 3 00°F to 1 800°F] with the most rapid formation
at 870°C [1 600°F] . It is formed whenever the alloy is in the 700°C to 980°C [1 3 00°F to 1 800°F] temperature range,
being there is an accumulative effect. The total exposure time for sigma formation includes time at the steel mill during
in-process heating and exposure time during welding including repair welding unless there is an intervening anneal
above 1 040°C [1 900°F] . The proper level of nitrogen delays sigma formation, but does not prevent it. It has been shown
that in the case of alloy 2205 with nitrogen in the upper range of 0. 1 4% to 0. 20%, there is about a five-minute exposure
time at 870°C [1 600°F] available before the amount of sigma formed causes a significant loss of toughness and corro-
sion resistance.
As time at temperature in processing the wrought products is equally as important as time incurred during welding,
AS TM A923 , Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stain-
less Steels, is a very useful document to utilize as it describes three test methods for detecting detrimental intermetallic
phases. The methods include illustrations of acceptable microstructures, Charpy impact test acceptance criteria, and a
ferric chloride corrosion test. ASTM A923 can be specified as a procurement requirement and is particularly useful for
the thicker product forms. It is an aid in assuring that a significant portion of the allowable “five minutes at sigma forma-
tion temperature” has not been used at the steel mill, allowing less time at temperature during welding. AS TM A1 084 is
a standard for the lean DSS for detecting detrimental intermetallic phases and should be used in place of ASTM A923
for the lean DSS .
With nitrogen present in the duplex stainless steels, there is a potential to form chromium nitrides in the interior of large
ferrite grains in the heat-affected zone (HAZ) that can result from too rapid cooling and/or inappropriate alloy balance.
Large amounts of chromium nitrides could create chromium depleted areas that if not corrected by annealing could
reduce corrosion resistance. However, the higher level of nitrogen such as (0. 1 4% to 0. 20%) found in 2205 (UNS
S3 2205) promotes austenite which has a much higher solubility of nitrogen, resulting in the elimination of chromium
nitrides in the second-generation duplex stainless steels. Second-generation alloys are also made to very low carbon levels,
reducing the concern for carbide formation.
Alpha prime is an embrittling phase that forms in ferritic stainless steels with over 1 6% chromium, as well as in the fer-
rite phase of DS S, when exposed in the temperature range of 400°C to 5 40°C [750°F to 1 000°F] with peak embrittling
occurring at 475 °C [885°F] . The phenomena is commonly referred to as 475°C [885°F] embrittlement and results in a
severe loss of room temperature ductility and toughness. The time to embrittle at 475°C [885 °F] can vary from a few
minutes for a DS S with a low level of nitrogen and large amount of ferrite to several hours for alloys with lower ferrite
and higher nitrogen. It is the concern for alpha prime embrittlement that ASME limits DSS to an upper service tempera-
ture limit of 3 1 5°C [600°F] while other standards such as some European codes limit welded alloy 2205 to 250°C
[480°F] .
The time and temperature to form the phases discussed above, i.e. , sigma, carbides, nitrides, and alpha prime is illus-
trated in Figure 2 for 2205 that was annealed at 1 050°C [1 920°F] . The “nose” of the lines is the start of the particular
phase formation with transformation continuing for a period of time. The time to reach a deleterious level may or may
not be reached during the time. Alloys 23 04 and 2507 are shown for comparison. Significant points to note are:
(1 ) While chromium carbides and nitrides start to form in 1 –2 minutes, this is actually slower than in the ferritic and
highly alloyed austenitic grades and as noted earlier these phases are seldom of a practical concern.
(2) Sigma and chi formation takes place at a somewhat higher temperature, but at about the same time as carbides and
nitrides. It will be noted that transformation of the higher alloyed 25 07 initiates in less time and the leaner alloy 23 04
takes considerably longer time than 2205 .
(3 ) The “nose” of the alpha prime formation is at 475°C [885°F] and an increase in hardness occurs followed by a
reduction in toughness.
6
AWS D1 0.1 8M/D1 0.1 8:201 8
1 1 00 201 2
1 000 1 832
2507 S IGMA
CHI
900 1 652
2 304
TEMPERATURE (°C) 8 00 1 472
TEMPERATURE (°F)
700 CARBIDE
1 292
NITRIDE
600 1112
500 ALPHA
932
HARDNE SS PRIME TOUGHNE SS
400 752
3 00 572
200 3 92
0 1 10 1 00 1 000 1 0 000
2205 TIME (MINUTE S )
2 304
2507
Note: Duplex grades 2304 and 2507 are shown for comparison.
Source: Adapted, with permission, from International Molybdenum Association (IMOA), Practical Guidelines for the Fabrication of
Duplex Stainless Steels, Revised Edition, 2001 , Figure 4.
6. Corrosion
The DSS s exhibit good corrosion resistance in a wide range of environments and in general are equal or better than com-
parable austenitic grades. The high chromium content provides good resistance to oxidizing acids and the levels of
molybdenum and nickel provide resistance to weakly reducing acids.
The alloys’ excellent resistance to crevice corrosion and pitting corrosion in chloride containing environments accounts
for one of the principle uses for the DSSs. For example, 2205 is superior to Type 3 1 6 while the superduplex stainless
steels (SDSSs) have comparable resistance to the higher alloy content 6% molybdenum alloys in pitting and crevice cor-
rosion resistance in chloride containing environments. In a microstructure containing as little as 3 0% ferrite, the duplex
alloys have far superior resistance to stress corrosion cracking than the austenitic grades. However, there is a note of cau-
tion in that the ferrite phase is susceptible to hydrogen embrittlement and the DSSs are not well suited to applications
where hydrogen is charged into the metal.
When the service environment is very corrosive for the DS S alloy, weld corrosion tests may be imposed. Weld corrosion
testing and welding procedure controls for corrosion considerations are discussed in Annex A.
7
AWS D1 0.1 8M/D1 0.1 8:201 8
The choices for j oint designs are similar to those for austenitic stainless steels, with the exception of closed root j oint
designs. It is suggested to avoid closed root j oint designs unless the weldment is thin wall tubing, uses a J-groove config-
uration, or is to be solution annealed after welding. This is because little or no filler metal can be used for the root pass
with a closed root, and without the higher nickel of the filler metal, the root pass tends to retain excessive ferrite under
the rapid cooling conditions of welding in thicker material. Appropriate open root designs are shown in Figure 3 . For
more details on j oint designs, see AWS D1 0.1 1 M/D1 0.1 1 , Recommended Practices for Root Pass Welding of Pipe Without
Backing . Use of backing rings is not recommended for most applications since the crevice between the pipe wall and the
backing ring increases the possibility of crevice corrosion when the fluid being handled is a corrosive media.
7.2 Open Root Joints. Typical open root j oint designs are shown in Figure 3 . Figure 3 (A) is a standard V-groove with
3 7-1 /2° bevels and a root face of dimension “C.” As with austenitics, the bevel angle (Angle A) can be reduced, for
example to 3 0°, if desired to reduce residual stresses and weld metal volume. The limit on angle reduction is that point
where lack of side wall fusion is a possibility for the welding process used and weld accessibility.
In manual welding, the root opening requirement is determined by the method used to add filler metal. A root opening
equal to or slightly smaller than the filler metal wire diameter is used with the keyhole technique. In this technique, the
filler metal is introduced intermittently as necessary to fill the gap. A larger opening is used with the continuous feed
technique in which the filler metal is always in the opening and can be melted continuously if desired.
C
(A) C (B)
B
(D)
C
(C)
A
A = 3 7-1 /2° ± 2-1 /2°
B = 1 0° ± 1 °
C = 2 mm ± 1 mm [1 /1 6 in ± 1 /3 2 in]
D = 2 TIME S AMOUNT OF OFF S ET
E = 3 0° MAX.
R = 6 mm [1 /4 in] C D E
(E)
8
AWS D1 0.1 8M/D1 0.1 8:201 8
For heavier wall thickness, Figure 3 (B ) or 3 (C) is often used. The U-groove j oint design, as in Figure 3 (C) is useful
when inserts are used since it allows good torch access to the root.
7.3 Consumable Inserts. Consumable inserts are an alternate to the manually fed filler metal technique in making the
pipe root pass weld. Full penetration welds with good root contour are obtainable. The choice between the manually fed
filler metal technique and consumable inserts often varies from industry to industry and with the welder’s work experi-
ence. AWS A5 . 3 0/A5. 3 0M, Specification for Consumable Inserts , lists five different consumable insert shapes of differ-
ent sizes, but no DSS compositions are listed in that standard.
Limited insert shapes, with compositions similar to those of GTAW filler metal compositions found in AWS
A5 . 9/A5 . 9M, Specification for Bare Stainless Steel Welding Electrodes and Rods , can be obtained from consumable
insert manufacturers. These insert rings are generally enriched in nickel as compared to corresponding base metal com-
positions to assist in achieving a balanced microstructure and acceptable weld bead profile with small diameter thin-wall
orbital welding. Inserts have been used in orbital welding small diameter thin-wall tubing and are also an option in man-
ual welding larger diameter heavier wall pipes. In installing the insert, the ring is fitted and tacked on one side, then the
j oint is fit-up and tacked on the other side of the j oint. Care and caution must be taken when tacking inserts to avoid pre-
stressing the weld j oint. Also, care must be taken to avoid oxidized tack welds which in turn could lead to areas of lack
of fusion or weld defects.
The success of this technique is dependent upon welder proficiency with the gas tungsten arc process and adequacy of
interior gas purge. With experience, the welder is able to recognize when the insert has melted and the molten pool
reaches proper height and width to form the proper root reinforcement. S peed of travel is adj usted accordingly. Less skill
may be required to weld j oints with consumable inserts than to weld j oints without backing.
7.4 Autogenous Orbital GTAW. Autogenous orbital welding with a groove weld in the square butt configuration is
practical for small diameters (25 mm [1 in] or less) with thinner walls (3 mm [1 /8 in] or less).
7.5 Orbital GTAW with Filler Metal Addition. For both single pass and multipass orbital GTAW, the filler metal may
be added automatically by cold wire or hot wire addition.
7.5.1 Single Pass Orbital GTAW with Wire Feed. For thin-wall small diameter tubing or pipe, a closed root butt
weld j oint with a bevel through part of the wall thickness may be used if the j oint can be welded in a single pass. The
bevel helps to facilitate penetration and to achieve a flatter weld bead than with a standard groove weld in the square butt
configuration with the addition of wire.
7.5.2 Multipass Orbital GTA Welding with Wire Feed. For heavier wall thickness up to approximately 1 2 mm
[0. 50 in] and multipass welding, a modified “J” j oint design shown in Figure 4 has been used. However, an extended
land can affect corrosion performance due to excessive overheating or reheating even when the lower heat second pass
approach, as described in Annex A, is observed. (See Annex A, Figure A. 1 . ) Torch oscillation may be used to distribute
the heat input across the weld j oint concentrating the heat near the side of the j oint so full penetration is achieved without
excessive heat input. This combination of using an extended land with torch oscillation can aid in controlling heat inputs
9
AWS D1 0.1 8M/D1 0.1 8:201 8
to desirable ranges. A further advantage of the root face extension is in preventing the weld pool from “climbing” the
side walls of the joint. In developing the welding procedure specification (WPS), dimensions of both the root face and
root face extension have been found to be critical and may vary with pipe diameter. Root face thicknesses as small as 1.2
mm [0.05 in] have been used which in turn requires tight control over joint alignment.
8. Filler Metals
In welding DSSs it is good practice to always add filler metal whenever possible and practical. Autogenous DSS welds
tend to be higher in ferrite than the base metal being welded. Also, fast weld cooling rates increase the amount of ferrite
in the weld. Filler metal 2209 is the standard filler metal for welding 2205 and many of the lean DSSs. Filler metal
E2209 has a nickel content of 7.5% to 9.5% compared to 4.5% to 6.5% for 2205 base metal. With this nickel adjustment,
a much better ferrite to austenite balance is obtained. An exception to the need for a nickel enhanced filler metal would
be when the weld receives a final full solution anneal.
There are near matching composition proprietary filler metals for many of the lean and super DSSs. Suggested filler
metals are shown in Table 5. It is also advisable to consult the alloy producer of proprietary alloys for their filler metal
recommendations and filler metal availability.
Nickel alloy filler metals have also been used to weld both the standard and super DSSs. One such nickel alloy filler
metal for which data is available is ERNiCrMo-1 4, found in AWS A5.14/A5.14M, Specification for Nickel and Nickel-
Alloy Bare Welding Electrodes and Rods . Welds made with this filler metal have pitting corrosion resistance comparable
to those made with super DSS filler metal. Since the nickel alloy welds are fully austenitic, there is no concern regarding
Table 5
Welding Filler Metals for Duplex Stainless Steels
Base Metal Base Metal
Common Name UNS Number Bare Wire SMAW Electrodes FCAW Electrodes
AWS A5.22/A5.22M
LDX 2101 S32101 LDX 2101 LDX 2101
E2209TX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M
ER2209 E2209
AWS A5.22/A5.22M
2304 S32304 2304 2304
E2209TX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M AWS A5.22/A5.22M
ER2209 E2209 E309LTX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M
ER309L E309L
AWS A5.9/A5.9M AWS A5.4/A5.4M AWS A5.22/A5.22M
2003 S32003
ER2209 E2209 E2209TX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M AWS A5.22/A5.22M
2205 S32205
ER2209 E2209 E2209TX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M AWS A5.22/A5.22M
255 S32550
ER2553 E2553 E2553TX-X
AWS A5.9/A5.9M AWS A5.4/A5.4M
2507 S32750 E2507TX-X
ER2594 E2594
AWS A5.9/A5.9M AWS A5.4/A5.4M
ZERON® 100 S32760 E2594TX-X
ER2594 E2595
10
AWS D1 0.1 8M/D1 0.1 8:201 8
obtaining a balance of austenite and ferrite. All-weld metal yield strength of ERNiCrMo-14 welds made by the GTAW
process have exceeded the minimum 560 MPa [80 000 psi] yield strength of the super DSS base metal using a rather low
heat input of 0.8 kJ/mm [20 kJ/in] or a higher heat input of 1.3 kJ/mm [33 kJ/in]. The all-weld metal tensile strength also
exceeded the minimum base metal properties at both levels of heat input. Charpy V-notch weld impact properties were
in excess of 60 J [44 ft·lbs] for both –50°C [–58°F] and –196°C [–320°F] indicating good weld metal toughness.
A commonly encountered dissimilar metal weld is between DSS and an austenitic stainless steel such as Type 304L or
316L. For joining 304L to DSS, 308L filler metal is adequate, while for joining 31 6L to DSS, 316L filler metal is ade-
quate. In joining any of the DSSs to carbon or low alloy steel, a suitable filler metal is 309/309L or 309LMo.
9. Welding Processes
9.1 General. The welding processes of GTAW, GMAW, SMAW, FCAW, and SAW have all been used with success on
these alloys.
Welders that have experience with austenitic stainless steels should be able to apply the skills and techniques acquired
with these alloys to DSSs. The welding characteristics of the two families of alloys are similar; however, the duplex
weld puddle is more viscous than austenitic stainless steel and thus more difficult to weld by hand.
The GTAW process is considered the best choice for the root pass of pipe welds when all welding is from the OD (out-
side diameter). Automatic or mechanized welding such as orbital GTAW are capable of producing high quality root pass
welds with consistent internal weld profiles.
9.2 Single Pass Welding Small Diameter Tubing
9.2.1 Autogenous Orbital GTAW. In smaller diameter tubes (25 mm [1 in] or less) with thinner walls (3 mm [1 /8
in] or less), autogenous orbital welding with the higher controlled heat input and a special shielding gas mixture (see
9.2.2) is able to consistently produce phase-balanced welds. A square butt joint configuration is used for these smaller
diameter tube welds.
9.2.2 Consumable Insert. There is also the option of using consumable insert rings to provide filler metal addition.
Fusion welds on closed square butt joints or closed square butt joints with inserts are normally completed in a single
pass. A commonly used shielding gas is 88% argon, 10% helium, and 2% nitrogen mixture, where helium is added to
increase penetration and nitrogen is used to promote the formation of austenite. The addition of nitrogen is of special
benefit in welding SDSSs to obtain a desired ferrite-austenite balance. Purging gas is discussed in 10.6.
With autogenous orbital welds made with or without a consumable insert and with the low sulfur content of most DSSs,
there may be a tendency towards the formation of external weld bead concavity at the 12 o’ clock location and internal
weld concavity at the 6 o’ clock location when welding in the 5G position. Pressure balancing with a pressure-measuring
device is frequently used to control the weld bead profile of autogenous welds on small diameter DSSs as well as for
austenitic stainless steels.
9.2.3 Autogenous Orbital Square-Butt Welds with Penetrating Flux. One approach in obtaining a full penetration
autogenous orbital weld using a square groove pipe joint is the use of a penetrating (GTAW) flux. The paste-like pene-
tration enhancing flux is carefully applied to the outside of the joint following the manufacturer’s recommended proce-
dure. The weld will normally be accomplished in one pass. Argon is used for both the internal purge and the welding
shielding gas. A special procedure to control the internal purge pressure is needed to prevent excessive weld penetration
or OD concavity. After the weld is made, there is a tenacious coating of flux that requires removal with a powered nylon
cleaning wheel. The use of stainless steel wire brushes is not recommended.
9.2.4 Single Pass Weld with Wire. Small diameter thin wall DSS tubing has been successfully welded with orbital
GTAW with the addition of filler wire. A slight bevel on the closed root square butt end preparation may be used.
9.3 Root Pass Welding Heavier Walls. On heavier wall thickness, an orbital GTA pipe weld is typically made using a
modified “J” preparation shown in Figure 4. On DSS, the addition of wire filler metal on the root pass is recommended.
The root face on the “J” preparation can be extended to assure repeatable penetration of the joint. Care must be taken
when welding the second pass to avoid excessive remelting of the root pass which may result in underfill or concavity on
the inside diameter (ID) root surface (suck-back).
11
AWS D1 0.1 8M/D1 0.1 8:201 8
9.4 Fill Welding. In fill welding, automated or orbital GTAW systems with wire feed results in high quality piping
welds. For production fill welding GMAW, FCAW, and SAW offer advantages. 1 In SAW, a metallurgically basic flux is
a good choice to avoid loss of elements that could affect the preferred weld metal composition. However, the increased
heat input and inclusion content normally associated with SAW can influence corrosion and toughness results. On heavy
sections (> 25 mm [1 in]), it may be necessary to increase welding heat input to obtain a slower cooling rate and the nec-
essary austenite-ferrite balance. Where both corrosion resistance and toughness are important issues, microprocessor or
waveform controlled pulse GMAW will typically provide more reproducible and satisfactory results. SMAW may be a
choice for field welding applications.
In GMAW there are a number of proprietary welding shielding gases used in welding DSS and SDSS alloys. Most gases
are argon with various additions of helium, nitrogen, and CO2. The selection of shielding gases and welding parameters
for FCAW should reflect the filler metal manufacturer’s recommendations.
Process modifications such as hot wire GTAW, welding wire manipulation or vibration, and GMAW power source
waveform control offer increased arc welding deposition over the nonmodified processes.
10.3 Preheat. Preheating is not recommended with duplex stainless steels except to dry the surface or when the temper-
ature is below 16°C [60°F], or when welding heavy sections (wall thickness > 50 mm [2 in]) where a preheat of 50°C
[1 22°F] may be appropriate.
10.4 Interpass Temperature. The maximum interpass temperature control often used for 2205 and the leaner DSS is
150°C [300°F] while the maximum for SDSSs is 65°C [150°F]. However, these temperatures are conservative and
higher temperatures of 200°C [400°F] and 1 50°C [300°F], respectively, are often employed. Basically there is no single
interpass temperature that covers all situations. The lower the maximum interpass temperature, the less time the HAZ is
in the sigma formation range which may be a consideration for multipass weld joints or when maximum corrosion resis-
tance is of primary concern. On the other hand, lower interpass temperatures introduce the economic constraint of
increased welding times. Consequently, there is no single interpass temperature that covers all situations.
1 “Development of mechanized field girth welding of high-alloy corrosion-resistant pipeline materials,” by R. E. Avery and C. M.
12
AWS D1 0.1 8M/D1 0.1 8:201 8
10.5 Heat Input. Heat input is often a compromise between a heat input high enough to avoid fast cooling with the
resultant tendency to form excessive ferrite and heat input low enough to avoid excessive time in the 700°C to 980°C
[1 300°F to 1800°F] sigma formation range. A heat input range commonly used for DSS is 0.5 kJ/mm to 2.5 kJ/mm
[1 2.5 kJ/in to 62.5 kJ/in]. However, there are codes and user specifications that restrict the maximum heat input to
1 .75 kJ/mm [44.4 kJ/in] for alloy 2205 and 1.5 kJ/mm [38 kJ/in] for the SDSS. Lean duplex stainless steels have been
successfully welded with substantially higher heat inputs than those cited above. Special heat input guides for the root
pass and first fill pass of duplex and super duplex stainless steels are discussed in Annex A.
10.6 Purging (Backing) Gas. Nitrogen is the most suitable backing gas for DSS because it protects the root surface
from nitrogen loss, especially in GTAW. It is also less expensive than argon, although argon has been used successfully.
Hydrogen addition, as is sometimes used with austenitic steels, is dangerous for DSS because of the possibility of hydro-
gen embrittlement and should be avoided. See AWS D10.11M/D10.11, Recommended Practices for Root Pass Welding of
Pipe Without Backing , for guides in pipe purging techniques and purging gas specifications. When using an oxygen ana-
lyzer, an oxygen content of less than 0.2% is a good starting point to determine if the surface discoloration is satisfactory.
The gas tungsten arc process is the most reliable process to make a quality root pass weld. A gas purge is essential in
providing a full penetration weld that is essentially free of oxidation. An extreme example of root pass oxidation made
without purging or with improper purging is a condition commonly referred to as a ‘sugared’ weld. A heavily oxidized
(sugared) weld often has weld defects, has poor corrosion resistance in many environments, and should be removed.
More often the weld and HAZ may have various degrees of heat-tint discoloration due to some level of oxygen in the
purge. Parts being purged should be clean and dry prior to assembly as excessive moisture can also contribute to tinting
of the root side. Depending upon the service, the presence of heat-tint can significantly reduce pitting or crevice corro-
sion resistance or particles of oxide may be a source of product contamination. For applications where heat-tint discolor-
ation could influence service performance, a weld discoloration level guide such as shown in AWS D18.1 /D18.1M,
Specification of Welding Austenitic Stainless Steel Tube and Pipe Systems in Sanitary (Hygienic) Applications , is more
useful than specifying an oxygen level.
Nitrogen may be included in the purge gas and/or the shielding gas to compensate for any loss of nitrogen during weld-
ing. Nitrogen additions to the shielding (torch) gas are typically 1% to 2%. Nitrogen additions up to 100% have been
used in purge gas (back purge). A reduction of nitrogen in the weld will increase the amount of ferrite and in turn affect
the ferrite to austenite balance. Nitrogen additions for ferrite balance are often used in automatic welding operations
where there is closer control of welding parameters than in manual welding.
10.7 Postweld Heat Treatment. Localized postweld heat treatment is seldom performed or considered necessary for
piping assemblies. The as-welded structure is normally satisfactory when proper welding procedures are used. If a heat
treatment is employed after welding, it must be a full anneal. The correct annealing temperature depends upon whether
or not filler metal with higher nickel content than that of the base metal was used. If no filler metal was used, or if match-
ing nickel filler metal was used, then an appropriate annealing temperature is generally 1 040°C [1900°F] minimum.
However, if enriched nickel filler metal, such as 2209, is used, then the annealing temperature needs to be higher
(1 150°C [2100°F]) in order to dissolve all the intermetallic phases that form during heating to the annealing temperature.
The higher nickel content makes sigma phase stable to higher temperatures. Water quenching directly from the anneal-
ing temperature is necessary to avoid sigma formation on cooling after annealing. 2 As discussed previously, time in the
31 5°C to 980°C [600°F to 1 800°F] range should be kept to a minimum to minimize the development of harmful phases.
Some situations where postweld or post fabrication heat treatment may be appropriate are:
(1 ) When cold deformation exceeds 15% such as the U bending of tubes,
(2) Welding with a process where heat input cannot be kept within the recommended range, and
(3) After hot bending.
If for some reason a postweld heat treatment is considered necessary, it is advisable to consult the base metal manufacturer
for heat treatment specifics.
2 Kotecki, D. J.; 1989; “Heat treatment of duplex stainless steel weld metals.” Welding Journal, 68(11): 431-s–441-s.
13
AWS D1 0.1 8M/D1 0.1 8:201 8
14
AWS D1 0.1 8M/D1 0.1 8:201 8
11.8 Mass Spectrometer Testing Method. This method employs an electronic instrument using helium as a tracer gas
and is capable of detecting very minute leaks. Several procedures are available when using the mass spectrometer,
including the helium blanket, the helium probe, and the instrument probe techniques. Considerable technical knowledge
is required for procedure preparation, but actual operation may be performed by shop personnel after a short training
period. This method is generally used only on very critical pipe work.
11.9 Ferrite Measurement. Electronic hand-held measurement devices, such as a Feritscope® , 3 can be a useful tool for
monitoring ferrite content in a weld during fabrication. They are not practical for very small diameter tubing due to the
measurement distortion produced by the curvature of the tube, but can be used on larger diameter tubing and to check the
root of larger diameter piping prior to the welding of additional passes. Magne-Gage®4 testing may be used to measure
the amount of ferrite along the top centerline of a given weld bead and requires only slight surface grinding so that it is a
nondestructive test. See AWS A4.2M (ISO 8249 MOD), Standard Procedures for Calibrating Magnetic Instruments to
Measure the Delta Ferrite Content of Austenitic and Duplex Ferritic-Austenitic Stainless Steel Weld Metal , for calibra-
Welding Guidelines for the Chemical, Oil, and Gas Industries
tion criteria. See API 582, Standard Test
, ASTM E562,
Method for Determining Volume Fraction by Systematic Manual Point Count , and 5.1 for ferrite point count criteria.
Contractual requirements take precedence over ferrite count criteria and acceptable ferrite limits.
The use of ferritescope devices requires proper surface preparation to avoid erroneous measurements.
11.10 Charpy Impact Test. The Charpy impact test is used to provide a measure of base metal or weld toughness. It is
one of the tests used in ASTM A923, Standard Test Methods for Detecting Detrimental Intermetallic Phase in Wrought
Duplex Austenitic/Ferritic Stainless Steels
. The Charpy impact test is also specified by some users on DSS welds for
special applications where weld toughness is a concern. Charpy impact tests are particularly indicated where low tem-
perature environments are expected.
11.11 Corrosion Tests. Contractual requirements take precedence; see Annex A for measurement method references.
3 Feritscope is a registered trademark of Helmut Fischer GmbH Institut für Elektronik und Messtechnik, Sindelfingen/Germany.
4 Magne-Gage is a registered trademark of Magne-Gage Sales & Service Co., Inc.
15
AWS D1 0.1 8M/D1 0.1 8:201 8
16
AWS D1 0.1 8M/D1 0.1 8:201 8
Annex A (Informative)
Guidelines for Weld Corrosion Testing and Welding
Procedure Controls for Corrosion Considerations
This annex is not part of this standard but is included for informational purposes only.
A1. Introduction
Some DSSs are being used in quite severe corrosive environments where there can be concerns regarding the weld and
heat-affected zone (HAZ) corrosion resistance. This annex addresses guidelines that have been found helpful in per-
forming corrosion tests and welding procedure controls for optimum corrosion resistance. It should be recognized that
for most normal services, DSS welds made using qualified welding procedures perform entirely satisfactorily, and care-
ful consideration should be given before imposing expensive corrosion testing.
5 Effective Welding of Duplex & Superduplex Stainless Steels, Graham Holloway, Metrode Products.
17
AWS D1 0.1 8M/D1 0.1 8:201 8
(3) Weld 3—Root with optimum corrosion resistance— balanced root and second pass heat input—medium heat input
root, 1 .43 kJ/mm [37 kJ/in] and second pass about 75% of root pass heat input, 1 .2 kJ/mm [30 kJ/in].
It is acceptable to use the wider range of heat input after the controlled root and second pass.
Another option to maximize root pass weld metal corrosion resistance is to use the SDSS filler metal, ER2594, found in
AWS A5.9/A5.9M (ISO 1 4343:2009 MOD), for the root pass in welding alloy 2205. In welding the SDSS, an added
option is the use of Ar–2% N2 for the shielding (torch) gas. For more information, see API 582, Welding Guidelines for
the Chemical, Oil, and Gas Industries, ASTM A923, and ASTM A1 084.
18
AWS D1 0.1 8M/D1 0.1 8:201 8
Annex B (Informative)
Informative References
This annex is not part of this standard but is included for informational purposes only.
Welding Guidelines for the Chemical, Oil, and Gas Industries, American Petroleum Institute.
API 582,
ANSI Z49.1, Safety in Welding, Cutting, and Allied Processes, American Welding Society.
ASME B31.3, Power Piping , ASME International.
ASME Boiler and Pressure Vessel Code, Sections I, III, V, VIII, ASME International.
ASTM A380/A380M, Standard Practice for Cleaning, Descaling, and Passivation of Stainless Steel Parts, Equipment,
and Systems
, ASTM International.
ASTM A789/A789M, Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing for
General Service
, ASTM International.
ASTM A790/A790M, Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Pipe, ASTM
International.
ASTM A815/A815M, Standard Specification for Wrought Ferritic, Ferritic/Austenitic, and Martensitic Stainless Steel
Piping Fittings
, ASTM International.
ASTM A890/A890M, Standard Specification for Castings, Iron-Chromium-Nickel-Molybdenum Corrosion-Resistant,
Duplex (Austenitic/Ferritic) for General Application, ASTM International.
ASTM A923, Standard Test Methods for Detecting Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stain-
less Steels, ASTM International.
ASTM A928/A928M, Standard Specification for Ferritic/Austenitic (Duplex) Stainless Steel Pipe Electric Fusion
Welded with Addition of Filler Metal, ASTM International.
ASTM A995/A995M, Standard Specification for Castings, Austenitic-Ferritic (Duplex) Stainless Steel, for Pressure-
Containing Parts, ASTM International.
ASTM A1 084, Standard Test Method for Detecting Detrimental Phases in Lean Duplex Austenitic/Ferritic Stainless
Steels, ASTM International.
ASTM E562, Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count, ASTM Inter-
national.
ASTM G48, Standard Test Methods for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys
by Use of Ferric Chloride Solution, ASTM International.
AWS A4.2M (ISO 8249:2000 MOD), Standard Procedures for Calibrating Magnetic Instruments to Measure the Delta
Ferrite Content of Austenitic and Duplex Ferritic-Austenitic Stainless Steel Weld Metal, American Welding Society.
AWS A5.4/A5.4M, Specification for Stainless Steel Electrodes for Shielded Metal Arc Welding , American Welding
Society.
AWS A5.9/A5.9M (ISO 14343:2009 MOD), Welding Consumables—Wire Electrodes, Strip Electrodes, Wires, and
Rods for Arc Welding of Stainless and Heat Resisting Steels—Classification, American Welding Society.
19
AWS D1 0.1 8M/D1 0.1 8:201 8
AWS A5 . 1 1 /A5. 1 1 M, Specification for Nickel and Nickel-Alloy Electrodes for Shielded Metal Arc Welding , American
Welding Society.
AWS A5. 1 2M/A5. 1 2 (IS O 6848: 2004 MOD), Specification for Tungsten and Oxide Dispersed Tungsten Electrodes for
Arc Welding and Cutting , American Welding S ociety.
Specification for Nickel and Nickel-Alloy Bare Welding Electrodes and Rods
AWS A5 . 1 4/A5 . 1 4M, , American Welding
S ociety.
AWS A5. 22/A5. 22M, Specification for Stainless Steel Flux Cored and Metal Cored Welding Electrodes and Rods ,
American Welding Society.
AWS A5. 3 0/A5. 3 0M, Specification for Consumable Inserts , American Welding Society.
AWS A5 . 3 2M/A5. 3 2 (ISO 1 41 75: 2008 MOD), Welding Consumables—Gases and Gas Mixtures for Fusion Welding
and Allied Processes , American Welding Society.
AWS A5.3 4/A5.34M, Specification for Nickel-Alloy Electrodes for Flux Cored Arc Welding , American Welding Society.
AWS D1 8.1 /D1 8.1 M, Specification for Welding of Austenitic Stainless Steel Tube and Pipe Systems in Sanitary
(Hygienic) Applications , American Welding Society.
AWS Welding Handbook , Volume 4, Chapter 5, “Stainless and Heat Resistant Steels,” Eighth Edition, American Welding
S ociety.
NIOSH Criteria Document 76-1 29 and 77-1 64, National Institute for Occupational S afety and Health.
20
AWS D1 0.1 8M/D1 0.1 8:201 8
Annex C (Informative)
Requesting an Official Interpretation
on an AWS Standard
This annex is not part of this standard but is included for informational purposes only.
C1. Introduction
The following procedures are here to assist standard users in submitting successful requests for official interpretations to
AWS standards. Requests from the general public submitted to AWS staff or committee members that do not follow
these rules may be returned to the sender unanswered. AWS reserves the right to decline answering specific requests; if
AWS declines a request, AWS will provide the reason to the individual why the request was declined.
C2. Limitations
The activities of AWS technical committees regarding interpretations are limited strictly to the interpretation of provi-
sions of standards prepared by the committees. Neither AWS staff nor the committees are in a position to offer interpre-
tive or consulting services on (1 ) specific engineering problems, (2) requirements of standards applied to fabrications
outside the scope of the document, or (3 ) points not specifically covered by the standard. In such cases, the inquirer
should seek assistance from a competent engineer experienced in the particular field of interest.
Managing Director
S tandards Development
American Welding Society
8669 NW 3 6 St, # 1 3 0
Miami, FL 3 3 1 66
C3.2 Contact Information. All inquiries shall contain the name, address, email, phone number, and employer of the
inquirer.
C3.3 Scope. Each inquiry shall address one single provision of the standard unless the issue in question involves two or
more interrelated provisions. The provision(s) shall be identified in the scope of the request along with the edition of the
standard (e. g. , D1 . 1 : 2006) that contains the provision(s) the inquirer is addressing.
C3.4 Question(s). All requests shall be stated in the form of a question that can be answered ‘ yes’ or ‘ no’ . The request
shall be concise, yet complete enough to enable the committee to understand the point of the issue in question. When the
point is not clearly defined, the request will be returned for clarification. Sketches should be used whenever appropriate,
and all paragraphs, figures, and tables (or annexes) that bear on the issue in question shall be cited.
C3.5 Proposed Answer(s). The inquirer shall provide proposed answer(s) to their own question(s).
21
AWS D1 0.1 8M/D1 0.1 8:201 8
C3.6 Background. Additional information on the topic may be provided but is not necessary. The question(s) and pro-
posed answer(s) above shall stand on their own without the need for additional background information.
Communication concerning an official interpretation is directed through the AWS staff member who works with that
technical committee. The policy requires that all requests for an official interpretation be submitted in writing. S uch
requests will be handled as expeditiously as possible, but due to the procedures that must be followed, some requests for
an official interpretation may take considerable time to complete.
22
AWS D1 0.1 8M/D1 0.1 8:201 8
23
AWS D1 0.1 8M/D1 0.1 8:201 8
24