Sikarep® Sa: Product Data Sheet
Sikarep® Sa: Product Data Sheet
Sikarep® Sa: Product Data Sheet
SikaRep® SA
MULTI-PURPOSE, ECONOMICAL, PATCHING AND REPAIR MORTAR
PRODUCT INFORMATION
Composition Polymer containing cementitious mortar with different additives
Packaging 25 kg bag
Appearance / Colour Grey Powder
Shelf life 12 months minimum from production date
Storage conditions Store in a dry area in original sealed packaging at temperatures between +5
°C and +35 °C. Protect from direct sunlight, heat and moisture.
Maximum Grain Size ~1.5 mm
TECHNICAL INFORMATION
Compressive Strength ≥ 35 N/mm2 (w/p = 0.16) (ASTM C109)
Tensile Adhesion Strength ≥ 1.5 N/mm2 (concrete failure) (BS 1881 Part 208)
APPLICATION INFORMATION
Mixing Ratio 4.0 - 4.5 L of water per 25 kg bag
Fresh Mortar Density ~2.05 kg/l (25 °C)
Yield ~14.1 L per 25 kg bag
Layer Thickness Min. 5 mm per layer
Max. 30 mm per layer
1/3
Ambient Air Temperature +5 °C min. / +40 °C max.
Substrate Temperature +5 °C min. / +40 °C max.
Pot Life ~45 min (25 °C)
SUBSTRATE QUALITY / PRE-TREATMENT Where ambient conditions may lead to rapid surface
drying, the use of light water fogging for 48 hours or
▪ Substrates must be properly cured, structurally application of a suitable water based curing com-
sound, free of any loose or friable particles, clean, pound like Antisol®-WB is recommended. Do not com-
dry and free of any contaminants such as dust, dirt, mence fogging until final set has been reached.
oil, grease, cement laitance or efflorescence.
▪ Depending on the substrate condition and contamin- CLEANING OF EQUIPMENT
ants to be removed from the surface, perform ad- Application and mixing tools should be cleaned with
equate preparation techniques, such as water-jet water while the material is still fresh. Hardened mater-
washing or blast cleaning, in order to remove all ial can only be removed mechanically.
traces of any materials that could reduce the
product's adhesion to the substrate.
▪ For applications in hot climates / environments and / IMPORTANT CONSIDERATIONS
or on absorbent substrates, thoroughly pre-dampen Do not over work the finished surface as this will pro-
the surface immediately prior to the product applica- duce a cement rich surface texture, which may cause
tion, but avoid any ponding / standing water on the the formation of random (crazing) cracking in the sur-
surface, which must not be damp to touch and not face. Over work of the finished surface could also dis-
with a dark-matt / wet surface appearance i.e. it turb the mortar bond on the concrete substrate.
must be saturated surface dry (SSD).
2/3
LEGAL NOTES
The information, and, in particular, the recommenda-
tions relating to the application and end-use of Sika
products, are given in good faith based on Sika's cur-
rent knowledge and experience of the products when
properly stored, handled and applied under normal
conditions in accordance with Sika's recommenda-
tions. In practice, the differences in materials, sub-
strates and actual site conditions are such that no war-
ranty in respect of merchantability or of fitness for a
particular purpose, nor any liability arising out of any
legal relationship whatsoever, can be inferred either
from this information, or from any written recom-
mendations, or from any other advice offered. The
user of the product must test the product’s suitability
for the intended application and purpose. Sika re-
serves the right to change the properties of its
products. The proprietary rights of third parties must
be observed. All orders are accepted subject to our
current terms of sale and delivery. Users must always
refer to the most recent issue of the local Product Data
Sheet for the product concerned, copies of which will
be supplied on request.