Project (Chemistry) : Preparation of Potash Alum

Preparation of Potash Alum
PROJECT (CHEMISTRY)
To prepare potash alum from aluminium scrap
Year 2009 - 2010
Chemistry Project
Name of Institute:…………………………………..
This is to certify that Mr. ………………….of

class twelve, of ……………………………………….has
satisfactorily completed the project in Chemistry for the
AISSCE as prescribed by CBSE in the year 2009-2010.
Date :
Roll No. :……………
Signature of Internal Signature of External

Examiner Examiner
Chemistry Project
__________________ __________________
Acknowledgement
I thank my chemistry teacher

……………………….. and ……………………………
for their guidance and support. I also thank my Principal
…………………………. I would also like to thank my
parents and my sister for encouraging me during this
course of this project. Finally I would like to thank CBSE
for giving me this opportunity to undertake this project.
Chemistry Project
Introduction
Aluminium because of its low density, high
tensile strength and resistance and resistance to corrosion
is widely used for the manufacture of aeroplanes,
automobiles lawn furniture as well as for aluminium cans.
Being good conductor of electricity it is used for
transmission of electricity. Aluminium is also used for
making utensils. The recycling of aluminium cans and
other aluminium products is a very positive contribution
to saving our natural resources. Most of the recycled
aluminium is melted and recast into other aluminium
metal products or used in the production of various
aluminium compounds, the most common of which are
the alums. Alums are double sulphates having general
formula
X2SO4.M2(SO4)3.24H2O
Chemistry Project
Introduction
Some important alums and their names are given below:
K2SO4.Al2(SO4)3.24H2O - Potash Alum
Na2SO4.Al2(SO4)3.24H2O - Soda Alum
K2SO4.Cr2(SO4)3.24H2O - Chrome Alum
(NH)2SO4.Fe2(SO4)3.24H2O - Ferric Alum
Potash alum is used in papermaking, in fire

extinguishers in food stuffs and in purification of water
soda alum used in baking powders and chrome alum is
used in tanning leather and water proofing fabrics.
Chemistry Project
Chemistry Project
Aim
To prepare potash alum from aluminium scrap
Chemistry Project
Requirements
 250 ml flask
 Funnel
 Beaker
 Scrap aluminium or cola can
 Potassium hydroxide solution (KOH)
 6 M Sulphuric Acid (H2SO4)
 Water Bath
 Ethanol
Chemistry Project
Theory
Aluminum metal is treated with hot aqueous KOH
solution. Aluminium dissolves as potassium aluminate,
KAl(OH)4, salt.
2Al(s) + 2KOH(aq) + 6H2O(l)  2KAl(OH)4 (aq) + 3H2
Potassium aluminate solution on treatment with dil.

Sulphuric acid first gives precipitate Al(OH)3, which
dissolves on addition of small excess of H2SO4 and
heating.
2KOH(aq) + H2SO4(aq)  2Al(OH)3 (s) + K2SO4(aq) + 2H2O(l)
2Al(OH)3 (s) + 3 H2SO4(aq)  Al2(SO4)3(aq) +6H2O(l)
The resulting solution is concentrated to near saturation

and cooled. On cooling crystals of potash alum
crystallize out.
K2SO4(aq) + Al2(SO4)3(aq) + 24H2O(l)  K2SO4.Al2(SO4)3. 24H2O(s)
Chemistry Project
Reactions
Reactions
2Al(s) + 2KOH(aq) + 6H2O(l)  2KAl(OH)4 (aq) + 3H2

2Al(OH)3 (s) + 3 H2SO4(aq)  Al2(SO4)3(aq) +6H2O(l)
2KOH(aq) + H2SO4(aq)  2Al(OH)3 (s) + K2SO4(aq) + 2H2O(l)
Procedure
Chemistry Project
 Clean a small piece of scrap aluminium with steel

wool and cut it into very small pieces. Aluminium
foil may be taken instead of scrap aluminium.
 Put the small pieces of scrap aluminium or

aluminium foil(about 1.00g) into a conical flask and
add about 50 ml of 4 M KOH solution to dissolve
the aluminium.
 The flask may be heated gently in order to facilitate

dissolution. Since during this step hydrogen gas is
evolved this step must be done in a well ventilated
area.
 Continue heating until all of the aluminium reacts.
 Filter the solution to remove any insoluble

impurities and reduce the volume to about 25 ml by
heating.
Procedure
Chemistry Project
 Allow the filtrate to cool. Now add slowly 6 M

H2SO4 until insoluble Al(OH)3 just forms in the
solution.
 Gently heat the mixture until the Al(OH)3

precipitate dissolves.
 Cool the resulting solution in an ice-bath for about

30 minutes whereby alum crystals should separate
out. For better results the solution may be left
overnight for crystallization to continue.
 In case crystals do not form the solution may be

further concentrated and cooled again.
 Filter the crystals from the solution using vacuum

pump, wash the crystals with 50/50 ethanol-water
mixture.
Procedure
Chemistry Project
 Continue applying the vacuum until the crystals

appear dry.
 Determine the mass of alum crystals.
Chemistry Project
Observations
Mass of aluminium metal =…………….g
Mass of potash alum =…………….g
Theoretical yield of potash alum =……………g
Percent yield =……………%
Result
Chemistry Project
Potash alum was prepared from aluminium

scrap.
Bibliography
Chemistry Project
 Wikipedia,
http://en.wikipedia.org/wiki/alum
 Chemicalland.com
 books.google.co.in
Chemistry Project

Project (Chemistry) : Preparation of Potash Alum

Uploaded by

Copyright:

Available Formats

Project (Chemistry) : Preparation of Potash Alum

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Project (Chemistry) : Preparation of Potash Alum

Uploaded by

Copyright:

Available Formats

Preparation of Potash Alum

To prepare potash alum from aluminium scrap

Year 2009 - 2010

This is to certify that Mr. ………………….of

Roll No. :……………

Signature of Internal Signature of External

I thank my chemistry teacher

Some important alums and their names are given below:

K2SO4.Al2(SO4)3.24H2O - Potash Alum

Na2SO4.Al2(SO4)3.24H2O - Soda Alum

K2SO4.Cr2(SO4)3.24H2O - Chrome Alum

(NH)2SO4.Fe2(SO4)3.24H2O - Ferric Alum

Potash alum is used in papermaking, in fire

To prepare potash alum from aluminium scrap

 Scrap aluminium or cola can

 Potassium hydroxide solution (KOH)

 6 M Sulphuric Acid (H2SO4)

2Al(s) + 2KOH(aq) + 6H2O(l)  2KAl(OH)4 (aq) + 3H2

Potassium aluminate solution on treatment with dil.

2KOH(aq) + H2SO4(aq)  2Al(OH)3 (s) + K2SO4(aq) + 2H2O(l)

2Al(OH)3 (s) + 3 H2SO4(aq)  Al2(SO4)3(aq) +6H2O(l)

The resulting solution is concentrated to near saturation

K2SO4(aq) + Al2(SO4)3(aq) + 24H2O(l)  K2SO4.Al2(SO4)3. 24H2O(s)

2Al(s) + 2KOH(aq) + 6H2O(l)  2KAl(OH)4 (aq) + 3H2

 Clean a small piece of scrap aluminium with steel

 Put the small pieces of scrap aluminium or

 The flask may be heated gently in order to facilitate

 Continue heating until all of the aluminium reacts.

 Filter the solution to remove any insoluble

 Allow the filtrate to cool. Now add slowly 6 M

 Gently heat the mixture until the Al(OH)3

 Cool the resulting solution in an ice-bath for about

 In case crystals do not form the solution may be

 Filter the crystals from the solution using vacuum

 Continue applying the vacuum until the crystals

 Determine the mass of alum crystals.

Mass of aluminium metal =…………….g

Mass of potash alum =…………….g

Theoretical yield of potash alum =……………g

Percent yield =……………%

Potash alum was prepared from aluminium