Journal of Civil Engineering and Construction Technology Experimental and

analytical investigation of ferrocement water pipe

Article · May 2013

DOI: 10.5897/JCECT2013.0230

CITATION READS

1 10,961

3 authors:

Yousry Bayoumy Shaheen Boshra Eltaly

Menoufia University Menoufia University
75 PUBLICATIONS   210 CITATIONS    40 PUBLICATIONS   110 CITATIONS   

SEE PROFILE SEE PROFILE

Kameel Mungrue
University of the West Indies, St. Augustine
53 PUBLICATIONS   276 CITATIONS   

SEE PROFILE

Some of the authors of this publication are also working on these related projects:

Alternative Supplementary Cementitous Materials View project

Single Tertiary centre retrospective cohort View project

All content following this page was uploaded by Boshra Eltaly on 11 September 2018.

The user has requested enhancement of the downloaded file.

 Vol. 4(4), pp. 157-167, May, 2013
DOI 10.5897/JCECT2013.0230
Journal of Civil Engineering and Construction
ISSN 1996-0816 © 2013 Academic Journals Technology
http://www.academicjournals.org/JCECT

Full Length Research Paper

Experimental and analytical investigation of

ferrocement water pipe
Y. B. I. Shaheen, B. Eltaly* and M. Kameel
Civil Engineering Department, Faculty of Engineering, Minufiya University, Egypt.
Accepted 11 April, 2013

The main objective of this research is to investigate the possibility of using ferrocement concrete in
constructing water supply pipe. The current work presents the comparison between the performance of
ferrocement pipe and reinforcement concrete pipe under static load as starting step to study the
performance of this type of pipe under impact load. The current paper presents an experimental models
of ferrocement and concrete water pipes and their numerical models using the finite element method.
Finite element models were developed to simulate the behavior of the pipes through nonlinear
response and up to failure, using the ANSYS Package. Additionally, the comparison between the
theoretical and experimental models results is presented and discussed.

Key words: Ferrocment, water pipe, nonlinear analysis, finite element analysis.

INTRODUCTION

Ferrocement is type of reinforcement concrete. It axial load capacity and the axial stiffness of repairing
commonly composed of hydraulic cement mortar reinforced concrete column compared to the control
reinforced with closely spaced layers of continuous and columns. Kaish et al. (2011) and Xiong (2004)
relatively small size wire mesh. The mesh may be made investigated the possibility of using ferrocement jacket in
of metallic or other suitable materials (Blake, 2001). It is strengthening of square reinforced concrete short
low cost, durable, weather-resistance, lightweight and column. Their results indicated that using this method of
particularly its versatility comparing to the reinforced strengthening improved the column behavior. Various
concrete (Ali, 1995). Robles-Austriaco et al. (1981) researches were carried out to study ferrocement
indicated that ferrocement is an excellent material for elements (beam, slabs and column) to investigate its
housing construction. Also Al-Kubaisy and Jumaat (2000) behavior under applied loads up to failure. Ibrahim (2011)
studied the possibility of using ferrocement cover in the and Hago et al. (2005) studied the ultimate capacity of
tension zone of reinforced concrete slab. wired mesh-reinforced cementations slabs and simply
This material is also used in repairing the reinforcement supported slab panels; respectively with different types of
element such as beams, slabs or walls (Fahmy et al. reinforced wired mesh. Nassif and Najm (2004)
1997; Elavenil and Chandrasekar, 2007; Jumaat, 2006). investigated an experimental and a theoretical model for
Mourad and Shang (2012) used ferrocement jacket in ferrocement–concrete composite beams. Various types
repairing reinforced concrete column. Their test results of reinforced concrete beam overlaid on a thin section of
indicated that using the ferrecement jacket increases the ferrocement (cement paste and wire mesh) were tested

*Corresponding author. E-mail: [email protected]

158 J. Civ. Eng. Constr. Technol.

a-Polypropylene fiber b- Expanded steel mesh c- Welded steel mesh

Figure 1. Reinforcement steel meshes and fibers used.

up to failure under two-point loading system. Their results reinforcement system. Two types of steel wire meshes (welded wire
showed that the proposed composite beam has good mesh and expanded metal mesh) as shown in Figure 1 were used
in the reinforcement of the ferrocement pipes. The two types are
ductility, cracking strength and ultimate capacity more locally produced and available in the Egyptian market on
than reinforced concrete beam. Shannag and Ziyyad commercial scale. The expanded wire mesh type with 1.5 × 2.1 mm
(2007) increased the strength of ferrocement mortar by diameter and 19.7 × 43.7 mm grid size and welded wire mesh type
adding discontinuous fibers glass. Shannag and Mourad with 0.72 mm diameter and 12 × 12 mm grid size were used. In the
(2012) developed high strength mortar matrices contain five types of pipes, the weight of reinforcement was constant as
various combinations of silica fume and fly ash, and shown in Table 1.
provide a good balance between workability and strength.
Chandrasekhar et al. (2006) studied the shear strength of Properties of the used materials
simply supported ferrocement rectangular plates. In their
study, tests on ferrocement elements with different layers The sieve analysis was done on the used sand for the ferrocement
of mesh were conducted. They observed that increase in mortar mix and its results are presented in Table 2 was done on the
used aggregate for the concrete mix. Also properties of both of the
the number of layers of the mesh reinforcement
used sand and aggregate satisfied the Egyptian Standard
increases the shear capacity of the plate. An Specifications (E.S.S.) requirements (2007). The chemical and
experimental study on simply supported ferrocement physical properties of the cement were analyzed according to
plates was conducted by Ibrahim (2011). In his study, E.S.S. (2007) for concrete works. Fresh drinking water and free
flexural steel was designed to preclude failure in modes from impurities was used for mixing and curing of the test
due to shear other than flexure. A good agreement specimens. Fiber, silica fume with a powder form and a light-gray
color and its chemical composition is given in Table 3 and super
between the classical shear equations prediction and his plasticizer EDECRETE DM2, complies with ASTM C494-86, with a
experimental results is obtained water supply pipe is very specific weight of 1.05 at 20°C were used to increase the strength
important structure that is used to supply water to and the workability of the mortar mix.
individual buildings. Supply pipes should be strength and Six ferrocement mortar mixes were designed and tested under
durable. There are several types of these pipes according compression load to select the best proportions of the ferrocement
to their constructed material; metallic pipes, cement pipes constituent’s materials. The selecting mortar mix based on
achieving the maximum compressive strength and the moderate
and plastic pipes. The main objective of this study is workability has a sand/cement ratio and water/cement ratio of 2 and
studying the performance of ferrocement pipe and 0.35; respectively and fiber with ratio of 900 g/m3 of the mortar
reinforcement pipe under line load. Also this research matrix and silica fume were added as indicated in Table 4.
presents a theoretical finite element model using ANSYS Compression and tensile tests were carried out for the hardened
(2006) program and a comparison between the mortar according to E.S.S (2007). From the tests results, the
compressive stress (Fcu) is considered as 33.4 and 47 MPa after 7
experimental and theoretical results.
and 28 days; respectively and the tensile stress is considered as
3.6 MPa after 28 days. The modulus of elasticity of concrete and
stress-strain curve were employed the Egyptian Code for design
EXPERIMENTAL MODEL and construction the reinforced concrete structures (2001) and
Kaewunruen and Remennikov work (2006). The modulus of
Five different types of pipes with 300 and 30 mm internal diameter elasticity of concrete (Ec) can be calculated from equation 1 by
and thickness; respectively was cast and tested under static load in considering the compressive strength of concrete at 28 days (Fcu).
reinforcement laboratory in Faculty of Engineering-Minufiya The multi-linear isotropic stress-strain curve for the concrete can be
University. The first type is reinforcement concrete pipe and the computed by Equation 2. The stress-strain curve for the used
anther types are ferrocement pipes with different in the type of ferrocement mortar is presented in Figure 2.
 Shaheen et al. 159

Table 1. Reinforcement system of the tested pipes.

Weight of
Model No. Type of reinforcement Mortar
Steel (kg/m)
RCP (6 Bars + 6 Stirrups) Ø 6 mm Conc.
FP1 (6 Bars + 6 Stirrups) Ø 6 mm Ferro.
FP2 One layer of welded metal + One expanded metal Ferro. 3.0
FP3 Two stirrups Ø6 mm + One layer of expanded metal Ferro.
FP4 Three stirrups Ø6 mm + Three layers of welded metal Ferro.

Table 2. Sieve analysis results for the used sand.

2 Fcu
ε 0= (3)
Sieve size (mm) % Passing by weight Limits of (E.E.S.) Ec
4.75 100 100
2.83 95 100-85 Where, f is stress at any strain (ε) and ε0 is the strain at the ultimate
compressive strength at 28 days and can be found from Equation
1.4 79 100-75 (3).
0.7 68 80-60 The control pipe was reinforced with conventionally mild steel
0.35 17 30-10 and has an ordinary concrete mixture. This mixture is the same as
0.15 2 10-0 that was used in Egyptian pipes factories. The conventionally
mixture was consisted of 0.8 gravel, 0.4 m3 sand, 350 kg cement
and 160 L of water. Twelve cubes 100 × 100 × 100 mm were cast
and tested according to E.S.S (2007) to determine the compressive
Table 3. Chemical composition of silica fume. strength of the mixture after 7, and 28. Table 5 shows the
compressive strength and the tensile splitting strength of the
concrete mixture. Figure 3 presents the stress-strain curve for the
Chemical composition Weight % used concrete mixture. Three samples of each type of the steel
SiO2 92 - 94 meshes were tested using the Universal Testing Machine as shown
Carbon 3-5 in Figure 4. The specification and the mechanical properties of the
steel meshes are illustrated and shown in Table 6. For the mild
Fe2O3 0.1 - 0.5
steel, the modulus of elasticity and yield strength were considered
CaO 0.1 - 0.15 as 210 GPa and 2240 MPa; respectively.
AL2O3 0.2 - 0.3
MgO 0.1 - 0.2
Testing of pipes
MnO 0.008
K2O 0.1
A Gibson form was constructed with an outside diameter equal 300
Na2O 0.1 mm and has top and bottom cylinder to control the thickness of
pipes. The casting processes were done as following steps. At the
beginning, the reinforcements were prepared by their required
diameters. Then they were put in the forms in their position (in the
Table 4. Consisted material of the ferrocement mixture. middle of the section) as shown in Figure 5. At the second, the
concrete was casted by plastering as shown in Figure 6. Finally, the
Material Ratio related to cement final face was finished. Within 24 h the specimens were turned
upside down to allow the sides to harden. The specimens were
Cement 0.9
stored in the laboratory atmosphere until testing after 28 days. The
Silica fume 0.1 specimens were covered using a wet cloth while water was
Sand 2 sprinkled twice a day for curing. The faces of each specimen were
Fiber 900 g/m3 painted in white to facilitate crack detection before the testing. The
specimen was placed in the testing position on steel frame as
Water 0.35 shown in Figure 7. Two rigid steel beams were used under pipe as
Adecrete DM2 1% supports and another one was used up to pipe under the
increasable load to distribute the concentrated load along pipe.

E c = 139140 .22 F cu (1) THEORETICAL MODEL

In the current theoretical work, finite element ANSYS program

E cε (2006) was used to study theoretically the behavior of the tested
f = pipes up to failure. Solid65 element was used in the modeling of
(
1+ ε ε 0
)2 (2)
ferrocement and concrete mix (Hoque, 2006; Singh, 2006; Aboul-
Anen et al., 2009). The Solid 65 element is defined by eight nodes.
160 J. Civ. Eng. Constr. Technol.

50
45
40
35
)a
P 30
M
( 25
ss
e 20
rt
S 15
10
5
0
0 0.0005 0.001 0.0015 0.002 0.0025 0.003
Strain
Figure 2. Stress-strain curve of the selected ferrocement mortar.

Table 5. Properties of the used concrete mixture.

Age Compressive Tensile splitting Modulus of

(days) strength (MPa) strength (MPa) elasticity (GPa)
7 17 1.9 ---
28 28.5 2.4 23.5

Each node has three degrees of freedom (translations in the nodal

x, y, and z directions). Link 8 element was used to represent steel
bar and stirrups. It has three degrees of freedom at each node
(translations in the nodal x, y, and z directions). Theoretical model
is indicated in Figure 8.

RESULTS AND DISCUSSION

In this part, the results of the experimental program are

presented and discussed. The load at the first crack and
the failure load are shown in Table 7. The experimental
detected crack patterns of the tested pipes are shown in
Figure 9. The experimental relationship between the total
applied load and the deflection of the five types of pipes
are shown in Figure 10. From this table and the two
figures, it can be seen that the four ferrocement pipes
failed at total load greater than the reinforced pipes. Also
it can be concluded that the fifth type of pipes (FP4) failed
at greatest failure load.
The comparison between the results of the
experimental program and the current theoretical model
Figure 3. Testing of steel mesh by using Instron Testing are exposed and discussed in this part of the work. The
Machine. total applied load - deflection curves of the five types of
 Shaheen et al. 161

30

25

20
Stress (MPa)

15

10

0
0 0.0005 0.001 0.0015 0.002 0.0025 0.003
Strain
Figure 4. Stress-strain curve of the used concrete.

Table 6. Mechanical properties of the used steel meshes.

Modulusof
Mesh type Fy (MPa) Fu (MPa)
elasticity (GPa)
Expanded metal mesh 250 350 120
Welded wire mesh 400 600 170

Figure 5. Steel in the form. Figure 6. Casting the pipe by plastering.

pipes that were obtained from the experimental work and ECONOMIC ASSESSMENT OF FERROCEMENT
the theoretical models are indicated in Figures 11 to 15.
From these curves, it can be concluded that the response It can be observed that the reinforcement represents the
obtained from theoretical work was quite similar to the major cost factor in ferrocement, followed by the labor
actual response of the experimental results, especially in cost. Labor cost can be reduced through efficient
the initial region. planning and mechanized production processes. High
162 J. Civ. Eng. Constr. Technol.

Figure 7. Pipe testing and loading system.

Figure 8. Theoretical model.

Table 7. Experimental first cracking and failure loads. (i) Low consumption of materials.
(ii) It can take any shape most of the times without
First cracking Failure load using form working.
Model No.
load (KN) (KN) (iii) When worked correctly, it is practically
RCP 10 16 impermeable.
FP1 14 20
FP2 16 24 a) Good behavior to cracking.
FP3 15 22 b) Easy to be repaired.
FP4 18 32 c) It can be prefabricated.

It is interesting to note from Table 8 that there is high cost

saving by employing ferrocement pipes for all developed
ferrocemen pipes, FP1, FP2, FP3 and FP4 compared
cost of the steel mesh is mostly due to the cost of with conventional reinforcement pipe, RCP. The average
production of the mesh system itself and to the limited cost saving of ferrocement pipes is approximately equal
demand. With increasing market, steel mesh system can 25% compared with that of conventional reinforced
be produced more efficiently and at a lower cost. concrete pipe. The ultimate strength of pipe FP4 is
Therefore, resulting in a remarkable reduction of the approximately twice of that of reinforced control pipe with
ferrocement cost among the more significant qualities of significant deformation characteristics and cracking
the ferrocement mentioned earlier: behavior.
 Shaheen et al. 163

Figure 9. cracking patterns of tested pipes.

Figure 10. Experimental load-deflection curve.

164 J. Civ. Eng. Constr. Technol.

Figure 11. Experimental and theoretical load-deflection curve of RCPP.

Figure 12. Experimental and theoretical load-deflection curve of FP1.

 Shaheen et al. 165

Figure 12. Experimental and theoretical load-deflection curve of FP1.

Figure 13. Experimental and theoretical load-deflection curve of FP2

166 J. Civ. Eng. Constr. Technol.

Figure 14. Experimental and theoretical load-deflection curve of FP3.

Figure 15. Experimental and theoretical load-deflection curve of FP4.

 Shaheen et al. 167

Table 8. Cost comparison and strengths of developed concrete and ferrocement pipes.

Model Cost of Cost of Total cost First crack Ultimate

Type of reinforcement
No. mortar matrix reinforcement Egyptian pound load (KN) load (KN)
RCP (6 Bars + 6 Stirrups) Ø 6 mm 20 (concrete) 21.3 41.3 10 16
FP1 (6 Bars + 6 Stirrups) Ø 6 mm 14.6 21.30 35.9 14 20
FP2 One layer of welded metal + One expanded metal 14.6 14 28.6 16 24
FP3 Two stirrups Ø6 mm + One layer of expanded metal 14.6 12.1 26.7 15 22
FP4 Three stirrups Ø6 mm + Three layers of welded metal 14.6 19.06 33.66 18 32

Conclusions Fahmy EH, Shaheen YB, Korany YS (1997). “Use of Ferrocement

Laminates for Repairing Reinforced Concrete Slabs.” J.
Ferrocement 27(3):219-232.
The main goal of the current research is studying the Hago AW, Al-Jabri KS, Alnuaimi AS, Al-Moqbali H, Al-Kubaisy MA
ability of using ferrocement concrete in design and (2005). “Ultimate and Service Behavior of Ferrocement Roof Slab
construction of the water supply pipes. Four ferrocment Panels.” Constr. Build. Mater. 19:31–37.
pipes that were different in the reinforcement system Hoque MM (2006). “3D Nonlinear Mixed Finite-element Analysis of
were casted and tested up to failure and their results RC Beams and Plates with and without FRP Reinforcement.” M.
were compared with anther casted and tested reinforced Sc. Thesis, University of Manitoba, Winnipeg, Manitoba, Canada.
Ibrahim HM (2011). “Experimental Investigation of Ultimate
concrete pipe. Also theoretical models were developed Capacity of Wired Mesh-ReinforcedCementitious Slabs.” Constr.
using ANSYS program and their results were compared Build. Mater. 25:251–259.
with the experimental results. From the current results, it Ibrahim HM (2011). “Shear Capacity of Ferrocement Plates in
can be concluded that the investigation finite element Flexure.” Eng. Struct. 33:1680–1686.
models for the five types of pipes give accurate results in Jumaat M, Alam A (2006). “Flexural Strengthening of Reinforced
Concrete Beams Using Ferrocement Laminate with Skeletal
comparison with the experimental results. Furthermore it
Bars.” J. Appl. Sci. Res. 2(9):559-566.
can be clearly seen that the ferrocement pipes behaves Kaewunruen S, Remennikov A (2006). “Nonlinear Finite Element
under the applied load better than the reinforced pipes. Modeling of Railway Prestressed Concrete Sleeper.” The Tenth
Also it can be concluded that the fifth type of pipes (FP4) East Asia-Pacific Conference on Structural Engineering and
that was reinforced with welded wire meshes collapsed at Construction, Bangkok, Thailand, pp. 323-328.
greatest failure load. Kaish MA, Alam AB, Jamil MR, Zain MF, Wahed MA (2012).
“Improved Ferrocement Jacketing for Restrengthening of Square
Ferrocement pipes were produced with high strength, RC Short Column.” Constr. Build. Mater. 36:228–237.
crack resistance and 25% economic saving could be Mourad SM, Shannag MJ (2012). “Repair and Strengthening of
useful for developed and developing countries alike. Reinforced Concrete Square Columns Using Ferrocement
Jackets.” Cem. Concrete Compos. 34:288–294.
Nassif HH, Najm H (2004). “Experimental and Analytical
REFERENCES Investigation of Ferrocement–Concrete Composite Beams.”
Cem. Concrete Compos. 26:787-796.
Aboul-Anen B, El-Shafey A, El-Shami M (2009). “Experimental and Shannag MJ, Mourad SM (2012). “Flowable High Strength
Analytical Model of Ferrocement Slabs.” Int. J. Recent Trends Cementitious Matrices for Ferrocement Applications.” Constr.
Eng. IJJCE, Oulu, Finland. Build. Mater. 36:933–939.
Ali AA (1995). “Applications of Ferrocement as a Low Cost Shannag J, Ziyyad T (2007). “Flexural Response of Ferrocement
Construction Material in Malaysia.” J. Ferrocement 25(2):123- with Fibrous Cementitious Matrices.” Constr. Build. Mater.
128. 21:1198–1205.
Al-Kubaisy MA, Jumaat MZ (2000). “Flexural Behavior of Singh G (2006). “Finite Element Analysis of Reinforced Concrete
Reinforced Concrete Slabs with Ferrocement Tension Zone Shear Walls.” M. Sc. Thesis, Deemed University, India.
Cover.” Constr. Build. Mater. 14:245-252. Robles-Austriaco L, Pama RP, Valls J (1981). “Ferrocement an
ANSYS (2006). “Help and Manual.” 11th Ed., ANSYS Inc., PA, USA. Innovative Technology for Housing.” J. Ferrocement 11(1):23-47.
Blake LS (2001). “Civil Engineer's Reference Book.” Butterworth- Xiong GJ, Wu XY, Li FF, Yan Z (2011). “Load Carrying Capacity
Heinemann, Reed Educational and Professional Publishing Ltd, and Ductility of Circular Concrete Columns Confined by
Oxford. Ferrocement Including Steel Bars.” Constr. Build. Mater.
Chandrasekhar T, Gunneswara TD, Ramana NV (2006). “An 25:2263–2268.
Appraisal of the Shear Resistance of Ferrocement Elements.”
Asian J. Civ. Eng. Build. Hous. 7(6):591-602.
Elavenil S, Chandrasekar V (2007). “Analysis of Reinforced
Concrete Beams Strengthened with Ferrocement.” Int. J. Appl.
Eng. Res. 2(3):431-440.