M5005L is a narrow MWD HDPE produced using Spherilene Technology. It is recommended for injection molding of heavy duty crates and industrial products as well as extrusion compression molded caps. The precise control of morphology and MWD during polymerization gives it superior processability and improved performance properties over conventional HDPE grades. It has a melt flow index of 4.5 g/10 min, a density of 0.950 g/cm3, and a tensile strength at yield of 22 MPa.
M5005L is a narrow MWD HDPE produced using Spherilene Technology. It is recommended for injection molding of heavy duty crates and industrial products as well as extrusion compression molded caps. The precise control of morphology and MWD during polymerization gives it superior processability and improved performance properties over conventional HDPE grades. It has a melt flow index of 4.5 g/10 min, a density of 0.950 g/cm3, and a tensile strength at yield of 22 MPa.
M5005L is a narrow MWD HDPE produced using Spherilene Technology. It is recommended for injection molding of heavy duty crates and industrial products as well as extrusion compression molded caps. The precise control of morphology and MWD during polymerization gives it superior processability and improved performance properties over conventional HDPE grades. It has a melt flow index of 4.5 g/10 min, a density of 0.950 g/cm3, and a tensile strength at yield of 22 MPa.
M5005L is a narrow MWD HDPE produced using Spherilene Technology. It is recommended for injection molding of heavy duty crates and industrial products as well as extrusion compression molded caps. The precise control of morphology and MWD during polymerization gives it superior processability and improved performance properties over conventional HDPE grades. It has a melt flow index of 4.5 g/10 min, a density of 0.950 g/cm3, and a tensile strength at yield of 22 MPa.
M5005L is a Narrow MWD HDPE produced by Spherilene Technology
M5005L is recommended for injection molding of heavy duty Crates, Industrial products and for injection molded as well as extrusion compression molded caps for packaged drinking water
The precise control of morphology & MWD during polymerization confers superior processability & improved performance properties compared to conventional HDPE grades
Property Test Method Unit Value
Melt Flow Index (2.16 kg, 190°C) ASTM D1238 g/10 min 4.5 3 Density (23°C) ASTM D1505 g/cm 0.950
Physical Property
Tensile Strength at Yield MPa 22
ASTM D638 Tensile Strength at Break MPa 32 (50 mm/min) Elongation at Break % 950
Heat Deflection Temperature (0.455 MPa) ASTM D648 °C 78
DSC Melting Temperature ASTM D3418 °C 132
Suggested Processing Conditions
Barrel Temperature °C 185 – 235
Nozzle Temperature °C 235
* Halene H is the registered trademark of High Density Polyethylene of HPL
Mechanical Properties are on Injection Molded test specimens prepared as per ASTM D4101
The information & data presented herein are typical values and should not be construed as specification. No warranty or guarantee expressed or implied is made regarding performance. The information & data are subject to change without prior intimation based on research & development work undertaken by the company.