Klingersil C-4400: Tests and Certifications

This document provides information on the KLINGERSIL C-4400 material, which is a high quality non-asbestos grade gasket material based on aramid fiber with nitrile rubber binder. It lists the material's certifications and tests, availability in sheet and reinforced forms, general properties like resistance to oils and fuels, and typical specifications for a 2.0mm thick sheet like compressibility, stress relaxation, thickness increase after fluid immersion, and thermal conductivity. An application guidelines chart shows the material's suitability across a range of pressures and temperatures.

Uploaded by

moh rageh
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
140 views2 pages

Klingersil C-4400: Tests and Certifications

This document provides information on the KLINGERSIL C-4400 material, which is a high quality non-asbestos grade gasket material based on aramid fiber with nitrile rubber binder. It lists the material's certifications and tests, availability in sheet and reinforced forms, general properties like resistance to oils and fuels, and typical specifications for a 2.0mm thick sheet like compressibility, stress relaxation, thickness increase after fluid immersion, and thermal conductivity. An application guidelines chart shows the material's suitability across a range of pressures and temperatures.

Uploaded by

moh rageh
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

 

KLINGERSIL
C-4400

High quality non-asbestos grade based TESTS AND CERTIFICATIONS


on aramid fibre with nitrile rubber binder.
A general purpose material for many » BS 7531 Grade Y
industrial-sealing applications. » ÖVGW Reg.No. G 1.912
» Firesafe ISO 10497
The Klinger group has been recognised » DIN-DVGW
as the market leader in gaskets and » BAM -tested
sealing for over a century. Our research » Germanischer Lloyd
and development laboratories have » TA-Luft (Clean Air)
investigated over 250 different fibre » Elastomer-Guideline
forms in the search for asbestos free
alternatives. The search has resulted in AVAILABILITY
a range of high quality and high
performance asbestos free materials » Sheeting (m): 2.0 x 1.5*, 4.0 x 1.5
that have been proven in service » Thickness (mm): 0.25, 0.4, 0.5, 0.75, 1.0, 1.5, 2.0, 2.5, 3.0

GENERAL PROPERTIES * - Denotes standard sheet size


» Good resistance to oils, fuels,
hydrocarbons Also available with re-inforcements:
» Good creep resistance KLINGERsil C-4408, mild steel mesh
» Low leakage KLINGERsil C-4409, expanded mild steel
» Very successful in internal
combustion engine applications
» 3xA anti-stick finish on both sides

 
Issue: 01 - 28/08/19
 
APPLICATION GUIDELINES

100
KLINGERSIL C-4400
90
80
Pressure (bar)

Caution: May be suitable but


70 essential that you refer to Klinger for
60 advice
50 Usually Satisfactory, but suggest you
40 refer to Klinger for advice
30
20 Usually Satisfactory to Use Without
10 Reference
0 NOTE: Chemical Compatibility should
-200

-50

be considered in every case.


100

200

350

Temperature (˚C)
TYPICAL SPECIFICATIONS
(Typical Values for 2.0mm thick material)

PROPERTIES CONDITIONS VALUES


Compressibility ASTM F 36 J 11 %
Recovery ASTM F 36 J 55 %
50MPa, 16h/175°C 37MPa
Stress relaxation DIN 52913
50MPa, 16h/300°C 25MPa
Stress relaxation BS 7531 40MPa 16h/300˚C 25MPa
Klinger cold/hot compression, Thickness decrease 23°C 10 %
50MPa Thickness decrease at 300°C 20 %
Tightness DIN 28090-2 0.02mg/s.m
Thickness increase after fluid Oil IRM 903 5h/150°C 3%
immersion ASTM F 146 Fuel B:5h/23°C 5%
Density 1.6g/cm3
Average surface resistance ΡO 1.4x1012 Ω
Average specific volume resistance ΡD 1.2x1012 Ω cm
Average dielectric strength 21.6 kV/mm
Average power factor 1kHz,ca. 2mm thick 0.075 tan δ
Average dielectric constant 1kHz,ca. 2mm thick 7.7 εr
Thermal conductivity λ 0.40-0.42W/mK

 