    API 571 Study Guide-Practice Questions For API 570 Exam - Caustic Stress Corrosion Cracking - Caustic Embrittlement (4.5.3)

    Uploaded by

    NIMA
    The document contains practice questions for an exam on caustic stress corrosion cracking and caustic embrittlement. It includes 10 multiple choice questions about factors that contribute to caustic stress corrosion cracking in equipment, how to reduce the likelihood of it, and temperature recommendations for stress relieving different carbon steel caustic systems based on NaOH concentration. Nickel alloys are recommended above 205°F for a 30% NaOH solution to prevent caustic stress corrosion cracking.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    API 571 Study Guide-Practice Questions For API 570 Exam - Caustic Stress Corrosion Cracking - Caustic Embrittlement (4.5.3)

    Uploaded by

    NIMA
    43 views5 pages
    The document contains practice questions for an exam on caustic stress corrosion cracking and caustic embrittlement. It includes 10 multiple choice questions about factors that contribute to caustic stress corrosion cracking in equipment, how to reduce the likelihood of it, and temperature recommendations for stress relieving different carbon steel caustic systems based on NaOH concentration. Nickel alloys are recommended above 205°F for a 30% NaOH solution to prevent caustic stress corrosion cracking.

    Original Description:

    API 570-3

    Original Title

    API 570 326-10

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document contains practice questions for an exam on caustic stress corrosion cracking and caustic embrittlement. It includes 10 multiple choice questions about factors that contribute to caustic stress corrosion cracking in equipment, how to reduce the likelihood of it, and temperature recommendations for stress relieving different carbon steel caustic systems based on NaOH concentration. Nickel alloys are recommended above 205°F for a 30% NaOH solution to prevent caustic stress corrosion cracking.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    43 views5 pages

    API 571 Study Guide-Practice Questions For API 570 Exam - Caustic Stress Corrosion Cracking - Caustic Embrittlement (4.5.3)

    Uploaded by

    NIMA
    The document contains practice questions for an exam on caustic stress corrosion cracking and caustic embrittlement. It includes 10 multiple choice questions about factors that contribute to caustic stress corrosion cracking in equipment, how to reduce the likelihood of it, and temperature recommendations for stress relieving different carbon steel caustic systems based on NaOH concentration. Nickel alloys are recommended above 205°F for a 30% NaOH solution to prevent caustic stress corrosion cracking.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 5

    5/22/2021 API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stress Corrosion Cracking-

    racking- Caustic Embrittlement (4.5.3) Flashcard…

    API 571 Study Guide- Practice Questions for API 570


    Exam- Caustic Stress Corrosion Cracking- Caustic
    Embrittlement (4.5.3)
    Terms in this set (10)

    Caustic Embrittlement A
    can cause cracks that
    normally initiate:
    A. On the surface
    adjacent to welds.
    B. At the mid-wall
    adjacent to welds.
    C. On the surface in the
    base metal.
    D. At the mid-wall in the
    base metal.

    Which alloys are more C


    resistant to Caustic
    Stress Corrosion
    Cracking?
    A. Chromes
    B. Ferrites
    C. Nickels
    D. Sulfides

    API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stre...
    https://quizlet.com/479824585/api-571-study-guide-practice-questions-for-api-570-exam-caustic-stress-corrosion-cracking-caustic-embrittlement-453-fl… 1/5
    5/22/2021 API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stress Corrosion Cracking- Caustic Embrittlement (4.5.3) Flashcard…

    Which of the following E


    is not a factor in the
    Caustic Stress
    Corrosion Cracking?
    A. Caustic strength
    B. Material
    C. Stress
    D. Temperature
    E. Time

    In a caustic system, D
    which of the following if
    improperly designed
    can contribute to
    Caustic Stress
    Corrosion Cracking?
    A. Flanges
    B. Nozzles
    C. Reducers
    D. Heat Tracing

    Which of the following D


    is a common way that
    Operations causes
    Caustic Stress
    Corrosion Cracking in
    caustic equipment?
    A. Increasing flow rate.
    B. Lowering the ph
    C. Overpressure
    D. Steam cleaning

    API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stre...
    https://quizlet.com/479824585/api-571-study-guide-practice-questions-for-api-570-exam-caustic-stress-corrosion-cracking-caustic-embrittlement-453-fl… 2/5
    5/22/2021 API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stress Corrosion Cracking- Caustic Embrittlement (4.5.3) Flashcard…

    The likelihood of C
    Caustic Stress
    Corrosion Cracking can
    be reduced by:
    A. Increasing the
    operational
    temperature.
    B. Reducing the fluid
    velocity.
    C. Stress-relieving.
    D. Using low-hydrogen
    electrodes.

    A carbon steel caustic C


    system has a 10%
    concentration of NaOH
    (caustic). Above what
    temperature is stress-
    relieving
    recommended?
    A. 80 degree F
    B. 140 degree F
    C. 176 degree F
    D. 220 degree F

    API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stre...
    https://quizlet.com/479824585/api-571-study-guide-practice-questions-for-api-570-exam-caustic-stress-corrosion-cracking-caustic-embrittlement-453-fl… 3/5
    5/22/2021 API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stress Corrosion Cracking- Caustic Embrittlement (4.5.3) Flashcard…

    A carbon steel caustic B


    system has a 30%
    concentration of NaOH
    (caustic). Above what
    temperature is stress-
    relieving
    recommended?
    A. 62 degree F
    B. 140 degree F
    C. 220 degree F
    D. Carbon steel is not
    recommended for this
    percentage of caustic.

    A carbon steel caustic D


    system has a 10%
    concentration of NaOH
    (caustic). Above what
    temperature is stress-
    relieving no longer
    effective?
    A. 60 degree F
    B. 106 degree F
    C. 176 degree F
    D. 220 degree F

    API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stre...
    https://quizlet.com/479824585/api-571-study-guide-practice-questions-for-api-570-exam-caustic-stress-corrosion-cracking-caustic-embrittlement-453-fl… 4/5
    5/22/2021 API 571 Study Guide- Practice Questions for API 570 Exam- Caustic Stress Corrosion Cracking- Caustic Embrittlement (4.5.3) Flashcard…

    A caustic system has a D


    30% concentration of
    NaOH (caustic). Above
    what temperature are
    nickel alloys
    recommended?
    A. 60 degree F
    B. 97 degree F
    C. 138 degree F
    D. 205 degree F

    https://quizlet.com/479824585/api-571-study-guide-practice-questions-for-api-570-exam-caustic-stress-corrosion-cracking-caustic-embrittlement-453-fl… 5/5