API 5L Pipe Specification (PSL1, PSL2, SOUR SERVICE)

For more info please visit https://www.octalsteel.com/api-5l-pipe-specification

Chemical Composition for API 5L PSL1 pipe Wall thickness ≤ 25.0 mm (0.984 in)

Chemical composition for API 5L PSL1 Pipe


Wall Thickness ≤ 25.0 mm (0.984 in)
Mass fraction, based upon heat and product analyses
Steel Grade
(Steel Name) %
C Mn P S V Nb Ti
max max min. max max max max max
Seamless pipe
L175 or A25 0.21 0.60 - 0.030 0.030 - - -
L175P or A25P 0.21 0.60 0.045 0.080 0.030 - - -
L210 or A 0.22 0.90 - 0.030 0.030 - - -
L245 or B 0.28 1.20 - 0.030 0.030 c,d c,d d
L290 or X42 0.28 1.30 - 0.030 0.030 d d d
L320 or X46 0.28 1.40 - 0.030 0.030 d d d
L360 or X52 0.28 1.40 - 0.030 0.030 d d d
L390 or X56 0.28 1.40 - 0.030 0.030 d d d
L415 or X60 0.28 1.40 - 0.030 0.030 f f f
L450 or X65 0.28 1.40 - 0.030 0.030 f f f
L485 or X70 0.28 1.40 - 0.030 0.030 f f f
Welded (ERW, LSAW, SSAW) pipe
L175 or A25 0.21 0.60 - 0.030 0.030 - - -
L175P or A25P 0.21 0.60 0.045 0.080 0.030 - - -
L210 or A 0.22 0.90 - 0.030 0.030 - - -
L245 or B 0.26 1.20 - 0.030 0.030 c,d c,d d
L290 or X42 0.26 1.30 - 0.030 0.030 d d d
L320 or X46 0.26 1.40 - 0.030 0.030 d d d
L360 or X52 0.26 1.40 - 0.030 0.030 d d d
L390 or X56 0.26 1.40 - 0.030 0.030 d d d
L415 or X56 0.26 1.40 - 0.030 0.030 f f f
L450 or X65 0.26 1.45 - 0.030 0.030 f f f
L485 or X70 0.26 1.65 - 0.030 0.030 f f f

a. Cu ≤ 0,50 %; Ni ≤ 0,50 %; Cr ≤ 0,50 % and Mo ≤ 0.15%


b. For each reduce of 0.01% Carbon Max, an increase of 0.05% of maximum Mn is permited, up to a maximum of 1.65%
for grade ≥ B or L245, but ≤ X52 or L360; Up to max 1.75% for grades above L360 or X52, but below L485 or X70;
And up to 2.00% max for grade X70 or L485.
c. Unless otherwise agreed, Nb + V ≤ 0.06%.
d. Nb + V + Ti ≤ 0.15%.
e. Unless otherwise agreed.
f. Unless otherwise agreed, Nb + V + Ti ≤ 0.15%.
g. B shall be not added in on purpose, and maximum B is 0.001%.
Chemical Composition for API 5L PSL2 Pipe with t ≤ 25.0 mm (0.984 in)

Carbon
Mass fraction, based upon heat and product analyses a
Steel Grade equivalent
(Steel Name) % maximum % maximum
b b
C Si Mn P S V Nb Ti Other CE IIW CEPcm
Seamless and welded pipes
L245R or BR 0.24 0.40 1.20 0.025 0.015 c c 0.04 e,l 0.43 0.25
L290R or X42R 0.24 0.40 1.20 0.025 0.015 0.06 0.05 0.04 e,l 0.43 0.25
L245N or BN 0.24 0.40 1.20 0.025 0.015 c c 0.04 e,l 0.43 0.25
L290N or X42N 0.24 0.40 1.20 0.025 0.015 0.06 0.05 0.04 e,l 0.43 0.25
L320N or X46N 0.24 0.40 1.40 0.025 0.015 0.07 0.05 0.04 d,e,l 0.43 0.25
L360N or X52N 0.24 0.45 1.40 0.025 0.015 0.10 0.05 0.04 d,e,l 0.43 0.25
L390N or X56N 0.24 0.45 1.40 0.025 0.015 0.10 0.05 0.04 d,e,l 0.43 0.25
f f f
L415N or X60N 0.24 0.45 1.40 0.025 0.015 0.10 0.05 0.04 g,h,l as agreed
L245Q or BQ 0.18 0.45 1.40 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L290Q or X42Q 0.18 0.45 1.40f 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L320Q or X46Q 0.18 0.45 1.40 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L360Q or X52Q 0.18 0.45 1.50 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L390Q or X56Q 0.18 0.45 1.50 0.025 0.015 0.07 0.05 0.04 d,e,l 0.43 0.25
f f f
L415Q or X60Q 0.18 0.45 1.70 0.025 0.015 g g g h,l 0.43 0.25
f f f
L450Q or X65Q 0.18 0.45 1.70 0.025 0.015 g g g h,l 0.43 0.25
f f f
L485Q or X70Q 0.18 0.45 1.80 0.025 0.015 g g g h,l 0.43 0.25
f f f
L555Q or X80Q 0.18 0.45 1.90 0.025 0.015 g g g i,j as agreed
L625Q or X90Q 0.16 0.45 1.90 0.020 0.010 g g g j,k as agreed
L690Q or X100Q 0.16 0.45 1.90 0.020 0.010 g g g j,k as agreed
Welded pipe
L245M or BM 0.22 0.45 1.20 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L290M or X42M 0.22 0.45 1.30 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L320M or X46M 0.22 0.45 1.30 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
L360M or X52M 0.22 0.45 1.40 0.025 0.015 d d d e,l 0.43 0.25
L390 or X56M 0.22 0.45 1.40 0.025 0.015 d d d e,l 0.43 0.25
f f f
L415 or X60M 0.12 0.45 1.60 0.025 0.015 g g g h,l 0.43 0.25
f f f
L450 or X65M 0.12 0.45 1.60 0.025 0.015 g g g h,l 0.43 0.25
f f f
L485M or X70M 0.12 0.45 1.70 0.025 0.015 g g g h,l 0.43 0.25
f f f
L555M or X80M 0.12 0.45 1.85 0.025 0.015 g g g i,l 0.43 0.25
f f
L625 or X90M 0.10 0.55 2.10 0.020 0.010 g g g i,l - 0.25
f f
L690M or X100M 0.10 0.55 2.10 0.020 0.010 g g g i,j 0.25
f f
L830M or X120M 0.10 0.55 2.10 0.020 0.010 g g g i,j 0.25

a. Based upon product analysis. For seamless pipe with t > 20,0 mm (0.787 in), the CE limits shall be as agreed.
The CEIIW limits apply if C > 0,12 % and the CEPcm limits apply if C ≤ 0,12 %.
b. For each reduction of 0,01 % below the specified maximum for C, an increase of 0,05 % above the specified maximum for
Mnpermissible,
is up to a maximum of 1,65 % for grades ≥ L245 or B, but ≤ L360 or X52; up to a maximum of 1,75 % for grades >
L360 or but < L485 or X70; up to a maximum of 2,00 % for grades ≥ L485 or X70, but ≤ L555 or X80; and up to a maximum of
X52,
2,20 % for> L555 or X80.
grades
c. Unless otherwise agreed, Nb + V ≤ 0,06 %.
d. Nb + V + Ti ≤ 0,15 %.
e. Unless otherwise agreed, Cu ≤ 0,50 %; Ni ≤ 0,30 %; Cr ≤ 0,30% and Mo ≤ 0,15 %.
f. Unless otherwise agreed.
g. Unless otherwise agreed, Nb + V + Ti ≤ 0,15 %.
h. Unless otherwise agreed, Cu ≤ 0,50 %; Ni ≤ 0,50 %; Cr ≤ 0,50% and Mo ≤ 0, 50 %.
i. Unless otherwise agreed, Cu ≤ 0,50 %; Ni ≤ 1,00 %; Cr ≤ 0,50% and Mo ≤ 0, 50 %.
j. B ≤ 0,004 %.
k. Unless otherwise agreed, Cu ≤ 0,50 %; Ni ≤ 1,00 %; Cr ≤ 0,55% and Mo ≤ 0, 80 %.
l. For all PSL 2 pipe grades except those grades to which footnote j already applies, the following applies.
Unless otherwise agreed no intentional addition of B is permitted and residual B ≤ 0,001%.
API 5L PSL 1 Pipe Mechanical Properties (Tensile strength, Yeild strength, Elongation)

Weld seam of EW, LSAW,


Pipe body of seamless and welded pipe
SSAW and COW pipes

Pipe grade Elongation


Yield strength Tensile strength Tensile strength
(on 50mm or 2 in)
Rt0.5 Rm Af Rm
MPa (psi), min MPa (psi), min % minimum MPa (psi), min
L175 or A25 175 (25 400) 310 (45 000) c 310 (45 000)
L175P or A25P 175 (25 400) 310 (45 000) c 310 (45 000)
L210 or A 210 (30 500) 335 (48 600) c 335 (48 600)
L245 or B 245 (35 500) 415 (60 200) c 415 (60 200)
L290 or X42 290 (42 100) 415 (60 200) c 415 (60 200)
L320 or X46 320 (46 400) 435 (63 100) c 435 (63 100)
L360 or X52 360 (52 200) 460 (66 700) c 460 (66 700)
L390 or X56 390(56 600) 490 (71 100) c 490 (71 100)
L415 or X60 415 (60 200) 520 (75 400) c 520 (75 400)
L450 or X65 450 (65 300) 535 (77 600) c 535 (77 600)
L485 or X70 485 (70 300) 570 (82 700) c 570 (82 700)

c. For the specified minimum elongation, Af shall be using below equation:

Where
C is 1940 for calculations using IS units and 625000 for calculations using USC units;

Axc is the applicable tensile test piece cross-section area, expressed in square mm or square inch, as follows:

2 2
- for circular cross-section test pieces, 130mm for 12.7 mm and 8.9 mm diameter test pieces; and 65 mm
2
(0.10 in ) for 6,4 mm (0.250 in) diameter test pieces;
2 2
- for full-section test pieces, the lesser of a) 485 mm (0.75 in ) and b) the cross-sectional area of the test piece,
derived using the specified outside diameter and the specified wall thickness of the pipe, rounded to the nearest
2 2
10 mm (0.01 in );
- for strip test pieces, the lesser of a) 485 mm2 (0.75 in2) and b) the cross-sectional area of the test piece, derived
using the specified width of the test piece and the specified wall thickness of the pipe, rounded to the nearest
2
10 mm2 (0.01 in );

U is the specified minimum tensile strength, expressed in megapascals (pounds per square inch).
API 5L PSL 2 Pipe Mechanical Properties (Tensile Strength, Yield Strength, Elongation)

Weld seam of HFW,


Pipe body of seamless and welded pipes
SAW and COW pipes

Pipe grade a a a,c Elongation (on d


Yield strength Tensile strength Ratio Tensile strength
50 mm or 2 in)
Rt0.5 Rm Rt0.5/Rm Af Rm
MPa (psi) MPa (psi) % MPa (psi)
minimum maximum minimum maximum maximum minimum minimum
L245R or BR
L245N or BN 245 450 e 415 415
655 (95 000) 0.93 f
L245Q or BQ (35 500) (65 300) e (60 200) (60 200)
L245M or BM
L290R or X42R
L290N or X42N 290 495 415 415
655(95 000) 0.93 f
L290Q or X42Q (42 100) (71 800) (60 200) (60 200)
L290M or X42M
L320N or X46N
320 525 435 435
L320Q or X46Q 655 (95 000) 0,93 f
(46 400) (76 100) (63 100) (63 100)
L320M or X46M
L360N or X52N
360 530 460 760 460
L360Q or X52Q 0,93 f
(52 200) (76 900) (66 700) (110 200) (66 700)
L360M or X52M
L390N or X56N
390 545 490 760 490
L390Q or X56Q 0,93 f
(56 600) (79 000) (71 100) (110 200) (71 100)
L390M or X56M
L415N or X60N
415 565 520 760 520
L415Q or X60Q 0,93 f
(60 200) (81 900) (75 400) (110 200) (75 400)
L415M or X60M
L450Q or X65Q 450 600 535 760 535
0,93 f
L450M or X65M (65 300) (87 000) (77 600) (110 200) (77 600)
L485Q or X70Q 485 635 570 760 570
0,93 f
L485M or X70M (70 300) (92 100) (82 700) (110 200) (82 700)
L555Q or X80Q 555 705 625 825 625
0,93 f
L555M or X80M (80 500) (102 300) (90 600) (119 700) (90 600)
625 775 695 915 695
L625M or X90M 0,95 f
(90 600) (112 400) (100 800) (132 700) (100 800)
625 775 695 915 g 695
L625Q or X90Q 0,97 f
(90 600) (112 400) (100 800) (132 700) (100 800)
b b
690 840 760 990 h 760
L690M or X100M b b 0,97 f
(100 100) (121 800) (110 200) (143 600) (110 200)
b b
690 840 760 990 h 760
L690Q or X100Q b b 0,97 f
(100 100) (121 800) (110 200) (143 600) (110 200)
b b
830 1050 915 1 145 h 915
L830M or X120M b b 0,99 f
(120 400) (152 300) (132 700) (166 100) (132 700)

a. For intermediate grades, the difference between the specified maximum yield strength and the specified minimum yield strength
shall be as given in the table for the next higher grade, and the difference between the specified minimum tensile strength and the
specified minimum yield strength shall be as given in the table for the next higher grade. For intermediate grades up to Grade L320 or
X46, the tensile strength shall be ≤ 655 MPa (95 000 psi). For intermediate grades greater than Grade L320 or X46 and lower than
Grade L555 or X80, the tensile strength shall be ≤ 760 MPa (110 200 psi).For intermediate grades higher than Grade L555 or X80, the
maximum permissible tensile strength shall be obtained by interpolation. For SI units, the calculated value shall be rounded to the
nearest 5 MPa. For USC units, the calculated value shall be rounded to the nearest 100 psi.
b. For grades > L625 or X90, Rp0,2 applies.
c. This limit applies for pipe with D > 323,9 mm (12.750 in).
d. For intermediate grades, the specified minimum tensile strength for the weld seam shall be the same value as was determined for
the pipe body using footnote a).
e. For pipe requiring longitudinal testing, the maximum yield strength shall be ≤ 495 MPa (71 800 psi).
f. The specified minimum elongation, A f, shall be as determined using the following equation:

Where
C is 1940 for calculations using IS units and 625000 for calculations using USC units;

Axc is the applicable tensile test piece cross-section area, expressed in square mm or square inch, as follows:

2 2
- for circular cross-section test pieces, 130mm for 12.7 mm and 8.9 mm diameter test pieces; and 65 mm
2
(0.10 in ) for 6,4 mm (0.250 in) diameter test pieces;
2 2
- for full-section test pieces, the lesser of a) 485 mm (0.75 in ) and b) the cross-sectional area of the test piece,
derived using the specified outside diameter and the specified wall thickness of the pipe, rounded to the nearest
2 2
10 mm (0.01 in );
- for strip test pieces, the lesser of a) 485 mm2 (0.75 in2) and b) the cross-sectional area of the test piece, derived
using the specified width of the test piece and the specified wall thickness of the pipe, rounded to the nearest
2
10 mm2 (0.01 in );

U is the specified minimum tensile strength, expressed in megapascals (pounds per square inch).
Lower values of R t0,5/R m may be specified by agreement.
g. Lower values of Rt0,5/Rm may be specified by agreement.
h. For grades > L625 or X90, Rp0,2 /Rm applies. Lower values of Rp0,2 /Rm may be specified by agreement.
Chemical Composition for API 5L Sour Service Pipe Wall thickness ≤ 25.0 mm (0.984 in)

Chemical composition for API 5L Sour Service Pipe with wall thickness ≤ 25.0 mm (0.984 in)

Mass fraction, based upon heat and product analyses Carbon equivalent
Steel Grade % maximum
(Steel Name) % maximum
b b c,d
C Si Mn P S V Nb Ti other CE IIW CE Pcm
Seamless and welded pipes
e h
L245NS or BNS 0.14 0.40 1.35 0.020 0.003 0.04 g 0.36 0.19
e h
L290NS or X42NS 0.14 0.40 1.35 0.020 0.003 0.05 0.05 0.04 - 0.36 0.19
e h
L320NS or X46NS 0.14 0.40 1.40 0.020 0.003 0.07 0.05 0.04 g 0.38 0.20
e h
L360NS or X52NS 0.16 0.45 1.65 0.020 0.003 0.10 0.05 0.04 g 0.43 0.22
e h
L245QS or XQBS 0.14 0.40 1.35 0.020 0.003 0.04 0.04 0.04 - 0.34 0.19
e h
L290QS or X42QS 0.14 0.40 1.35 0.020 0.003 0.04 0.04 0.04 - 0.34 0.19
e h
L320QS or X46QS 0.15 0.45 1.40 0.020 0.003 0.05 0.05 0.04 - 0.36 0.20
e h
L360QS or X52QS 0.16 0.45 1.65 0.020 0.003 0.07 0.05 0.04 g 0.39 0.20
e h
L390QS or X56QS 0.16 0.45 1.65 0.020 0.003 0.07 0.05 0.04 g 0.40 0.21
e h
L415QS or X60QS 0.16 0.45 1.65 0.020 0.003 0.08 0.05 0.04 g,i,k 0.41 0.22
e h
L450QS or X65QS 0.16 0.45 1.65 0.020 0.003 0.09 0.05 0.06 g,i,k 0.42 0.22
e h
L485QS or X70QS 0.16 0.45 1.65 0.020 0.003 0.09 0.05 0.06 g,i,k 0.42 0.22
Welded pipe
e
L245MS or BMS 0.10 0.40 1.25 0.020 0.002 0.04 0.04 0.04 - - 0.19
e
L290MS or X42MS 0.10 0.40 1.25 0.020 0.002 0.04 0.04 0.04 - - 0.19
e
L320MS or X46MS 0.10 0.45 1.35 0.020 0.002 0.05 0.05 0.04 - - 0.20
e
L360MS or X52MS 0.10 0.45 1.45 0.020 0.002 0.05 0.06 0.04 - - 0.20
e
L390MS or X56MS 0.10 0.45 1.45 0.020 0.002 0.06 0.08 0.04 g - 0.21
e
L415MS or X60MS 0.10 0.45 1.45 0.020 0.002 0.08 0.08 0.06 g,i - 0.21
e
L450MS or X65MS 0.10 0.45 1.60 0.020 0.002 0.10 0.08 0.06 g,i,k - 0.22
e
L485MS or X70MS 0.10 0.45 1.60 0.020 0.002 0.10 0.08 0.06 g,i,k - 0.22
a. Based upon product analysis (see 9.2.4 and 9.2.5). The CEIIW limits apply if C > 0.12 % and the CEPcm limits apply if C ≤ 0.12 %.

b. For each reduction of 0.01 % below the specified maximum for C, an increase of 0.05 % above the specified maximum for Mn is
permissible, up to a maximum increase of 0.20 %.

c. Altotal ≤ 0.060 %; N ≤ 0.012 %; Al/N ≥ 2:1 (not applicable to titanium-killed or titanium-treated steel); Cu ≤ 0.35 % (if agreed, Cu
≤ 0.10 %); Ni ≤ 0.30 %; Cr ≤ 0.30 %; Mo ≤ 0.15 %; B ≤ 0.0005 %.
d. For welded pipe where calcium is intentionally added, unless otherwise agreed, Ca/S ≥ 1.5 if S > 0.0015 %. For SMLS and welded pipes, Ca ≤
0.006 %.

e. The maximum limit for S may be increased to ≤ 0.008 % for SMLS pipe and, if agreed, to ≤ 0.006 % for welded pipe. For such higher S levels
in welded pipe, lower Ca/S ratios may be agreed.

f. Unless otherwise agreed, Nb + V ≤ 0.06 %.


g. Nb + V + Ti ≤ 0.15 %.
h. For SMLS pipe, the listed CEPcm value may be increased by 0.03.
i. If agreed, Mo ≤ 0.35 %.
j. If agreed, Cr ≤ 0.45 %.
k. If agreed, Cr ≤ 0.45% and Ni ≤ 0.50%.
API 5L Sour Service Pipe Mechanical Properties (Tensile Strength, Yield Strength, Elongation)

Mechanical Properties for API 5L Sour Service Pipe

a a Elongation (on
Yield strength Tensile strength b Tensile
Ratio 50 mm or 2 in)
Rt0,5 Rm strengthc Rm
Rt0,5/Rm Af
Pipe steel grade MPa(psi) MPa(psi) MPa(psi)
%

minimum maximum minimum maximum maximum minimum minimum

L245NS or BNS
L245QS or BQS 245 (35500) 450 (65300) 415 (60200) 655 (95000) 0.93 e 415 (60200)
L245MS or BMS
L290NS or X42NS
L290QS or X42QS 290 (42100) 495 (71800) 415 (60200) 655 (95000) 0.93 e 415 (60200)
L290MS or X42MS
L320NS or X46NS
L320QS or X46QS 320 (46400) 525 (76100) 435 (63100) 655 (95000) 0.93 e 435 (63100)
L320MS or X46MS
L360NS or X52NS
L360QS or X52QS 360 (52200) 530 (76900) 460 (66700) 760 (110200) 0.93 e 460 (66700)
L360MS or X52MS

L390QS or X56QS
390 (56600) 545 (79000) 490 (71100) 760 (110200) 0.93 e 490 (71100)
L390MS or X56MS

L415QS or X60QS
415 (60200) 565 (81900) 520 (75400) 760 (110200) 0.93 e 520 (75400)
L415MS or X60MS

L450QS or X65QS
450 (65300) 600 (87000) 535 (77600) 760 (110200) 0.93 e 535 (77600)
L450MS or X65MS

L485QS or X70QS
485 (70300) 635 (92100) 570 (82700) 760 (110200) 0.93 e 570 (82700)
L485MS or X70MS

a. For intermedia grades, the difference between the specified maximum yield strength and the specified minimum yield
strength shall be as given in the table for the next higher grade, and the difference between the specofied minimum tensile
strength and the specified minimum yield strength shall be given in the table for the next higher grade. For intermediate
grades, the tensile strength shall be ≤760MPa(110200psi).

b. This limit applies for pipe with D>323.9mm (12.750 in).


c. For intermedia grades, the specified minimum tensile strength for the weld seam shall be the same value as was
determined for the pipe body using footnote a).
d. For pipe requiring longitudinal testing, the maximum yield strength shall be ≤495MPa (71800 psi).

e. The specified minimum elongation, Af on 50 mm or 2 in, expressed in percent and rounded to the nearest percent, shall
be as determined using the following equition:
where
C is 1940 for calculations using SI units and 625000 for calculations using USC units;

Axc is the applicable tensile test piece cross-sectional area, expressed in square millimetres (square inches), as follows:

- for circular cross-section test pieces, 130 mm (0.2 in) for 12.7mm (0.5 in) and 8,9mm(0.350 in)diameter test pieces; and
65 mm2(0.1in2)for 6.4mm(0.250in)diameter test pieces;

- for full-section test pieces, the esser of a) 485mm2 (0.75 in2) and b)the cross-sectional area of the test piece, derived
using the specified outside diameter and the specified wall thickness of the pipe, rounded to the nearest 10 mm2(0.01 in2);

- for strip test pieces, the lesser of a) 485mm2 (0.75 in2) and b)the cross-sectional area of the test piece, derived using
the specified width of the test piece and the specified wall thickness of the pipe, rounded to the nearest 10 mm2 (0.01 in2)
U is the specified minimum tensile strength, expressed in megapascals (pounds per square inch)