DEUTSCHE NORM June 2006

DIN EN 12517-1 {
ICS 25.160.40
Supersedes
DIN EN 12517:2003-01

Non-destructive testing of welds –

Part 1: Evaluation of welded joints in steel, nickel, titanium and their
alloys by radiography –
Acceptance levels
English version of DIN EN 12517-1:2006-06

Zerstörungsfreie Prüfung von Schweißverbindungen –

Teil 1: Bewertung von Schweißverbindungen in Stahl, Nickel, Titan und ihren Legierungen
mit Durchstrahlung –
Zulässigkeitsgrenzen
Englische Fassung DIN EN 12517-1:2006-06

Document comprises 17 pages

© No part of this standard may be reproduced without prior permission of

DIN Deutsches Institut für Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,
has the exclusive right of sale for German Standards (DIN-Normen).
English price group 10
www.din.de
www.beuth.de
!,o-?"
11.06 9761028
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

DIN EN 12517-1:2006-06

National foreword
This standard has been prepared by CEN/TC 121 ‘Welding’ (Secretariat: Germany).

The responsible German body involved in its preparation was the Normenausschuss Materialprüfung (Materi-
als Testing Standards Committee), Technical Committee NMP 822 Durchstrahlungsprüfung und Strahlen-
schutz.

Amendments

This standard differs from DIN EN 12517:2003-01 as follows:

a) The standard now consists of two parts, Part 1 dealing with welded joints in steel, nickel, titanium and
their alloys and Part 2 with welded joints in aluminium and its alloys.

b) Table 2 has been completely revised taking into account the specifications of EN ISO 5817:2003.

c) Annexes B and C have been added.

d) Annex ZA has been dropped.

Previous editions

DIN EN 12517: 1998-03, 2003-01

2
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EUROPEAN STANDARD EN 12517-1

NORME EUROPÉENNE
EUROPÄISCHE NORM March 2006

ICS 25.160.40 Supersedes EN 12517:1998

English Version

Non-destructive testing of welds - Part 1: Evaluation of welded

joints in steel, nickel, titanium and their alloys by radiography -
Acceptance levels

Essais non destructifs des assemblages soudés - Partie 1: Zerstörungsfreie Prüfung von Schweißverbindungen -
Évaluation par radiographie des assemblage soudés en Teil 1: Bewertung von Schweißverbindungen in Stahl,
acier, nickel, titane et leurs alliages - Niveaux d'acceptation Nickel, Titan und ihren Legierungen mit Durchstrahlung -
Zulässigkeitsgrenzen

This European Standard was approved by CEN on 6 February 2006.

CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the Central Secretariat or to any CEN member.

This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official
versions.

CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,
Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.

EUROPEAN COMMITTEE FOR STANDARDIZATION

COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG

Management Centre: rue de Stassart, 36 B-1050 Brussels

© 2006 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 12517-1:2006: E
worldwide for CEN national Members.
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Contents Page

Foreword......................................................................................................................................................................3
1 Scope ..............................................................................................................................................................4
2 Normative references ....................................................................................................................................4
3 Radiographic technique ................................................................................................................................4
4 General............................................................................................................................................................5
5 Acceptance levels..........................................................................................................................................5
Annex A (informative) Guide to the limitations of radiographic testing ............................................................10
A.1 Volumetric imperfections in butt welds.....................................................................................................10
A.2 Cracks in butt welds ....................................................................................................................................10
A.3 Planar imperfections in butt welds ............................................................................................................10
Annex B (informative) Examples for determination of area percentage (%) of imperfections........................11
Annex C (normative) Sum of acceptable areas ....................................................................................................13
Bibliography ..............................................................................................................................................................15

2
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Foreword
This document (EN 12517-1:2006) has been prepared by Technical Committee CEN/TC 121 “Welding”, the
secretariat of which is held by DIN.

This European Standard shall be given the status of a national standard, either by publication of an identical text or
by endorsement, at the latest by September 2006, and conflicting national standards shall be withdrawn at the
latest by September 2006.

This document supersedes EN 12517:1998.

This document has been prepared under a mandate given to CEN by the European Commission and the European
Free Trade Association, and supports essential requirements of EU Directive(s).

EN 12517 comprises a series of European Standards for industrial radiographic films which is made up of the
following:

EN 12517-1 Non-destructive testing of welds – Part 1: Evaluation of welded joints in steel, nickel, titanium and
their alloys by radiography – Acceptance levels

EN 12517-2 Non-destructive testing of welds – Part 2: Evaluation of welded joints in aluminium and its alloys by
radiography – Acceptance levels

According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark,
Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta,
Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United
Kingdom.

3
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

1 Scope
This document specifies acceptance levels for indications from imperfections in butt welds of steel, nickel, titanium
and their alloys detected by radiographic testing. If agreed, the acceptance levels may be applied to other types of
welds or materials.

The acceptance levels may be related to welding standards, application standards, specifications or codes. This
European Standard assumes that the radiographic testing has been carried out in accordance with EN 1435.

When assessing whether a weld meets the requirements specified for a weld quality level, the sizes of
imperfections permitted by standards are compared with the dimensions of indications revealed by a radiograph
made of the weld.

2 Normative references
The following referenced documents are indispensable for the application of this European Standard. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced document
(including any amendments) applies.

EN 1435, Non-destructive examination of welds — Radiographic examination of welded joints

EN ISO 5817, Welding — Fusion-welded joints in steel, nickel, titanium and their alloys (beam welding excluded) —
Quality levels for imperfections (ISO 5817:2003)

EN ISO 6520-1, Welding and allied processes — Classification of geometric imperfections in metallic materials —
Part 1: Fusion welding (ISO 6520-1:1998)

3 Radiographic technique
Depending on the weld quality level, radiographic technique A or B in accordance with EN 1435 is used as shown
in Table 1.

Table 1 – Radiographic testing

Quality levels in accordance Testing techniques and Acceptance levels in

with EN ISO 5817 classes in accordance with accordance with
EN 1435 EN 12517

B B 1

C Ba 2

D A 3

a However, the minimum number of exposure for circumferential weld testing may correspond to the requirements of

class A of EN 1435.

4
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

4 General
Welded joints should be visually tested and evaluated in accordance with EN 970 before radiographic testing.

The acceptance levels in this European Standard are basically valid for evaluation of imperfections which cannot
be detected and evaluated by visual testing. Surface imperfections (such as undercut and excessive penetration,
surface damage, weld spatter etc.) which, due to object geometry, cannot be evaluated, but where the interpreter
suspects the EN ISO 5817 quality levels are not fulfilled, shall be subject to more specific testing.

When quantification of undercut and/or excessive penetration by radiographic testing is required, specific
procedures using test exposures may be applied in order to establish a basis for approximate quantification in
accordance with the requirements of EN ISO 5817. This shall be specified.

5 Acceptance levels
The acceptance levels for indications are shown in Table 2 and Table 3. The types of imperfections are selected
from EN ISO 5817 and defined in EN ISO 6520-1.

The symbols used in Table 2 and Table 3 are the following:

l length of indication, in millimetres;

s nominal butt weld thickness, in millimetres;

t material thickness, in millimetres;

L any 100 mm testing length, in millimetres;

wp width of the weld, or cross surface imperfection, in millimetres

h width of indication, the width or height of surface imperfection, in millimetres;

d diameter of pore; in millimetres;

b width of excess penetration of weld, in millimetres;

A sum of projected areas of indications related to L x wp, in %;

Σl summary length of imperfections within L, in millimetres.

Indications shall not be divided into different ranges L.

5
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Table 2 – Acceptance levels for internal indications in butt welds

Type of internal
imperfections in
No. Acceptance level 3 a Acceptance level 2 a Acceptance level 1
accordance with
EN ISO 6520-1

1 Cracks (100) Not permitted Not permitted Not permitted

2a Porosity and gas pores A ≤ 2,5 % A ≤ 1,5 % A≤1%
(2012, 2011)
d ≤ 0,4s, max. 5 mm d ≤ 0,3s, max. 4 mm d ≤ 0,2s, max. 3 mm
Single layer
L = 100 mm L = 100 mm L = 100 mm
2b Porosity and gas pores A ≤ 5 % A≤3% A≤2%
(2012, 2011)
d ≤ 0,4s, max. 5 mm d ≤ 0,3s, max. 4 mm d ≤ 0,2s, max. 3 mm
Multilayer
L = 100 mm L = 100 mm L = 100 mm

3b Clustered (localized) A ≤ 16% A ≤ 8% A ≤ 4%

porosity (2013)
d ≤ 0,4s, max. 4 mm d ≤ 0,3s, max. 3 mm d ≤ 0,2s, max. 2 mm
L = 100 mm L = 100 mm L = 100 mm

4ac Linear porosity (2014) A≤8% A≤4% A≤2%

Single layer d ≤ 0,4s, max. 4 mm d ≤ 0,3s, max. 3 mm d ≤ 0,2s, max. 2 mm
L = 100 mm L = 100 mm L = 100 mm

4bc Linear porosity (2014) A ≤ 16 % A≤8% A≤4%

Multilayer d ≤ 0,4s, max. 4 mm d ≤ 0,3s, max. 3 mm d ≤ 0,2s, max. 2 mm
L = 100 mm L = 100 mm L = 100 mm

5d Elongated cavities h < 0,4s, max. 4 mm h < 0,3s, max. 3 mm h < 0,2s, max. 2 mm
(2015) and wormholes
(2016) Σl ≤ s, max. 75 mm, Σl ≤ s, max. 50 mm, Σl ≤ s, max. 25 mm,
L=100 mm L=100 mm L=100 mm

6e Shrinkage cavity (202) h < 0,4s, max. 4 mm

Not permitted Not permitted
(other than crater pipes) l ≤ 25 mm
7 Crater pipe (2024) h ≤ 0,2t, max. 2 mm
Not permitted Not permitted
l ≤ 0,2t, max. 2 mm

8d Slag inclusions (301), h < 0,4s, max. 4 mm h < 0,3s, max. 3 mm h < 0,2s, max. 2 mm
flux inclusions (302) and
oxide inclusions (303) Σl ≤ s, max. 75 mm Σl ≤ s, max. 50 mm Σl ≤ s, max. 25 mm
L = 100 mm L = 100 mm L = 100 mm

9 Metallic inclusions (304) l ≤ 0,4s, max. 4 mm l ≤ 0,3s, max. 3 mm l ≤ 0,2s, max. 2 mm

(other than copper)

(to be continued)

6
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Table 2 (concluded)

Type of internal
imperfections in
No. Acceptance level 3 a Acceptance level 2 a Acceptance level 1
accordance with
EN ISO 6520-1

10 Copper inclusions Not permitted

Not permitted Not permitted
(3042)

11e Lack of fusion (401) Permitted, but only

intermittently and not
Not permitted Not permitted
breaking the surface
Σl ≤ 25 mm, L = 100 mm

12e Lack of penetration

Σl ≤ 25 mm, L = 100 mm
(402) Not permitted Not permitted

a Acceptance levels 3 and 2 may be specified with suffix X, which denotes that all indications over 25 mm are unacceptable.
b See Annex C, Figure C.1 and Figure C.2 (normative)
c See Annex C, Figure C.3 and Figure C.4 (normative)
d See Annex C, Figure C.5 and Figure C.6 (normative)
e If the length of the weld is below 100 mm, then the maximum length of indications shall not exceed 25% of that weld.

7
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Table 3 – Surface imperfections: The acceptance levels are those defined for visual testing.
These defects are normally evaluated by visual testing

Type of surface
imperfections in
No. Acceptance level 3 a Acceptance level 2 a Acceptance level 1
accordance with
EN ISO 6520-1

13 Crater cracks (104) Not permitted Not permitted Not permitted

Smooth transition is Smooth transition is Smooth transition is

14a Undercut, continues and
required required required
intermittent (5011,5012)
For t > 3 mm For t > 3 mm For t > 3 mm

h ≤ 0,2t, max. 1 mm
h ≤ 0,1t, max. 0,5 mm h ≤ 0,05t, max. 0,5 mm
For 0,5 mm ≤ t ≤ 3 mm
For 0,5 mm ≤ t ≤ 3 mm For
l ≤ 25 mm, h ≤ 0,2t
l ≤ 25 mm, h ≤ 0,1t 0,5 mm ≤ t ≤ 3 mm

not permitted

14b Shrinkage groove (root Smooth transition is Smooth transition is Smooth transition is
undercut 5013) required required required
For t > 3 mm For t > 3 mm For t > 3 mm

l ≤ 25 mm, l ≤ 25 mm, l ≤ 25 mm,

h ≤ 0,2t, max. 2 mm, h ≤ 0,1t, max. 1 mm h ≤ 0,05t, max. 0,5 mm

For 0,5 mm ≤ t ≤ 3 mm For 0,5 mm ≤ t ≤ 3 mm For 0,5 mm ≤ t ≤ 3 mm

h ≤ 0,2 mm + 0,1t l ≤ 25 mm, h ≤ 0,1t Not permitted

15a Excess penetration (504) h ≤ 1 mm + 0,6 b h ≤ 1 mm + 0,3 b h ≤ 1 mm + 0,1 b

0,5 mm ≤ t ≤ 3 mm

15b Excess penetration (504) h ≤ 1 mm + 1,0 b, h ≤ 1 mm + 0,6 b, h ≤ 1 mm + 0,2 b,

t > 3mm
max. 5 mm max. 4 mm max. 3 mm

16 Stray arc (601) Permitted, if the

properties of the parent Not permitted Not permitted
metal are not affected

17 Spatter (602) Acceptance depends on application, e.g. material, corrosion protection

l ≤ 25 mm:
18a Root concavity (515) h ≤ 0,2 mm + 0,1 t
Not permitted
0,5 mm ≤ s ≤ 3 mm
h ≤ 0,1 t

(to be continued)

8
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Table 3 (concluded)

Type of surface
a Acceptance level 2 a Acceptance level 1
No. imperfections in Acceptance level 3
accordance with
EN ISO 6520-1
l ≤ 25 mm, l ≤ 25 mm, l ≤ 25 mm,
18b Root concavity (515)
s > 3 mm
h ≤ 0,2 t, h ≤ 0,1 t, h ≤ 0,05 t,

max. 2 mm max. 1 mm max. 0,5 mm

Poor restart (517) Permitted,

19

The limit depends on the Not permitted Not permitted

s ≥ 0,5 mm
type of imperfection (see
EN ISO 5817)

Sagging (509) l ≤ 25 mm, l ≤ 25 mm,

20a
Not permitted
Incompletely filled groove h ≤ 0,25 t h ≤ 0,1 t
(511)

0,5 mm ≤ s ≤ 3 mm

Sagging (509) l ≤ 25 mm, l ≤ 25 mm, l ≤ 25 mm,

20b

Incompletely filled groove h ≤ 0,25 t, h ≤ 0,1 t, h ≤ 0,05 t,

(511)
max. 2 mm max. 1 mm max. 0,5 mm
s > 3 mm

Linear misalignment h ≤ 0,2 mm + 0,25 t h ≤ 0,2 mm + 0,15 t h ≤ 0,2 mm + 0,1 t

21a
(507)

0,5 mm ≤ s ≤ 3 mm

Linear misalignment, h ≤ 0,25 t, max. 5 mm h ≤ 0,15 t, max. 4 mm h ≤ 0,1 t, max. 3 mm

21b
longitudinal welds (507)

s > 3 mm

Linear misalignment, h ≤ 0,5 t, h ≤ 0,5 t, h ≤ 0,5 t,

21c
circumferential welds
(507) max. 4 mm max. 3 mm max. 2 mm

s ≥ 0,5 mm

a Acceptance levels 3 and 2 may be specified with suffix X, which denotes that all indications over 25 mm are unacceptable.

9
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Annex A
(informative)

Guide to the limitations of radiographic testing

NOTE The numbers between brackets conform to those used in EN ISO 6520-1.

A.1 Volumetric imperfections in butt welds

Porosities and gas pores (2011, 2013, 2015 and 2017)

Wormholes and elongated cavities (2016 and 2015)

Solid inclusions (300)

Copper inclusions (3042)

The above imperfections listed in Table 2 will be readily detected using radiographic technique A or B of EN 1435
as shown in Table 1 of this European Standard.

A.2 Cracks in butt welds

Crater cracks (104)

Cracks (100)

The detectability of cracks by radiographic testing depends on the crack height, the ramification (presence of
branching parts), opening width, direction of the X-ray beam to crack orientation and radiographic technique
parameters.

Reliable detection of all cracks is therefore limited. The use of radiographic technique B or better, as specified in
EN 1435, will provide better crack detectability than radiographic technique A.

A.3 Planar imperfections in butt welds

Lack of fusion (401)

Lack of penetration (402)

The detection of lack of fusion and lack of penetration depends on characteristics of imperfections and radiographic
technique parameters.

Lack of side-wall fusion will probably not be detected (except it is associated with other imperfections such as slag
inclusions) unless it is radiographed in direction of the side-wall.

10
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Annex B
(informative)

Examples for determination of area percentage (%) of imperfections

The following figures give a presentation of different area percentage (%) of imperfections. This should assist the
assessment of imperfections on radiographs and fracture surfaces.

Figure B.1 — 1 %

Figure B.2 — 1,5 %

Figure B.3 — 2 %

Figure B.4 — 2,5 %

11
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Figure B.5 — 3 %

Figure B.6 — 4 %

Figure B.7 — 5 %

Figure B.8 — 8 %

Figure B.9 — 16 %

12
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Annex C
(normative)

Sum of acceptable areas

Figure C.1 — Clustered porosity, D > dA2

Figure C.2 — Clustered porosity, D < dA2

The sum of the different pore areas (A1+A2….) related to the evaluation area L X wp (Figure C.1).

If D is less than dA1 or dA2, whatever is smaller, an envelope surrounding the porosity area A1+A2 shall be
considered as one area of imperfection (Figure C.2).

Figure C.3 — Linear porosity, D > d2

13
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Figure C.4 — Linear porosity, D < d2

 d12 × π d 2 2 × π 
The sum of the different pore areas  + + ... related to the evaluation area L X wp (Figure C.3).
 4 4
 
If D is smaller than the smaller diameter of one of the neighbouring pores, the full connected area of the two pores
is to be taken into the sum of imperfections (Figure C.4).

Figure C.5 — Elongated cavities and wormholes, D > l3

Figure C.6 — Elongated cavities and wormholes, D < l3

The sum of the length of indications Σl shall be determined for each testing length L (Figure C.5).

If D is smaller than the shorter length of one of the neighbouring imperfections, the full connection of the two
imperfections is to be taken into the sum of imperfections (Figure C.6).

14
 Licença de uso exclusivo para DEDINI S/A INDUSTRIAS DE BASE

EN 12517-1:2006 (E)

Bibliography

[1] EN 970, Non-destructive examination of fusion welds — Visual examination

[2] EN 12062, Non-destructive examination of welds — General rules for metallic materials

[3] IIW catalogue of reference radiographs for assessment of weld imperfections according to ISO 5817

15