Electron Beam Welding Procedure Qualification Record WPQR (Qmob) #EBW 2015 01

Download as pdf or txt
Download as pdf or txt
You are on page 1of 18

EDMS NO. REV.

VALIDITY

1512110 0.0 APPROVED


REFERENCE

J3022578
CERN
CH1211 Geneva 23
Switzerland
Date: 2015-05-08

ELECTRON BEAM WELDING  
PROCEDURE QUALIFICATION RECORD 
WPQR (QMOB)
N° EBW‐2015‐01
 

CCC CRYOSTAT 
   

DOCUMENT PREPARED BY: DOCUMENT CHECKED BY: DOCUMENT APPROVED BY:

Paula Freijedo Menendez J. Pierre Brachet Gilles Favre


Thierry Tardy EN-MME-FW EN-MME-FW
EN/MME-FW

 
 
BPQR N° / REFERENCE EDMS NO. REV. VALIDITY

B-2015-01 / J3022578 1512110 0.0 APPROVED

Page 2

TABLE OF CONTENTS 

GENERAL INFORMATION .............................................................................................................. 3

RECORD EBW TEST ....................................................................................................................... 3

RESULT TESTS ............................................................................................................................... 6

ANNEX (ES) ................................................................................................................................... 6

 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
BPQR N° / REFERENCE EDMS NO. REV. VALIDITY

B-2015-01 / J3022578 1512110 0.0 APPROVED

Page 3

1‐ GENERAL INFORMATION 
REFERENCE P‐WPS:  2015‐026‐FW & 2015‐027‐FW 
WELDING PROCESS:   STANDARD REFERENCE: 
ELECTRON BEAM WELDING                                              ISO 15614‐11. Specification and qualification of 
(N° 511 according to ISO 4063)  welding procedures for metallic materials‐ Welding 
procedure Test‐ Electron and laser beam welding 
WELD DATE:  24 / 02 / 2015
WELDER NAME:  Thierry Tardy  ID:  ‐‐
N° SAMPLES: 2  ID. SAMPLES: Q‐1 & Q‐1.5
MANUFACTURER: CERN‐EN/MME‐FW  NOTIFIED BODY : CERN INTERNAL QUALIFICATION
 
2‐ RECORD EBW TEST 

Equipment Type   PTR
Join type  BW
Depth of penetration  Q‐1: 1mm / Q‐1.5:1.5mm
Filler metal   N.A
Vacuum  5 x 10-4 
Welding position  PA
Other information: See p‐WPS 2015‐026‐FW & 2015‐027‐FW for welding parameters (See Annex 1) 
 
ASSEMBLY DESIGN 

Q‐1: Thickness 1mm  
Q‐1.5: Thickness 1.5mm 
 
 
 
 
 
 

BASE METALS:   

SPECIFICATION  GROUP THICKNESS  DIAMETER  CERTIFICATE      


  STANDARD or REFERENCE 
/ GRADE  ISO/TR  (mm)  (mm)  EN 10204 3.1      
CERN THECNICAL 
1.  1.4429 / 316LN  8.1  1 / 1  ‐  N°1 (Annex 2) 
SPECIFICATION Nº1002 
CERN THECNICAL 
2.  1.4429 / 316LN  8.1  1.5 / 1.5   ‐  N°2 (Annex 2) 
SPECIFICATION Nº1002 
 
BPQR N° / REFERENCE EDMS NO. REV. VALIDITY

B-2015-01 / J3022578 1512110 0.0 APPROVED

Page 4

HEAT TREATMENT:  N.A 
PROCEDURE   
PREHEAT  °C  PREHEAT    POST HEAT  POST HEAT   
TEMP  TIME TEMP TIME
PWHT MIN  °C  PWHT  °C  HEATING  °C/h COOLING RATE  °C/h
MAX  RATE 
 
CLEANING : 

CLEANING METHOD BEFORE 
Degreasing  
WELDING 

CLEANING METHOD AFTER 
‐ 
WELDING 

 
PICTURES 

 
 
 
 
 
 
 
WE CERTIFY THAT THE STATEMENT IN THIS RECORD ARE CORRECT AND THAT THE   
TESTS WELDS PREPARED, WELDED AND TESTED SATISFACTORILY IN ACCORDANCE WITH THE 
REQUERIMENTS OF ISO‐15614‐11 INDICATED ABOVE 
 
                     
 
 
 
BPQR N° / REFERENCE EDMS NO. REV. VALIDITY

B-2015-01 / J3022578 1512110 0.0 APPROVED

Page 5

3‐ RESULTS TEST 
 

ACCEPTANCE 
SEQUENCE TEST  STANDARD  RESULTS  REPORT N° 
CRITERIA 

EN ISO 13919‐1     
VISUAL INSPECTION  ISO 17637  SATISFACTORY  ‐ 
Level B 

EN ISO 13919‐1     
DYE PENETRANT  ISO 3452‐1  SATISFACTORY  ‐ 
Level B 

RADIOGRAPHIC  EN ISO 13919‐1      EDMS Nº1507381  


EN 17636‐2  SATISFACTORY 
EXAMINATION  Level B  https://edms.cern.ch/document/1507381/1 

Tensile strength of the 
specimen shall not be lower 
than the minimum value  EDMS Nº 1502555 
TENSILE TEST  SATISFACTORY 
specified for the application  https://edms.cern.ch/document/1502555/1 

indicated in CERN THECNICAL 
SPECIFICATION Nº1002 Ed.5 
Q‐1 : EDMS N°1502555 &
https://edms5.cern.ch/document/1502555/1  
METALLOGRAPHIC  EN ISO 13919‐1     
EN 17639  SATISFACTORY   Q ‐1.5 : EDMS Nº1505509 
EXAMINATION  Level B 
https://edms5.cern.ch/document/1505509/1  

 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
BPQR N° / REFERENCE EDMS NO. REV. VALIDITY

B-2015-01 / J3022578 1512110 0.0 APPROVED

Page 6

4‐ ANNEX (ES) : 
ANNEX N°1: P‐WPS 
ANNEX N°2: MATERIAL CERTIFICATES 
‐ N‐1: STAINLESS‐STEEL CERTIFICATE THICKNESS 1MM 
‐ N‐2: STAINLESS‐STEEL CERTIFICATE THICKNESS 1.5MM 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
 
Page 1 of 2 
 

                     EUROPEAN ORGANIZATION WELDING PROCEDURE  WPS No.: 2015‐026‐FW 


                     FOR NUCLEAR RESEARCH   Rev.: 0 
1211 Geneva 23 ‐ Switzerland  SPECIFICATION – EBW  Date: 25‐02‐2015 
Preliminary 
Operator: T. Tardy  Machine: PTR  Location: Building 100 
Ref. WPQR:   Ref. standard: ISO 15614‐11  Job No.: J3022578 
Client: Lees Andrew John  Project: CCC Cryostat 
PREPARATION 
Joint configuration:  Butt weld  Joint type: N.A.  Single/Double:  Single side 
Cleaning:  Welding position: PA  Backing: Yes 
JOINT SKETCH 
 

 
 
 
PARENT METAL(S) 
  Name / Grade  Standard  Group Delivery cond. Thickness (mm)  Diameter(mm)
I  316LN / 1.4429  EN 10028‐7  8.1    1  ‐ 
II  316LN / 1.4429  EN 10028‐7  8.1    1  ‐ 
FILLER METAL 
  Trade name  Classification  Group 
I  N.A.     
II       
WELDING PARAMETERS 
Working distance (mm):  400  HV (KV):    SW:  N.A.  Vacuum (mbar):  5 x 10‐4
  First pass  Second pass   Third pass 
Foc (mA)        1000 / 420     
Ibeam(mA)  7,5     
Welding speed(mm/s)  16,7     
Slope in (mm/°)  5mm     
Overlap (mm/°)  10°     
Slope out (mm/°)  5mm     
Pattern No.  1     
Frequency (Hz)  100     
Deflection 
Amplitude X   15     
Amplitude Y  0     
Frequency (Hz):  N.A     
Duty (%):  N.A     
Pulsation  Mode:  N.A     
Pulse (mA):  N.A     
Ratio:  N.A     

   
CERN  CH‐1211 Geneva 23 Switzerland    
Page 2 of 2 
 

TACKING PARAMETERS 
Foc (mA):      1000 / 420  Ibeam(mA):  7,5  Welding speed(mm/s):  16,7 
Slope in (mm/°):  5mm  Length (mm/°):   Slope out (mm/°):  5 
Deflection pattern No.:  1  Freq. (Hz):  Amplitude(mm)       X: 15          Y:0 
Pulsation freq. (Hz): N.A.  Duty (%):N.A.  Mode:  N.A  Pulse(mA): N.A  Ratio: N.A 
BEAM CALIBRATION 
IH (%):N.A.  ALIG X: N.A.  ALIG Y: N.A. 
UBIAS  (V): N.A.  STIG X: N.A.  STIG Y: N.A. 
HEAT TREATMENT 
Preheat temp.(°C): N.A.  Interpass temp.(°C): N.A.  PWHT procedure: N.A. 
ADDITIONAL COMMENTS 
 
 
 
 
 
 

ADDITIONAL INFO ENCLOSED 
 

Approved by  Date  Signature 


   
Thierry Tardy  17/03/15 
 

   
CERN  CH‐1211 Geneva 23 Switzerland    
Page 1 of 2 
 

                     EUROPEAN ORGANIZATION WELDING PROCEDURE  WPS No.: 2015‐027‐FW 


                     FOR NUCLEAR RESEARCH   Rev.: 0 
1211 Geneva 23 ‐ Switzerland  SPECIFICATION – EBW  Date: 25‐02‐2015 
Preliminary 
Operator: T. Tardy  Machine: PTR  Location: Building 100 
Ref. WPQR:   Ref. standard: ISO 15614‐11  Job No.: J3022578 
Client: Lees Andrew John  Project: CCC Cryostat 
PREPARATION 
Joint configuration:  Butt weld  Joint type: N.A.  Single/Double:  Single side 
Cleaning:  Welding position: PA  Backing: Yes 
JOINT SKETCH 
   

 
PARENT METAL(S) 
  Name / Grade  Standard  Group Delivery cond. Thickness (mm)  Diameter(mm)
I  316LN / 1.4429  EN 10028‐7  8.1    1.5  ‐ 
II  316LN / 1.4429  EN 10028‐7  8.1    1.5  ‐ 
FILLER METAL 
  Trade name  Classification  Group 
I  N.A.     
II       
WELDING PARAMETERS 
Working distance (mm):  400  HV (KV):    SW:  N.A.  Vacuum (mbar):  5 x 10‐4
  First pass  Second pass   Third pass 
Foc (mA)        1000 / 420     
Ibeam(mA)  9,5     
Welding speed(mm/s)  16,7     
Slope in (mm/°)  5mm     
Overlap (mm/°)  10°     
Slope out (mm/°)  5mm     
Pattern No.  1     
Frequency (Hz)  100     
Deflection 
Amplitude X   15     
Amplitude Y  0     
Frequency (Hz):  N.A     
Duty (%):  N.A     
Pulsation  Mode:  N.A     
Pulse (mA):  N.A     
Ratio:  N.A     

   
CERN  CH‐1211 Geneva 23 Switzerland    
Page 2 of 2 
 

TACKING PARAMETERS 
Foc (mA):     1000 / 420  Ibeam(mA):  5  Welding speed(mm/s):  16,7 
Slope in (mm/°):  5mm  Length (mm/°):   Slope out (mm/°):  5mm 
Deflection pattern No.:  1  Freq. (Hz): 100  Amplitude(mm)       X:    15       Y:  0 
Pulsation freq. (Hz): N.A.  Duty (%):N.A.  Mode:  N.A  Pulse(mA): N.A  Ratio: N.A 
BEAM CALIBRATION 
IH (%):N.A.  ALIG X: N.A.  ALIG Y: N.A. 
UBIAS  (V): N.A.  STIG X: N.A.  STIG Y: N.A. 
HEAT TREATMENT 
Preheat temp.(°C): N.A.  Interpass temp.(°C): N.A.  PWHT procedure: N.A. 
ADDITIONAL COMMENTS 
 
 
 
 
 
 

ADDITIONAL INFO ENCLOSED 
 

Approved by  Date  Signature 


   
Thierry Tardy  17/03/15 
 

   
CERN  CH‐1211 Geneva 23 Switzerland    
N-1