Scribd Logo
Upload

Welcome to Scribd!

  • 27 views

    20160401114119-6566 6569 6571 17NiCrMo64 17NiCrMoS64 20NiCrMoS64

    Uploaded by

    Önder Yontar
    This document provides material specification details for Saarstahl 17NiCrMo6-4 case hardening steel. It lists the material numbers, international grades, chemical composition ranges, typical applications, recommended heat treatment processes and temperatures, and expected mechanical properties after various treatments. The steel is suitable for forging, hot rolling, carburizing, core hardening, and case hardening to produce parts with hardness ranges from 149-255 HB depending on the treatment and diameter of the part.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    20160401114119-6566 6569 6571 17NiCrMo64 17NiCrMoS64 20NiCrMoS64

    Uploaded by

    Önder Yontar
    27 views1 page
    This document provides material specification details for Saarstahl 17NiCrMo6-4 case hardening steel. It lists the material numbers, international grades, chemical composition ranges, typical applications, recommended heat treatment processes and temperatures, and expected mechanical properties after various treatments. The steel is suitable for forging, hot rolling, carburizing, core hardening, and case hardening to produce parts with hardness ranges from 149-255 HB depending on the treatment and diameter of the part.

    Original Title

    20160401114119-6566_6569_6571_17NiCrMo64_17NiCrMoS64_20NiCrMoS64 (1)

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides material specification details for Saarstahl 17NiCrMo6-4 case hardening steel. It lists the material numbers, international grades, chemical composition ranges, typical applications, recommended heat treatment processes and temperatures, and expected mechanical properties after various treatments. The steel is suitable for forging, hot rolling, carburizing, core hardening, and case hardening to produce parts with hardness ranges from 149-255 HB depending on the treatment and diameter of the part.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    27 views1 page

    20160401114119-6566 6569 6571 17NiCrMo64 17NiCrMoS64 20NiCrMoS64

    Uploaded by

    Önder Yontar
    This document provides material specification details for Saarstahl 17NiCrMo6-4 case hardening steel. It lists the material numbers, international grades, chemical composition ranges, typical applications, recommended heat treatment processes and temperatures, and expected mechanical properties after various treatments. The steel is suitable for forging, hot rolling, carburizing, core hardening, and case hardening to produce parts with hardness ranges from 149-255 HB depending on the treatment and diameter of the part.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Material specification sheet

    Saarstahl - 17NiCrMo6-4 (18NiCrMo6-4) - 17NiCrMoS6-4 - 20NiCrMoS6-4

    Material No.: Former brand name: International steel grades:

    1.6566 BS: 17NiCrMo6-4


    1.6569 AFNOR: 17NiCrMo6-4
    1.6571 SAE:

    Material group: Case hardening steels according to DIN EN 10084

    Chemical C Si Mn P S Cr Mo Ni
    composition: 0,14 0,60 0,80 0,15 1,20
    (Typical analysis in %) <0,40 <0,035 <0,035
    0,20 0,90 1,10 0,25 1,50

    Application: Alloyed case hardening steel.

    Hot forming and Forging or hot rolling: 1100 - 850°C


    heat treatment: Normalising: 830 - 870°C
    Soft annealing: 650 - 700°C
    Carburising: 880 - 980°C
    Core hardening: 830 - 870°C
    Intermediate annealing: 650 - 700°C
    Case hardening: 780 - 820°C
    Tempering: 150 - 200°C

    Mechanical Treated for cold shearability, +S: max. 255 HB


    Properties: Soft annealed, +A: max. 229 HB
    Treated for strength, +TH: 179 - 229 HB
    Treated for ferrite and pearlite
    structure and hardness range,
    +FP: 149 - 201 HB

    after hardening and tempering at 200°C:

    Diameter d [mm] d <= 16 16 <d <= 40 40 <d <= 100

    Tensile strength Rm [N/mm²] min. 1200 min. 1000 min. 900