Chemical Composition of Deposit Metal（%） Mechanical Performance of Deposit Metal

AWS Welding Type of

Brand Name GB Impact Work Application
A5.1 Position Current Бs
C Si Mn S P Cr Ni Mo Cu БbMpa(kgf/mm2) δs(%) AKV
Mpa(kgf/mm2)
J
Welding of important low carbon steel structure and
WHJ420 E4300 F.V.OH.H AC.DC ≤0.12 ≤0.35 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 0 ≥27
high quality carbon steel pipes.
Used for welding high temperature and high
0.35-
WHJ420G E4300 F.V.OH.H AC.DC ≤0.12 ≤0.30 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 0 ≥27 pressure pipes of carbon steel used in generating
0.70
electric power.
WHJ421 E4313 E6013 F.V.OH.H AC.DC ≤0.12 ≤0.35 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 0 75 Welding of general low carbon steel structures.
WHJ421Fe16 E4324 E6024 F.HF AC.DC ≤0.12 ≤0.35 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥17 0 85 Welding of low carbon steel for shipbuilding and
other general carbon steel structures of similar
WHJ421Fe18 E4324 E6024 F.HF AC.DC ≤0.12 ≤0.35 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥17 0 90
strength.
Welding of important structures of low carbon steel
WHJ422 E4303 F.V.OH.H AC.DC ≤0.12 ≤0.25 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 0 ≥27
and low alloy steel of similar strength,
WHJ425 E4311 E6011 VD.F.OH.H AC.DC ≤0.20 ≤0.30 0.30-0.60 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 -30 ≥27 Welding of steel sheets and pipes for building.
WHJ426 E4316 E6016 F.V.OH.H AC.DC ≤0.12 ≤0.90 ≤1.25 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 -30 ≥27
WHJ426Fe E4316 E6018 F.V.OH.H AC.DC ≤0.12 ≤0.90 ≤1.25 ≤0.035 ≤0.030 ≥420(43) ≥330(34) ≥22 -30 ≥27 Welding of important structures of low carbon steel
WHJ427 E4315 E6015 F.V.OH.H DC+ ≤0.12 ≤0.90 ≤1.25 ≤0.035 ≤0.040 ≥420(43) ≥330(34) ≥22 -30 ≥27 and some low alloy steel
WHJ427Ni E4315 E6015 F.V.OH.H DC+ ≤0.12 ≤0.50 0.5-0.85 ≤0.035 ≤0.040 ≤0.70 ≥420(43) ≥330(34) ≥22 -40 ≥27
High efficient electrode for welding 16Mn and some
WHJ501Fe18 E5024 E6024 F.HF AC.DC ≤0.10 ≤0.50 ≈0.8 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥23 0 ≥47
low alloy steel structures.
Welding of 16Mn and general low alloy steel
WHJ502 E5003 F.V.OH.H AC.DC ≤0.12 ≤0.30 0.4-0.9 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥20 0 ≥27
structures of similar strength.
Welding of 16Mn and general low alloy steel
WHJ502Fe18 E5023 E7024 F.HF AC.DC ≤0.12 ≤0.90 0.50-0.90 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥17 0 90
structures of similar strength.
WHJ505 E5011 E7011 VD.F.OH.H AC.DC ≤0.20 ≤0.20 0.4-0.6 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥20 -30 ≥27 Welding of pipes of carbon steel and low alloy steel.
WHJ506 E5016 E7016 F.V.OH.H AC.DC ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27
Welding of medium carbon steel and some important
WHJ506X E5016 E7016 VD.F.OH.H AC.DC ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27
low alloy steel structures, for example 16Mn.
WHJ506H E5016-1 E7016-1 F.V.OH.H AC.DC ≤0.12 ≤0.70 ≤1.60 ≤0.035 ≤0.035 ≥490(50) ≥400(41) ≥22 -45 ≥27
WHJ506Fe E5018 E7018 F.V.OH.H AC.DC ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27 High efficient electrode for welding 16Mn and some
WHJ506Fe18 E5028 E7028 F.HF AC.DC ≤0.10 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -20 ≥27 low alloy steel structures.
WHJ507 E5015 E7015 F.V.OH.H DC+ ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27
Welding of medium carbon steel and some important
WHJ507H E5015 E7015 F.V.OH.H DC+ ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27
low alloy steel structures, for example 16Mn
WHJ507X E5015 E7015 VD.F.OH.H DC+ ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27
WHJ507Fe E5018 E7018 F.V.OH.H DC+ ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -30 ≥27 High efficient electrode for welding 16Mn and some
WHJ507Fe16 E5028 E7028 F.HF DC+ ≤0.12 ≤0.75 ≤1.60 ≤0.035 ≤0.040 ≥490(50) ≥400(41) ≥22 -20 ≥27 low alloy steel structures.