Nitoflor SL2000 constructive solutions

Flow applied, 2mm thick epoxy resin based

floor topping

Uses
Pot Life @ 250C @350C

Nitoflor SL2000 : 45 min 20 min

Nitoflor SL2000 is designed for use in wide range of industrial
environments where a lasting solution to floor maintenance Nitoprime 25 : 2-3 hours 1-1.5 hours
problems is required. It provides a dense, impervious, col-
Cure time-
oured and chemically resistant floor surface which is hygienic
Foot traffic : 24 hours 16 hours
and easy to clean. Typical applications include: Vehicular traffic : 48 hours 36 hours
Clean rooms Chemical resistance : 7 days 4 days
Laboratories Physical properties
Kitchens Mixed density : 1.72 g/cc
Plant rooms
Compressive strength
Light industrial plants @7 days (BS 6319) : 50 N/mm2 50 N/mm2

Advantages Flexural strength

@7 days (BS 6319) : 26 N/mm2 26 N/mm2
Fast application - minimises downtime
Tensile strength : 12 N/mm2 12 N/mm2
Chemically resistant - good resistance to a wide range @7 days (BS 6319)
of chemicals
Abrasion resistance : 0.1mg/ cycle-loss of
Durable - good abrasion resistance weight (ASTM D 4060)
(with CS 17 wheel of
Hygienic - provide a dense, impervious, seamless floor 1000g weight)
surface which is easily cleaned Shore D Hardness as per
(ASTM D 2240) : >75
Attractive - available in a wide range of colours to
enhance the working environment Adhesion Strength : > 1.5N/mm2
@ 7 days (ASTM D4541)
Description
Chemical Properties
Nitoflor SL2000 consists of graded aggregates bound
in a pigmented epoxy resin binder. It is supplied as a
Nitoflor SL2000 has excellent resistance at ambient tempera-
fourcomponent system, pre-weighed for on-site mixing.
tures to a wide range of industrial chemicals. Specific data
When laid, it provides a smooth, light-reflective surface. It is is available on request.
available in a range of standard colours.
Note that it is especially important that spillage is cleaned up
Specification quickly since much higher concentrations of chemicals may
Flow-applied epoxy floor topping occur on evaporation.

The designated floor areas shall be surfaced with Nitoflor Design criteria
SL2000, a 2 mm thick flow-applied epoxy resin floor topping.
The topping shall achieve a minimum compressive strength Nitoflor SL2000 is designed for application at a nominal
of 50 N/mm2 and a flexural strength of 26 N/mm2 at 7 days thickness of 2mm.
when tested to BS6319. At 250C, it shall be capable of accept-
ing foot traffic at 24 hours and vehicular traffic at 48 hours. Substrates should be dry and not suffer, or be likely to
Properties suffer, from rising damp. If necessary, suitable damp-proof
The values given below are average figures achieved in membranes should be installed during construction to prevent
laboratory tests. Actual values obtained on site may show this. Substrates should not have a relative humidity greater
minor variations from those quoted. than 75% at the time of installation.

Instructions for use

Nitoflor SL2000

Nitoflor SL2000 should be applied by specialist contractors

who must follow the procedures laid down in the Product
page 1 of 4
Nitoflor SL2000

Method Statement. Fosroc works with a network of such to the next stage. Do not proceed whilst the primer is ‘tacky’
applicators who have been trained in the correct installation as this will lead to unsightly marks on the finished surface.
procedures. The following steps are involved in the applica-
tion which would normally take place over a 2 to 3 day period Porous substrates may require a second primer coat - when
depending on the areas involved. the first coat is directly absorbed into the substrate - but
minimum overcoating times must still be observed (see table
Surface Preparation below).

It is essential that Nitoflor SL2000 is applied to sound, clean The minimum overcoating times will vary slightly according
and dry surfaces in order that maximum bond strength is to the porosity of the substrate. However, they should
achieved between the substrate and the flooring system. All be in accordance with the following ambient application
dust and debris should be removed prior to application of the temperatures.
product or its primer.
200C : 8-12 hours
New concrete floors
300C : 6-8 hours
New concrete, or cementitious substrates, should be at least
400C : 4-6 hours
28 days old and have a moisture content not exceeding 5%.
Laitance deposits on new concrete are best removed by light Mixing
grit blasting, mechanical scrabbling or grinding.
Nitoflor SL flooring is supplied in four pre-weighed packs (base,
Old concrete floors hardener, aggregate and colour pack) which are ready for
immediate on-site mixing. Part mixing of these components
Existing concrete floors which require refurbishment must
is not acceptable and will affect both performance and
be prepared to ensure a strong adhesive bond between the
appearance of the finished floor.
flooring system and the existing floor. Mechanical cleaning
methods are strongly recommended particularly where heavy Mixing should be carried out using either a forced action mixer;
contamination by oil and grease has occurred or existing or a heavy duty, slow-speed drill fitted with mixing paddle. All
coatings are present. To ensure adhesion, all contamination such equipment should be of a type and capacity approved
should be removed. by Fosroc. The components should be mixed in a suitably
sized mixing vessel.
Alternatively, blasting techniques can be used to provide the
required substrate The colour pack should be added to the base container and
mixed for 15-30 seconds, until homogeneous. Then add the
Steel surfaces
hardener and mix for further 30 seconds, until an even colour
Steel surfaces should be degreased and grit blasted to and texture is obtained.
SA2½ immediately prior to application. The prepared surface Thereafter, the contents of the graded aggregate pack should
should than be treated with one coat of Nitoprime 28. be slowly added and mixing carried out for a further 3 minutes
Priming until a completely homogenous material is obtained.

All surfaces to be treated with Nitoflor SL2000 should be primed Application

with Nitoprime 25, a solvent based epoxy resin primer designed The applicator should ensure that there are sufficient supplies
for maximum absorption and adhesion to concrete substrates. of plant, labour and materials to make the mixing and
Add the entire contents of the hardener tin to the base tin and subsequent application process a continuous one for any
mix the two primer components thoroughly for at least 2 minutes given, independent floor area.
- under no circumstances should part mixing be considered. Once mixed, the material must be used within its specified pot
life - see “Properties” section.
Once mixed, the primer should be applied immediately to
The material should be poured onto the prepared and primed
the prepared substrate using stiff brushes and/or rollers. The
substrate as soon as mixing is complete. It should be spread
primer should be well ‘scrubbed’ into the substrate to ensure
to the required thickness using a serrated trowel; with care
full coverage, but care should be taken to avoid over application
taken not to overwork the resin, spreading evenly and slowly.
or ‘ponding’.
Immediately after laying, the material should be rolled, using
a spiked nylon roller, to remove slight trowel marks, and to
Allow the primer to dry (see table below) before proceeding
assist air release. The rolling should be carried out using a

constructive solutions page 2 of 4

Nitoflor SL2000

‘back and forth’ technique along the same path. An overlap consult the local Fosroc office.
of 50% with adjacent paths is recommended. Nitoflor SL2000 should not be installed at temperatures
Further light rolling may be required to remove surface below 100C or above 450C. If in doubt, or for application
imperfections, or for subsequent release of trapped air, but outside these temperature limits, please consult your
should be prior to the setting of the product. nearest Fosroc office.

In common with all epoxy materials some light shade

Floor Joints changes may be experienced over the long term when
All existing expansion or movement joints should be followed placed in adverse exposure conditions. Any such change in
through the new floor surface. shade is not regarded as being detrimental to performance.

Estimating
Joint sealant & joint geometry should be compatible with
the floor type used, intended exposure conditions and likely Supply
movement characteristics of the substrate - consult the local
Nitoflor SL2000 : 15 litre pack
Fosroc office for more details.
(incl. colour pack)
Cleaning
Nitoprime 25 : 1 and 4 litre packs
Nitoprime 25, and Nitoflor SL2000 should be removed from Nitoflor Sol : 5 and 20 litre tins
tools and equipment with Fosroc Nitoflor Sol immediately after
use. Hardened material can only be removed mechanically. Coverage

Nitoflor SL2000 : 7.5 m2/pack @ 2 mm

Maintenance
thickness
The service life of a floor can be considerably extended by
Nitoprime 25 : 5.5 - 6.5 m2/ litre
good housekeeping. Regular cleaning may be carried out us-
ing a rotary scrubbing machine with a water miscible cleaning Note : The coverage figures given are theoretical. Due to wast-
agent at temperatures up to 500C. age factors and the variety and nature of possible substrates,
practical coverage figures will be reduced. Typically, an ad-
Technical support ditional 10% should be allowed for surface irregularities and
wastage although this will vary with site conditions.
Fosroc offers a comprehensive range of high performance,
high quality, flooring, jointing and repair products for both new Storage
and existing floor surfaces. In addition, the company offers a
Shelf life
comprehensive technical support service to specifiers, end
users and contractors. It is also able to offer on-site technical Nitoflor SL2000 has a shelf life of 12 months if kept in ware-
assistance, an AutoCAD facility and dedicated specification house conditions at 300C in the original, unopened pack.
assistance in locations all over the world.
Storage conditions

Limitations Store in dry conditions between 50C and 300C, away from
sources of heat and naked flames, in the original, unopened
Nitoflor SL2000 should not be applied on to surfaces
packs. If stored at high temperatures the shelf life will be
known to, or likely to suffer from, rising dampness, potential
reduced.
osmosis problems or have a relative humidity greater than
75% as measured in accordance with BS 8203 Appendix Precautions
A, or by protimeter. Health and safety
In areas where significant thermal shock is likely to occur,
please consult the local Fosroc office. Nitoflor SL2000, Nitoprime 25, Nitoprime 28 and Nitoflor Sol
should not come in contact with the skin and eyes, or be
Nitoflor SL2000 should not be applied to asphalt, weak or
swallowed.
friable concrete, unmodified sand/cement screeds, PVC
tiles or sheet or substrates known to move substantially
Ensure adequate ventilation and avoid inhalation of vapours.
e.g. steel walkways. For information on other substrates,
Some people are sensitive to resins, hardeners and solvents.

constructive solutions page 3 of 4

Nitoflor SL2000

Wear suitable protective clothing, gloves and eye protection. Additional information
Fosroc manufactures a wide range of complementary products
In case of contact with skin, rinse with plenty of clean water,
which include :
then cleans with soap and water. Do not use solvent. In case
of contact with eyes, rinse immediately with plenty of clean  waterproofing membranes & waterstops
water and seek medical advice. If swallowed seek medical  joint sealants & filler boards
attention immediately - do not induce vomitting.
 cementitious & epoxy grouts
Fire  specialised flooring materials
Nitoprime 25 and Nitoflor Sol are flammable. Keep away from Fosroc additionally offers a comprehensive package of prod-
sources of ignition. No smoking. In the event of fire extinguish ucts specifically designed for the repair and refurbishment
of damaged concrete. Fosroc’s ‘Systematic Approach’ to
with CO2 or foam. Do not use a water jet.
concrete repair features the following :
Nitoflor SL2000 is non-flammable.
hand-placed repair mortars
Flash points  spray grade repair mortars

Nitoprime 25 : 390C  fluid micro-concretes

 chemically resistant epoxy mortars
Nitoflor Sol : 330C
 anti-carbonation/anti-chloride protective coatings
Disposal  chemical and abrasion resistant coatings
Spillages of component products should be absorbed on to For further information on any of the above, please consult
earth, sand or other inert material and transferred to a suit- your local Fosroc office - as below.
able vessel. Disposal of such spillages or empty packaging
should be in accordance with local waste disposal regulations.

For further information, refer to the Product Material Safety

Data Sheet.

Important note :
Fosroc products are guaranteed against defective materials and manufacture and are sold
subject to its standard terms and conditions of sale, copies of which may be obtained on
request. Whilst Fosroc endeavours to ensure that any advice, recommendation specification
or information it may give is accurate and correct, it cannot, because it has no direct or
continuous control over where or how its products are applied, accept any liability either
Fosroc Chemicals directly or indirectly arising from the use of its products whether or not in accordance with
any advice, specification, recommendation or information given by it.
(India) Pvt. Ltd.
Head Office telephone fax e-mail
Embassy Point, No. 150,
2nd Floor, Infantry Road, +91 80-42521900 +91 80-22281510 [email protected]
Bangalore 560 001,
Karnataka

Regional Offices

Chennai Mumbai Noida Kolkata

Hills Centre,Old No 5, MBC Park, 12th floor, Office No.12B, Unit No. 601, Highway Tower-II 304, Jodhpur Park
New No 9, 3rd Cross Street, ‘D’ Block, Near G Corp/Hyper City A-13/2, 6th Floor, Sector– 62 Kolkata 700 068
Jeth Nagar, Raja Annamalaipuram, Kasarwadawali, Ghodbunder Road, Gautam Buddha Nagar, Ph:+91 33-65343188
Chennai 600 028. Thane (West) 400 615 Noida 201 309, Uttar Pradesh Fax: 033-2499-0280
Ph: +91 44 61304500 Ph: +91 22 6229 6800 Ph: +91 120 6121900
Fax: 022 62296809 Fax: 0120-4270622

www.fosroc.com
page 4 of 4 INDIA/2020/0513/A