Graphite Morphology: Fig. 4 Graphite Distributions Specified in ASTM A 247

There are five types of graphite distributions in gray iron (A-E) that are determined by the amount of undercooling during solidification. Type A graphite has randomly distributed flakes and optimizes mechanical properties, while Types B, D, and E form with higher undercooling and have non-random distributions. Type C graphite occurs in hypereutectic irons and appears as coarse, straight plates. The graphite distribution influences the mechanical and physical properties of gray iron.

Uploaded by

Inam Khan
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
376 views1 page

Graphite Morphology: Fig. 4 Graphite Distributions Specified in ASTM A 247

There are five types of graphite distributions in gray iron (A-E) that are determined by the amount of undercooling during solidification. Type A graphite has randomly distributed flakes and optimizes mechanical properties, while Types B, D, and E form with higher undercooling and have non-random distributions. Type C graphite occurs in hypereutectic irons and appears as coarse, straight plates. The graphite distribution influences the mechanical and physical properties of gray iron.

Uploaded by

Inam Khan
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Graphite Morphology

The mechanical and physical properties of gray iron are governed in part by the shape, size, amount, and distribution of
the graphite flakes. A method for evaluating graphite flake distribution and size is given in ASTM A 247, and the
metallography of cast irons is discussed in Ref 7, 8, 9.

There are five graphite flake distributions: A to E (Fig. 4). Type A graphite flakes are randomly distributed and oriented
throughout the iron matrix. This type of graphite is found in irons that solidify with a minimum amount of undercooling,
and type A is the structure desired if mechanical properties are to be optimized.

Type B graphite is formed in irons of near-eutectic


composition that solidify with a greater amount of
undercooling than that associated with type A graphite.
Rosettes containing fine graphite, which are characteristic
of type B, precipitate at the start of eutectic solidification.
The heat of fusion associated with their formation increases
the temperature of the surrounding liquid, thus decreasing
the undercooling and resulting in the formation of type A
graphite.

Types D and E graphite form when the amount of


undercooling is high but is not sufficient to cause carbide
formation. Both types are found in interdendritic regions.
Type D graphite is randomly distributed, while the type E
flakes have a preferred orientation. The manner in which
the plane of polish intersects the graphite flakes may be
responsible for this difference in orientation. Elements such
as titanium and aluminum have been found to promote
undercooled graphite structures. The iron matrix associated
with undercooled graphite is usually ferrite because
formation of the fine, highly branched flakes reduces
carbon diffusion distances and results in a low-carbon
matrix. Because ferrite has a lower tensile strength than
pearlite, there is a reduction in the anticipated strength of
the iron. Examples of type A, B, and D graphite found in
Fig. 4 Graphite distributions specified in ASTM A 247 commercial irons are shown in Fig. 5.

Fig. 5 Examples of type A (a), type B (b), and type D (c) graphite from foundry-produced gray irons. As-
polished. 100×

Type C graphite occurs in hypereutectic irons, particularly those with a high carbon content. Type C graphite precipitates
during the primary freezing of the iron. Kish graphite, as it is often called, appears as straight, coarse plates. It greatly