Lupox Gp1000H: Description Application

LUPOX GP1000H
Injection Molding, PBT
Description Application
High Flow, High Impact Automotive(Connector)
Properties Test Condition Test Method Unit Typical Value
Physical
Specific Gravity ASTM D792 - 1.28
Molding Shrinkage (Flow), 3.2mm ASTM D955 % 1.2 ~ 2.0
Melt Flow Rate 250℃/2.16kg ASTM D1238 g/10min 45
Mechanical
Tensile Strength, 3.2mm ASTM D638
@ Yield 50mm/min kg/cm2 480
Tensile Elongation, 3.2mm ASTM D638
@ Yield 50mm/min % -
@ Break 50mm/min % > 100
Flexural Strength, 3.2mm 2.8mm/min ASTM D790 kg/cm2 700
Flexural Modulus, 3.2mm 2.8mm/min ASTM D790 kg/cm2 20,000
IZOD Impact Strength, 3.2mm ASTM D256
(Notched) 23℃ kg·cm/cm 5.5
Thermal
Melt Temperature @ Break ASTM D3418 ℃ 225
Heat Deflection Temperature, 6.4mm ASTM D648
(Unannealed) 18.6kg ℃ 54
4.6kg ℃ 154
Flammability UL94
0.71mm class HB
1.5mm class HB
3.3mm class HB
Relative Temperature Index UL 746B
Electrical ℃ 140
Mechanical with Impact ℃ 130
Mechanical without Impact ℃ 140
Electrical
Comparative Tracking Index(CTI) Solution A IEC 60112 Volts 600
Surface Resistivity IEC 60093 Ohm -
Volume Resistivity 23℃ ASTM D257 Ohm·cm 1.0E+17
Arc Resistance 23℃ ASTM D495 sec -
Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm 23
Note) All properties, except melt flow rate are measured on injection molulded specimens and after 48 hours storage at 23℃, 50% relative humidty.
Updated : 9-Nov-09
The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee,
expressed or implied, (i) that the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG
Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the
typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the
suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to
assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use conditions. The data contained herein can be
changed without notice as a result of the quality improvement of the products.
LUPOX GP1000H
Injection Molding, PBT
Description Application
High Flow, High Impact Automotive(Connector)
Processing Guide (Injection Molding)
Processing Parameters Unit Value

Drying Temperature ℃ 100 ~ 120
Drying Time hrs 3~5
Minimum Moisture Content % 0.02
Melt Temperature ℃ 240 ~ 250
Rear ℃ 230 ~ 235
Cylinder Temperature Middle ℃ 235 ~ 245
Front ℃ 235 ~ 245
Nozzle Temperature ℃ 240 ~ 250
Mold Temperature ℃ 40 ~ 80
Back Pressure kg/cm2 -
Screw Speed rpm -
Note) Back Pressure & Screw Speed are only mentioned as general guidelines.
These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.
Updated : 9-Nov-09
The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee,
expressed or implied, (i) that the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG
Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the
typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the
suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to
assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use conditions. The data contained herein can be
changed without notice as a result of the quality improvement of the products.

Lupox Gp1000H: Description Application

Uploaded by

Copyright:

Available Formats

Lupox Gp1000H: Description Application

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Lupox Gp1000H: Description Application

Uploaded by

Copyright:

Available Formats

LUPOX GP1000H

Injection Molding, PBT

Properties Test Condition Test Method Unit Typical Value

Processing Guide (Injection Molding)

Processing Parameters Unit Value