Corning® Gorilla® Glass 6

Corning® Gorilla® Glass 6 is engineered to better survive drops from the worldwide
average height. In lab tests, it successfully survives up to 1.6-meter drops onto rough
surfaces, while still maintaining the superior scratch performance synonymous with
Gorilla® Glass. At 1.6 meters, alternative aluminosilicate and soda lime glasses didn’t
survive a single drop. Gorilla Glass 6 has up to 2x improvement in scratch performance
compared to alternative aluminosilicate.
Lorem ipsum

Product Information
Benefits Optical
• Improved drop performance, up to 1.6m Refractive Index* (590 nm)
• High resistance to scratch and sharp contact damage Core Glass 1.50
• High retained strength after use Compression Layer 1.51
• Superior surface quality Photo-elastic constant 29.8 nm/cm/MPa
Transmission
@ 0.6 mm thickness ≥ 90.5%

Applications
100

90

Ideal protective cover material for the front and back of all 80

electronic devices: 70
Wavelength Transmittance

% Transmittance
60 380 2000 ≥ 90.5%

• Smartphones • Smart Home devices 50

• Notebook PCs • Cameras 40

Corning® Gorilla® Glass 6

• Tablets • Commercial and 30

• Smartwatches Point of Sale Displays 20

and wearables
10

0
200 400 600 800 1000 1200 1400 1600 1800 2000 2200 2400

Wavelength (nm)

*Refractive index is used for FSM-based measurements since it is unaffected by

Thickness ion-exchange conditions.

Standard 0.4 mm – 0.9 mm Chemical Durability

Durability is measured via weight loss per surface area after
immersion in the solvents shown below. Values are highly
dependent upon actual testing conditions.
Viscosity Reagent Time Temperature Weight Loss
Softening Point (107.6 poises) 885 °C (°C) (mg/cm2)
Annealing Point (1013.2 poises) 624 °C
HCI – 5% 24 hrs. 95 6.7
Strain Point (1014.7 poises) 572 °C NH4F:HF – 10% 20 min. 20 1.6
HF – 10% 20 min. 20 22.7
NaOH – 5% 6 hrs. 95 2.7

Properties Electrical
Density 2.40g/cm3 Frequency (MHz) Dielectric Constant Loss Tangent
Young’s Modulus 77 GPa
Poisson’s Ratio 0.21 54 6.80 0.008
Shear Modulus 31.9 GPa 163 6.78 0.009
Vickers Hardness (200g load) 272 6.77 0.010
Unstrengthened 611 kgf/mm2 381 6.76 0.010
Strengthened 678 kgf/mm2 490 6.75 0.010
Fracture Toughness 0.70 MPa m0.5 599 6.74 0.010
Coefficient of Expansion (0-300°C) 75.2 x 10-7/°C 912 6.75 0.010
1499 6.71 0.011
1977 6.70 0.012
Chemical Strengthening 2466 6.70 0.012
Please contact a Corning Account Manager for chemical 2986 6.69 0.013
strengthening capability based on thickness and application. Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and 1355-R.
Drop Test Performance Scratch Test Performance
Face Drop on 180 grit Sandpaper We tested for scratch threshold using our Knoop Diamond Scratch Test.
with Corning® Puck, 0.8mm Glass

4.0 Competitive Al-Si Gorilla® Glass 5 Gorilla® Glass 6

Normalized Average Height to Failure (m)

(4 Newton Load) (4 Newton Load) (4 Newton Load)

3.5

3.0

2.5

2.0

1.5

1.0

0.5

0
Competitive Al-Si Gorilla® Glass 5 Gorilla® Glass 6

Always Tough. Always Innovating.

Corning® Gorilla® Glass 6