    Department of Structural Engineering: M B M Engineering College

    Uploaded by

    Ajayvidyanand Sharma
    The document contains test results from a structural engineering department for reinforcement steel bars of various diameters (10 mm, 12 mm, 16 mm, 20 mm). Tension, cold bend, and unit weight tests were performed according to relevant Indian standards. For each diameter and test, three samples were tested and the results such as yield strength, ultimate tensile strength, and unit weight were reported and found to meet the IS standard requirements. The tests indicate that the steel bars conform to specifications and can be used for reinforcement.

    Copyright:

    © All Rights Reserved
    Download as DOC, PDF, TXT or read online from Scribd

    Department of Structural Engineering: M B M Engineering College

    Uploaded by

    Ajayvidyanand Sharma
    58 views4 pages
    The document contains test results from a structural engineering department for reinforcement steel bars of various diameters (10 mm, 12 mm, 16 mm, 20 mm). Tension, cold bend, and unit weight tests were performed according to relevant Indian standards. For each diameter and test, three samples were tested and the results such as yield strength, ultimate tensile strength, and unit weight were reported and found to meet the IS standard requirements. The tests indicate that the steel bars conform to specifications and can be used for reinforcement.

    Original Title

    Report PWD Barmer.doc

    Copyright

    © © All Rights Reserved

    Available Formats

    DOC, PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document contains test results from a structural engineering department for reinforcement steel bars of various diameters (10 mm, 12 mm, 16 mm, 20 mm). Tension, cold bend, and unit weight tests were performed according to relevant Indian standards. For each diameter and test, three samples were tested and the results such as yield strength, ultimate tensile strength, and unit weight were reported and found to meet the IS standard requirements. The tests indicate that the steel bars conform to specifications and can be used for reinforcement.

    Copyright:

    © All Rights Reserved
    Download as DOC, PDF, TXT or read online from Scribd
    Download as doc, pdf, or txt
    58 views4 pages

    Department of Structural Engineering: M B M Engineering College

    Uploaded by

    Ajayvidyanand Sharma
    The document contains test results from a structural engineering department for reinforcement steel bars of various diameters (10 mm, 12 mm, 16 mm, 20 mm). Tension, cold bend, and unit weight tests were performed according to relevant Indian standards. For each diameter and test, three samples were tested and the results such as yield strength, ultimate tensile strength, and unit weight were reported and found to meet the IS standard requirements. The tests indicate that the steel bars conform to specifications and can be used for reinforcement.

    Copyright:

    © All Rights Reserved
    Download as DOC, PDF, TXT or read online from Scribd
    Download as doc, pdf, or txt
    of 4

    DEPARTMENT OF STRUCTURAL ENGINEERING

    M B M ENGINEERING COLLEGE
    FACULTY OF ENGINEERING & ARCHITECTURE, JAI NARAIN VYAS UNIVERSITY, JODHPUR
    No. JNVU/FE/PSE/2019-20/ 1109 Date: 2/9/2020
    To,
    Executive Engineer,
    Public Works Department,
    Dn Gudamalani, Barmer.
    Sub: Testing Report of Reinforcement Steel Bars of 10 mm (JSW NEO STEEL 500D)
    Ref: Your Letter No. 591 dated 26.8.2020
    Sir,
    The sample received by the party, has been tested in the laboratory as per relevant IS and the following results have been found:
    TENSION TEST
    S. No. Nominal Nominal Gauge length 0.2 % Proof Ultimate Stress % Remarks
    Dia. (mm) Area (mm2) (mm) Stress (N/mm2) (N/mm2) Extension
    1 10 74.53 50 525.40 626.90 22.0 Star fracture
    2 10 74.48 50 531.73 639.27 24.0 Partial cup and cone fracture
    3 10 75.37 50 525.45 637.63 22.0 Partial cup and cone fracture
    COLD BEND TEST
    S. No. Nominal Dia. (mm) Remarks
    1 10 No cracks on the external surface of U-Bend
    2 10 No cracks on the external surface of U-Bend
    3 10 No cracks on the external surface of U-Bend
    UNIT WEIGHT TEST
    S. No. Nominal Dia. (mm) Length (mm) Weight (kg) Unit Weight (kg/m) IS: 1786Value (kg/m)
    1 10 1005 588 0.610 0.617
    2 10 1004 587 0.608 0.617
    3 10 1004 594 0.612 0.617

    COUNTERSIGNED

    (Dr. Ajay Sharma) (Dr. Archana Bohra Gupta)


    Testing Incharge Testing Incharge
    (Dr. Ajay Sharma)
    HEAD
    DEPARTMENT OF STRUCTURAL ENGINEERING
    M B M ENGINEERING COLLEGE
    FACULTY OF ENGINEERING & ARCHITECTURE, JAI NARAIN VYAS UNIVERSITY, JODHPUR
    No. JNVU/FE/PSE/2019-20/ 1109 Date: 2/9/2020
    To,
    Executive Engineer,
    Public Works Department,
    Dn Gudamalani, Barmer.
    Sub: Testing Report of Reinforcement Steel Bars of 12 mm (JSW NEO STEEL 500D)
    Ref: Your Letter No. 591 dated 26.8.2020
    Sir,
    The sample received by the party, has been tested in the laboratory as per relevant IS and the following results have been found:
    TENSION TEST
    S. No. Nominal Nominal Gauge length 0.2 % Proof Ultimate Stress % Remarks
    2 2 2
    Dia. (mm) Area (mm ) (mm) Stress (N/mm ) (N/mm ) Extension
    1 12 112.36 60 506.92 633.65 23.33 Partial cup & cone fracture
    2 12 111.59 60 514.41 638.02 21.67 Star fracture
    3 12 112.61 60 509.75 632.24 21.67 Star fracture
    COLD BEND TEST
    S. No. Nominal Dia. (mm) Remarks
    1 12 No cracks on the external surface of U-Bend
    2 12 No cracks on the external surface of U-Bend
    3 12 No cracks on the external surface of U-Bend
    UNIT WEIGHT TEST
    S. No. Nominal Dia. (mm) Length (mm) Weight (kg) Unit Weight (kg/m) IS: 1786Value (kg/m)
    1 12 1001 0.883 0.882 0.888
    2 12 1000 0.876 0.876 0.888
    3 12 1005 0.888 0.884 0.888

    COUNTERSIGNED

    (Dr. Ajay Sharma) (Dr. Archana Bohra Gupta)


    Testing Incharge Testing Incharge
    (Dr. Ajay Sharma)
    HEAD
    DEPARTMENT OF STRUCTURAL ENGINEERING
    M B M ENGINEERING COLLEGE
    FACULTY OF ENGINEERING & ARCHITECTURE, JAI NARAIN VYAS UNIVERSITY, JODHPUR
    No. JNVU/FE/PSE/2019-20/ 1109 Date: 2/9/2020
    To,
    Executive Engineer,
    Public Works Department,
    Dn Gudamalani, Barmer.
    Sub: Testing Report of Reinforcement Steel Bars of 16 mm (JSW NEO STEEL 500D)
    Ref: Your Letter No. 591 dated 26.8.2020
    Sir,
    The sample received by the party, has been tested in the laboratory as per relevant IS and the following results have been found:
    TENSION TEST
    S. No. Nominal Nominal Gauge length 0.2 % Proof Ultimate Stress % Remarks
    2 2 2
    Dia. (mm) Area (mm ) (mm) Stress (N/mm ) (N/mm ) Extension
    1 16 190.19 80 514.73 631.71 23.75 Partial cup & cone fracture
    2 16 190.70 80 518.01 634.69 22.50 Star fracture
    3 16 194.33 80 510.63 627.41 22.50 Star fracture
    COLD BEND TEST
    S. No. Nominal Dia. (mm) Remarks
    1 16 No cracks on the external surface of U-Bend
    2 16 No cracks on the external surface of U-Bend
    3 16 No cracks on the external surface of U-Bend
    UNIT WEIGHT TEST
    S. No. Nominal Dia. (mm) Length (mm) Weight (kg) Unit Weight (kg/m) IS: 1786Value (kg/m)
    1 16 1000 1.493 1.572 1.580
    2 16 1000 1.497 1.578 1.580
    3 16 1001 1.527 1.570 1.580

    COUNTERSIGNED

    (Dr. Ajay Sharma) (Dr. Archana Bohra Gupta)


    Testing Incharge Testing Incharge
    (Dr. Ajay Sharma)
    HEAD
    DEPARTMENT OF STRUCTURAL ENGINEERING
    M B M ENGINEERING COLLEGE
    FACULTY OF ENGINEERING & ARCHITECTURE, JAI NARAIN VYAS UNIVERSITY, JODHPUR
    No. JNVU/FE/PSE/2019-20/ 1109 Date: 2/9/2020
    To,
    Executive Engineer,
    Public Works Department,
    Dn Gudamalani, Barmer.
    Sub: Testing Report of Reinforcement Steel Bars of 20 mm (JSW NEO STEEL 500D)
    Ref: Your Letter No. 591 dated 26.8.2020
    Sir,
    The sample received by the party, has been tested in the laboratory as per relevant IS and the following results have been found:

    TENSION TEST
    S. No. Nominal Nominal Gauge length 0.2 % Proof Ultimate Stress % Remarks
    2 2 2
    Dia. (mm) Area (mm ) (mm) Stress (N/mm ) (N/mm ) Extension
    1 20 313.53 100 510.93 617.55 20.0 Shear fracture
    2 20 312.81 100 512.11 625.91 22.0 Star fracture
    3 20 312.72 100 505.14 628.94 21.0 Star fracture
    COLD BEND TEST
    S. No. Nominal Dia. (mm) Remarks
    1 20 No cracks on the external surface of U-Bend
    2 20 No cracks on the external surface of U-Bend
    3 20 No cracks on the external surface of U-Bend
    UNIT WEIGHT TEST
    S. No. Nominal Dia. (mm) Length (mm) Weight (kg) Unit Weight (kg/m) IS: 1786Value (kg/m)
    1 20 1006 2.476 2.461 2.470
    2 20 1001 2.458 2.466 2.470
    3 20 1007 2.472 2.465 2.470

    COUNTERSIGNED

    (Dr. Ajay Sharma) (Dr. Archana Bohra Gupta)


    Testing Incharge Testing Incharge

    (Dr. Ajay Sharma)


    HEAD