    This document provides technical information about ELIX ULTRA HH 4115 PG, an ABS plating grade resin. It has very high heat resistance and impact strength, even at low temperatures. The resin has good flowability, dimensional precision, and low shrinkage. It has lower density than PC/ABS. The resin is an acrylonitrile-butadiene-styrene copolymer modified with polycarbonate and poly(styrene-co-maleimide). Typical properties include a melt flow rate of 3 g/10min at 230°C, tensile strength of 5650 psi, and notched impact strength of 27.7 ft-lb/in2 at 73°F.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Elix Ultra hh4115

    Uploaded by

    DiegoTierradentro
    57 views3 pages
    This document provides technical information about ELIX ULTRA HH 4115 PG, an ABS plating grade resin. It has very high heat resistance and impact strength, even at low temperatures. The resin has good flowability, dimensional precision, and low shrinkage. It has lower density than PC/ABS. The resin is an acrylonitrile-butadiene-styrene copolymer modified with polycarbonate and poly(styrene-co-maleimide). Typical properties include a melt flow rate of 3 g/10min at 230°C, tensile strength of 5650 psi, and notched impact strength of 27.7 ft-lb/in2 at 73°F.

    Original Title

    elix ultra hh4115

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides technical information about ELIX ULTRA HH 4115 PG, an ABS plating grade resin. It has very high heat resistance and impact strength, even at low temperatures. The resin has good flowability, dimensional precision, and low shrinkage. It has lower density than PC/ABS. The resin is an acrylonitrile-butadiene-styrene copolymer modified with polycarbonate and poly(styrene-co-maleimide). Typical properties include a melt flow rate of 3 g/10min at 230°C, tensile strength of 5650 psi, and notched impact strength of 27.7 ft-lb/in2 at 73°F.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    57 views3 pages

    Elix Ultra hh4115

    Uploaded by

    DiegoTierradentro
    This document provides technical information about ELIX ULTRA HH 4115 PG, an ABS plating grade resin. It has very high heat resistance and impact strength, even at low temperatures. The resin has good flowability, dimensional precision, and low shrinkage. It has lower density than PC/ABS. The resin is an acrylonitrile-butadiene-styrene copolymer modified with polycarbonate and poly(styrene-co-maleimide). Typical properties include a melt flow rate of 3 g/10min at 230°C, tensile strength of 5650 psi, and notched impact strength of 27.7 ft-lb/in2 at 73°F.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 3

    Technical Information

    ELIX ULTRA HH 4115 PG


    Very high heat resistance ABS plating grade

    ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20

    Major Benefits

    . Extreme impact resistance with low temperature ductility


    . Very high impact up to -30ºC
    . Well balanced flowability, heat resistance and flexibility
    . Low emission and odor grade
    . Lower mould deposits in injection molding processing applications
    . Good dimensional precision, low shrinkage and CLTE.
    . Lower density than PC/ABS

    Chemical composition

    Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and


    poly(styrene-co-maleimide)

    Physical form

    White to slightly yellowish pellets.

    Handling information

    Please see the Material Safety Data Sheet for relevant health & safety information.

    Page 1 of 3
    Technical Information

    Typical properties1

    Property Test Standard Unit Value Unit Value


    Condition
    SI Metrics US Conventional
    Rheological properties
    Melt volume-flow rate 260°C, 5kg ISO 1133 cm3/10min 14
    Melt flow rate 230°C, 3.8kg ASTM D1238 g/10min 3

    Molding shrinkage, parallel 60x60x2 mm ISO 294-4 % 0.65-0.75


    Molding shrinkage, normal 60x60x2 mm ISO 294-4 % 0.65-0.75
    Mechanical properties (23ºC /50% H.R.)
    Yield stress 50 mm/min ISO 527-1,2 MPa 42
    5 mm/min ASTM D 638 MPa 39 psi 5650
    Strain at yield 5mm/min ISO 527-1,2 % 7
    Strain at break 50 mm/min ISO 527-1,2 % 53
    5 mm/min ASTM D 638 % 53
    Tensile modulus 1 mm/min ISO 527-1,2 MPa 2000
    5 mm/min ASTM D 638 psi 290000
    Flexural modulus 2 mm/min ISO 178 MPa 2000
    1.3 mm/min ASTM D 790 psi 290000
    Flexural strength 2 mm/min ISO 178 MPa 68 psi 9850
    Izod notched impact strength 23 ºC (73ºF) ISO 180-1A kJ/m2 58 ft-lb/in2 27.7
    -30 ºC (-22ºF) ISO 180-1A kJ/m2 41 ft-lb/in2 19.6
    ASTM D 256
    73ºF (23ºC) (3.2mm) 1/8” J/m 780 ft-lb/in 14.6
    ASTM D 256
    73ºF (23ºC) (6.4mm) 1/4” J/m 565 ft-lb/in 10.6
    ASTM D 256
    -22ºF (-30ºC) (3.2mm) 1/8” J/m 505 ft-lb/in 9.4
    Charpy notched impact strength 23 ºC (73ºF) ISO 179-1eA kJ/m2 53 ft-lb/in2 25.3
    -22ºF (-30ºC) ISO 179-1eA kJ/m2 40 ft-lb/in2 19.1
    Ball indentation hardness ISO 2039-1 N/mm2 90
    Thermal properties
    Vicat softening temperature B50;50ºC/h ISO 306 ºC 113
    50N;50ºC/h ASTM D 1525 ºF 235
    B120;120ºC/h ISO 306 ºC 115 ºF 239
    Deflection temperature under load* 1.80 MPa ISO 75-1,2 ºC 101 ºF 214
    Deflection temperature under load* 0.45 MPa ISO 75-1,2 ºC 113 ºF 235
    CLTE, parallel 23 to 55ºC ISO 11359 -1,2 10-4/K 0.89
    Burning behavior UL 94 1.6 mm UL 94 Class HB
    Burning rate (US-FMVSS) 200x105x2mm ISO 3795 mm/min < 40 in/min < 1.6
    Other properties (23ºC)
    Density 25ºC ISO 1183-1 g/cm3 1.07 lb/in3 0.0386

    Processing conditions for test specimens


    Injection molding-melt temperature ISO 294 ºC 240 ºF 464
    Injection molding-mold temperature ISO 294 ºC 70 ºF 158
    Injection molding-injection velocity ISO 294 mm/s 240 in/s 9.5

    *(annealed 4h/80ºC; 4h/176ºF)

    Notes : 1.control measurements in other places may issue different results due to influences of machinery, equipment,
    test method or storage conditions.

    Page 2 of 3
    Technical Information

    Disclaimer for sales products


    Disclaimer for sales products
    This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without
    warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the
    obligation to verify the information currently provided ʹespecially that contained in our safety data and technical information
    sheetsʹ and to test our products as to their suitability for the intended processes and uses. The application, use and processing of
    our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore,
    entirely your own responsibility. Our products are sold and our advisory service is given in accordance with the current version of
    our General Conditions of Sale and Delivery.

    Test values
    Unless specified to the contrary, the values given have been established on standardised test specimens at room temperature. The
    figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the
    properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the colouring.

    Processing note
    Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To
    preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be
    ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In
    order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed
    processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of
    operator error or defects in the heating system, special care and controls are essential in these areas.