FLEXcon® FLEXmount® L-344/V-344 Series Adhesive

Product Description
FLEXcon’s general purpose adhesive. This permanent acrylic adhesive offers high shear and excellent
adhesion to metals, and high-surface energy plastics.

Product Adhesive Thickness Adhesive Color

FLEXmount® TT 200 L-344/V-344 2.0 Clear

FLEXmount® TT 400 L-344/V-344 4.0 Clear

Performance Benefits
• L/V-344 adheres to metal and high-energy surfaces.
• The adhesive performs within a wide service temperature range of -40°F to 302°F (-40°C to 150°C).
• Available on transfer tapes, double-coated products and decal stock.
• Adhesive thickness, liners, films and topcoats can be customized to comply with different converting,
assembly and end-use requirements.

Certification Recognition
• ISO 9001:2008 Certified Manufacturer
• UL Recognized

Finishing Options
Master Log rolls can be cut to meet the needs of your manufacturing process or end use requirements.
Roll sizes start at 1". For custom finishing, standard charges apply.

Product Technical Data


Expected Exterior Life Dependant on life of substrate; adhesive is suitable for outdoor applications

Service Temperature Range -40°F to 302°F (-40°C to 150°C)

Minimum Application Temperature 50°F (10°C)

Storage Stability Two years stored at 70°F (21°C) and 50% RH


FLEXcon® FLEXmount® L-344/V-344 Adhesive Series

Product Technical Data


Thickness
Adhesive (+/- 10%) 1.9-2.1 (48-53) +/-0.1 (3) ASTM D 3652
(Mils [Microns])

Average Average Average


15 min 3 days RT 3 days 160°F
ASTM D 3330
Oz/in (N/m) Oz/in (N/m) Oz/in (N/m) (Modified for dwell time)
Peel Average
90° angle 12”/min Acrylic - - 71 (781) - -
(All peels laminated
Glass - - 64 (704) - - to 2 mil foil)
Polypropylene - - 26 (286)
Stainless Steel 47 (517) 69 (759) 109 (1199)

2.0 mil Clear Polyester 2.0 mil Aluminum Foil ASTM D 3654
Expected Shear
(1 hr. dwell, 1 sq. in. surface,
(hours) 20 25 4 lb. load)

2.0 mil Clear Polyester 2.0 mil Aluminum Foil


Method A
Tack (gm)
ASTM D 2979
920 950

Thickness
Adhesive (+/- 10%) 3.9-4.1 (99-104) +/-0.2 (5) ASTM D 3652
(Mils [Microns])

Average Average Average


15 min 3 days RT 3 days 160°F
ASTM D 3330
Oz/in (N/m) Oz/in (N/m) Oz/in (N/m) (Modified for dwell time)
Peel Average
90° angle 12”/min Acrylic - - 92 (1012) - -
(All peels laminated
Glass - - 76 (836) - - to 2 mil foil)
Polypropylene - - 33 (363)
Stainless Steel 62 (682) 87 (957) 131 (1441)

4.0 mil Clear Polyester 4.0 mil Aluminum Foil ASTM D 3654
Expected Shear
(1 hr. dwell, 1 sq. in. surface,
(hours) 20 4 4 lb. load)

4.0 mil Clear Polyester 4.0 mil Aluminum Foil


Method A
Tack (gm)
ASTM D 2979
1350 1030

Product Technical Data: Humidity Resistance


Adhesive on PM 200 Clear film 90° angle 12”/min
7 days + 24 hour recovery
2 mil Clear Polyester

Adhesion Retention All testing on SS panel at 100°F


and 95% RH. 24 hour dwell time
No visual change, 90% adhesion gain
on SS panel before humidity
exposure.

Product Technical Data: Chemical Resistance


Adhesive on PM 200 Clear film
Solvent
2.0 mil clear polyester 90° angle 12”/min
1 hour at RT in Gasoline (unleaded) Edge penetration 15% adhesion loss with 24 hour recovery

Adhesion Retention 1 hour at RT in MEK (Methyl Ethyl Ketone) Edge penetration 15% adhesion loss
All testing on SS panel at
72 hours at 120°F (49°C) in Oil (SAE 10w-30) No visual change, 20% adhesion gain 24 hour dwell time before
72 hours at RT in Salt Water (6% by weight) No visual change, 65% adhesion gain immersion.

100 hours at RT in Water No visual change, 55% adhesion gain


FLEXcon® FLEXmount® L-344/V-344 Adhesive Series

Product Technical Data: UL Surface Test Results

Additional Conditions

Additional Conditions
Stock Thickness (mm)

Polyester Face Stock


Temperature Range

Temperature Range
Polycarbonate Face

Application Use

Application Use
Thickness (mm)
Application Surface

Acrylic Paint (AC PT) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 125°C to -40°C O
Acrylic Powerderd Pain (AC PDR PT) .075-.508 I/O 80°C to -40°C D/O
Acrylonitrile Butadiene Styrene (ABS) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 80°C to -40°C O
Alkyd Paint (AK PT) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 125°C to -40°C O
Aluminum (AL) .075-.508 I/O 100°C to -40°C D/O .025-.127 I/O 150°C to -40°C O
Epoxy Paint (RP PT) .075-.508 I/O 80°C to -40°C D/O
Epoxy Powder Paint (RP PDR PT) .075-.508 I/O 80°C to -40°C D/O
Galvanized Steel (GS) .075-.508 I/O 100°C to -40°C D/O .025-.127 I/O 125°C to -40°C
Melamine (ME) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 80°C to -40°C
Nylon - Polyamide (PA) .075-.508 ® I/O 80°C to -40°C D/O .025-.127 I/O 80°C to -40°C O
FLEXmount L-778/V-778 Series
Phenolic - Phenol Formaldehyde (PH) .075-.508 I/O 80°C to -40°C D/O
Polycarbonate (PC)
Adhesive .025-.127 I/O 80°C to -40°C
Polyester Paint (PER PT) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 125°C to -40°C O
Polyester Powder Paint (PER PDR PT) .075-.508 I/O 80°C to -40°C D/O
Polypropylene (PP) .075-.508 I/O 80°C to -40°C D/O .025-.127 I 80°C O
Polystyrene (PS) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 60°C to -40°C
Polyurethane Paint (PUR PT) .075-.508 I/O 80°C to -40°C D/O
Polyurethane Powder Paint (PUR PDR PT) .075-.508 I/O 80°C to -40°C D/O
Porcelain (PRCLN) .025-.127 I/O 125°C to -40°C
Stainless Steel (SS) .075-.508 I/O 100°C to -40°C D/O .025-.127 I/O 125°C to -40°C
Unsaturated Polyester - Thermoset (UP) .075-.508 I/O 80°C to -40°C D/O .025-.127 I/O 80°C to -40°C

Product Technical Data: Ink Adhesion


Thickness (mm)

Indoor Use (Ink


Temperature

Outdoor Use
Regulation

Conditions
Additional
(Ink Color)
Facestock

Facestock
Ink series

Printing
Process
UL/CUL

Range

Color)

Sericol “GSO” Series Polycarbonate .003 - .020 UL Screen -40°C to 100°C All All O, D

Application Use Additional Conditions Key USR Standard- UL 969

D= Occasional exposure to Detergents UL- PGGU2.MH10170; UL - PGJI2.MH16635


F2= Occasional exposure to Fuel Oil #2 CUL - PGJI8.MH16635; CUL-PGG48.MH10170
I= Indoor, O= Outdoor
G= Occasional exposure to Gasoline (splashing)
I/O= Indoor and Outdoor
K= Occasional exposure to Kerosene
All tests performed on 1 to 4 mil transfer tapes
O= Occasional exposure to lubricating oils
Standard Differential and Double-Faced Release Liners
200 Poly LA, Poly C2S
2.0 mil (52 microns) clear polyester liner is smooth for uniform adhesive wet-out. Conforms to tight angles and
works well for automated assembly and robotic application. Ideal for roll-to-roll or roll-to-sheet.
Master Width 60"
55 LA K, 55 D/F K
3.2 mil (81 micron) white densified 55 lb. kraft liner for roll-to-roll converting. Ideal for rotary diecutting. Typical
end-use applications include automotive underhood and safety/hazard and warning labels.
Master Width 60"
60 LA PFW, 60 D/F PFW
4.3 mil (109 micron) white polycoated 60 lb. layflat liner for roll-to-roll or roll-to-sheet converting. Provides excellent
moisture stability for sheet processing. Typical end-use applications include graphic overlays.
Master Width 54" & 60"
84 LA PFT, 84 D/F PFT
6.4 mil (163 micron) tan polycoated 84 lb. layflat liner for roll-to-sheet converting. Ideal for kiss-cutting end tabs and
nameplates. Typical end-use applications include thin and rigid nameplates.
Master Width 54" & 60"

Application Techniques
When applying pressure-sensitive adhesives it is necessary to provide pressure during lamination. Starting at the
top peel back a 1” section of the release liner, align and apply. Using a plastic squeegee, stiff cardboard, or a soft
cloth will help provide the necessary pressure at the point of lamination. Continue removing the release liner and
smooth out with the squeegee. Heat can increase bond strength when bonding to metal parts (generally this same
increase is observed at room temperature over longer times, weeks). For plastic parts, the bond strength is not
enhanced with the addition of heat.

For best results, the application surface and the surrounding ambient atmosphere should be 50°F (10°C) or above.
If applying the adhesive below 50°F (10°C), the application surface should be cleaned with isopropyl alcohol
(rubbing alcohol) to insure good initial adhesion.

When bonding a thin, smooth, flexible material to a smooth surface, it is generally acceptable to use 2 mils of
adhesive. If a texture is visible on one or both surfaces, the 4 mil adhesive would be suggested. If both materials are
rigid, it may be necessary to use a thicker adhesive to successfully bond the components.

Product Performance and Suitability


All of the descriptive information, the typical performance data, and recommendations for the use of FLEXcon
products shall be used only as a guide and do not reflect the specification or specification range for any particular
property of the product. Furnishing such information is merely an attempt to assist you after you have indicated
your contemplated use and shall in no event constitute a warranty of any kind by FLEXcon. All purchasers of
FLEXcon products shall be responsible for independently determining the suitability of the material for the purpose
for which it is purchased. No distributor, salesman, or representative of FLEXcon is authorized to give any warranty,
guaranty, or make any representation in addition or contrary to the above.

5/30/2017

FLEXcon Company, Inc. • 1 FLEXcon Industrial Park • Spencer, MA 01562-2642 • T 508.885.8200 • F 508.885.8400